CN109468881A - A method of improving stone paper packaging material printing quality - Google Patents
A method of improving stone paper packaging material printing quality Download PDFInfo
- Publication number
- CN109468881A CN109468881A CN201811382424.3A CN201811382424A CN109468881A CN 109468881 A CN109468881 A CN 109468881A CN 201811382424 A CN201811382424 A CN 201811382424A CN 109468881 A CN109468881 A CN 109468881A
- Authority
- CN
- China
- Prior art keywords
- stone paper
- coupling agent
- silane coupling
- packaging material
- printing quality
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of methods for improving stone paper packaging material printing quality, include the following steps: (1) removal of impurities processing, the processing of (2) atomized spray, (3) drying process, (4) corona treatment, (5) storage processing.The present invention has carried out special processing to stone paper packing material, it will be apparent that improves it and prints processing performance, the precision of printing is good, condition is high, quality is stable, the great market competitiveness and application value.
Description
Technical field
The invention belongs to printing technologies, and in particular to a method of improve stone paper packaging material printing quality.
Background technique
Stone paper, is also Shi Kezhi, and stone paper new technology is based on mineral resources calcium carbonate the most abundant in the earth's crust
Raw material is wanted, using high molecular material and a variety of inorganic matters as auxiliary material, utilizes the macromolecule interfacial principles of chemistry and filling-modified skill
Art is recycled through a kind of invertibity that special process is process, and has the characteristics that the novel papermaking technology of modern technologies.By
After trapezoidal milling machining, the calcium carbonate in lime stone is extracted, ore is then worn into high calcium by SCM superfine mill
The superfine powder of 1500-2500 mesh then carries out second operation work, and mother is made in the additive that 85% modified calcium carbonate adds upper 15%
Paper or bag is made finally by film blowing device is squeezed in grain.
For stone paper compared with traditional wood pulp paper, stone paper has its unique advantage, and this kind of paper production not cut down tree
Wood, the not discharge of waste water and gas is more more smooth than traditional paper, it had not only promoted the transition of traditional paper-making industry but also had promoted
The upgrading of chemical industry, in the following under cover huge business opportunity.In terms of printing production: stone paper is because of its stiffness, absorbency
More there is superiority than conventional paper, the printing effect that it is presented prints more aobvious solid layer feeling than traditional paper, and stone paper is wide at present
It is general to be useful in gift box, cosmetic container, packing case, handbag production, printed design, poster publicity, publicity specification, map, do not do
Glue, drop production, the industry being related to also embrace a wide spectrum of ideas.But at present but there is printing figure in the printed matter made of stone paper
The problems such as text is apprehensive, color saturation is bad, and affect the further expansion application of stone paper.
Summary of the invention
The purpose of the present invention is being directed to existing problem, a kind of side for improving stone paper packaging material printing quality is provided
Method.
The present invention is achieved by the following technical solutions:
A method of stone paper packaging material printing quality is improved, is included the following steps:
(1) removal of impurities is handled:
Air-blowing processing is carried out with surface of the compressed air to stone paper, with remaining granule foreign standby in air removal stone paper
With;
(2) atomized spray is handled:
After step (1) treated stone paper tiling is put well, recycle atomized spray equipment by the water-soluble liquid mist of silane coupling agent
Change is sprayed on the surface of stone paper;
(3) it is dried:
By step (2), treated that stone paper is put into vacuum oven is dried, and the water content of stone paper is done
It is dry spare to taking out after 5 ~ 7%;
(4) corona treatment:
By step (3), treated, and stone paper is put into plasma processing apparatus, and the voltage for controlling electric discharge is 4 ~ 4.5kV,
Electric current is 35 ~ 40mA, and frequency is 18 ~ 20kHz, is taken out stone paper after 2 ~ 3min of processing spare;
(5) storage is handled:
By step (4), treated that stone paper is put into takes out and can carry out at printing after 5 ~ 7h of storage processing in nitrogen environment
Reason.
Further, control pressure is 0.4 ~ 0.45MPa when air-blowing as described in step (1) is handled.
Further, in silane coupling agent aqueous solution described in step (2) silane coupling agent volume fraction be 20 ~
25%;The silane coupling agent is silane coupling agent kh550, silane coupling agent kh560, any in silane coupling agent kh570
It is a kind of;The atomized spray amount of the silane coupling agent aqueous solution is the 22 ~ 26% of stone paper gross mass.
Further, it is 1 ~ 10Pa, temperature that the air pressure in vacuum oven is controlled when drying process described in step (3)
It is 70 ~ 75 DEG C.
Further, it is air that atmosphere is controlled when corona treatment described in step (4).
Further, its electrode discharge form is that dielectric impedance corona is put when corona treatment described in step (4)
Electricity, block media select aluminium oxide ceramics.
Further, the temperature control of nitrogen environment described in step (5) is 22 ~ 25 DEG C, relative humidity is 60 ~ 65%.
The present invention has carried out special working process to stone paper, effectively improves its printing using quality, improves
Its application value eliminates most defect problems of existing stone paper.Wherein, removal of impurities processing first is carried out to stone paper, blown away
The little particles impurity such as raw material on stone paper surface is convenient for subsequent processing, atomized spray processing has then been carried out, by silane
Coupling agent aqueous solution atomized spray, so that silane coupling agent has been immersed in stone paper, changes carbon on the surface of stone paper
The surface-active of the matrixes such as sour calcium, resin, especially optimizes the surface property of resin matrix, when common printed processing, because of tree
Affinity is not strong between aliphatic radical body and ink, and the part colours for being easy to cause surface resin matrix to be printed are not deep, persistence is not high,
And its affinity is able to promote improvement after treatment;And it equally will affect in calcium carbonate there is also certain impurity component
The effect of printing, this measure equally enhance its printable processing performance;It is then dried, with vacuum drying treatment
Mode can remove excessive moisture, and can guarantee the physical and chemical performance for not damaging paper, then carry out corona treatment, although
Silane coupling agent can improve the surface-active of calcium carbonate, but part silane coupling agent can be in calcium carbonate after atomized spray processing
Surface filming, transition have wrapped the surface of calcium carbonate, cause subsequent printing ink to penetrate into and combine the problems such as ineffective, this progress
Corona treatment the overlay film of silane coupling agent can be abolished, improve the specific surface area of calcium carbonate, while can also be to carbon
The type and content that sour calcium carries out surface active groups are enhanced, so that calcium carbonate is adsorbing fixed ink with General Physics
While, also there is the performance for being chemically crosslinked fixed ink well, further ensure whole printing effect;Finally carry out
Storage processing, is conducive to the stabilization of stone paper surface property.
The present invention has the advantage that compared with prior art
The present invention has carried out special processing to stone paper packing material, it will be apparent that improves it and prints processing performance, printing
Precision it is good, condition is high, quality is stable, the great market competitiveness and application value.
Specific embodiment
Embodiment 1
A method of stone paper packaging material printing quality is improved, is included the following steps:
(1) removal of impurities is handled:
Air-blowing processing is carried out with surface of the compressed air to stone paper, with remaining granule foreign standby in air removal stone paper
With;
(2) atomized spray is handled:
After step (1) treated stone paper tiling is put well, recycle atomized spray equipment by the water-soluble liquid mist of silane coupling agent
Change is sprayed on the surface of stone paper;
(3) it is dried:
By step (2), treated that stone paper is put into vacuum oven is dried, and the water content of stone paper is done
It is dry spare to taking out after 5%;
(4) corona treatment:
By step (3), treated, and stone paper is put into plasma processing apparatus, and the voltage for controlling electric discharge is 4kV, electric current
For 35mA, frequency 18kHz, handle stone paper is taken out after 2min it is spare;
(5) storage is handled:
By step (4), treated that stone paper is put into takes out after storage processing 5h in nitrogen environment and can carry out printing treatment.
Further, control pressure is 0.4MPa when air-blowing as described in step (1) is handled.
Further, the volume fraction of silane coupling agent is 20% in silane coupling agent aqueous solution described in step (2);
The silane coupling agent is silane coupling agent kh550;The atomized spray amount of the silane coupling agent aqueous solution is stone paper
The 22% of gross mass.
Further, it is 1 ~ 10Pa, temperature that the air pressure in vacuum oven is controlled when drying process described in step (3)
It is 70 DEG C.
Further, it is air that atmosphere is controlled when corona treatment described in step (4).
Further, its electrode discharge form is that dielectric impedance corona is put when corona treatment described in step (4)
Electricity, block media select aluminium oxide ceramics.
Further, the temperature control of nitrogen environment described in step (5) is 22 DEG C, relative humidity 60%.
Embodiment 2
A method of stone paper packaging material printing quality is improved, is included the following steps:
(1) removal of impurities is handled:
Air-blowing processing is carried out with surface of the compressed air to stone paper, with remaining granule foreign standby in air removal stone paper
With;
(2) atomized spray is handled:
After step (1) treated stone paper tiling is put well, recycle atomized spray equipment by the water-soluble liquid mist of silane coupling agent
Change is sprayed on the surface of stone paper;
(3) it is dried:
By step (2), treated that stone paper is put into vacuum oven is dried, and the water content of stone paper is done
It is dry spare to taking out after 6%;
(4) corona treatment:
By step (3), treated, and stone paper is put into plasma processing apparatus, and the voltage for controlling electric discharge is 4.3kV, electricity
Stream is 38mA, frequency 19kHz, is taken out stone paper after processing 2.5min spare;
(5) storage is handled:
By step (4), treated that stone paper is put into takes out after storage processing 6h in nitrogen environment and can carry out printing treatment.
Further, control pressure is 0.43MPa when air-blowing as described in step (1) is handled.
Further, the volume fraction of silane coupling agent is 22% in silane coupling agent aqueous solution described in step (2);
The silane coupling agent is silane coupling agent kh560;The atomized spray amount of the silane coupling agent aqueous solution is stone paper
The 25% of gross mass.
Further, it is 1 ~ 10Pa, temperature that the air pressure in vacuum oven is controlled when drying process described in step (3)
It is 72 DEG C.
Further, it is air that atmosphere is controlled when corona treatment described in step (4).
Further, its electrode discharge form is that dielectric impedance corona is put when corona treatment described in step (4)
Electricity, block media select aluminium oxide ceramics.
Further, the temperature control of nitrogen environment described in step (5) is 24 DEG C, relative humidity 63%.
Embodiment 3
A method of stone paper packaging material printing quality is improved, is included the following steps:
(1) removal of impurities is handled:
Air-blowing processing is carried out with surface of the compressed air to stone paper, with remaining granule foreign standby in air removal stone paper
With;
(2) atomized spray is handled:
After step (1) treated stone paper tiling is put well, recycle atomized spray equipment by the water-soluble liquid mist of silane coupling agent
Change is sprayed on the surface of stone paper;
(3) it is dried:
By step (2), treated that stone paper is put into vacuum oven is dried, and the water content of stone paper is done
It is dry spare to taking out after 7%;
(4) corona treatment:
By step (3), treated, and stone paper is put into plasma processing apparatus, and the voltage for controlling electric discharge is 4.5kV, electricity
Stream is 40mA, frequency 20kHz, is taken out stone paper after processing 3min spare;
(5) storage is handled:
By step (4), treated that stone paper is put into takes out after storage processing 7h in nitrogen environment and can carry out printing treatment.
Further, control pressure is 0.45MPa when air-blowing as described in step (1) is handled.
Further, the volume fraction of silane coupling agent is 25% in silane coupling agent aqueous solution described in step (2);
The silane coupling agent is silane coupling agent kh570;The atomized spray amount of the silane coupling agent aqueous solution is stone paper
The 26% of gross mass.
Further, it is 1 ~ 10Pa, temperature that the air pressure in vacuum oven is controlled when drying process described in step (3)
It is 75 DEG C.
Further, it is air that atmosphere is controlled when corona treatment described in step (4).
Further, its electrode discharge form is that dielectric impedance corona is put when corona treatment described in step (4)
Electricity, block media select aluminium oxide ceramics.
Further, the temperature control of nitrogen environment described in step (5) is 25 DEG C, relative humidity 65%.
Comparative example 1
This comparative example 1 compared with Example 2, eliminates the processing of step (2) atomized spray, and method and step in addition to this is homogeneous
Together.
Comparative example 2
This comparative example 2 compared with Example 2, eliminates step (4) corona treatment, and method and step in addition to this is homogeneous
Together.
Comparative example 3
This comparative example 3 compared with Example 2, eliminates the processing of step step (2) atomized spray and step (4) plasma
Processing, method and step in addition to this are all the same.
Control group
Special processing operation is not carried out to stone paper.
In order to compare effect of the present invention, select with the commercially available common stones paper of a batch as experimental subjects, respectively with above-mentioned reality
Example 2, comparative example 1, comparative example 2, comparative example 3, the corresponding method of control group is applied to be processed, then into
The printing treatment of row same process, finally to treated, stone paper carries out performance measurement, specific correlation data such as the following table 1 institute
Show:
Table 1
Note: contact angle described in upper table 1 is the quiet contact angle measured between stone paper and ink, and that reflects stone papers to oil
Ink receives performance, and it is poorer that numerical value shows to receive performance more greatly;The subjective assessment is to observe king by patriot's number
(180 times of camera lenses) takes figure to the stone paper sampling amplification after printing, carries out subjectivity to lines, text, ink dot, bleeding degree and comment
Valence, with it is excellent, good, in, poor four grades are indicated;The color density difference is that CMYK color is printed in stone paper after treatment
Block impregnates take out afterwards for 24 hours in water, and naturally dry for 24 hours, surveys the difference of its front and back color density, characterizes the water resistance and stabilization of printing
Property.
The printing processing performance of the method for the present invention treated stone paper has obtained apparent increasing it can be seen from upper table 1
By force, the field and value that it is used, the great market competitiveness and economic benefit are expanded.
Claims (7)
1. a kind of method for improving stone paper packaging material printing quality, which comprises the steps of:
(1) removal of impurities is handled:
Air-blowing processing is carried out with surface of the compressed air to stone paper, with remaining granule foreign standby in air removal stone paper
With;
(2) atomized spray is handled:
After step (1) treated stone paper tiling is put well, recycle atomized spray equipment by the water-soluble liquid mist of silane coupling agent
Change is sprayed on the surface of stone paper;
(3) it is dried:
By step (2), treated that stone paper is put into vacuum oven is dried, and the water content of stone paper is done
It is dry spare to taking out after 5 ~ 7%;
(4) corona treatment:
By step (3), treated, and stone paper is put into plasma processing apparatus, and the voltage for controlling electric discharge is 4 ~ 4.5kV,
Electric current is 35 ~ 40mA, and frequency is 18 ~ 20kHz, is taken out stone paper after 2 ~ 3min of processing spare;
(5) storage is handled:
By step (4), treated that stone paper is put into takes out and can carry out at printing after 5 ~ 7h of storage processing in nitrogen environment
Reason.
2. a kind of method for improving stone paper packaging material printing quality according to claim 1, which is characterized in that step
(1) control pressure is 0.4 ~ 0.45MPa when the air-blowing described in is handled.
3. a kind of method for improving stone paper packaging material printing quality according to claim 1, which is characterized in that step
(2) volume fraction of silane coupling agent is 20 ~ 25% in the silane coupling agent aqueous solution described in;The silane coupling agent is
Silane coupling agent kh550, silane coupling agent kh560, any one in silane coupling agent kh570;The silane coupling agent
The atomized spray amount of aqueous solution is the 22 ~ 26% of stone paper gross mass.
4. a kind of method for improving stone paper packaging material printing quality according to claim 1, which is characterized in that step
(3) air pressure when drying process described in control vacuum oven is 1 ~ 10Pa, temperature is 70 ~ 75 DEG C.
5. a kind of method for improving stone paper packaging material printing quality according to claim 1, which is characterized in that step
(4) control atmosphere is air when corona treatment described in.
6. a kind of method for improving stone paper packaging material printing quality according to claim 1, which is characterized in that step
(4) its electrode discharge form is dielectric impedance corona discharge when corona treatment described in, and block media selects oxidation
Aluminium ceramics.
7. a kind of method for improving stone paper packaging material printing quality according to claim 1, which is characterized in that step
(5) the temperature control of the nitrogen environment described in is 22 ~ 25 DEG C, relative humidity is 60 ~ 65%.