CN109456005A - 一种聚合物水泥防水砂浆 - Google Patents
一种聚合物水泥防水砂浆 Download PDFInfo
- Publication number
- CN109456005A CN109456005A CN201811543571.4A CN201811543571A CN109456005A CN 109456005 A CN109456005 A CN 109456005A CN 201811543571 A CN201811543571 A CN 201811543571A CN 109456005 A CN109456005 A CN 109456005A
- Authority
- CN
- China
- Prior art keywords
- equal
- filler
- polymer cement
- mesh
- cement materials
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种聚合物水泥防水砂浆，包括液料组分和粉料组分，所述液料组分包括醋叔乳液，所述粉料组分包括水泥、填料、40～70目砂子、71～140目砂子，所述水泥大于等于200目，所述填料为大于等于600目的填料，所述醋叔乳液包括大于等于200nm且小于等于300nm的乳液粒子，砂子、水泥、填料和乳液粒子形成连续的颗粒级配。本发明具有良好的湿润性，无需对施工基面提前润湿，滚涂施工于硅钙板干基面时均匀无障碍；连续的颗粒级配使得砂浆可以更好地滚涂均匀，且滚涂过程中砂浆易推开，涂布更加均匀平整，达到更加优异的施工效果，在提高施工效果的同时，降低人工成本和时间成本，对于防水砂浆的施工具有重要意义。
Description
技术领域
本发明属于化工涂料技术领域，具体涉及一种聚合物水泥防水砂浆。
背景技术
聚合物水泥防水砂浆是以水泥、细骨料为主要材料制作的，主要用于建筑物屋面及内外墙面渗漏的修复或抗渗处理、各类水池和游泳池的防水防渗等。聚合物改性水泥防水砂浆的应用已有60多年的历史，与传统的仅用水泥基水硬性防水材料不同，通过聚合物的改性，使其成为双黏结剂体系，并形成一种互补的状态，具有粘结强度高、施工方便、耐腐蚀、耐高温、耐老化的优点。聚合物改性水泥防水砂浆可分为单组份砂浆和双组份砂浆，根据使用范围和性能的不同，双组份防水砂浆可分为柔性防水砂浆和刚性防水砂浆。
柔性防水砂浆是用于抗压或防潮部位的具有抗裂性能和延展力的防水涂层材料，大多执行GB/T 23445-2009标准，由于其液粉比较高，且液料中的乳液用量较多，因此柔性防水砂浆具有极好的柔性和抗裂性能，无论是刷涂还是滚涂都可非常顺畅，施工性能良好。
刚性防水砂浆用于有一定承载力或不需要承载力的部位，抗裂性能较差，大多执行JC/T 2090-2011或JC/T 984-2011标准，由于现有技术的液粉比较低，湿润度较低，对施工基面的湿润作用较差，施工人员需要将施工基面提前用水润湿后才可使用，因此现有技术主要采用刷涂的方式进行施工，有时甚至需要批刮施工，不适用于多种施工情况之外，施工效率也大大降低。
在批刮、刷涂、滚涂三种施工工艺中，滚涂的施工效率更高、施工方法更为简单方便且施工效果良好，因此提供一款免湿润、滚涂顺畅的双组份聚合物水泥防水砂浆对防水施工是很有必要的。
发明内容
为解决现有技术中存在的缺陷和不足，本发明的主要目的在于提供一种聚合物水泥防水砂浆，所述防水砂浆包括醋叔乳液和连续的颗粒级配，该防水砂浆在施工前无需对施工基面提前润湿，可使用滚涂的方式施工，且滚涂均匀无障碍，提高了施工效率，具有良好的施工效果，施工面平整光滑，没有颗粒凹凸感。
为达到上述目的，本发明通过以下技术方案实现：
一种聚合物水泥防水砂浆，其特征在于，包括液料组分和粉料组分，按照质量比重所述液料组分包括：
醋叔乳液 25％～45％；
液态消泡剂 0.2％～0.4％；
防腐剂 0.1％～0.3％；
水 50％～74％；
按照质量比重所述粉料组分包括：
40～70目砂子 10％～20％；
71～140目砂子 9％～37％；
水泥 40％～60％；
填料 2％～10％；
减水剂 0.05％～0.2％；
粉态消泡剂 0.1～0.2％；
憎水剂 0.2～0.4％；
保水剂 0.07～0.1％；
所述水泥大于等于200目，所述填料为大于等于600目的填料，所述醋叔乳液包括大于等于200nm且小于等于300nm的乳液粒子，所述砂子、水泥、填料和醋叔乳液形成连续的颗粒级配。
优选地，所述液料组分与所述粉料组分的质量比为0.28:1～0.4:1。
优选地，所述醋叔乳液，是由醋酸乙烯酯、叔碳酸乙烯酯为主要单体共聚合成的高分子乳液。
优选地，所述液态消泡剂包括有机硅类消泡剂。
优选地，所述水泥包括硅酸盐水泥。
优选地，所述填料包括硅灰、偏高岭土、矿渣中的至少一个。
优选地，所述减水剂包括三聚氰胺减水剂、缩甲醛苯磺酸钠盐和聚羧酸减水剂中的至少一种。
优选地，所述粉态消泡剂包括矿物油类消泡剂。
优选地，所述憎水剂包括有机硅憎水剂、硬脂酸锌、硬脂酸钙中的至少一种。
优选地，所述保水剂包括羟乙基甲基纤维素醚、羟丙基甲基纤维素醚中的至少一种，粘度大于等于10000mPa.S且小于等于40000mPa.S。
本发明具有以下有益效果：
1、本产品中的填料具有一定的活性，可以参与碱性反应，有利于提高防水砂浆的致密性，使防水砂浆不易沉底，达到良好的抗渗效果；
2、本产品的砂子为40目～70目和70目～140目的石英砂，由于40目～70 目的石英砂太粗，因此不常用于防水砂浆中，但本产品将两个颗粒级的石英砂均加入进水泥砂浆中，在涂布时，所有颗粒堆叠在一起，大大小小的颗粒可以相互填充颗粒之间的空隙，连接致密，与现有技术相比，涂布更加均匀，达到更好的施工效果；
3、本产品中颗粒大小有40目～70目砂子、70目～140目的砂子、200目以上的水泥、600目以上的填料以及200nm～300nm的乳液粒子，形成了一个连续的颗粒级配，润湿程度高，使得砂浆在使用过程中有利于滚涂施工，不需要现有技术中的干燥墙面润湿工序，并且施工面滚涂均匀，施工面平整光滑，粘结强度高、耐高温、耐老化优点突出。
4、本发明人通过多次实验，最终选择以非离子表面活性剂为主要乳化剂的具有防水抗碱化能力的醋叔乳液，现有技术中主要将醋叔乳液应用于乳胶漆中，由于水泥具有强碱性，乳液在加入时会发生破乳，从而使乳液的稳定性下降，而本发明加入具有防水抗碱化能力的醋叔乳液，乳液的稳定性提高，可在极大程度上提高防水砂浆的湿润性，所述醋叔乳液以非离子乳化体系为主、具有钙离子稳定性，由醋酸乙烯酯、叔碳酸乙烯酯为主要单体共聚合成的高分子乳液，固体含量55％；
5、本发明的防水砂浆具有良好的湿润性，施工人员在使用前无需将施工基面润湿，滚涂施工于硅钙板干基面时均匀无障碍，可以更好地滚涂均匀，且滚涂过程中砂浆易推开，涂布更加均匀平整，可达到更加优异的施工效果，在提高施工效果的同时，降低人工成本和时间成本，对于防水砂浆的施工具有重要意义。
具体实施方式
以下通过具体实施例再对本发明的上述内容作进一步的详细说明。但不应将此理解为本发明上述主题的范围仅局限于以下的实施例。在不脱离本发明上述技术思想的情况下，根据本领域普通技术知识和惯用手段做出的各种替换或变更，均应包括在本发明的范围内。
实施例1
本发明提供一种聚合物水泥防水砂浆，包括液料组分和粉料组分，本实施例中的液料组分与粉料组分的比值为0.28:1，各组分的具体含量如表1-1所示：
表1-1实施例1的配方成分表
将上述液料倒入干净的搅拌容器中，然后按照比例一边搅拌一边缓慢加入粉料，充分搅拌3～5分钟直至生成无粉团、均匀的胶浆。
根据国家标准对本实施例的聚合物水泥防水砂浆进行测试，检测结果如表 1-2所示：
表1-2实施例1的检测结果表
实施例2
本发明提供一种聚合物水泥防水砂浆，包括液料组分和粉料组分，本实施例中的液料组分与粉料组分的比值为0.34:1，各组分的具体含量如表2-1所示：
表2-1实施例2的配方成分表
将上述液料倒入干净的搅拌容器中，然后按照比例一边搅拌一边缓慢加入粉料，充分搅拌3～5分钟直至生成无粉团、均匀的胶浆。
根据国家标准对本实施例的聚合物水泥防水砂浆进行测试，检测结果如表 2-2所示：
表2-2实施例2的检测结果表
实施例3
本发明提供一种聚合物水泥防水砂浆，包括液料组分和粉料组分，本实施例中的液料组分与粉料组分的比值为0.37:1，各组分的具体含量如表3-1所示：
表3-1实施例3的配方成分表
将上述液料倒入干净的搅拌容器中，然后按照比例一边搅拌一边缓慢加入粉料，充分搅拌3～5分钟直至生成无粉团、均匀的胶浆。
根据国家标准对本实施例的聚合物水泥防水砂浆进行测试，检测结果如表 3-2所示：
表3-2实施例3的检测结果表
实施例4
本发明提供一种聚合物水泥防水砂浆，包括液料组分和粉料组分，本实施例中的液料组分与粉料组分的比值为0.40:1，各组分的具体含量如表4-1所示：
表4-1实施例4的配方成分表
将上述液料倒入干净的搅拌容器中，然后按照比例一边搅拌一边缓慢加入粉料，充分搅拌3～5分钟直至生成无粉团、均匀的胶浆。
根据国家标准对本实施例的聚合物水泥防水砂浆进行测试，检测结果如表 4-2所示：
表4-2实施例4的检测结果表
实施例5
本发明提供的防水砂浆涂布均匀性的测试实验，具体步骤如下：
(1)用滚筒将现有防水砂浆和实施例1～4的防水砂浆分别均匀滚涂于基材上(混凝土层、水泥砂浆抹灰层)滚涂两遍，当第一层干固后(2～3小时，刚好不粘手)，可滚涂第二层，滚涂方向与第一层的滚涂方向垂直；
(2)在1平方米的范围内分别测定现有防水砂浆和实施例1～4的防水砂浆的涂布气泡个数、防水膜厚度差和砂浆用量误差。
检测结果如表5所示：
表5防水砂浆涂布均匀性测试结果
由表5及滚涂过程可知，本发明的防水砂浆涂布于干基面上时，无需提前对干基面进行湿润处理，滚涂过程中砂浆易推开，不会由于基面的干燥而产生阻碍；涂布完成时，本发明砂浆中的气泡较现有防水砂浆的气泡少，涂布更加均匀平整，因此本产品具有良好的湿润性；
本发明的防水砂浆滚涂于干基面时，由于砂浆中特有的颗粒级配而使得滚涂顺畅无阻碍，砂浆滚涂均匀，1平方米内最大和最小涂层厚度之差约为 8％～9％，较现有的防水砂浆小，1平方米内滚涂防水砂浆用量误差约为8％～9％，横向和纵向的滚涂效果一致，不会产生鼓包、拖尾以及越涂越薄等问题，滚涂效果较现有防水砂浆更平整、均匀，因此具有良好的滚涂施工性。
综上所述，本发明的聚合物水泥防水砂浆的各项指标均达到国家标准，具有良好的湿润性，无需对施工基面提前润湿，滚涂施工于硅钙板干基面时均匀无障碍，可以更好地滚涂均匀，且滚涂过程中砂浆易推开，涂布更加均匀平整，可达到更加优异的施工效果，在提高施工效果的同时，降低人工成本和时间成本，对于防水砂浆的施工具有重要意义。
以上实施例的各技术特征可以进行任意的组合，为使描述简洁，未对上述实施例中的各个技术特征所有可能的组合都进行描述，然而，只要这些技术特征的组合不存在矛盾，都应当认为是本说明书记载的范围。
以上实施例仅表达了本发明的几种实施方式，其描述较为具体和详细，但并不能因此而理解为对发明专利范围的限制。应当指出的是，对于本领域的普通技术人员来说，在不脱离本发明构思的前提下，还可以做出若干变形和改进，这些都属于本发明的保护范围。因此，本发明专利的保护范围应以所附权利要求为准。
Claims (10)
1.一种聚合物水泥防水砂浆，其特征在于，包括液料组分和粉料组分，按照质量比重所述液料组分包括：
醋叔乳液 25％～45％；
液态消泡剂 0.2％～0.4％；
防腐剂 0.1％～0.3％；
水 50％～74％；
按照质量比重所述粉料组分包括：
40～70目砂子 10％～20％；
71～140目砂子 9％～37％；
水泥 40％～60％；
填料 2％～10％；
减水剂 0.05％～0.2％；
粉态消泡剂 0.1～0.2％；
憎水剂 0.2～0.4％；
保水剂 0.07～0.1％；
所述水泥大于等于200目，所述填料为大于等于600目的填料，所述醋叔乳液包括大于等于200nm且小于等于300nm的乳液粒子，所述砂子、水泥、填料和醋叔乳液形成连续的颗粒级配。
2.根据权利要求1所述的一种聚合物水泥防水砂浆，其特征在于，所述液料组分与所述粉料组分的质量比为0.28:1～0.4:1。
3.根据权利要求1所述的一种聚合物水泥防水砂浆，其特征在于，所述醋叔乳液，是由醋酸乙烯酯、叔碳酸乙烯酯为主要单体共聚合成的高分子乳液。
4.根据权利要求1所述的一种聚合物水泥防水砂浆，其特征在于，所述液态消泡剂包括有机硅类消泡剂。
5.根据权利要求1所述的一种聚合物水泥防水砂浆，其特征在于，所述水泥包括硅酸盐水泥。
6.根据权利要求1所述的一种聚合物水泥防水砂浆，其特征在于，所述填料包括硅灰、偏高岭土、矿渣中的至少一个。
7.根据权利要求1所述的一种聚合物水泥防水砂浆，其特征在于，所述减水剂包括三聚氰胺减水剂、缩甲醛苯磺酸钠盐和聚羧酸减水剂中的至少一种。
8.根据权利要求1所述的一种聚合物水泥防水砂浆，其特征在于，所述粉态消泡剂包括矿物油类消泡剂。
9.根据权利要求1所述的一种聚合物水泥防水砂浆，其特征在于，所述憎水剂包括有机硅憎水剂、硬脂酸锌、硬脂酸钙中的至少一种。
10.根据权利要求1所述的一种聚合物水泥防水砂浆，其特征在于，所述保水剂包括羟乙基甲基纤维素醚、羟丙基甲基纤维素醚中的至少一种，粘度大于等于10000mPa.S且小于等于40000mPa.S。