CN109439033B - 一种无机涂料墙体用除霉防霉喷剂 - Google Patents
一种无机涂料墙体用除霉防霉喷剂 Download PDFInfo
- Publication number
- CN109439033B CN109439033B CN201811290137.XA CN201811290137A CN109439033B CN 109439033 B CN109439033 B CN 109439033B CN 201811290137 A CN201811290137 A CN 201811290137A CN 109439033 B CN109439033 B CN 109439033B
- Authority
- CN
- China
- Prior art keywords
- mildew
- parts
- montmorillonite
- water
- inorganic coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明属于建筑物防霉技术领域。本发明公开了一种无机涂料墙体用除霉防霉喷剂，其由以下重量份的原料制得，煅烧贝壳粉100份，石膏20～25份，白炭黑30～40份，聚乙烯醇10～15份，分散剂10～15份，钛白粉10～15份，蒙脱石长效防霉剂11～15份，无水乙醇40～50份，水100～130份。本发明中采用对人无害的组分，其兼具杀菌与抗菌功效，在快速杀菌后还能起到长效抑菌效果；本发明针对无机墙体材料具有良好的相容性，并且具有美白效果，使用后能够牢固得附着在墙体表面，不发生剥离和脱落。
Description
技术领域
本发明涉及建筑物防霉技术领域，尤其是涉及一种无机涂料墙体用除霉防霉喷剂。
背景技术
建筑物在潮湿气候或者环境里容易产生霉菌，尤其是南方的梅雨季节，楼层低的房子或者地下室极易发霉，霉菌孢子容易飘散，被人体吸入，影响人体健康，霉菌也影响墙体的美观，产生霉菌后的处理往往需要重新粉刷，带来诸多不便。
发明内容
为解决上述问题，本发明提供了一种针对无机涂料墙体兼具杀菌和抑菌两种效果，能够方便喷涂在发霉墙体表面在迅速杀灭霉菌的同时能够美白墙体的无机涂料墙体用除霉防霉喷剂。
为实现上述目的，本发明采用的技术方案如下：
一种无机涂料墙体用除霉防霉喷剂，由以下重量份的原料制得：
煅烧贝壳粉100份，石膏20～25份，白炭黑30～40份，聚乙烯醇10～15份，分散剂10～15份，钛白粉10～15份，蒙脱石长效防霉剂11～15份，无水乙醇40～50份，水100～130份。
本发明的配方中的主要成分为无机成分，并且与无机涂料组分相近，具有良好的相容性；利用特殊工艺制得的煅烧贝壳粉具有快速杀菌作用能够起到快速除霉的作用，而添加的蒙脱石长效防霉剂具有长效抑菌作用，能够才较长时间内起到对霉菌的抑制作用；无机涂料主要为白色的石膏或石灰材质，因此在组分中包含了具有高白度的钛白粉赋予处理后的墙面以白度；石膏是一种气硬性材料，其在水溶液能够稳定存在不发生硬化，在空气中能够发生硬化反应，适量添加石膏能够保证处理后，本发明中的固体成分牢固的附着在墙体上不发生脱落，而聚乙烯醇能够增加喷剂的粘稠度，也能增进喷剂在墙体上的附着性能。
作为优选，石膏为硬石膏。
作为优选，分散剂为羟乙基纤维素、月桂醇聚氧乙烯醚或山梨醇酐单棕榈酸酯中的一种。
作为优选，蒙脱石长效防霉剂由以下方法制得，将蒙脱石与蒙脱石重量1.0～1.5倍的1mol/L乙酸钾溶液混合，然后以1000～2000rpm转速下球磨1～1.5小时，然后静置1～2小时制得蒙脱石混合浆，然后将蒙脱石混合浆干燥并在300～400℃下处理30～40分钟制得初插层蒙脱石，然后将初插层蒙脱石与其重量0.1～0.3倍的季铵盐、其重量0.05～0.07倍的硅烷偶联剂、其重量0.8～1.0倍的水混合并在1500～2500rpm转速下球磨50～70分钟，接着干燥后制得蒙脱石长效防霉剂。
作为优选，季铵盐为十二烷基二甲基苯基溴化铵、双溴化十四烷基二甲基乙基溴化铵或甲基丙烯酰氧十二烷基溴吡啶中的一种。
本发明中的蒙脱石长效防霉剂制备主要分两步，第一步为层间距的扩大，第二步为抗菌组分接枝。第一步采用将蒙脱石和乙酸钾溶液混合并球磨的方法进行，蒙脱石层间具有丰富的层间离子，这些层间离子具有较高的活性，将乙酸钾与蒙脱石混合球磨后，蒙脱石能够被机械破碎，成为尺寸更小的颗粒并能够活化其层间离子的活性，这一过程中，乙酸钾也能部分进入蒙脱石的层间，球磨之后的静置是为了使更多的乙酸钾替换蒙脱石层间具有高活性的离子，也即使更多的乙酸钾进入蒙脱石的层间并稳定存在，静置后高温处理，将蒙脱石层间的乙酸钾除去，进而完成了蒙脱石层间距的扩大，为下一步的耐高温高聚物的***做好了准备；第二步抗菌成分的接枝，抗菌成分选用季铵盐，经过第一步形成的初插层蒙脱石与季铵盐、偶联剂、水混合球磨进行插层改性，利用机械力将季铵盐***经第一步处理后的蒙脱石的层间，季铵盐的***能够赋予抗菌性能，同时季铵盐接枝到蒙脱石上能够延长抗菌功能的时效，使得能够在较低成本下获得较好的抗菌效果。上述两步插层处理都采用机械力插层，这样方法简便，能够快速生产，而且二步插层处理的效果较好。
作为优选，煅烧贝壳粉由以下方法制得，将贝壳去除贝类组织后粉碎，在1～1.5mol/L的硝酸中浸泡10～15分钟，用水清洗干净，然后再在2～2.5mol/L的氢氧化钾溶液中浸泡20～30分钟，用水清洗干净，最后在600～700℃煅烧2～4小时冷却后制得煅烧贝壳粉。
作为优选，白炭黑添加前经以下处理，将白炭黑与其等重的0.5～1.0mol/L硝酸溶液混合后球磨处理30～40分钟，然后用水清洗干净，接着将其加入到1～2mol/L的氢氧化钾溶液中搅拌浸泡10～20分钟，用水清洗至中性后烘干。
白炭黑经过上述处理后会在其表面生成一定量的硅酸钠，生成的硅酸钠能够增稠喷剂，也能够赋予喷剂中的组分更好的附着在墙体表面。
作为优选，无机涂料墙体用除霉防霉喷剂由以下方法制得：
将聚乙烯醇溶解于无水乙醇中制得A液，然后将石膏溶解于水中，向水中加入分散剂并溶解，接着依次加入煅烧贝壳粉、白炭黑、钛白粉和蒙脱石长效防霉剂并混合均匀制得B液，最后将A液缓慢的加入到B液中混合均匀后制得无机涂料墙体用除霉防霉喷剂。
作为优选，煅烧贝壳粉、白炭黑、钛白粉和蒙脱石长效防霉剂的粒径都为85微米及以下，
或，在添加前将煅烧贝壳粉、白炭黑、钛白粉和蒙脱石长效防霉剂粉碎至85微米及以下。
因此，本发明具有以下有益效果：本发明中采用对人无害的组分，其兼具杀菌与抗菌功效，在快速杀菌后还能起到长效抑菌效果；本发明针对无机墙体材料具有良好的相容性，并且具有美白效果，使用后能够牢固得附着在墙体表面，不发生剥离和脱落。
具体实施方式
下面结合具体实施方式对本发明的技术方案作进一步的说明。
显然，所描述的实施例仅是本发明的一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其它实施例，都属于本发明保护的范围。
在本发明中，若非特指，所有的设备和原料均可从市场上购得或是本行业常用的，下述实施例中的方法，如无特别说明，均为本领域常规方法。
实施例1
一种无机涂料墙体用除霉防霉喷剂，由以下重量份的原料制得：
煅烧贝壳粉100份，硬石膏20份，白炭黑30份，聚乙烯醇10份，山梨醇酐单棕榈酸酯10份，钛白粉10份，蒙脱石长效防霉剂11份，无水乙醇40份，水100份；
无机涂料墙体用除霉防霉喷剂由以下方法制得：将聚乙烯醇溶解于无水乙醇中制得A液，然后将石膏溶解于水中，向水中加入分散剂并溶解，接着依次加入煅烧贝壳粉、白炭黑、钛白粉和蒙脱石长效防霉剂并混合均匀制得B液，最后将A液缓慢的加入到B液中混合均匀后制得无机涂料墙体用除霉防霉喷剂。
其中，蒙脱石长效防霉剂由以下方法制得，将蒙脱石与蒙脱石重量1.0倍的1mol/L乙酸钾溶液混合，然后以1000rpm转速下球磨1小时，然后静置1小时制得蒙脱石混合浆，然后将蒙脱石混合浆干燥并在300℃下处理30分钟制得初插层蒙脱石，然后将初插层蒙脱石与其重量0.1倍的甲基丙烯酰氧十二烷基溴吡啶、其重量0.05倍的硅烷偶联剂、其重量0.8倍的水混合并在1500rpm转速下球磨50分钟，接着干燥后制得蒙脱石长效防霉剂；
煅烧贝壳粉由以下方法制得，将贝壳去除贝类组织后粉碎，在1mol/L的硝酸中浸泡10分钟，用水清洗干净，然后再在2mol/L的氢氧化钾溶液中浸泡20分钟，用水清洗干净，最后在600℃煅烧4小时冷却后制得煅烧贝壳粉；
白炭黑添加前经以下处理，将白炭黑与其等重的0.5mol/L硝酸溶液混合后球磨处理30分钟，然后用水清洗干净，接着将其加入到1mol/L的氢氧化钾溶液中搅拌浸泡10分钟，用水清洗至中性后烘干；
此外，煅烧贝壳粉、白炭黑、钛白粉和蒙脱石长效防霉剂的粒径都为85微米及以下。
实施例2
一种无机涂料墙体用除霉防霉喷剂，由以下重量份的原料制得：
煅烧贝壳粉100份，硬石膏25份，白炭黑40份，聚乙烯醇15份，羟乙基纤维素15份，钛白粉15份，蒙脱石长效防霉剂15份，无水乙醇50份，水130份；
无机涂料墙体用除霉防霉喷剂由以下方法制得：将聚乙烯醇溶解于无水乙醇中制得A液，然后将石膏溶解于水中，向水中加入分散剂并溶解，接着依次加入煅烧贝壳粉、白炭黑、钛白粉和蒙脱石长效防霉剂并混合均匀制得B液，最后将A液缓慢的加入到B液中混合均匀后制得无机涂料墙体用除霉防霉喷剂。
其中，蒙脱石长效防霉剂由以下方法制得，将蒙脱石与蒙脱石重量1.5倍的1mol/L乙酸钾溶液混合，然后以2000rpm转速下球磨1.5小时，然后静置2小时制得蒙脱石混合浆，然后将蒙脱石混合浆干燥并在400℃下处理40分钟制得初插层蒙脱石，然后将初插层蒙脱石与其重量0.3倍的十二烷基二甲基苯基溴化铵、其重量0.07倍的硅烷偶联剂、其重量1.0倍的水混合并在2500rpm转速下球磨70分钟，接着干燥后制得蒙脱石长效防霉剂；
煅烧贝壳粉由以下方法制得，将贝壳去除贝类组织后粉碎，在1.5mol/L的硝酸中浸泡15分钟，用水清洗干净，然后再在2.5mol/L的氢氧化钾溶液中浸泡30分钟，用水清洗干净，最后在700℃煅烧2小时冷却后制得煅烧贝壳粉；
白炭黑添加前经以下处理，将白炭黑与其等重的1.0mol/L硝酸溶液混合后球磨处理40分钟，然后用水清洗干净，接着将其加入到2mol/L的氢氧化钾溶液中搅拌浸泡20分钟，用水清洗至中性后烘干；
此外，在添加前将煅烧贝壳粉、白炭黑、钛白粉和蒙脱石长效防霉剂粉碎至85微米及以下。
实施例3
一种无机涂料墙体用除霉防霉喷剂，由以下重量份的原料制得：
煅烧贝壳粉100份，硬石膏22份，白炭黑33份，聚乙烯醇12份，月桂醇聚氧乙烯醚12份，钛白粉12份，蒙脱石长效防霉剂12份，无水乙醇44份，水110份；
无机涂料墙体用除霉防霉喷剂由以下方法制得：将聚乙烯醇溶解于无水乙醇中制得A液，然后将石膏溶解于水中，向水中加入分散剂并溶解，接着依次加入煅烧贝壳粉、白炭黑、钛白粉和蒙脱石长效防霉剂并混合均匀制得B液，最后将A液缓慢的加入到B液中混合均匀后制得无机涂料墙体用除霉防霉喷剂。
其中，蒙脱石长效防霉剂由以下方法制得，将蒙脱石与蒙脱石重量1.2倍的1mol/L乙酸钾溶液混合，然后以1300rpm转速下球磨1.2小时，然后静置1.4小时制得蒙脱石混合浆，然后将蒙脱石混合浆干燥并在350℃下处理33分钟制得初插层蒙脱石，然后将初插层蒙脱石与其重量0.15倍的双溴化十四烷基二甲基乙基溴化铵、其重量0.055倍的硅烷偶联剂、其重量0.85倍的水混合并在1800rpm转速下球磨55分钟，接着干燥后制得蒙脱石长效防霉剂；
煅烧贝壳粉由以下方法制得，将贝壳去除贝类组织后粉碎，在1.2mol/L的硝酸中浸泡12分钟，用水清洗干净，然后再在2.2mol/L的氢氧化钾溶液中浸泡23分钟，用水清洗干净，最后在650℃煅烧3小时冷却后制得煅烧贝壳粉；
白炭黑添加前经以下处理，将白炭黑与其等重的0.6mol/L硝酸溶液混合后球磨处理33分钟，然后用水清洗干净，接着将其加入到1.5mol/L的氢氧化钾溶液中搅拌浸泡15分钟，用水清洗至中性后烘干；
此外，煅烧贝壳粉、白炭黑、钛白粉和蒙脱石长效防霉剂的粒径都为85微米及以下。
实施例4
一种无机涂料墙体用除霉防霉喷剂，由以下重量份的原料制得：
煅烧贝壳粉100份，硬石膏23份，白炭黑37份，聚乙烯醇13份，月桂醇聚氧乙烯醚14份，钛白粉14份，蒙脱石长效防霉剂14份，无水乙醇47份，水120份；
无机涂料墙体用除霉防霉喷剂由以下方法制得：将聚乙烯醇溶解于无水乙醇中制得A液，然后将石膏溶解于水中，向水中加入分散剂并溶解，接着依次加入煅烧贝壳粉、白炭黑、钛白粉和蒙脱石长效防霉剂并混合均匀制得B液，最后将A液缓慢的加入到B液中混合均匀后制得无机涂料墙体用除霉防霉喷剂。
其中，蒙脱石长效防霉剂由以下方法制得，将蒙脱石与蒙脱石重量1.3倍的1mol/L乙酸钾溶液混合，然后以1600rpm转速下球磨1.3小时，然后静置1.7小时制得蒙脱石混合浆，然后将蒙脱石混合浆干燥并在350℃下处理38分钟制得初插层蒙脱石，然后将初插层蒙脱石与其重量0.25倍的双溴化十四烷基二甲基乙基溴化铵、其重量0.065倍的硅烷偶联剂、其重量0.95倍的水混合并在2200rpm转速下球磨65分钟，接着干燥后制得蒙脱石长效防霉剂；
煅烧贝壳粉由以下方法制得，将贝壳去除贝类组织后粉碎，在1.3mol/L的硝酸中浸泡13分钟，用水清洗干净，然后再在2.3mol/L的氢氧化钾溶液中浸泡27分钟，用水清洗干净，最后在650℃煅烧3小时冷却后制得煅烧贝壳粉；
白炭黑添加前经以下处理，将白炭黑与其等重的0.9mol/L硝酸溶液混合后球磨处理37分钟，然后用水清洗干净，接着将其加入到1.5mol/L的氢氧化钾溶液中搅拌浸泡15分钟，用水清洗至中性后烘干；
此外，在添加前将煅烧贝壳粉、白炭黑、钛白粉和蒙脱石长效防霉剂粉碎至85微米及以下。
抗霉菌效果检测
按化工行业标准HG/T 3950-2007附录B中记载的抗菌涂料-抗霉菌性能试验方法相关内容进行测试。
按上述标准中记载的方法准备5组空白对照组并标记为对照组1～5，将由上述实施例1～5制得的无机涂料墙体用除霉防霉喷剂按上述标准中记载的方法制备抗菌试板，每一实施例样品均制作5个抗菌试板，制备抗菌试板时将实施例1～5中的喷剂喷到试板上待溶剂挥发后再进行测试，同时溶剂挥发后在试板上形成的液斑应符合上述标准中的要求；将上述方法制得的实施例1～5试验组记为实施例1～5。
检测结果如下：
样品长霉等级按上述标准附录B中B4记载的评判标准进行评定。
5个对照组长霉面积均大于10%，可以作为该试验的空白对照组；
实施例1中五个抗菌试板中有3个抗菌试板的检测结果等级为0级，因此实施例1中样品的长霉等级定为0级；
实施例2中五个抗菌试板中有5个抗菌试板的检测结果等级为0级，因此实施例1中样品的长霉等级定为0级；
实施例3中五个抗菌试板中有4个抗菌试板的检测结果等级为0级，因此实施例1中样品的长霉等级定为0级；
实施例4中五个抗菌试板中有5个抗菌试板的检测结果等级为0级，因此实施例1中样品的长霉等级定为0级；
实施例5中五个抗菌试板中有5个抗菌试板的检测结果等级为0级，因此实施例1中样品的长霉等级定为0级。
由上述结果可知，本发明中制得的无机涂料墙体用除霉防霉喷剂抗霉菌等级按上述标准为0级。
应当理解的是，对于本领域普通技术人员来说，可以根据上述说明加以改进或变换，而所有这些改进和变换都应属于本发明所附权利要求的保护范围。
Claims (8)
1.一种无机涂料墙体用除霉防霉喷剂，其特征在于由以下重量份的原料制得：
煅烧贝壳粉100份，石膏20～25份，白炭黑30～40份，聚乙烯醇10～15份，分散剂10～15份，钛白粉10～15份，蒙脱石长效防霉剂11～15份，无水乙醇40～50份，水100～130份；
所述的蒙脱石长效防霉剂由以下方法制得，将蒙脱石与蒙脱石重量1.0～1.5倍的1mol/L乙酸钾溶液混合，然后以1000～2000rpm转速下球磨1～1.5小时，然后静置1～2小时制得蒙脱石混合浆，然后将蒙脱石混合浆干燥并在300～400℃下处理30～40分钟制得初插层蒙脱石，然后将初插层蒙脱石与其重量0.1～0.3倍的季铵盐、其重量0.05～0.07倍的硅烷偶联剂、其重量0.8～1.0倍的水混合并在1500～2500rpm转速下球磨50～70分钟，接着干燥后制得蒙脱石长效防霉剂。
2.根据权利要求1所述的一种无机涂料墙体用除霉防霉喷剂，其特征在于：
所述的石膏为硬石膏。
3.根据权利要求1所述的一种无机涂料墙体用除霉防霉喷剂，其特征在于：
所述的分散剂为羟乙基纤维素、月桂醇聚氧乙烯醚或山梨醇酐单棕榈酸酯中的一种。
4.根据权利要求1所述的一种无机涂料墙体用除霉防霉喷剂，其特征在于：
所述的季铵盐为十二烷基二甲基苯基溴化铵、双溴化十四烷基二甲基乙基溴化铵或甲基丙烯酰氧十二烷基溴吡啶中的一种。
5.根据权利要求1所述的一种无机涂料墙体用除霉防霉喷剂，其特征在于：
所述的煅烧贝壳粉由以下方法制得，将贝壳去除贝类组织后粉碎，在1～1.5mol/L的硝酸中浸泡10～15分钟，用水清洗干净，然后再在2～2.5mol/L的氢氧化钾溶液中浸泡20～30分钟，用水清洗干净，最后在600～700℃煅烧2～4小时冷却后制得煅烧贝壳粉。
6.根据权利要求1所述的一种无机涂料墙体用除霉防霉喷剂，其特征在于：
所述白炭黑添加前经以下处理，将白炭黑与其等重的0.5～1.0mol/L硝酸溶液混合后球磨处理30～40分钟，然后用水清洗干净，接着将其加入到1～2mol/L的氢氧化钾溶液中搅拌浸泡10～20分钟，用水清洗至中性后烘干。
7.根据权利要求1所述的一种无机涂料墙体用除霉防霉喷剂，其特征在于由以下方法制得：
将聚乙烯醇溶解于无水乙醇中制得A液，然后将石膏溶解于水中，向水中加入分散剂并溶解，接着依次加入煅烧贝壳粉、白炭黑、钛白粉和蒙脱石长效防霉剂并混合均匀制得B液，最后将A液缓慢的加入到B液中混合均匀后制得无机涂料墙体用除霉防霉喷剂。
8.根据权利要求1或7所述的一种无机涂料墙体用除霉防霉喷剂，其特征在于：
所述煅烧贝壳粉、白炭黑、钛白粉和蒙脱石长效防霉剂的粒径都为85微米及以下，
或，在添加前将煅烧贝壳粉、白炭黑、钛白粉和蒙脱石长效防霉剂粉碎至85微米及以下。