CN109399929A - Transmutation blue glaze and preparation method thereof - Google Patents
Transmutation blue glaze and preparation method thereof Download PDFInfo
- Publication number
- CN109399929A CN109399929A CN201811517175.4A CN201811517175A CN109399929A CN 109399929 A CN109399929 A CN 109399929A CN 201811517175 A CN201811517175 A CN 201811517175A CN 109399929 A CN109399929 A CN 109399929A
- Authority
- CN
- China
- Prior art keywords
- glaze
- transmutation
- component
- blue
- oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of transmutation blue glaze and preparation method thereof, the component and each component mass percent contained in glaze used in transmutation blue glaze is as follows: silica 61%;Aluminum oxide 13%;Di-iron trioxide 0.8%;Magnesia 0.1%;Calcium oxide 15%;Potassium oxide 4.5%;Sodium oxide molybdena 2.7%;Barium monoxide 0.007%;Titanium dioxide 0.1%;Phosphorus pentoxide 0.02%;Vanadic anhydride 2.8%;Surplus is inevitable impurity.Red or copper red color is presented in glaze of the invention, colorful, and unexpected effect is presented.
Description
Technical field
The present invention relates to a kind of transmutation blue glazes and preparation method thereof.
Background technique
Currently, the moulding of porcelain billet is the basis of quality product in porcelain industry, the allotment of glaze keeps porcelain more gorgeous
Colorful, the porcelain billet of same moulding often because of the difference of glaze, and generates different influences to the vision of consumer.
Summary of the invention
The technical problem to be solved by the present invention is to overcome the deficiencies of existing technologies, a kind of transmutation blue glaze, its glaze are provided
Sky blue is presented in face, and decorative effect is strong, and color is beautiful, glaze jade-like stone profit.
In order to solve the above-mentioned technical problem, the technical scheme is that a kind of transmutation blue glaze, in glaze used in it
The component and each component mass percent contained is as follows:
Silica 60.5%;
Aluminum oxide 13%;
Di-iron trioxide 0.8%;
Magnesia 0.1%;
Calcium oxide 15%;
Potassium oxide 4.5%;
Sodium oxide molybdena 2.7%;
Barium monoxide 0.007%;
Titanium dioxide 0.1%;
Phosphorus pentoxide 0.02%;
Vanadic anhydride 2.8%;
Surplus is inevitable impurity.
The present invention also provides a kind of preparation method of transmutation blue glaze, the step of method in contain:
S1: it stocks up according to the component and each component mass parts of glaze;
S2: glaze: ball: mass ratio=1:1:1.5 of water is pressed, wet ball grinding 15~18 hours, the glaze after ball milling was sieved
With remove iron, then be tuned into the glaze slip of 40~45 Baume degrees;
S3: after the chinaware body for taking appearance bright and clean immerses the glaze slip, through being fired under 1220 DEG C -1380 DEG C of oxidizing atmospheres
Product.
After above-mentioned technical proposal, using the formula of this transmutation blue glaze, sky blue, decorative effect is presented in glaze
By force, color is beautiful, glaze jade-like stone profit.
Specific embodiment
In order that the present invention can be more clearly and readily understood, below according to specific embodiment, to the present invention make into
One step detailed description.
A kind of transmutation blue glaze, the component and each component mass percent contained in glaze used in it are as follows:
Silica 60.5%;
Aluminum oxide 13%;
Di-iron trioxide 0.8%;
Magnesia 0.1%;
Calcium oxide 15%;
Potassium oxide 4.5%;
Sodium oxide molybdena 2.7%;
Barium monoxide 0.007%;
Titanium dioxide 0.1%;
Phosphorus pentoxide 0.02%;
Vanadic anhydride 2.8%;
Surplus is inevitable impurity.
Contain in the step of preparation method of the transmutation blue glaze, method:
S1: it stocks up according to the component and each component mass parts of glaze;
S2: glaze: ball: mass ratio=1:1:1.5 of water is pressed, wet ball grinding 15~18 hours, the glaze after ball milling was sieved
With remove iron, then be tuned into the glaze slip of 40~45 Baume degrees;
S3: after the chinaware body for taking appearance bright and clean immerses the glaze slip, through being fired under 1220 DEG C -1380 DEG C of oxidizing atmospheres
Product.
The transmutation blue glaze that above embodiments are prepared, by it has been observed that sky blue can be presented in its glaze, color is bright
Beautiful, glaze jade-like stone profit meets design requirement.
Particular embodiments described above, pair present invention solves the technical problem that, technical scheme and beneficial effects carry out
It is further described, it should be understood that the above is only a specific embodiment of the present invention, is not limited to this
Invention, all within the spirits and principles of the present invention, any modification, equivalent substitution, improvement and etc. done should be included in this hair
Within bright protection scope.
Claims (2)
1. a kind of transmutation blue glaze, it is characterised in that the component and each component mass percent contained in glaze used in it is such as
Under:
Silica 60.5%;
Aluminum oxide 13%;
Di-iron trioxide 0.8%;
Magnesia 0.1%;
Calcium oxide 15%;
Potassium oxide 4.5%;
Sodium oxide molybdena 2.7%;
Barium monoxide 0.007%;
Titanium dioxide 0.1%;
Phosphorus pentoxide 0.02%;
Vanadic anhydride 2.8%;
Surplus is inevitable impurity.
2. a kind of preparation method of transmutation blue glaze as described in claim 1, it is characterised in that contain in the step of method:
S1: it stocks up according to the component and each component mass parts of glaze;
S2: glaze: ball: mass ratio=1:1:1.5 of water is pressed, wet ball grinding 15~18 hours, the glaze after ball milling was sieved and removes
Iron, then it is tuned into the glaze slip of 40~45 Baume degrees;
S3: after the chinaware body for taking appearance bright and clean immerses the glaze slip, through firing finished product under 1220 DEG C -1380 DEG C of oxidizing atmospheres.