CN109133647A - Starry sky reacts blue glaze and preparation method thereof - Google Patents
Starry sky reacts blue glaze and preparation method thereof Download PDFInfo
- Publication number
- CN109133647A CN109133647A CN201811152921.4A CN201811152921A CN109133647A CN 109133647 A CN109133647 A CN 109133647A CN 201811152921 A CN201811152921 A CN 201811152921A CN 109133647 A CN109133647 A CN 109133647A
- Authority
- CN
- China
- Prior art keywords
- parts
- coat enamel
- component
- ground coat
- glaze
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of starry sky to react blue glaze and preparation method thereof, starry sky reacts blue glaze and contains ground coat enamel and overglaze, the component and each component mass parts that ground coat enamel material contains used in the ground coat enamel are as follows: 40~45 parts of feldspar powder, 40~50 parts of Shi porcelain billet mud, 18~20 parts of iron oxide, 5~7 parts of manganese carbonate, 5~8 parts of wollastonite;Cobalt oxide and millesimal copper oxide that mass percent is 3/1000ths~6 are also added in the ground coat enamel material;The component and each component mass parts that glaze material used in the overglaze contains are as follows: 35~40 parts of low temperature frit, 30~35 parts of quartz calcines 25~30 parts of spodumene, 10~12 parts of calcite, 3~6 parts of Guizhou clay, 2~4 parts of Jiepai clay, 5~10 parts of calcinated talc powder, 8~12 parts of titanium dioxide.Its glaze paint generates indistinct starry sky orchid effect, looks at a glance boundless, and people is allowed to generate unlimited reverie.
Description
Technical field
The present invention relates to a kind of starry sky to react blue glaze and preparation method thereof.
Background technique
Currently, the moulding of porcelain billet is the basis of quality product in porcelain industry, the allotment of glaze keeps porcelain more gorgeous
Colorful, the porcelain billet of same moulding often because of the difference of glaze paint, and generates different influences to the vision of consumer.
Summary of the invention
The technical problem to be solved by the present invention is to overcome the deficiencies of existing technologies, a kind of blue glaze of starry sky reaction is provided, it
Glaze paint generate indistinct starry sky orchid effect, look at a glance boundless, people allowed to generate unlimited reverie.
In order to solve the above-mentioned technical problem, the technical scheme is that a kind of starry sky reacts blue glaze, it contain ground coat enamel and
Overglaze, the component and each component mass parts that ground coat enamel material used in the ground coat enamel contains are as follows:
40~45 parts of feldspar powder, 40~50 parts of Shi porcelain billet mud, 18~20 parts of iron oxide, 5~7 parts of manganese carbonate, wollastonite 5~
8 parts;Cobalt oxide and millesimal copper oxide that mass percent is 3/1000ths~6 are also added in the ground coat enamel material;
The component and each component mass parts that glaze material used in the overglaze contains are as follows:
35~40 parts of low temperature frit, 30~35 parts of quartz, 25~30 parts of spodumene of calcining, 10~12 parts of calcite, Guizhou
3~6 parts, 2~4 parts of Jiepai clay, 5~10 parts of calcinated talc powder, 8~12 parts of titanium dioxide of soil.
Further, the component of the low temperature frit and the mass parts of each component are as follows: feldspar powder: 26~30 parts;Calcite:
20~25 parts;Borax: 25~30 parts;Silica flour: 20~25 parts;Talcum powder: 20~25 parts;Potassium nitrate: 20~25 parts.
Further, the calcining spodumene is calcined using spodumene by 1350 DEG C~1400 DEG C of temperature environment.
The present invention also provides the preparation method that a kind of starry sky reacts blue glaze, the step of method in contain:
S1: ground coat enamel slurry and overglaze slurry are prepared respectively;Wherein, the preparation process that the preparation process of ground coat enamel slurry and overglaze are starched is such as
Under: it stocks up respectively according to the mass parts of each component and each component;According to material: ball: mass ratio=1:1.5:0.5 of water, wet process ball
Then mill 6~10 hours crosses 160 mesh screens, then be tuned into the glaze slip that concentration is 25-30 Baume degrees;
S2: ground coat enamel is applied on biscuit using ground coat enamel slurry, then spray plane glaze is starched using overglaze, enters kiln after dry, by 1160-
1200 DEG C of temperature environment burns finished product.
After above-mentioned technical proposal, starry sky glaze paint of the invention generates indistinct starry sky orchid effect, hopes at a glance
It goes boundless, people is allowed to generate unlimited reverie.
Specific embodiment
In order that the present invention can be more clearly and readily understood, below according to specific embodiment, to the present invention make into
One step detailed description.
Embodiment one
A kind of starry sky reacts blue glaze, it contains ground coat enamel and overglaze, ground coat enamel material contains used in the ground coat enamel component and
Each component mass parts are as follows:
40 parts of feldspar powder, 40 parts of Shi porcelain billet mud, 18 parts of iron oxide, 5 parts of manganese carbonate, 5 parts of wollastonite;In the ground coat enamel material also
Add cobalt oxide and millesimal copper oxide that mass percent is 3/1000ths;
The component and each component mass parts that glaze material used in the overglaze contains are as follows:
35 parts of low temperature frit, 30 parts of quartz, 25 parts of spodumene of calcining, 10 parts of calcite, 3 parts of Guizhou clay, 2 parts of Jiepai clay,
5 parts of calcinated talc powder, 8 parts of titanium dioxide.
The component of the low temperature frit and the mass parts of each component are as follows: feldspar powder: 26 parts;Calcite: 20 parts;Borax:
25 parts;Silica flour: 20 parts;Talcum powder: 20 parts;Potassium nitrate: 20 parts.
The calcining spodumene is calcined using spodumene by 1350 DEG C~1400 DEG C of temperature environment.
Contain in the step of preparation method of the blue glaze of starry sky reaction, method:
S1: ground coat enamel slurry and overglaze slurry are prepared respectively;Wherein, the preparation process that the preparation process of ground coat enamel slurry and overglaze are starched is such as
Under: it stocks up respectively according to the mass parts of each component and each component;According to material: ball: mass ratio=1:1.5:0.5 of water, wet process ball
Then mill 6 hours crosses 160 mesh screens, then be tuned into the glaze slip that concentration is 25-30 Baume degrees;
S2: ground coat enamel is applied on biscuit using ground coat enamel slurry, then spray plane glaze is starched using overglaze, enters kiln after dry, by 1160-
1200 DEG C of temperature environment burns finished product.
Embodiment two
A kind of starry sky reacts blue glaze, it contains ground coat enamel and overglaze, ground coat enamel material contains used in the ground coat enamel component and
Each component mass parts are as follows:
45 parts of feldspar powder, 50 parts of Shi porcelain billet mud, 20 parts of iron oxide, 7 parts of manganese carbonate, 8 parts of wollastonite;In the ground coat enamel material also
Add cobalt oxide and millesimal copper oxide that mass percent is 6/1000ths;
The component and each component mass parts that glaze material used in the overglaze contains are as follows:
40 parts of low temperature frit, 35 parts of quartz, 30 parts of spodumene of calcining, 12 parts of calcite, 6 parts of Guizhou clay, 4 parts of Jiepai clay,
10 parts of calcinated talc powder, 12 parts of titanium dioxide.
The component of the low temperature frit and the mass parts of each component are as follows: feldspar powder: 30 parts;Calcite: 25 parts;Borax:
30 parts;Silica flour: 25 parts;Talcum powder: 25 parts;Potassium nitrate: 25 parts.
The calcining spodumene is calcined using spodumene by 1350 DEG C~1400 DEG C of temperature environment.
Contain in the step of preparation method of the blue glaze of starry sky reaction, method:
S1: ground coat enamel slurry and overglaze slurry are prepared respectively;Wherein, the preparation process that the preparation process of ground coat enamel slurry and overglaze are starched is such as
Under: it stocks up respectively according to the mass parts of each component and each component;According to material: ball: mass ratio=1:1.5:0.5 of water, wet process ball
Then mill 10 hours crosses 160 mesh screens, then be tuned into the glaze slip that concentration is 25-30 Baume degrees;
S2: ground coat enamel is applied on biscuit using ground coat enamel slurry, then spray plane glaze is starched using overglaze, enters kiln after dry, by 1160-
1200 DEG C of temperature environment burns finished product.
Embodiment three
A kind of starry sky reacts blue glaze, it contains ground coat enamel and overglaze, ground coat enamel material contains used in the ground coat enamel component and
Each component mass parts are as follows:
42 parts of feldspar powder, 45 parts of Shi porcelain billet mud, 19 parts of iron oxide, 6 parts of manganese carbonate, 7 parts of wollastonite;In the ground coat enamel material also
Add cobalt oxide and millesimal copper oxide that mass percent is 5/1000ths;
The component and each component mass parts that glaze material used in the overglaze contains are as follows:
37 parts of low temperature frit, 32 parts of quartz, 26 parts of spodumene of calcining, 11 parts of calcite, 4 parts of Guizhou clay, 3 parts of Jiepai clay,
7 parts of calcinated talc powder, 10 parts of titanium dioxide.
The component of the low temperature frit and the mass parts of each component are as follows: feldspar powder: 27 parts;Calcite: 22 parts;Borax:
27 parts;Silica flour: 22 parts;Talcum powder: 22 parts;Potassium nitrate: 22 parts.
The calcining spodumene is calcined using spodumene by 1350 DEG C~1400 DEG C of temperature environment.
Contain in the step of preparation method of the blue glaze of starry sky reaction, method:
S1: ground coat enamel slurry and overglaze slurry are prepared respectively;Wherein, the preparation process that the preparation process of ground coat enamel slurry and overglaze are starched is such as
Under: it stocks up respectively according to the mass parts of each component and each component;According to material: ball: mass ratio=1:1.5:0.5 of water, wet process ball
Then mill 8 hours crosses 160 mesh screens, then be tuned into the glaze slip that concentration is 25-30 Baume degrees;
S2: ground coat enamel is applied on biscuit using ground coat enamel slurry, then spray plane glaze is starched using overglaze, enters kiln after dry, by 1160-
1200 DEG C of temperature environment burns finished product.
The starry sky that three above embodiment is prepared reacts blue glaze, and it is blue to generate indistinct starry sky on glaze surface
Effect meets design requirement.
Particular embodiments described above, pair present invention solves the technical problem that, technical scheme and beneficial effects carry out
It is further described, it should be understood that the above is only a specific embodiment of the present invention, is not limited to this
Invention, all within the spirits and principles of the present invention, any modification, equivalent substitution, improvement and etc. done should be included in this hair
Within bright protection scope.
Claims (4)
1. a kind of starry sky reacts blue glaze, it is characterised in that it contains ground coat enamel and overglaze, and ground coat enamel material used in the ground coat enamel contains
Component and each component mass parts it is as follows:
40~45 parts of feldspar powder, 40~50 parts of Shi porcelain billet mud, 18~20 parts of iron oxide, 5~7 parts of manganese carbonate, 5~8 parts of wollastonite;
Cobalt oxide and millesimal copper oxide that mass percent is 3/1000ths~6 are also added in the ground coat enamel material;
The component and each component mass parts that glaze material used in the overglaze contains are as follows:
35~40 parts of low temperature frit, 30~35 parts of quartz, 25~30 parts of spodumene of calcining, 10~12 parts of calcite, Guizhou clay 3~
6 parts, 2~4 parts of Jiepai clay, 5~10 parts of calcinated talc powder, 8~12 parts of titanium dioxide.
2. starry sky according to claim 1 reacts blue glaze, it is characterised in that: the component of the low temperature frit and each component
Mass parts are as follows: feldspar powder: 26~30 parts;Calcite: 20~25 parts;Borax: 25~30 parts;Silica flour: 20~25 parts;Talcum
Powder: 20~25 parts;Potassium nitrate: 20~25 parts.
3. starry sky according to claim 1 reacts blue glaze, it is characterised in that: the calcining spodumene is passed through using spodumene
1350 DEG C~1400 DEG C of temperature environment is calcined.
4. the preparation method that a kind of starry sky according to any one of claims 1 to 3 reacts blue glaze, it is characterised in that method
Contain in step:
S1: ground coat enamel slurry and overglaze slurry are prepared respectively;Wherein, the preparation process of ground coat enamel slurry and the preparation process of overglaze slurry are as follows:
It stocks up respectively according to the mass parts of each component and each component;According to material: ball: mass ratio=1:1.5:0.5 of water, wet ball grinding 6
~10 hours, 160 mesh screens are then crossed, then are tuned into the glaze slip that concentration is 25-30 Baume degrees;
S2: ground coat enamel is applied on biscuit using ground coat enamel slurry, then spray plane glaze is starched using overglaze, enters kiln after dry, by 1160-1200
DEG C temperature environment burn finished product.