CN109354727A - A kind of colorful rubber product and its manufacture craft - Google Patents
A kind of colorful rubber product and its manufacture craft Download PDFInfo
- Publication number
- CN109354727A CN109354727A CN201811242189.XA CN201811242189A CN109354727A CN 109354727 A CN109354727 A CN 109354727A CN 201811242189 A CN201811242189 A CN 201811242189A CN 109354727 A CN109354727 A CN 109354727A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber product
- colorful rubber
- colorful
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of colorful rubber product and its manufacture crafts.Colorful rubber product includes being composed of the following parts by weight: 30-50 parts of natural rubber, 20-40 parts of light calcium, 4-6 parts of White Carbon black, 9-11 parts of naphthenic oil, 2-4 parts of zinc oxide, 0.2-0.6 parts of polyethylene glycol, 0.5-1.5 parts of stearic acid, 0.5-1 parts of protection wax, 0.5-1.5 parts of anti-aging agent, 3-5 parts of magnesium carbonate, 1-3 parts of sulphur, 2-4 parts of promotor.Compared with prior art, the beneficial effects of the present invention are: component used in the present invention is conventional raw material, it is easy to get and low in cost, obtained colorful rubber product style, structure novel, workmanship is exquisite, quality is preferable, deep to be liked by masses, has preferable market prospects, and the manufacture craft of the colorful rubber product provided, process is succinct, has saved the time, reduces costs.
Description
Technical field
The present invention relates to field of rubber technology more particularly to a kind of colorful rubber product and its manufacture crafts.
Background technique
With the development of the times, colorful rubber product is becoming increasingly popular, and the type of colorful rubber product has much for example
Colorful rubber gloves, color rubber mat, colorful rubber cell-phone cover, colorful rubber toy etc., but colored rubber in the prior art
Glue article construction, style are single, and no novelty, quality not can guarantee, in addition, the manufacture craft of colorful rubber product is more numerous
It is trivial, it takes a long time, higher cost.
In view of this, it is necessary to colorful rubber product in the prior art and its manufacture craft be improved, to solve
The above problem.
Summary of the invention
The purpose of the present invention one is to disclose a kind of colorful rubber product, and component used is conventional raw material, is easy to get
And low in cost, gained colorful rubber product style, structure novel, workmanship is exquisite, and quality is preferable, deep to be liked having by masses
Preferable market prospects.
To achieve the above object, the present invention provides a kind of colorful rubber products, including the component by following parts by weight
Composition: 30-50 parts of natural rubber, 20-40 parts of light calcium, 4-6 parts of White Carbon black, 9-11 parts of naphthenic oil, 2-4 parts of zinc oxide, poly- second two
0.2-0.6 parts of alcohol, 0.5-1.5 parts of stearic acid, 0.5-1 parts of protection wax, 0.5-1.5 parts of anti-aging agent, 3-5 parts of magnesium carbonate, sulphur 1-
3 parts, 2-4 parts of promotor.
In some embodiments, it including is composed of the following parts by weight: 40 parts of natural rubber, 30 parts of light calcium,
5 parts of White Carbon black, 10 parts of naphthenic oil, 3 parts of zinc oxide, 0.5 part of polyethylene glycol, 1 part of stearic acid, 0.7 part of protection wax, anti-aging agent 0.8
Part, 4 parts of magnesium carbonate, 2 parts of sulphur, 3 parts of promotor.
The purpose of the present invention two is to disclose a kind of manufacture craft of colorful rubber product, and process is succinct, has saved the time,
It reduces costs, style, structure novel is made, workmanship is exquisite, and quality is preferable, and it is deep to be liked by masses, there is preferable city
The colorful rubber product of field prospect.
To achieve the above object, the present invention provides a kind of manufacture craft of colorful rubber product, include the following steps:
Step 1: by natural rubber, light calcium, White Carbon black, naphthenic oil, zinc oxide, polyethylene glycol, stearic acid, protection wax, prevent always
Agent, magnesium carbonate are put into mixer and are kneaded, and after mixing, take out and stand；
Step 2: pouring into open mill, and sulphur and promotor is added, out print；
Step 3: print is placed on press machine and stamps out required shape；
Step 4: the print after punching press is put into the bed die of three layers of mold and is once vulcanized；
Step 5: the print after taking one piece of punching press again is put into the middle mould of three layers of mold and carries out post-cure, takes out two vulcanizations
Product afterwards；
Step 6: an interiors of products is packed into BB and cries wherein；
Step 7: two products are carried out suturing on sewing machine and reserve opening for filling-in cotton；
Step 8: it carries out filling cotton by opening for filling-in cotton on cotton-filling machine；
Step 9: bound edge is carried out on sewing machine and sutures to obtain colorful rubber product.
In some embodiments, in step 1, mixing time 20min-40min, melting temperature is 100 degree -120
Degree takes out and stands 20h-25h.
In some embodiments, in step 2, print with a thickness of 2mm-4mm.
In some embodiments, in step 4, vulcanization time 0.5min-1.5min, curing temperature be 140 degree-
160 degree.
In some embodiments, in step 5, vulcanization time 1min-3min, curing temperature is 140 degree -160
Degree.
Compared with prior art, it the beneficial effects of the present invention are: component used in the present invention is conventional raw material, is easy to get
And it is low in cost, obtained colorful rubber product style, structure novel, workmanship is exquisite, and quality is preferable, and it is deep to be liked by masses,
With preferable market prospects, and the manufacture craft of the colorful rubber product provided, process is succinct, has saved the time, reduces
Cost.
Specific embodiment
Below with reference to each embodiment, the present invention is described in detail, but it should be stated that, these embodiments are simultaneously
Non- limitation of the present invention, those of ordinary skill in the art are according to these embodiments in made function, method or structure
Equivalent transformation or substitution, all belong to the scope of protection of the present invention within.
Embodiment one:
Present embodiment discloses a kind of colorful rubber products, including are composed of the following parts by weight: 30 parts of natural rubber,
20 parts of light calcium, 4 parts of White Carbon black, 9 parts of naphthenic oil, 2 parts of zinc oxide, 0.2 part of polyethylene glycol, 0.5 part of stearic acid, protection wax 0.5
Part, 0.5 part of anti-aging agent, 3 parts of magnesium carbonate, 1 part of sulphur, 2 parts of promotor.
Present embodiment discloses a kind of manufacture crafts of colorful rubber product, include the following steps:
Step 1: by natural rubber, light calcium, White Carbon black, naphthenic oil, zinc oxide, polyethylene glycol, stearic acid, protection wax, prevent always
Agent, magnesium carbonate are put into mixer and are kneaded, and after mixing, take out and stand；
Step 2: pouring into open mill, and sulphur and promotor is added, out print；
Step 3: print is placed on press machine and stamps out required shape；
Step 4: the print after punching press is put into the bed die of three layers of mold and is once vulcanized；
Step 5: the print after taking one piece of punching press again is put into the middle mould of three layers of mold and carries out post-cure, takes out two vulcanizations
Product afterwards；
Step 6: an interiors of products is packed into BB and cries wherein；
Step 7: two products are carried out suturing on sewing machine and reserve opening for filling-in cotton；
Step 8: it carries out filling cotton by opening for filling-in cotton on cotton-filling machine；
Step 9: bound edge is carried out on sewing machine and sutures to obtain colorful rubber product.
In some embodiments, in step 1, mixing time 20min, melting temperature is 100 degree, takes out and stands
20h。
In some embodiments, in step 2, print with a thickness of 2mm.
In some embodiments, in step 4, vulcanization time 0.5min, curing temperature is 140 degree.
In some embodiments, in step 5, vulcanization time 1min, curing temperature is 140 degree.
Embodiment two:
Present embodiment discloses a kind of colorful rubber products, including are composed of the following parts by weight: 40 parts of natural rubber,
30 parts of light calcium, 5 parts of White Carbon black, 10 parts of naphthenic oil, 3 parts of zinc oxide, 0.5 part of polyethylene glycol, 1 part of stearic acid, 0.7 part of protection wax,
0.8 part of anti-aging agent, 4 parts of magnesium carbonate, 2 parts of sulphur, 3 parts of promotor.
Present embodiment discloses a kind of manufacture crafts of colorful rubber product, include the following steps:
Step 1: by natural rubber, light calcium, White Carbon black, naphthenic oil, zinc oxide, polyethylene glycol, stearic acid, protection wax, prevent always
Agent, magnesium carbonate are put into mixer and are kneaded, and after mixing, take out and stand；
Step 2: pouring into open mill, and sulphur and promotor is added, out print；
Step 3: print is placed on press machine and stamps out required shape；
Step 4: the print after punching press is put into the bed die of three layers of mold and is once vulcanized；
Step 5: the print after taking one piece of punching press again is put into the middle mould of three layers of mold and carries out post-cure, takes out two vulcanizations
Product afterwards；
Step 6: an interiors of products is packed into BB and cries wherein；
Step 7: two products are carried out suturing on sewing machine and reserve opening for filling-in cotton；
Step 8: it carries out filling cotton by opening for filling-in cotton on cotton-filling machine；
Step 9: bound edge is carried out on sewing machine and sutures to obtain colorful rubber product.
In some embodiments, in step 1, mixing time 30min, melting temperature is 110 degree, takes out and stands
24h。
In some embodiments, in step 2, print with a thickness of 3mm.
In some embodiments, in step 4, vulcanization time 1min, curing temperature is 150 degree.
In some embodiments, in step 5, vulcanization time 2min, curing temperature is 150 degree.
Embodiment three:
Present embodiment discloses a kind of colorful rubber products, including are composed of the following parts by weight: 50 parts of natural rubber,
40 parts of light calcium, 6 parts of White Carbon black, 11 parts of naphthenic oil, 4 parts of zinc oxide, 0.6 part of polyethylene glycol, 1.5 parts of stearic acid, 1 part of protection wax,
1.5 parts of anti-aging agent, 5 parts of magnesium carbonate, 3 parts of sulphur, 4 parts of promotor.
Present embodiment discloses a kind of manufacture crafts of colorful rubber product, include the following steps:
Step 1: by natural rubber, light calcium, White Carbon black, naphthenic oil, zinc oxide, polyethylene glycol, stearic acid, protection wax, prevent always
Agent, magnesium carbonate are put into mixer and are kneaded, and after mixing, take out and stand；
Step 2: pouring into open mill, and sulphur and promotor is added, out print；
Step 3: print is placed on press machine and stamps out required shape；
Step 4: the print after punching press is put into the bed die of three layers of mold and is once vulcanized；
Step 5: the print after taking one piece of punching press again is put into the middle mould of three layers of mold and carries out post-cure, takes out two vulcanizations
Product afterwards；
Step 6: an interiors of products is packed into BB and cries wherein；
Step 7: two products are carried out suturing on sewing machine and reserve opening for filling-in cotton；
Step 8: it carries out filling cotton by opening for filling-in cotton on cotton-filling machine；
Step 9: bound edge is carried out on sewing machine and sutures to obtain colorful rubber product.
In some embodiments, in step 1, mixing time 40min, melting temperature is 120 degree, takes out and stands
25h。
In some embodiments, in step 2, print with a thickness of 4mm.
In some embodiments, in step 4, vulcanization time 1.5min, curing temperature is 160 degree.
In some embodiments, in step 5, vulcanization time 3min, curing temperature is 160 degree.
The series of detailed descriptions listed above only for feasible embodiment of the invention specifically
Protection scope bright, that they are not intended to limit the invention, it is all without departing from equivalent implementations made by technical spirit of the present invention
Or change should all be included in the protection scope of the present invention.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiments being understood that.
Claims (7)
1. a kind of colorful rubber product, which is characterized in that including being composed of the following parts by weight: natural rubber 30-50
Part, 20-40 parts of light calcium, 4-6 parts of White Carbon black, 9-11 parts of naphthenic oil, 2-4 parts of zinc oxide, 0.2-0.6 parts of polyethylene glycol, stearic acid
0.5-1.5 parts, 0.5-1 parts of protection wax, 0.5-1.5 parts of anti-aging agent, 3-5 parts of magnesium carbonate, 1-3 parts of sulphur, 2-4 parts of promotor.
2. colorful rubber product according to claim 1, which is characterized in that including the group grouping by following parts by weight
At: 40 parts of natural rubber, 30 parts of light calcium, 5 parts of White Carbon black, 10 parts of naphthenic oil, 3 parts of zinc oxide, 0.5 part of polyethylene glycol, stearic acid 1
Part, 0.7 part of protection wax, 0.8 part of anti-aging agent, 4 parts of magnesium carbonate, 2 parts of sulphur, 3 parts of promotor.
3. a kind of manufacture craft of colorful rubber product as claimed in claim 1 or 2, which comprises the steps of:
Step 1: by natural rubber, light calcium, White Carbon black, naphthenic oil, zinc oxide, polyethylene glycol, stearic acid, protection wax, prevent always
Agent, magnesium carbonate are put into mixer and are kneaded, and after mixing, take out and stand；
Step 2: pouring into open mill, and sulphur and promotor is added, out print；
Step 3: print is placed on press machine and stamps out required shape；
Step 4: the print after punching press is put into the bed die of three layers of mold and is once vulcanized；
Step 5: the print after taking one piece of punching press again is put into the middle mould of three layers of mold and carries out post-cure, takes out two vulcanizations
Product afterwards；
Step 6: an interiors of products is packed into BB and cries wherein；
Step 7: two products are carried out suturing on sewing machine and reserve opening for filling-in cotton；
Step 8: it carries out filling cotton by opening for filling-in cotton on cotton-filling machine；
Step 9: bound edge is carried out on sewing machine and sutures to obtain colorful rubber product.
4. the manufacture craft of colorful rubber product according to claim 3, which is characterized in that in step 1, when mixing
Between be 20min-40min, melting temperature be 100 degree -120 degree, take out standing 20h-25h.
5. the manufacture craft of colorful rubber product according to claim 3, which is characterized in that in step 2, print
With a thickness of 2mm-4mm.
6. the manufacture craft of colorful rubber product according to claim 3, which is characterized in that in step 4, when vulcanization
Between be 0.5min-1.5min, curing temperature be 140 degree -160 spend.
7. the manufacture craft of colorful rubber product according to claim 3, which is characterized in that in step 5, when vulcanization
Between be 1min-3min, curing temperature be 140 degree -160 spend.