CN109338586A - A kind of moisture absorption heating warp knit cut pile fabric production technology - Google Patents
A kind of moisture absorption heating warp knit cut pile fabric production technology Download PDFInfo
- Publication number
- CN109338586A CN109338586A CN201811150465.XA CN201811150465A CN109338586A CN 109338586 A CN109338586 A CN 109338586A CN 201811150465 A CN201811150465 A CN 201811150465A CN 109338586 A CN109338586 A CN 109338586A
- Authority
- CN
- China
- Prior art keywords
- warp knit
- fabric
- moisture absorption
- cut pile
- absorption heating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of moisture absorption heating warp knit cut pile fabric production technologies, it include the viscose rayon of the terylene elater of 83dtex/72f, 30~45% EKS fiber, 60~70% bamboo fiber that weight ratio is 50~65% and 45~60% in moisture absorption heating warp knit cut pile fabric, the production technology of moisture absorption heating warp knit cut pile fabric carries out shaping the following steps are included: twisting fabric after molding to warp knit by HKS3 tricot machine, then fabric is carried out base inspection, dyeing, dehydration open-width, drying, cut pile and last clot and is processed.The present invention, which twists the fabric formed by the warp knit by terylene elater, EKS fiber, bamboo fiber and viscose rayon, has highly hygroscopic, fever and good permeability, the moisture generated when human motion can be absorbed, it is chemically reacted in fibrous inside, therefore fabric can have moisture absorption exothermal effect, so that the temperature inside clothes is risen to 2~4 °, is fabricated to clothing and strengthens wearing comfort.
Description
Technical field
The present invention relates to a kind of warp-knitted face fabric production technology, in particular to a kind of moisture absorption heating warp knit cut pile fabric produces work
Skill.
Background technique
It is divided into knitting, braiding and non-woven in fabric production process, wherein knitting is divided into warp knit and weft knitting again, warp knit is to belong to
A kind of textile technology in knitting field, with one group or several groups of yarns arranged in parallel, in through all working to feeding machine
On needle, at the same lopping and form knitted fabric, this method is known as warp knit, and the knitted fabric of formation is known as knitted fabric, with science
The development of technology and the continuous improvement of living standard, people are higher and higher to functionality and the comfort requirement of clothes, in order to full
Requirement of the sufficient people to textile, continually developing novel textile material and improving dress designing structure becomes textile designs and hair
The main trend of exhibition, cut pile, which refers to cut by the looped pile of common towel, cuts processing, so that fabric surface is covered with smooth villus, cuts
Villus towel can two-sided all cut piles, can also with single side cut pile, another side still for looped pile, can also with velvet pile formed grain pattern pile loop
Coexist, mutually print lining, the characteristics of sheared towel be it is soft, using comfortable, have stronger hygroscopicity and pliability than common towel,
And general warp knit cut pile fabric itself, do not have good ventilative moisture absorption exothermal effect, in recent years, " light, thin, warm " is taken
New concept is popular, realizes that emerging for the spontaneous heating shell fabric of warming requirement further improves weaving newly by autonomous heat production mode
The value of material.
Summary of the invention
The technical problem to be solved by the present invention is to overcome the defects of the prior art, provide a kind of moisture absorption heating warp knit cut pile face
Material manufacturing technique twists the fabric tool formed by the warp knit by terylene elater, EKS fiber, bamboo fiber and viscose rayon
There are highly hygroscopic, fever and good permeability, the moisture generated when human motion can be absorbed, in fibrous inside
Reaction is learned, therefore fabric there can be moisture absorption exothermal effect, the temperature inside clothes is enable to rise to 2~4 °, makes ready-made clothes
Object strengthens wearing comfort.
In order to solve the above-mentioned technical problems, the present invention provides the following technical solutions:
A kind of moisture absorption heating warp knit cut pile fabric production technology of the present invention includes in the moisture absorption heating warp knit cut pile fabric
Having weight ratio is terylene elater, 30~45% EKS fiber, 60~70% bamboo fiber of 50~65% 83dtex/72f
And 45~60% viscose rayon, the production technology of moisture absorption heating warp knit cut pile fabric the following steps are included:
A. machine parameter:
HKS3 tricot machine type is selected, machine number is 28 needles/25.4mm, and working width is 427cm (168 "), and sley bar number is
3;
B. technique tissue:
Choose terylene elater, 30~45% EKS fiber, 60~70% bamboo fibril of 50~65% 83dtex/72f
Dimension and 45~60% viscose rayon be used as raw material, and distinguish successively according to GB1:1-0/3-4//;GB2:1-0/1-2//;
GB3:1-0/2-4//;GB4:1-0/1-2//band yarn mode carry out band yarn arrangement;
C. it entrys:
GB1 is completely to wear, and warping radical is 588 * 8;
GB2 wears 6 skies for 1, and warping radical is 84*8;
GB3 is completely to wear, and warping radical is 588 * 8;
GB4 wears 4 skies for 1, and warping radical is 84*8;
D. warp run-in:
GB12180mm/rack;
GB21500mm/rack;
GB31350mm/rack;
GB42220mm/rack;
E. warp knit twisting fabric after molding will be carried out shaping by above step by HKS3 tricot machine, then by fabric
Carry out base inspection, dyeing, dehydration open-width, drying, cut pile and last clot processing.
It is red using disperse dyes 3B during being dyed in the step E as a preferred technical solution of the present invention
It as dyestuff, adds dispersing agent WA, penetrating agent JFC and acetic acid and is dyed as auxiliary agent, and in dyeing course, first by temperature liter
Temperature is warming up to after 120 DEG C again after dyestuff, auxiliary agent is added to 60 DEG C and keeps the temperature 30-45 minutes or so, soaks dyestuff with cloth completely
Dye is together.
The present invention twists the fabric formed by the warp knit by terylene elater, EKS fiber, bamboo fiber and viscose rayon
With highly hygroscopic, fever and good permeability, the moisture generated when human motion can be absorbed, is occurred in fibrous inside
Chemical reaction, therefore fabric can have moisture absorption exothermal effect, so that the temperature inside clothes is risen to 2~4 °, be fabricated to
Clothing strengthens wearing comfort.
Specific embodiment
Hereinafter, preferred embodiments of the present invention will be described, it should be understood that preferred embodiment described herein is only used
In the description and interpretation present invention, it is not intended to limit the present invention.
Embodiment 1
The present invention provides a kind of moisture absorption heating warp knit cut pile fabric production technology, includes in moisture absorption heating warp knit cut pile fabric
Having weight ratio is terylene elater, 30~45% EKS fiber, 60~70% bamboo fiber of 50~65% 83dtex/72f
And 45~60% viscose rayon, EKS is a kind of completely new material of self-heating and warm body, have the exothermic effect of moisture absorption
Fruit, bamboo fiber are bundle fiber, and it is irregular ellipse that longitudinal direction is made of more single fibers, and single fiber thickness is unevenly distributed
Round, kidney ellipsoid and polygon row section have been covered with the gap formed between big and small fiber, the cross section of single fiber on cross section
Inside there is lumen, and there is crackle at edge, radial cracking is deep, long, and there are many fine grooves for bamboo fiber longitudinal surface, with a little
Crackle, just because of these grooves and crack of the horizontal and vertical cross section structure of bamboo fiber cause fiber can be in moment
It absorbs or evaporates a large amount of moisture, through a large amount of gas, there is good hygroscopicity and gas permeability, viscose rayon can absorb
The moisture generated when human motion is chemically reacted in fibrous inside, therefore fabric can have moisture absorption exothermal effect, make clothing
Clothes inside temperature can rise to 2~4 ° of its moisture absorption heating warp knit cut pile fabrics production technology the following steps are included:
A. machine parameter:
HKS3 tricot machine type is selected, machine number is 28 needles/25.4mm, and working width is 427cm (168 "), and sley bar number is
3;
B. technique tissue:
Choose terylene elater, 30~45% EKS fiber, 60~70% bamboo fibril of 50~65% 83dtex/72f
Dimension and 45~60% viscose rayon be used as raw material, and distinguish successively according to GB1:1-0/3-4//;GB2:1-0/1-2//;
GB3:1-0/2-4//;GB4:1-0/1-2//band yarn mode carry out band yarn arrangement;
C. it entrys:
GB1 is completely to wear, and warping radical is 588 * 8;
GB2 wears 6 skies for 1, and warping radical is 84*8;
GB3 is completely to wear, and warping radical is 588 * 8;
GB4 wears 4 skies for 1, and warping radical is 84*8;
D. warp run-in:
GB12180mm/rack;
GB21500mm/rack;
GB31350mm/rack;
GB42220mm/rack;
E. warp knit twisting fabric after molding will be carried out shaping by above step by HKS3 tricot machine, then by fabric
Carry out base inspection, dyeing, dehydration open-width, drying, cut pile and last clot processing.
It is used as dyestuff using disperse dyes 3B is red during dyeing in step E, bright in colour, high-temperature dyeing performance is steady
It is fixed, for the dyeing of terylene, coloring plastic and transfer printing, adds dispersing agent WA, penetrating agent JFC and acetic acid and carried out as auxiliary agent
Dyeing, and in dyeing course, temperature is first warming up to 60 DEG C, is warming up to after 120 DEG C again after dyestuff, auxiliary agent is added and keeps the temperature 30-
45 minutes or so, disseminate dyestuff together with cloth completely.
Specifically, the production technology of moisture absorption heating warp knit cut pile fabric the following steps are included: select HKS3 tricot machine type,
Machine number is 28 needles/25.4mm, and working width is 427cm (168 "), and sley bar number is 3;Choose 50~65% 83dtex/72f
Terylene elater, 30~45% EKS fiber, 60~70% bamboo fiber and 45~60% viscose rayon as former
Material, and respectively successively according to GB1:1-0/3-4//;GB2:1-0/1-2//;GB3:1-0/2-4//;GB4:1-0/1-2//pad
Yarn mode carries out band yarn arrangement;It entrys mode are as follows: GB1 is completely to wear, and warping radical is 588 * 8;GB2 wears 6 skies, warping roots for 1
Number is 84*8;GB3 is completely to wear, and warping radical is 588 * 8;GB4 wears 4 skies for 1, and warping radical is 84*8;Warp run-in is
GB12180mm/rack;GB21500mm/rack;GB31350mm/rack;GB42220mm/rack;HKS3 warp knit will be passed through again
Machine is twisted fabric after molding to warp knit by above step and is carried out shaping, then by fabric carry out base inspection, dyeing, dehydration open-width,
Drying, cut pile and last clot processing are used as dyestuff using disperse dyes 3B is red during color, addition dispersing agent WA,
Penetrating agent JFC and acetic acid are dyed as auxiliary agent, and in dyeing course, temperature is first warming up to 60 DEG C, dyestuff, auxiliary agent is added
It is warming up to after 120 DEG C again afterwards and keeps the temperature 30-45 minutes or so, disseminate dyestuff together with cloth completely.
The present invention twists the fabric formed by the warp knit by terylene elater, EKS fiber, bamboo fiber and viscose rayon
With highly hygroscopic, fever and good permeability, the moisture generated when human motion can be absorbed, is occurred in fibrous inside
Chemical reaction, therefore fabric can have moisture absorption exothermal effect, so that the temperature inside clothes is risen to 2~4 °, be fabricated to
Clothing strengthens wearing comfort.
Finally, it should be noted that the foregoing is only a preferred embodiment of the present invention, it is not intended to restrict the invention,
Although the present invention is described in detail referring to the foregoing embodiments, for those skilled in the art, still may be used
To modify the technical solutions described in the foregoing embodiments or equivalent replacement of some of the technical features.
All within the spirits and principles of the present invention, any modification, equivalent replacement, improvement and so on should be included in of the invention
Within protection scope.
Claims (2)
1. a kind of moisture absorption heating warp knit cut pile fabric production technology, which is characterized in that in the moisture absorption heating warp knit cut pile fabric
It include terylene elater, 30~45% EKS fiber, 60~70% the bamboo original for the 83dtex/72f that weight ratio is 50~65%
Fiber and 45~60% viscose rayon, the production technology of moisture absorption heating warp knit cut pile fabric the following steps are included:
A. machine parameter:
HKS3 tricot machine type is selected, machine number is 28 needles/25.4mm, and working width is 427cm (168 "), and sley bar number is 3;
B. technique tissue:
Choose 50~65% terylene elater of 83dtex/72f, 30~45% EKS fiber, 60~70% bamboo fiber with
And 45~60% viscose rayon as raw material, and respectively successively according to GB1:1-0/3-4//;GB2:1-0/1-2//;GB3:1-
0/2-4//;GB4:1-0/1-2//band yarn mode carry out band yarn arrangement;
C. it entrys:
GB1 is completely to wear, and warping radical is 588 * 8;
GB2 wears 6 skies for 1, and warping radical is 84*8;
GB3 is completely to wear, and warping radical is 588 * 8;
GB4 wears 4 skies for 1, and warping radical is 84*8;
D. warp run-in:
GB12180mm/rack;
GB21500mm/rack;
GB31350mm/rack;
GB42220mm/rack;
E. fabric after molding will be twisted to warp knit by above step by HKS3 tricot machine to carry out shaping, then fabric will be carried out
Base inspection, dyeing, dehydration open-width, drying, cut pile and last clot processing.
2. a kind of moisture absorption heating warp knit cut pile fabric production technology according to claim 1, which is characterized in that the step
It is used as dyestuff using disperse dyes 3B is red during dyeing in E, addition dispersing agent WA, penetrating agent JFC and acetic acid are as auxiliary agent
It is dyed, and in dyeing course, temperature is first warming up to 60 DEG C, be warming up to after 120 DEG C and keep the temperature again after dyestuff, auxiliary agent is added
30-45 minutes or so, disseminate dyestuff together with cloth completely.