CN101603235A - Soybean fiber knitted terry and production technology thereof - Google Patents
Soybean fiber knitted terry and production technology thereof Download PDFInfo
- Publication number
- CN101603235A CN101603235A CNA2008100712119A CN200810071211A CN101603235A CN 101603235 A CN101603235 A CN 101603235A CN A2008100712119 A CNA2008100712119 A CN A2008100712119A CN 200810071211 A CN200810071211 A CN 200810071211A CN 101603235 A CN101603235 A CN 101603235A
- Authority
- CN
- China
- Prior art keywords
- fibre
- soybean fiber
- fiber knitted
- production technology
- soya
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Soybean fiber knitted terry is characterized in that: this knitted fabric is formed by veil and filling braiding and has fish scale shape institutional framework, and described filling is the pure spinning of fibre and soya.Described veil is cotton yarn preferably.Its production technology may further comprise the steps: grey cloth is weaved, the pre-treatment of refining enzyme, remove the oxygenase deoxidation, dye, soap.The fibre and soya terry, it is positive to be that cotton, reverse side are fibre and soya, can guarantee positive, reverse side form and aspect unanimity after the textile dyeing, and with dye on bathing once can make the fabric two sides dye identical shallow in look, be easy to generate the problem of two-phase when overcoming the dyeing of blending or interweaving product.Adopt fibre and soya as filling, can give full play to its warmth retention property good, soft, wear comfortable advantage.
Description
Technical field
The present invention relates to a kind of soybean fiber knitted terry and production technology thereof.
Background technology
Fibre and soya is the aftergrowth protein fibre that adopts soybean protein and polyvinyl alcohol mixing liquid to make through wet spinning and acetalation crosslinking Treatment.Fibre and soya mainly is made up of three parts: outermost layer is a modified protein, and the centre is the polyvinyl alcohol of part acetal, and inner core is the polypropylene that contains the sulfonic group monomer.Fibre and soya textiles, particularly its blending/interlace stitch fabric have sexy strong, soft, warmth retention property is good, moisture absorption the is ventilative characteristics of abundant, well-pressed, hair, are the linings of desirable high-grade underwear, Casual Wear, sportswear.
But because the chemical composition of fibre and soya and structure and existing fiber are different, there is bigger difference in its dyeing and finishing performance.Therefore, fibre and soya blended yarn woven fabric dyeing and finishing processing is the difficult problem that industry is badly in need of solution always.For example, to cotton/fibre and soya blended yarn pre-treatment, two kinds of fiber acid-proof alkalines of cause are inconsistent, fibre and soya brute force under high temperature, high-alkali effect has obvious decline (according to the detection fibers proportion of goods damageds up to 18%), making the fiber feel become coarse hardens, and natural cotton must just can reach under hydrogen peroxide scouring enzyme and long period high temperature action except that cotton knot, cotton assorted and to the requirement of whiteness, has produced contradiction thus.During dyeing,, be difficult to dye identical shallow middle look with cotton bath together, and, be easy to generate fault problems such as look is spent, look steeps, look is broken up the family because two kinds of fiber materialization structural behaviours are inconsistent because of fibre and soya itself has natural ecru.
Summary of the invention
The objective of the invention is to solve the deficiencies in the prior art, a kind of soybean fiber knitted terry is provided.
Another object of the present invention provides a kind of production technology of soybean fiber knitted terry.
Soybean fiber knitted terry provided by the invention is characterized in that: this knitted fabric is formed by veil and filling braiding and has fish scale shape institutional framework, and described filling is the pure spinning of fibre and soya.
Described veil is one or more of native cellulose fibre/regenerated celulose fibre/chemical fibre, can be pure spinning or blending.
Described veil is cotton yarn preferably.
The production technology of soybean fiber knitted terry provided by the invention may further comprise the steps: grey cloth is weaved, the pre-treatment of refining enzyme, remove the oxygenase deoxidation, dye, soap.
The pre-treatment of described refining enzyme is to adopt hydrogen peroxide and biorefining enzyme to handle 50min under 96 ℃ of temperature.
It is described that to remove the oxygenase deoxidation be to adopt 0.1% to remove oxygenase handle 20min under 55 ℃ of temperature.
Warm type REACTIVE DYES during described dyeing is adopted.
Described dyeing adopts liquid fixation alkali as color-fixing agent.
Described soaping is to adopt 1% soaping agent to handle 10min under 90 ℃ of temperature.
Beneficial effect of the present invention is:
(1) fibre and soya terry, it is positive to be that cotton, reverse side are fibre and soya, can guarantee positive, reverse side form and aspect unanimity after the textile dyeing, and with dye on bathing once can make the fabric two sides dye identical shallow in look, be easy to generate the problem of two-phase when overcoming the dyeing of blending or interweaving product.Adopt fibre and soya as filling, can give full play to its warmth retention property good, soft, wear comfortable advantage.
(2) aspect production technology: select for use the refining enzyme to carry out pre-treatment, alkalescence is low, can reduce the powerful influence of fibre and soya, and fibre loss is little, and washing easily; Selecting for use and remove the oxygenase deoxidation, is the oxygen G﹠W with residual decomposing hydrogen dioxide solution efficiently, eliminates its influence to dyestuff; Warm type REACTIVE DYES and liquid fixation alkali in the employing, even dyeing, COLOR FASTNESS height.
The specific embodiment
1, the selection of raw material
Select for use number 10S fibre and soya yarn to make filling, number 48S combed cotton is made veil, and fibre and soya and combed cotton ratio are 29.7% and 70.3%.
2, grey cloth is weaved
Adopt German Mayer﹠amp; 34 " the 22G four runway single knitting large circle machines braiding grey cloths that Cie company produces.Grey cloth adopts single face terry institutional framework.The woven technological parameter of grey cloth is: grammes per square metre 180g/cm
2, door 102 * 2cm, the long 13.5cm/100G of fibre and soya yarn, Quality Pure Cotton Yarn Production line length 28.5cm/100G, the hello yarn tension of fibre and soya yarn are 3～5g, the hello yarn tension of Quality Pure Cotton Yarn Production is 2～3g.
Knitting needle is arranged: 1213
Triangle arrangement: odd number is with flat pin trigonometric sum tuck cam, the whole stitch cams of even number, by following plan of weave jacquard weave:
| ????3 | ????- | ????- | ||
| ????2 | ????● | ????- | ||
| ????1 | ????- | ????● | ||
| ????1 | ????2 | ????3 | ????4 |
-lopping
-tuck
-flotation line
Weave and adopt that Italian volume can (Bianco) machine carries out that Song Shigan cuts open behind the machine controlled down, the individual layer clot, to solve cloth central fold problem.
3, pre-treatment
Prescription: hydrogen peroxide 5g/L, bioscouring enzyme SX-1 2g/L;
Technology: under 96 ℃ of temperature, handle 50min.
By finish and oil stain of being infected with in the grey cloth weaving process and the spot that pre-treatment can go yarn and fiber to adhere in spinning process, foreign material such as the cotton wax on the removal yarn fiber, cotton seed hulls guarantee the stability and the quality that dye.
4, remove the oxygenase deoxidation
Prescription: remove oxygenase 0.1%;
Technology: 55 ℃ of time 20min of temperature.
5, dyeing: dye shallow middle look
Prescription: middle warm type REACTIVE DYES 0.5-3%
Glauber salt 25%
Fixation alkali SH 1.5%
Technology: 65 ℃ of times 45 of temperature min.
6, soap
Prescription: soaping agent SNS 1%
Technology: 90 ℃ of time 10min of temperature.
7, loose formula oven dry
Equipment: Switzerland Santex company squezzing pine formula dryer;
Technology: 140 ℃ of temperature, speed of a motor vehicle 19m/min;
8, middle inspection
Check cloth cover is done wet whether consistent.Whether positive color is up to standard with the standard specimen aberration, and coloured flower, color dot, look steep.
9, finished product typing
Modular system: German Ba Bukeke company setting machine (BABCO-STAR, 2800mm)
Technology: 165 ℃ of speed of a motor vehicle 21m/min of temperature.
10, finished product inspection
The strict knitting finished fabric standard-required of FZ/T72004.2 of pressing is carried out.Trimmed size: door width of cloth 195cm, every square metre of dry weight 220 ± 5g/m
2
More than combine embodiment and describe the present invention, but this is not construed as limiting the invention.Any modifications and variations of having done under same design also all belong to the scope of protection of the invention.
Claims (9)
1, soybean fiber knitted terry is characterized in that: this knitted fabric is formed by veil and filling braiding and has fish scale shape institutional framework, and described filling is the pure spinning of fibre and soya.
2, soybean fiber knitted terry according to claim 1 is characterized in that: described veil is one or more of native cellulose fibre/regenerated celulose fibre/chemical fibre, can be pure spinning or blending.
3, soybean fiber knitted terry according to claim 1 and 2 is characterized in that: described veil is cotton yarn preferably.
4, the production technology of soybean fiber knitted terry may further comprise the steps: grey cloth is weaved, the pre-treatment of refining enzyme, remove the oxygenase deoxidation, dye, soap.
5, the production technology of soybean fiber knitted terry according to claim 4 is characterized in that: the pre-treatment of described refining enzyme is to adopt hydrogen peroxide and biorefining enzyme to handle 50min under 96 ℃ of temperature.
6, the production technology of soybean fiber knitted terry according to claim 4 is characterized in that: described to remove the oxygenase deoxidation be to adopt 0.1% to remove oxygenase handle 20min under 55 ℃ of temperature.
7, the production technology of soybean fiber knitted terry according to claim 4 is characterized in that: warm type REACTIVE DYES during described dyeing is adopted.
8, the production technology of soybean fiber knitted terry according to claim 4 is characterized in that: described dyeing adopts liquid fixation alkali as color-fixing agent.
9, the production technology of soybean fiber knitted terry according to claim 4 is characterized in that: described soaping is to adopt 1% soaping agent to handle 10min under 90 ℃ of temperature.