CN105220350A - One is antibacterial leads wet mercerising suede warp-knitted face fabric and processing technology thereof - Google Patents
One is antibacterial leads wet mercerising suede warp-knitted face fabric and processing technology thereof Download PDFInfo
- Publication number
- CN105220350A CN105220350A CN201510671252.1A CN201510671252A CN105220350A CN 105220350 A CN105220350 A CN 105220350A CN 201510671252 A CN201510671252 A CN 201510671252A CN 105220350 A CN105220350 A CN 105220350A
- Authority
- CN
- China
- Prior art keywords
- warp
- face fabric
- knitted face
- sley bar
- wet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses and a kind of antibacterially lead wet mercerising suede warp-knitted face fabric and processing technology thereof, comprise bamboo-carbon fibre technique, "+" font thin dawn leads wet adding and play polyester filament texturing craft, warping technology, warp-knitted face fabric weaving process, warp-knitted face fabric dyeing.The present invention adopts "+" font thin dawn to lead wet adding and plays polyester filament and bamboo-carbon fibre yarn interweaves, the operation such as to weave by warp knitting machine successfully to have developed the antibacterial of function admirable and lead wet mercerising suede warp-knitted face fabric, bamboo-carbon fibre effectively can suppress growing of bacterium on fabric, and "+" font thin dawn leads wet adding and plays polyester filament and have excellent moisture transported permeable performance.The warp-knitted face fabric of the present invention's exploitation had both had flexibility, warmth retention property, skin-friendly, the comfortableness of cotton excellence, had again good mechanical property, the heat resistance of terylene, also had antibacterially to lead wet advantage simultaneously.
Description
[technical field]
The present invention relates to the technical field of textile technology, particularly a kind of antibacterial technical field leading wet mercerising suede warp-knitted face fabric and processing technology thereof.
[background technology]
Weaving process comprise woven (also claiming tatting), knitting, braiding and non-woven, wherein knitting be divided into again through compile and weft knitting.Through compile be a kind of textile technology belonging to knitting field.With one group or several groups of yarns arranged in parallel, on all working pin of warp-wise feeding machine, lopping simultaneously and form knitted fabric, this method is called that, through compiling, the knitted fabric of formation is called tricot.Mercerising suede belongs to velveteen class, is the good fabric of lustrous surface that napping yarn obtains through mercerization finish, is also mercerising velveteen.With terylene warp knitting nap class fabric, though have vertical good stability of the dimension, fabric is well-pressed, and laddering is little, can not crimping, the advantages such as good permeability, also there is the defects such as flexibility, warmth retention property, skin-friendly, comfortableness difference, constrains the raising of product specification like this.Common mercerising suede warp-knitted face fabric serviceability is poor, function singleness, wash after crease easily.
[summary of the invention]
Object of the present invention solves the problems of the prior art exactly, proposition one is antibacterial leads wet mercerising suede warp-knitted face fabric and processing technology thereof, fabric can be made both to have had flexibility, warmth retention property, skin-friendly, the comfortableness of cotton excellence, there is again good mechanical property, the heat resistance of terylene, also have simultaneously and antibacterially lead wet advantage.
For achieving the above object, the present invention proposes and a kind of antibacterially lead wet mercerising suede warp-knitted face fabric, comprise flannelette napped fabric layer, base cloth layer, there is the structure of levels warp-knitted face fabric braiding, described flannelette napped fabric layer is positioned on base cloth layer, for interweaving monofilaments is interweaved structure between flannelette napped fabric layer and base cloth layer; The structure of described base cloth layer is suede pin tissue, and the structure of flannelette napped fabric layer is through flat tiltedly tissue; Described flannelette napped fabric layer by the front sley bar through adding bullet process and after guide bar knits form, front sley bar comprises front sley bar underlap, front sley bar coil, and rear sley bar comprises rear sley bar underlap, rear sley bar coil.
As preferably, described front sley bar underlap and rear sley bar underlap oppositely weave, and front sley bar coil and rear sley bar coil oppositely weave.
As preferably, described front sley bar is through taper liner yarn, and rear sley bar is through plain cushion yarn, and the situation of entrying of complete organization is, front sley bar and rear sley bar all adopt completely wears mode.
As preferably, described front sley bar is bamboo charcoal fiber yarn, and rear sley bar wetly adds bullet spun polyester thread for "+" font thin dawn leads.
The present invention proposes a kind of antibacterial processing technology leading wet mercerising suede warp-knitted face fabric, comprise the following steps successively:
A bamboo-carbon fibre technique: bamboo-carbon fibre take mao bamboon as raw material, have employed calcining new technology and the new technology of pure oxygen high temperature and nitrogen obstruct time delay, the micropore that bamboo charcoal is innately had is refinement and honeycomb more, and then to cut into slices melting with the polyester modification with honeycomb microporous structure trend, then carry out through the process of spinning, stretching, deformation processing the performance improving bamboo-carbon fibre successively;
B "+" the font thin dawn leads to wet to add and plays polyester filament texturing craft: it is lead at 55dtex/72f "+" the font thin dawn to wet to add bullet polyester filament that "+" font thin dawn leads the wet bullet polyester filament that adds, adopt elasticizer equipment to be processed to form 55dtex/72f "+" the font thin dawn to lead and wetly add bullet polyester filament, precursor is successively by the first roller on elasticizer, twist arrester, first hot case, false twister, second roller, the nozzle of interlace, tractive roller, second hot case, 3rd hot case and oiling to form 55dtex/72f "+" the font thin dawn after roller and leads and wetly add bullet polyester filament, the speed of a motor vehicle of elasticizer is: 450 ~ 500m/min, temperature in first hot case: 190 ~ 200 DEG C, temperature in second hot case: 140 ~ 160 DEG C, draw ratio: 1.60 ~ 1.65, speed ratio: 1.55, it is 3.82cN/dtex that 55dtex/72f "+" the font thin dawn leads the wet intensity adding bullet polyester filament, and crimp contraction is 15.0%,
C warping technology:
C1 bamboo-carbon fibre warping technology parameter: speed of beaming is 300 ~ 350m/min, tension in Warping: 6.20 ~ 7.82cN; Workshop temperature: 18 ~ 22 DEG C; Workshop relative humidity: 75% ~ 80%; Warping radical: front and back comb is 370; To entry mode: front and back comb is completely to be worn;
C255dtex/72f "+" the font thin dawn leads to wet to add and plays polyester filament warping technology parameter: speed of beaming is 300 ~ 400m/min, tension in Warping: 7.20 ~ 9.60cN; Workshop temperature: 18 ~ 22 DEG C; Workshop relative humidity: 75% ~ 80%; Warping radical: front and back comb is 370; To entry mode: front and back comb is completely to be worn;
D warp-knitted face fabric weaving process: by warp knitting machine, leads the wet bullet polyester filament that adds as rear comb using thin for 55dtex/72f "+" the font dawn, using bamboo-carbon fibre as being front comb, adopting the mode of two combs through putting down tiltedly tissue to weave and forming fabric embryo cloth;
E warp-knitted face fabric dyeing: prepare working solution under room temperature, warp-knitted face fabric is devoted oneself to work in liquid, with 2 DEG C/min ramp to 60 DEG C, then dyeing auxiliaries AC-G105 is added, continue to be warming up to 80 ~ 90 DEG C, insulation a period of time, take out warp-knitted face fabric, dry after washing, stand-by after then warp-knitted face fabric being carried out plucking, cropping process; Described working solution comprises each component of following ratio: black cationic dye: 5 ~ 6% (o.w.f), levelling agent: 0.2 ~ 0.5g/L, dyeing auxiliaries AC-G105:2 ~ 10g/L, glacial acetic acid: 0.4 ~ 1.2g/L; The bath raio of described working solution is: 1:25, and the pH value of working solution is 5;
F warp-knitted face fabric finishing technique: adopt two padding process that roll of leaching two to carry out water flexibility by dressing liquid to warp-knitted face fabric and arrange, finally successively through preliminary drying, bake, wash, soap and stoving process.
As preferably, dressing liquid in described step F is the mixed liquor of organic-silicon-modified hydrophilic polyether finishing agent and water; bath raio is 1:25; described organic-silicon-modified hydrophilic polyether finishing agent carries out modified formation by linearity block polyethers amino to organic silicone finishing agent; dressing liquid is that organic-silicon-modified hydrophilic polyether finishing agent and water are mixed to form according to the ratio of 1:30, the pick-up 9O% of padding process.
As preferably, the levelling agent in described step e adopts leveling agent d C, and product property is stablized, resistance to light and heat, acidproof but not alkaline-resisting, resistance to hard water, resistance to inorganic salts, non-volatility, should long storage periods, there is more powerful affinity to polyster fibre, have good homogenized diet to the dyeing of cation dyes.
Beneficial effect of the present invention: the present invention adopts "+" font thin dawn to lead wet adding and plays polyester filament and bamboo-carbon fibre yarn interweaves, the operation such as to weave by warp knitting machine successfully to have developed the antibacterial of function admirable and lead wet mercerising suede warp-knitted face fabric, bamboo-carbon fibre effectively can suppress growing of bacterium on fabric, and "+" font thin dawn leads wet adding and plays polyester filament and have excellent moisture transported permeable performance.The warp-knitted face fabric of the present invention's exploitation had both had flexibility, warmth retention property, skin-friendly, the comfortableness of cotton excellence, had again good mechanical property, the heat resistance of terylene, also had antibacterially to lead wet advantage simultaneously.
Feature of the present invention and advantage will be described in detail by reference to the accompanying drawings by embodiment.
[accompanying drawing explanation]
Fig. 1 is a kind of antibacterial process chart of leading wet mercerising suede warp-knitted face fabric processing technology of the present invention.
[detailed description of the invention]
Consult Fig. 1, the present invention is a kind of antibacterially leads wet mercerising suede warp-knitted face fabric, and comprise flannelette napped fabric layer, base cloth layer, have the structure of levels warp-knitted face fabric braiding, described flannelette napped fabric layer is positioned on base cloth layer, for interweaving monofilaments is interweaved structure between flannelette napped fabric layer and base cloth layer; The structure of described base cloth layer is suede pin tissue, and the structure of flannelette napped fabric layer is through flat tiltedly tissue; Described flannelette napped fabric layer by the front sley bar through adding bullet process and after guide bar knits form, front sley bar comprises front sley bar underlap, front sley bar coil, rear sley bar comprises rear sley bar underlap, rear sley bar coil, described front sley bar underlap and rear sley bar underlap oppositely weave, front sley bar coil and rear sley bar coil oppositely weave, described front sley bar is through taper liner yarn, rear sley bar is through plain cushion yarn, the situation of entrying of complete organization is, front sley bar and rear sley bar all adopt completely wears mode, described front sley bar is bamboo charcoal fiber yarn, and rear sley bar adds bullet spun polyester thread for "+" font thin dawn leads to wet
A kind of antibacterial processing technology leading wet mercerising suede warp-knitted face fabric of the present invention, comprises the following steps successively:
A bamboo-carbon fibre technique: bamboo-carbon fibre take mao bamboon as raw material, have employed calcining new technology and the new technology of pure oxygen high temperature and nitrogen obstruct time delay, the micropore that bamboo charcoal is innately had is refinement and honeycomb more, and then to cut into slices melting with the polyester modification with honeycomb microporous structure trend, then carry out through the process of spinning, stretching, deformation processing the performance improving bamboo-carbon fibre successively;
B "+" the font thin dawn leads to wet to add and plays polyester filament texturing craft: it is lead at 55dtex/72f "+" the font thin dawn to wet to add bullet polyester filament that "+" font thin dawn leads the wet bullet polyester filament that adds, adopt elasticizer equipment to be processed to form 55dtex/72f "+" the font thin dawn to lead and wetly add bullet polyester filament, precursor is successively by the first roller on elasticizer, twist arrester, first hot case, false twister, second roller, the nozzle of interlace, tractive roller, second hot case, 3rd hot case and oiling to form 55dtex/72f "+" the font thin dawn after roller and leads and wetly add bullet polyester filament, the speed of a motor vehicle of elasticizer is: 450 ~ 500m/min, temperature in first hot case: 190 ~ 200 DEG C, temperature in second hot case: 140 ~ 160 DEG C, draw ratio: 1.60 ~ 1.65, speed ratio: 1.55, it is 3.82cN/dtex that 55dtex/72f "+" the font thin dawn leads the wet intensity adding bullet polyester filament, and crimp contraction is 15.0%,
C warping technology:
C1 bamboo-carbon fibre warping technology parameter: speed of beaming is 300 ~ 350m/min, tension in Warping: 6.20 ~ 7.82cN; Workshop temperature: 18 ~ 22 DEG C; Workshop relative humidity: 75% ~ 80%; Warping radical: front and back comb is 370; To entry mode: front and back comb is completely to be worn;
C255dtex/72f "+" the font thin dawn leads to wet to add and plays polyester filament warping technology parameter: speed of beaming is 300 ~ 400m/min, tension in Warping: 7.20 ~ 9.60cN; Workshop temperature: 18 ~ 22 DEG C; Workshop relative humidity: 75% ~ 80%; Warping radical: front and back comb is 370; To entry mode: front and back comb is completely to be worn;
D warp-knitted face fabric weaving process: by warp knitting machine, leads the wet bullet polyester filament that adds as rear comb using thin for 55dtex/72f "+" the font dawn, using bamboo-carbon fibre as being front comb, adopting the mode of two combs through putting down tiltedly tissue to weave and forming fabric embryo cloth;
E warp-knitted face fabric dyeing: prepare working solution under room temperature, warp-knitted face fabric is devoted oneself to work in liquid, with 2 DEG C/min ramp to 60 DEG C, then dyeing auxiliaries AC-G105 is added, continue to be warming up to 80 ~ 90 DEG C, insulation a period of time, take out warp-knitted face fabric, dry after washing, stand-by after then warp-knitted face fabric being carried out plucking, cropping process; Described working solution comprises each component of following ratio: black cationic dye: 5 ~ 6% (o.w.f), levelling agent: 0.2 ~ 0.5g/L, dyeing auxiliaries AC-G105:2 ~ 10g/L, glacial acetic acid: 0.4 ~ 1.2g/L; The bath raio of described working solution is: 1:25, and the pH value of working solution is 5;
F warp-knitted face fabric finishing technique: adopt two padding process that roll of leaching two to carry out water flexibility by dressing liquid to warp-knitted face fabric and arrange, finally successively through preliminary drying, bake, wash, soap and stoving process;
Dressing liquid in described step F is the mixed liquor of organic-silicon-modified hydrophilic polyether finishing agent and water, bath raio is 1:25, described organic-silicon-modified hydrophilic polyether finishing agent carries out modified formation by linearity block polyethers amino to organic silicone finishing agent, dressing liquid is that organic-silicon-modified hydrophilic polyether finishing agent and water are mixed to form according to the ratio of 1:30, the pick-up 9O% of padding process, levelling agent in described step e adopts leveling agent d C, product property is stablized, resistance to light and heat, acidproof but not alkaline-resisting, resistance to hard water, resistance to inorganic salts, non-volatility, suitable long storage periods, more powerful affinity is had to polyster fibre, good homogenized diet is had to the dyeing of cation dyes.
The warp-knitted face fabric of the present invention's exploitation had both had flexibility, warmth retention property, skin-friendly, the comfortableness of cotton excellence, had again good mechanical property, the heat resistance of terylene, also had antibacterially to lead wet advantage simultaneously.
Above-described embodiment is to explanation of the present invention, is not limitation of the invention, anyly all belongs to protection scope of the present invention to the scheme after simple transformation of the present invention.
Claims (7)
1. antibacterially lead a wet mercerising suede warp-knitted face fabric, it is characterized in that: comprise flannelette napped fabric layer, base cloth layer, have the structure of levels warp-knitted face fabric braiding, described flannelette napped fabric layer is positioned on base cloth layer, for interweaving monofilaments is interweaved structure between flannelette napped fabric layer and base cloth layer; The structure of described base cloth layer is suede pin tissue, and the structure of flannelette napped fabric layer is through flat tiltedly tissue; Described flannelette napped fabric layer by the front sley bar through adding bullet process and after guide bar knits form, front sley bar comprises front sley bar underlap, front sley bar coil, and rear sley bar comprises rear sley bar underlap, rear sley bar coil.
2. one as claimed in claim 1 is antibacterial leads wet mercerising suede warp-knitted face fabric, and it is characterized in that: described front sley bar underlap and rear sley bar underlap oppositely weave, front sley bar coil and rear sley bar coil oppositely weave.
3. one as claimed in claim 1 is antibacterial leads wet mercerising suede warp-knitted face fabric, it is characterized in that: described front sley bar is through taper liner yarn, and rear sley bar is through plain cushion yarn, and the situation of entrying of complete organization is, front sley bar and rear sley bar all adopt completely wears mode.
4. one as claimed in claim 1 is antibacterial leads wet mercerising suede warp-knitted face fabric, it is characterized in that: described front sley bar is bamboo charcoal fiber yarn, and rear sley bar adds bullet spun polyester thread for "+" font thin dawn leads to wet.
5. the antibacterial processing technology leading wet mercerising suede warp-knitted face fabric, is characterized in that: comprise the following steps successively:
(A) bamboo-carbon fibre technique: bamboo-carbon fibre take mao bamboon as raw material, have employed calcining new technology and the new technology of pure oxygen high temperature and nitrogen obstruct time delay, the micropore that bamboo charcoal is innately had is refinement and honeycomb more, and then to cut into slices melting with the polyester modification with honeycomb microporous structure trend, then carry out through the process of spinning, stretching, deformation processing the performance improving bamboo-carbon fibre successively;
(B) "+" font thin dawn leads to wet to add and plays polyester filament texturing craft: it is lead at 55dtex/72f "+" the font thin dawn to wet to add bullet polyester filament that "+" font thin dawn leads the wet bullet polyester filament that adds, adopt elasticizer equipment to be processed to form 55dtex/72f "+" the font thin dawn to lead and wetly add bullet polyester filament, precursor is successively by the first roller on elasticizer, twist arrester, first hot case, false twister, second roller, the nozzle of interlace, tractive roller, second hot case, 3rd hot case and oiling to form 55dtex/72f "+" the font thin dawn after roller and leads and wetly add bullet polyester filament, the speed of a motor vehicle of elasticizer is: 450 ~ 500m/min, temperature in first hot case: 190 ~ 200 DEG C, temperature in second hot case: 140 ~ 160 DEG C, draw ratio: 1.60 ~ 1.65, speed ratio: 1.55, it is 3.82cN/dtex that 55dtex/72f "+" the font thin dawn leads the wet intensity adding bullet polyester filament, and crimp contraction is 15.0%,
(C) warping technology:
(C1) bamboo-carbon fibre warping technology parameter: speed of beaming is 300 ~ 350m/min, tension in Warping: 6.20 ~ 7.82cN; Workshop temperature: 18 ~ 22 DEG C; Workshop relative humidity: 75% ~ 80%; Warping radical: front and back comb is 370; To entry mode: front and back comb is completely to be worn;
(C2) 55dtex/72f "+" the font thin dawn leads to wet to add and plays polyester filament warping technology parameter: speed of beaming is 300 ~ 400m/min, tension in Warping: 7.20 ~ 9.60cN; Workshop temperature: 18 ~ 22 DEG C; Workshop relative humidity: 75% ~ 80%; Warping radical: front and back comb is 370; To entry mode: front and back comb is completely to be worn;
(D) warp-knitted face fabric weaving process: by warp knitting machine, leads the wet bullet polyester filament that adds as rear comb using thin for 55dtex/72f "+" the font dawn, using bamboo-carbon fibre as being front comb, adopting the mode of two combs through putting down tiltedly tissue to weave and forming fabric embryo cloth;
(E) warp-knitted face fabric dyeing: prepare working solution under room temperature, warp-knitted face fabric is devoted oneself to work in liquid, with 2 DEG C/min ramp to 60 DEG C, then dyeing auxiliaries AC-G105 is added, continue to be warming up to 80 ~ 90 DEG C, insulation a period of time, take out warp-knitted face fabric, dry after washing, stand-by after then warp-knitted face fabric being carried out plucking, cropping process; Described working solution comprises each component of following ratio: black cationic dye: 5 ~ 6% (o.w.f), levelling agent: 0.2 ~ 0.5g/L, dyeing auxiliaries AC-G105:2 ~ 10g/L, glacial acetic acid: 0.4 ~ 1.2g/L; The bath raio of described working solution is: 1:25, and the pH value of working solution is 5;
(F) warp-knitted face fabric finishing technique: adopt two padding process that roll of leaching two to carry out water flexibility by dressing liquid to warp-knitted face fabric and arrange, finally successively through preliminary drying, bake, wash, soap and stoving process.
6. a kind of antibacterial processing technology leading wet mercerising suede warp-knitted face fabric as claimed in claim 5, it is characterized in that: the dressing liquid in described step (F) is the mixed liquor of organic-silicon-modified hydrophilic polyether finishing agent and water; bath raio is 1:25; described organic-silicon-modified hydrophilic polyether finishing agent carries out modified formation by linearity block polyethers amino to organic silicone finishing agent; dressing liquid is that organic-silicon-modified hydrophilic polyether finishing agent and water are mixed to form according to the ratio of 1:30, the pick-up 9O% of padding process.
7. a kind of antibacterial processing technology leading wet mercerising suede warp-knitted face fabric as claimed in claim 5, it is characterized in that: the levelling agent in described step (E) adopts leveling agent d C, product property is stablized, resistance to light and heat, acidproof but not alkaline-resisting, resistance to hard water, resistance to inorganic salts, non-volatility, suitable long storage periods, has more powerful affinity to polyster fibre, has good homogenized diet to the dyeing of cation dyes.