CN109161159A - A kind of modified abrasion resistant material for casting - Google Patents
A kind of modified abrasion resistant material for casting Download PDFInfo
- Publication number
- CN109161159A CN109161159A CN201811016336.1A CN201811016336A CN109161159A CN 109161159 A CN109161159 A CN 109161159A CN 201811016336 A CN201811016336 A CN 201811016336A CN 109161159 A CN109161159 A CN 109161159A
- Authority
- CN
- China
- Prior art keywords
- parts
- casting
- resistant material
- abrasion resistant
- ingredient
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of modified abrasion resistant materials for casting, the material is made of the ingredient of following weight fraction ratio: 5-15 parts of phenolic resin, 9-11 parts of toluene, 5-8 parts of graphite powder, 1-3 parts of stalk, 3-7 parts of ethyl acetate, 5-7 parts of acetylcholine, 4-7 parts of titanium dioxide, 1-3 parts of white lime, 2-5 parts of Mohr's salt, 2-7 parts of n-butanol, 3-7 parts of silica flour, 3-5 parts of sodium cellulose glycolate, 1-3 parts of pentachlorophenol, 2-5 parts of dispersing agent, 3-7 parts of acetic anhydride, 5-12 parts of polyester resin, 2-6 parts of paraxylene, 8-15 parts of ethylbenzene, 9-12 parts of cupric oxide powder, 7-9 parts of nano calcium oxide, 2-4 parts of sodium carboxymethylcellulose, 2-5 parts of benzene sulfonic acid, 3-8 parts of molybdenum disulfide, 5-10 parts of crystalline silica.The present invention can be established wearing layer in cast(ing) surface, to greatly improve the wear-resisting property of casting, sufficiently be met the antiwear characteristic of casting under circumstances, effectively increase the service life of casting by scientific and reasonable material adapted.
Description
Technical field
The invention belongs to casting field more particularly to a kind of modified abrasion resistant materials for casting.
Background technique
With the high speed development of modern industry, it is wear-resisting that the mechanical equipments such as broken, grinding, excavation, steel rolling largely consume steel
Part, these wearing pieces, which not only will have high wearability also, needs enough impact resistances, and traditional homogenous material cannot
It meets the requirements, therefore, composite material is increasingly by everybody attention in recent years.
Currently, common wearing composite material more options potassium steel or rich chromium cast iron are body portion, selection pottery in the market
Porcelain particle or hard alloy or alloy bar are as reinforced portion.Potassium steel or rich chromium cast iron are only impacting big, stress height, abrasive material
It is just wear-resisting in the case where hard, and its yield strength is low, it is easily deformable, although and ceramic particle can enhance again to a certain extent
The wearability of condensation material, but due to the limitation of ceramic particle, so that the amplitude that the wear-resisting property of wearing composite material improves
It is limited, still it is unable to satisfy the biggish job requirements of tear strength.
Wearing composite material is prepared in conjunction with body portion as reinforced portion using hard alloy bar though having been reported that,
Preparation method fixes hard alloy bar using welding method, or makes pricker on matrix and inlay hole, then by hard
Alloy bar inlays hole pricker edge in the base by pricker, these manufacturing methods are not only cumbersome time-consuming, and welds it cannot be guaranteed that hard closes
Golden metal bar and body portion realize good combination, and the wear-resisting property of material is also had a greatly reduced quality.
Summary of the invention
It is an object of the invention to overcome problem above of the existing technology, a kind of modified abrasion resistant for casting is provided
Material can establish wearing layer in cast(ing) surface, to greatly improve the wear-resisting property of casting.
To realize above-mentioned technical purpose and the technique effect, the invention is realized by the following technical scheme:
A kind of modified abrasion resistant material for casting, the material are made of the ingredient of following weight fraction ratio: phenolic resin 5-
15 parts, 9-11 parts of toluene, 5-8 parts of graphite powder, 1-3 parts of straw, 3-7 parts of ethyl acetate, 5-7 parts of acetylcholine, titanium dioxide 4-7
Part, 1-3 parts of white lime, 2-5 parts of Mohr's salt, 2-7 parts of n-butanol, 3-7 parts of silica flour, 3-5 parts of sodium cellulose glycolate, pentachlorobenzene
1-3 parts of phenol, 2-5 parts of dispersing agent, 3-7 parts of acetic anhydride, 5-12 parts of polyester resin, 2-6 parts of paraxylene, 8-15 parts of ethylbenzene, oxidation
9-12 parts of copper powder, 7-9 parts of nano calcium oxide, 2-4 parts of sodium carboxymethylcellulose, 2-5 parts of benzene sulfonic acid, 3-8 parts of molybdenum disulfide, crystallization
5-10 parts of silica.
Further, the material is specifically made of the ingredient of following weight fraction ratio: 5 parts of phenolic resin, 9 parts of toluene,
6 parts of graphite powder, 1 part of straw, 3 parts of ethyl acetate, 5 parts of acetylcholine, 4 parts of titanium dioxide, 1 part of white lime, 2 parts of Mohr's salt, positive fourth
4 parts of alcohol, 3 parts of silica flour, 3 parts of sodium cellulose glycolate, 1 part of pentachlorophenol, 2 parts of dispersing agent, 3 parts of acetic anhydride, polyester resin 5
Part, 2 parts of paraxylene, 8 parts of ethylbenzene, 9 parts of cupric oxide powder, 7 parts of nano calcium oxide, 2 parts of sodium carboxymethylcellulose, 3 parts of benzene sulfonic acid,
3 parts of molybdenum disulfide, 6 parts of crystalline silica.
Further, the wear-resistant material further includes auxiliary material, the auxiliary material by following weight fraction ratio ingredient
It is made: 7-10 parts of isopropanol, 13-20 parts of vinyl silane triisopropoxide, 5-15 parts of aerosil, trioxa hexamethylene
5-15 parts of alkane, 11-22 parts of aqueous polyurethane emulsion, 14-21 parts of melamine resin, poly- terephthalyl alcohol 5-9 parts, deionized water
6-14 parts.
Further, the auxiliary material is specifically made of the ingredient of following weight fraction ratio: 8 parts of isopropanol, vinyl
Three 15 parts of isopropoxy silane, 10 parts of aerosil, 10 parts of trioxane, 17 parts of aqueous polyurethane emulsion, three
20 parts of cymel, 8 parts of poly- terephthalyl alcohol, 12 parts of deionized water.
The beneficial effects of the present invention are:
The present invention can establish wearing layer in cast(ing) surface, to greatly improve casting by scientific and reasonable material adapted
Wear-resisting property sufficiently meets the antiwear characteristic of casting under circumstances, effectively increases the service life of casting.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is common
Technical staff's all other embodiment obtained without creative efforts belongs to the model that the present invention protects
It encloses.
Embodiment 1:
A kind of modified abrasion resistant material for casting, the material are made of the ingredient of following weight fraction ratio: phenolic resin 5
Part, 9 parts of toluene, 5 parts of graphite powder, 1 part of straw, 3 parts of ethyl acetate, 5 parts of acetylcholine, 4 parts of titanium dioxide, 1 part of white lime, More
2 parts of salt, 2 parts of n-butanol, 3 parts of silica flour, 3 parts of sodium cellulose glycolate, 1 part of pentachlorophenol, 2 parts of dispersing agent, 3 parts of acetic anhydride,
5 parts of polyester resin, 2 parts of paraxylene, 8 parts of ethylbenzene, 9 parts of cupric oxide powder, 7 parts of nano calcium oxide, 2 parts of sodium carboxymethylcellulose,
2 parts of benzene sulfonic acid, 3 parts of molybdenum disulfide, 5 parts of crystalline silica.
Wear-resistant material further includes auxiliary material, which is made of the ingredient of following weight fraction ratio: isopropanol 7
Part, 13 parts of vinyl silane triisopropoxide, 5 parts of aerosil, 5 parts of trioxane, aqueous polyurethane emulsion
11 parts, 14 parts of melamine resin, 5 parts of poly- terephthalyl alcohol, 6 parts of deionized water.
Embodiment 2:
A kind of modified abrasion resistant material for casting, the material are made of the ingredient of following weight fraction ratio: phenolic resin 15
Part, 11 parts of toluene, 8 parts of graphite powder, 3 parts of straw, 7 parts of ethyl acetate, 7 parts of acetylcholine, 7 parts of titanium dioxide, 3 parts of white lime, not
You have 5 parts of salt, and 7 parts of n-butanol, 7 parts of silica flour, 3-5 parts of sodium cellulose glycolate, 3 parts of pentachlorophenol, 5 parts of dispersing agent, acetic anhydride 7
Part, 12 parts of polyester resin, 6 parts of paraxylene, 15 parts of ethylbenzene, 12 parts of cupric oxide powder, 9 parts of nano calcium oxide, carboxymethyl cellulose
4 parts of sodium, 5 parts of benzene sulfonic acid, 8 parts of molybdenum disulfide, 10 parts of crystalline silica.
Wear-resistant material further includes auxiliary material, which is made of the ingredient of following weight fraction ratio: isopropanol 10
Part, 20 parts of vinyl silane triisopropoxide, 15 parts of aerosil, 15 parts of trioxane, aqueous polyurethane cream
22 parts of liquid, 21 parts of melamine resin, 9 parts of poly- terephthalyl alcohol, 14 parts of deionized water.
Embodiment 3:
A kind of modified abrasion resistant material for casting, the material are made of the ingredient of following weight fraction ratio: phenolic resin 5
Part, 9 parts of toluene, 6 parts of graphite powder, 1 part of straw, 3 parts of ethyl acetate, 5 parts of acetylcholine, 4 parts of titanium dioxide, 1 part of white lime, More
2 parts of salt, 4 parts of n-butanol, 3 parts of silica flour, 3 parts of sodium cellulose glycolate, 1 part of pentachlorophenol, 2 parts of dispersing agent, 3 parts of acetic anhydride,
5 parts of polyester resin, 2 parts of paraxylene, 8 parts of ethylbenzene, 9 parts of cupric oxide powder, 7 parts of nano calcium oxide, 2 parts of sodium carboxymethylcellulose,
3 parts of benzene sulfonic acid, 3 parts of molybdenum disulfide, 6 parts of crystalline silica;
Wear-resistant material further includes auxiliary material, which is made of the ingredient of following weight fraction ratio: 8 parts of isopropanol, second
15 parts of three isopropoxy silane of alkenyl, 10 parts of aerosil, 10 parts of trioxane, aqueous polyurethane emulsion 17
Part, 20 parts of melamine resin, 8 parts of poly- terephthalyl alcohol, 12 parts of deionized water.
The present invention can establish wearing layer in cast(ing) surface, to greatly improve casting by scientific and reasonable material adapted
The wear-resisting property of part sufficiently meets the antiwear characteristic of casting under circumstances, effectively increases the service life of casting.
In the description of this specification, the description of reference term " one embodiment ", " example ", " specific example " etc. means
Particular features, structures, materials, or characteristics described in conjunction with this embodiment or example are contained at least one implementation of the invention
In example or example.In the present specification, schematic expression of the above terms may not refer to the same embodiment or example.
Moreover, particular features, structures, materials, or characteristics described can be in any one or more of the embodiments or examples to close
Suitable mode combines.
The basic principles, main features and advantages of the present invention have been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes
Change and improvement all fall within the protetion scope of the claimed invention.
Claims (4)
1. a kind of modified abrasion resistant material for casting, it is characterised in that: the material by following weight fraction ratio ingredient system
At: 5-15 parts of phenolic resin, 9-11 parts of toluene, 5-8 parts of graphite powder, 1-3 parts of straw, 3-7 parts of ethyl acetate, acetylcholine 5-7
Part, 4-7 parts of titanium dioxide, 1-3 parts of white lime, 2-5 parts of Mohr's salt, 2-7 parts of n-butanol, 3-7 parts of silica flour, sodium cellulose glycolate
3-5 parts, 1-3 parts of pentachlorophenol, 2-5 parts of dispersing agent, 3-7 parts of acetic anhydride, 5-12 parts of polyester resin, 2-6 parts of paraxylene, ethylbenzene
8-15 parts, 9-12 parts of cupric oxide powder, 7-9 parts of nano calcium oxide, 2-4 parts of sodium carboxymethylcellulose, 2-5 parts of benzene sulfonic acid, curing
3-8 parts of molybdenum, 5-10 parts of crystalline silica.
2. a kind of modified abrasion resistant material for casting according to claim 1, it is characterised in that: the material specifically by
The ingredient of following weight fraction ratio is made: 5 parts of phenolic resin, 9 parts of toluene, and 6 parts of graphite powder, 1 part of straw, 3 parts of ethyl acetate, second
5 parts of phatidylcholine, 4 parts of titanium dioxide, 1 part of white lime, 2 parts of Mohr's salt, 4 parts of n-butanol, 3 parts of silica flour, sodium cellulose glycolate 3
Part, 1 part of pentachlorophenol, 2 parts of dispersing agent, 3 parts of acetic anhydride, 5 parts of polyester resin, 2 parts of paraxylene, 8 parts of ethylbenzene, cupric oxide powder 9
Part, 7 parts of nano calcium oxide, 2 parts of sodium carboxymethylcellulose, 3 parts of benzene sulfonic acid, 3 parts of molybdenum disulfide, 6 parts of crystalline silica.
3. a kind of modified abrasion resistant material for casting according to claim 1, it is characterised in that: the wear-resistant material is also
Including auxiliary material, which is made of the ingredient of following weight fraction ratio: 7-10 parts of isopropanol, three isopropyl oxygen of vinyl
13-20 parts of base silane, 5-15 parts of aerosil, 5-15 parts of trioxane, 11-22 parts of aqueous polyurethane emulsion,
14-21 parts of melamine resin, poly- terephthalyl alcohol 5-9 parts, 6-14 parts of deionized water.
4. a kind of modified abrasion resistant material for casting according to claim 3, it is characterised in that: the auxiliary material tool
Body is made of the ingredient of following weight fraction ratio: 8 parts of isopropanol, 15 parts of vinyl silane triisopropoxide, and silica airsetting
10 parts of glue, 10 parts of trioxane, 17 parts of aqueous polyurethane emulsion, 20 parts of melamine resin, 8 parts of poly- terephthalyl alcohol,
12 parts of deionized water.