CN109158217A - 一种硫化铜矿的浮选捕收剂 - Google Patents
一种硫化铜矿的浮选捕收剂 Download PDFInfo
- Publication number
- CN109158217A CN109158217A CN201810693091.XA CN201810693091A CN109158217A CN 109158217 A CN109158217 A CN 109158217A CN 201810693091 A CN201810693091 A CN 201810693091A CN 109158217 A CN109158217 A CN 109158217A
- Authority
- CN
- China
- Prior art keywords
- parts
- copper
- kilograms
- tons
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种硫化铜矿的浮选捕收剂,属于矿物加工技术领域,包括以下重量份的原料:磷酸二烷基酯8‑10份、辛基酚聚氧乙烯醚1‑2份、硬脂酸聚氧乙烯酯2‑3份、三乙烯四胺1‑2份、邻羟基苯甲酸3‑5份、活化剂4‑5份;该捕收剂具有捕收和起泡双重性,捕收能力强、选择性好、矿物上浮速度快、浮选泡沫稳定、可有效提高精矿品位和回收率,是硫化铜矿石非常理想的选择性捕收剂。
Description
技术领域
本发明涉及选矿技术领域,特别是一种硫化铜矿的浮选捕收剂。
背景技术
随着国民经济的迅速发展,矿产资源的不断开发利用,矿石性质变得复杂多样,很多常规的浮选药剂方法越来越难以适应矿石性质的变化。低品位复杂难选铜硫矿就是其中的一种,尤其是含多种铜矿的复杂铜硫矿。由于各种铜矿的上浮速度不同,造成品位和回收率难以同时而有效的控制。
在目前的铜硫矿浮选工艺中占有主导地位的捕收剂为黄原酸盐、硫代磷酸盐和硫醇、硫胺酯、黄原酸酯、黑药酯、黄药等浮选药剂,但在实际的选矿中,结果多不能达到设计的要求,铜、硫分离不理想,铜精矿产品中含硫超标,铜精矿回收率偏低,造成矿藏资源的浪费,因此铜硫分离捕收剂仍需研发,研发一种能解决各种要求的选择性捕收剂是必需的。
发明内容
本发明的目的是提供一种硫化铜矿的浮选捕收剂及其使用方法,技术方案如下。
一种硫化铜矿的浮选捕收剂,包括以下重量份的原料:磷酸二烷基酯8-10份、辛基酚聚氧乙烯醚1-2份、硬脂酸聚氧乙烯酯2-3份、三乙烯四胺1-2份、邻羟基苯甲酸3-5份、活化剂4-5份。
所述活化剂由以下重量份的原料制成:亚油酸13-16份、十二烷基苯磺酸钠2-4份、硅烷偶联剂KH-560 2-3份、油酸聚氧乙烯酯2-3份、环甲基硅氧烷5-6份、反丁烯二酸3-4份、乙二胺四乙酸EDTA6-8份。
所述活化剂的制备方法:将亚油酸、十二烷基苯磺酸钠、硅烷偶联剂KH-560、油酸聚氧乙烯酯混合,加热至70~75℃,再加入环甲基硅氧烷,搅拌25-30分钟后,再加入反丁烯二酸、乙二胺四乙酸EDTA,继续搅拌50-65分钟。
所述捕收剂的制备方法:
将磷酸二烷基酯、辛基酚聚氧乙烯醚、硬脂酸聚氧乙烯酯、三乙烯四胺、邻羟基苯甲酸按比例混合,搅拌15-20分钟,再加入活化剂,在8000-9000转/分下搅拌 30-45分钟即得捕收剂。
所述捕收剂在使用时的加入量为40-120克/吨原矿。
本发明捕收剂具有捕收和起泡双重性,捕收能力强、选择性好、矿物上浮速度快、浮选泡沫稳定、可有效提高精矿品位和回收率,是硫化铜矿石非常理想的选择性捕收剂。
附图说明
图1为本发明实施例1步骤(2)的流程图;
图2为本发明实施例2步骤(2)的流程图;
图3为本发明实施例3步骤(2)的流程图。
具体实施方式
下面结合具体实施方式对本发明做进一步详细说明,但本发明的保护范围并不限于所述内容。
实施例1
本实施例一种硫化铜矿的浮选捕收剂,包括以下重量份的原料:磷酸二烷基酯8公斤、辛基酚聚氧乙烯醚1公斤、硬脂酸聚氧乙烯酯2公斤、三乙烯四胺1公斤、邻羟基苯甲酸3公斤、活化剂4公斤;其中活化剂准备以下重量份的原料:亚油酸13公斤、十二烷基苯磺酸钠2公斤、硅烷偶联剂KH-560 2公斤、油酸聚氧乙烯酯2公斤、环甲基硅氧烷5公斤、反丁烯二酸3公斤、乙二胺四乙酸EDTA6公斤,将亚油酸、十二烷基苯磺酸钠、硅烷偶联剂KH-560、油酸聚氧乙烯酯混合,加热至70℃,再加入环甲基硅氧烷,搅拌25分钟后,再加入反丁烯二酸、乙二胺四乙酸EDTA,继续搅拌50分钟,整个过程持续加热70℃保温,得到活化剂,取4公斤备用。
将本实施例的捕收剂使用浮选过程中,以广西某铜锌多金属硫化矿为矿样,原矿含Cu品位0.58%,原生硫化铜占有率为61.57%,次生硫化铜占有率30.22%,Zn品位2.24%,具体步骤如下:
(1)将磷酸二烷基酯8公斤、辛基酚聚氧乙烯醚1公斤、硬脂酸聚氧乙烯酯2公斤、三乙烯四胺1公斤、邻羟基苯甲酸3公斤进行混合,搅拌15分钟,再加入活化剂4公斤,在8000转/分下搅拌30分钟得到捕收剂;
(2)原矿采用抑锌浮铜的工艺选铜锌矿物;将原矿磨碎至-200目占91.15%,采用“一粗两精一扫” 的选别流程,中矿循环返回,得到铜精矿;暂时不考虑选锌,流程见图1,铜粗选的药剂制度为:碳酸钠800克/吨,搅拌作用时间为2min;硫酸锌1000克/吨,搅拌作用时间为5min;步骤(1)的捕收剂80克/吨,搅拌作用时间为3min;铜扫选的药剂制度为:碳酸钠400克/吨,搅拌作用时间为2min;硫酸锌500克/吨,搅拌作用时间为5min;步骤(1)的捕收剂60克/吨,作用时间为3min,铜一次精选的药剂制度为:碳酸钠400克/吨,搅拌作用时间为2min;硫酸锌500克/吨,搅拌作用时间为5min;铜二次精选的药剂制度为:碳酸钠200克/吨,搅拌作用时间为2min;硫酸锌300克/吨,搅拌作用时间为5min。
最终得到铜精矿中Cu品位为29.32%,回收率为94.68%。
采用乙硫氮代替本实施例的捕收剂,其他工艺不变,仅能使得铜精矿中Cu品位为26.15%,回收率为88.67%。
实施例2
本实施例一种硫化铜矿的浮选捕收剂,包括以下重量份的原料:磷酸二烷基酯9公斤、辛基酚聚氧乙烯醚1.5公斤、硬脂酸聚氧乙烯酯2.5公斤、三乙烯四胺1.5公斤、邻羟基苯甲酸4.5公斤、活化剂4.5公斤;其中活化剂准备以下重量份的原料:亚油酸15公斤、十二烷基苯磺酸钠3公斤、硅烷偶联剂KH-560 2.5公斤、油酸聚氧乙烯酯2.5公斤、环甲基硅氧烷5.5公斤、反丁烯二酸3.5公斤、乙二胺四乙酸EDTA7公斤;将亚油酸、十二烷基苯磺酸钠、硅烷偶联剂KH-560、油酸聚氧乙烯酯混合,加热至73℃,再加入环甲基硅氧烷,搅拌27分钟后,再加入反丁烯二酸、乙二胺四乙酸EDTA,继续搅拌60分钟,整个过程持续加热73℃保温,得到活化剂,取4.5公斤备用。
将本实施例的捕收剂使用浮选过程中,以四川某铜铁多金属硫化矿为矿样,原矿含Cu品位0.52%,原生硫化铜占有率为58.57%,次生硫化铜占有率32.22%,Fe品位21.54%,S品位20.57%,具体包括以下步骤:
(1)将磷酸二烷基酯9公斤、辛基酚聚氧乙烯醚1.5公斤、硬脂酸聚氧乙烯酯2.5公斤、三乙烯四胺1.5公斤、邻羟基苯甲酸4.5公斤进行混合,搅拌18分钟,再加入活化剂4.5公斤,在8500转/分下搅拌38分钟得到捕收剂;
(2)原矿采用抑硫浮铜的工艺选铜硫矿物;将原矿磨碎至-200目占90.85%,先采用“一粗三精两扫” 的选别流程,中矿循环返回,得到铜精矿,暂时不考虑选硫,流程见图2,铜粗选的药剂制度为:石灰1200克/吨,搅拌作用时间为2min;步骤(1)的捕收剂100克/吨,搅拌作用时间为3min;铜一次扫选的药剂制度为:石灰600克/吨,搅拌作用时间为2min;步骤(1)的捕收剂60克/吨,搅拌作用时间为3min;铜二次扫选的药剂制度为:石灰400克/吨,搅拌作用时间为2min;步骤(1)的捕收剂40克/吨,作用时间为3min,铜一次精选的药剂制度为:石灰800克/吨,搅拌作用时间为2min;铜二次精选的药剂制度为:石灰500克/吨,搅拌作用时间为2min;铜三次精选的药剂制度为:石灰300克/吨,作用时间为2min。
最终得到铜精矿中Cu品位为30.32%,回收率为93.68%。
采用Z-200代替本实施例的捕收剂,其他工艺不变,仅能使得该铜精矿中Cu品位为27.37%,回收率为87.54%。
实施例3
本实施例一种硫化铜矿的浮选捕收剂,包括以下重量份的原料:磷酸二烷基酯10公斤、辛基酚聚氧乙烯醚2公斤、硬脂酸聚氧乙烯酯3公斤、三乙烯四胺2公斤、邻羟基苯甲酸5公斤、活化剂5公斤;其中活化剂准备以下重量份的原料:亚油酸16公斤、十二烷基苯磺酸钠4公斤、硅烷偶联剂KH-560 3公斤、油酸聚氧乙烯酯3公斤、环甲基硅氧烷6公斤、反丁烯二酸4公斤、乙二胺四乙酸EDTA8公斤;将亚油酸、十二烷基苯磺酸钠、硅烷偶联剂KH-560、油酸聚氧乙烯酯混合,加热至75℃,再加入环甲基硅氧烷,搅拌30分钟后,再加入反丁烯二酸、乙二胺四乙酸EDTA,继续搅拌65分钟,整个过程持续加热75℃保温,得到活化剂,取5公斤备用
将本实施例的捕收剂使用浮选过程中,以云南某铜铅多金属硫化矿为矿样,原矿含Cu品位0.67%,原生硫化铜占有率为55.67%,次生硫化铜占有率28.57%,Pb品位3.27%,具体包括以下步骤:
(1)将磷酸二烷基酯10公斤、辛基酚聚氧乙烯醚2公斤、硬脂酸聚氧乙烯酯3公斤、三乙烯四胺2公斤、邻羟基苯甲酸5公斤进行混合,搅拌20分钟,再加入活化剂5公斤,在9000转/分下搅拌45分钟即得捕收剂;
(2)原矿采用抑铅浮铜的工艺选铜铅矿物;将原矿磨碎至-200目占95.77%,先采用“一粗四精三扫” 的选别流程,中矿循环返回,得到铜精矿,暂时不考虑选铅,流程见图3,铜粗选的药剂制度为:二氧化硫2500克/吨、石灰1000克/吨、淀粉800克/吨,搅拌作用时间为5min;步骤(1)的捕收剂120克/吨,搅拌作用时间为3min;铜一次扫选的药剂制度为:二氧化硫1200克/吨、石灰600克/吨、淀粉500克/吨,搅拌作用时间为5min;步骤(1)的捕收剂80克/吨,搅拌作用时间为3min,铜二次扫选的药剂制度为:二氧化硫800克/吨、石灰400克/吨、淀粉300克/吨,搅拌作用时间为5min;步骤(1)的捕收剂60克/吨,搅拌作用时间为3min,铜三次扫选的药剂制度为:二氧化硫600克/吨、石灰200克/吨、淀粉100克/吨,搅拌作用时间为5min;步骤(1)的捕收剂40克/吨,搅拌作用时间为3min,铜精选不加药。
最终得到铜精矿中Cu品位为39.24%,回收率为95.62%。
采用Z-200代替本实施例的捕收剂,其他工艺不变,仅能使得该铜精矿中Cu品位为29.31%,回收率为90.58%。
Claims (4)
1.一种硫化铜矿的浮选捕收剂,其特征在于,包括以下重量份的原料:磷酸二烷基酯8-10份、辛基酚聚氧乙烯醚1-2份、硬脂酸聚氧乙烯酯2-3份、三乙烯四胺1-2份、邻羟基苯甲酸3-5份、活化剂4-5份。
2.根据权利要求1所述硫化铜矿的浮选捕收剂,其特征在于,所述活化剂由以下重量份的原料制成:亚油酸13-16份、十二烷基苯磺酸钠2-4份、硅烷偶联剂2-3份、油酸聚氧乙烯酯2-3份、环甲基硅氧烷5-6份、反丁烯二酸3-4份、乙二胺四乙酸6-8份。
3.根据权利要求2所述硫化铜矿的浮选捕收剂,其特征在于,所述活化剂的制备方法:将亚油酸、十二烷基苯磺酸钠、硅烷偶联剂、油酸聚氧乙烯酯混合,加热至70-75℃,加入环甲基硅氧烷,搅拌25-30分钟后,再加入反丁烯二酸、乙二胺四乙酸,继续搅拌50-65分钟。
4.根据权利要求1所述硫化铜矿的浮选捕收剂,其特征在于,所述捕收剂在使用时的加入量为40-120克/吨原矿。