CN109135532A - The double-component aqueous PU plastic paint and its preparation process of scintilla water dispersion - Google Patents
The double-component aqueous PU plastic paint and its preparation process of scintilla water dispersion Download PDFInfo
- Publication number
- CN109135532A CN109135532A CN201810834307.XA CN201810834307A CN109135532A CN 109135532 A CN109135532 A CN 109135532A CN 201810834307 A CN201810834307 A CN 201810834307A CN 109135532 A CN109135532 A CN 109135532A
- Authority
- CN
- China
- Prior art keywords
- scintilla
- component
- agent
- water
- aqueous
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the double-component aqueous PU plastic paints and its preparation process of a kind of scintilla water dispersion, the double-component aqueous PU plastic paint is prepared by two kinds of components of A, B, in which: the component A is raw materials used as follows: scintilla water-based hydroxyl acrylic emulsion, scintilla aqueous one-component acrylic emulsion, coalescing agent, aqueous wetting agent, dispersing agent, levelling agent, mill base, pH adjusting agent, thickener, defoaming agent, scintilla water;The B component is isocyanide ester curing agent.The present invention can satisfy the use under current low temperature using the double-component aqueous PU plastic paint of scintilla water preparation, also have good performance in a variety of plastic cement types such as glass reinforced plastic, PC, ABS/PC, ABS, PC/BS, on game equipment of travelling, automotive upholstery door-plate, knob, have successful business application on ceiling light.
Description
Technical field
The invention belongs to chemical technology field, it is related to a kind of aqueous plastic paint and its preparation process, and in particular to Yi Zhongwei
The double-component aqueous PU plastic paint and its preparation process of molecule water dispersion.
Background technique
Since 2015, national environmental protection policy is put into effect in succession, and the oil in plastic paint field turns the increasing of water trend, various aqueous
Paint is also taken advantage of a situation to launch and be arrived in the market, but from the point of view of the feedback in market, the application of water paint has also suffered from certain limitation,
In an importance be since as solvent, the volatilization of water obviously receives the influence of temperature and humidity, and the freezing point of water
It is 0 DEG C, northerly most area, after entering the winter, water paint frost resistance is bad, is easy to freeze, be lauched in low temperature and high relative humidity
It volatilizees slower, the drying of water paint is greatly affected.Some water paints manufacturer is bad in order to solve water paint frost resistance
The problem of, excessive cosolvent can be added, reduce or be not added water, but so, VOC content can steeply rise, it is clear that
The original intention of environmentally friendly legislation is violated.
CN104341921A discloses a kind of aqueous plastic paint, mainly organizes as maleic anhydride modified acrylic emulsion 50
~60 parts, 5~10 parts of wax liquor, 2~3 parts of adhesion promoter, 2~4 parts of scratching resistant, 3~5 parts of coalescing agent, dipropylene glycol
1~2 part of methyl ether, 5~12 parts of water aluminum-silver slurry.The product has good hardness, adhesive force, and adhesion strength is good, still
The alcohol resistance energy of paint film, wear-resisting property and weather resistance are poor, are not able to satisfy the glass reinforced plastic with outdoor requirement and travel recreation
The performance requirement of product.
Summary of the invention
In order to solve the above problem that water paint faces, the present invention provides a kind of the double-component aqueous of scintilla water dispersion
PU plastic paint and its preparation process.The present invention using scintilla water be used as solvent, from routine tap water, deionized water it is different,
Scintilla water is small-micelle water, frost resistance, sag resistance, volatile performance have it is very big improve, use differential
The double-component aqueous PU plastic paint of sub- water preparation can satisfy the use under current low temperature, glass reinforced plastic, PC, ABS/PC, ABS,
Also there is good performance in a variety of plastic cement types such as PC/BS, door-plate, knob, top on game equipment of travelling, automotive upholstery
There is successful business application on lamp.Product of the invention has low VOC content, and aqueous, environmental protective can improve painting environments, paints
Film has excellent adhesive force, good surface hardness, alcohol resistance, wear-resisting property.
The purpose of the present invention is what is be achieved through the following technical solutions:
A kind of double-component aqueous PU plastic paint of scintilla water dispersion, is prepared by two kinds of components of A, B, in which:
The component A is by mass percentage, raw materials used as follows: scintilla water-based hydroxyl acrylic emulsion 20~
50%, scintilla aqueous one-component acrylic emulsion 10~30%, coalescing agent 0.5~1.5%, aqueous wetting agent 0.3~
0.5%, dispersing agent 0.2~0.4%, levelling agent 0.3~0.5%, mill base 0~30%, pH adjusting agent 0.1~0.2%, thickener
0.4~0.8%, defoaming agent 0.1~0.2%, surplus is scintilla water;
The B component is isocyanide ester curing agent;
The mass ratio of the component A and B component is 100:8~20.
A kind of preparation process of the double-component aqueous PU plastic paint of above-mentioned scintilla water dispersion, includes the following steps:
(1) preparation of component A
First in a mixing bowl, under conditions of low whipping speed is 300~500r/min, it is separately added into scintilla according to the ratio
Water, aqueous wetting agent, dispersing agent, defoaming agent, it is to be mixed uniformly after, then be separately added into scintilla water-based hydroxyl acrylic acid according to the ratio
Lotion, scintilla aqueous one-component acrylic emulsion, coalescing agent, levelling agent, pH adjusting agent, it is to be mixed uniformly after, add
Thickener and mill base after uniform stirring, filter and package after passed examination;
(2) preparation of B component
Check whether the state of isocyanates is normal, it is directly filling according to the ratio after normal;
(3) spraying application
It after the mixing of the ratio of component A and B component, stirs evenly, adds scintilla water and carry out out dilute, open dilute ratio
It is adjusted according to spray painting viscosity, muzzle bore, water addition ratio example can carry out room temperature probably after 10~20%, spraying
It is dry, 40min can also be dried at a temperature of 60 DEG C after surface drying.
In the present invention, the scintilla water-based hydroxyl acrylic emulsion is to be scattered in scintilla water with emulsifier-free emulsion polymerization
The hydroxyl acrylic emulsion that mode synthesizes, solid content are 44~46wt.%.
In the present invention, the scintilla one-component acrylic emulsion is to be scattered in scintilla water with homopolymerization or copolymerized form
The one-component acrylic emulsion of synthesis, solid content are 45~47wt.%.
In the present invention, the coalescing agent is propylene glycol phenylate, propandiol butyl ether, diethylene glycol dimethyl ether acetate, diethyl
One or more of glycol monobutyl ether acetate, dipropylene, dipropylene glycol methyl ether, butyl etc..
In the present invention, the thickener is the swollen agent for polyacrylic acid thickening of alkali soluble, one in phyllosilicate auxiliary rheological agents
Kind or two kinds.
In the present invention, the dispersing agent is block propylene acid copolymer type dispersing agent.
In the present invention, the defoaming agent is organic silicon type defoaming agent.
In the present invention, the pH adjusting agent is one or more of dimethylethanolamine, AMP-95, ammonium hydroxide.
In the present invention, the mill base is the resin-free color paste of Lai Liya Chemical Industry Science Co., Ltd development and production.
The present invention comprehensively considered the factors of the various aspects such as the collocation of film forming matter, scintilla water to the performance of paint film and at
It is influenced caused by this.In order to further promote the understanding of spirit for the essence of the present invention, now ingredient mechanism therein is given
It illustrates.
(1) using scintilla aqueous double-component PU as main film forming substance, it is ensured that the excellent weatherability of paint film, ethanol-tolerant
Property, good gloss, adhesive force, hardness etc..
The hydroxyl acrylic emulsion in aqueous double-component PU that the present invention uses is to use scintilla technology with no soap cream
The synthesis of liquid polymerization methods.It specifically gets on very well, present invention utilizes the spatial structures of scintilla water cluster and intermolecular various weak
Interact the synergistic effect of (such as hydrogen bond, Van der Waals force), and the directionality and selectivity of the interaction between scintilla make
Polymer emulsion forms unique three-dimensional structure, so that the aqueous acrylic emulsion for dispersing and synthesizing in scintilla water and city
Comparing with synthesis such as deionized waters on face, membrane formation mechanism is different, using the film forming mechanism of molecular level, with dampening
Evaporation, physicochemical aggregation occurs for the specific functional groups in adjacent polymer, so that water-based microemulsion polymeric system produces
Physical space crosslinking is given birth to, the critical solid content of this physical crosslinking is much lower compared with common micelle, in other words, this
Crosslinking phenomena can occur when water content is higher, more significant to system bring reinforcing effect, extend aqueous plastic paint
Storage time, shorten the drying time of aqueous plastic paint, improve the attachment of the wetting ability and paint film to plastic rubber substrate
Power improves the package ability to pigments and fillers particle, it is possible to reduce the use of related auxiliaries, the paint film for being prepared out also have
There are excellent weatherability, alcohol resistance, flexibility, hardness etc..The hydroxyl acrylic emulsion that emulsifier-free emulsion polymerization mode synthesizes
Ion is stabilized by ionic group, the hydrophilic radical being incorporated on polymer chain, the hydroxy obtained with usual manner
Yogurt liquid phase ratio, the two-component lotion that the present invention uses eliminate small-molecular emulsifier and the bad shadow such as absorb water, ooze out in film
It rings, improves adhesion property, water resistance and the solvent resistance of film.In conclusion the scintilla hydroxy that the present invention uses
Yogurt liquid is as main film forming substance, it is ensured that the excellent weatherability of paint film, alcohol resistance, good gloss, adhesive force, hardness
Deng.
(2) scintilla one-component acrylic emulsion is adulterated, is reduced costs, reduces and generates the undesirable appearances phenomenons such as prickly heat.
The one-component acrylic emulsion that the present invention uses is synthesized by being scattered in scintilla water in a manner of homopolymerization or copolymerization
Aqueous acrylic emulsion, compared on the market with synthesis such as deionized waters, this one-component acrylic emulsion is prepared
Aqueous plastic paint there is more excellent resist sagging performance, rate of drying faster etc..Although aqueous double-component PU has excellent
Different weatherability, alcohol resistance, good adhesive force, and be widely used on plastic cement field, the oil instantly turns the environmental protection of water
In tide, aqueous double-component PU potentiality are very big, can be phased out solvent based product.But during practical application, water
Property two-component PU there are also the self shortcomings that overcome of needs.On production cost, the price of aqueous double-component PU is much higher than same
The solvent based product of type, especially isocyanate curing agent are still based on imported product at present, and price is generally 80~90
First per kilogram or so, and the solvent type curing agent of same type only has half or so, this is also to hinder aqueous double-component PU into one
Where walking the resistance promoted, in construction technology, certain aqueous double-component PU are easy to produce prickly heat under high light state, influence table
Face effect, rate of drying are excessively slow.It is easy to receive in single-component water-based acrylic emulsion Costco Wholesale, rate of drying is very fast, still
It is lacking in weatherability, alcohol resistance.And the scintilla one-component acrylic emulsion of doped portion can play good association
Same effect.Confirm through overtesting, the scintilla one-component acrylic emulsion of doped portion, it is hardness, adhesive force, alcohol resistance, resistance to
Time property etc. is in the case that indexs significantly decrease, and lustrous surface is also without notable difference, but the prickly heat under high light state
Etc. bad phenomenons substantially reduce, production cost is greatly reduced, and drying property is also significantly improved.
(3) using scintilla water rather than common deionized water, tap water improve paint as the dissolving medium of water paint
The wetting of film, drying capacity improve the frost resistance and sag resistance of water paint.
Deionized water, distilled water, nature water be not in the form of single molecule existing for, but by several water
Molecule is flocked together by hydrogen bond action, is formed water cluster, is commonly called as water clusters, the size of the molecular cluster can not, it is expected that
It is generally made of 8~15 hydrones, and is that dynamically, average diameter is 2.6~6nm;And scintilla water is using special
Technique preparation, micel are 3~6 hydrone compositions, and average diameter 0.6bnm, activity is much larger than conventional deionization
The water of water, distilled water and nature, this be also the double-component aqueous PU plastic paint performance that is prepared using scintilla water not
It is same as the basic reason that conventional deionized water, tap water etc. are produced.Scintilla water improves the frost resistance of water paint, resists
Flow and drying property etc..
It specifically gets on very well, according to thermodynamic (al) calculating, if water is existed in the form of single hydrone, the fusing point of water is answered
It is -110 DEG C, boiling point should be 85 DEG C, but the fusing point of actually common water is 0 DEG C, and boiling point is 100 DEG C.Average 3~6 water
The micel of molecular composition scintilla water, and the micel of common water is made of 8-15 hydrone, therefore scintilla water
Fusing point and boiling point are far below common deionized water, distilled water, tap water, therefore the double-component aqueous PU plastic paint prepared
In northern cold winter, more difficult icing, the transport and construction in winter be safer.In addition, evaporation latent heat is lower, volatilization
Property it is stronger, further say, using scintilla water rather than common tap water, deionized water, distilled water preparation two-component
Drying property, the sag resistance of aqueous PU paint can be more preferable.
Compared with the prior art, the present invention has the advantage that
1, product of the invention has excellent adhesive force, sag resistance energy and scratch resistance capability, according to national standard GB/
The regulation of T9286-1988, the film adhesive tested can reach no more than 1 grade, or even to 0 grade, fully meet row
The performance of industry client needs.
2, product of the invention has used scintilla water as solvent, since scintilla water is different from the composition structure of light water
It makes, scintilla water activity is larger, and surface tension is smaller, and molecular structure arrangement is close neat, and fusing point and boiling point and heat of evaporation are remote
Lower than common water so that the aqueous double-component PU plastic paint prepared have good frost resistance, anti-sag and faster
Rate of drying significantly improves water paint in the drying and freeze proof problem of northern cold winter, improves double-component aqueous PU
Paint transport in winter and using safe, and surface effect is more more flat than the aqueous plastic paint using tap water or deionized water
Whole saturation.
3, product of the invention has excellent surface hardness, and according to the regulation of national standard GB/T6739-1996, test is obtained
Film coated surface hardness can reach H (Mitsubishi's pencil), it might even be possible to reach 2H (Mitsubishi's pencil), industry customer feedback is better than
Solvent based product.
4, product of the invention is using double-component aqueous PU as main film forming substance, ensure that including adhesive force, hardness, weather-proof
Property, alcohol resistance, gloss etc. are many to be had excellent performance, and is doped with one-component acrylic emulsion, is reduced production cost, also improves
Rate of drying.
5, product of the invention has high gloss of film degree, the double-component aqueous PU modeling of scintilla being made into the present invention
Shellac varnish gloss oil gloss can reach 93 °, complies fully with the game equipment client that travels and gloss of film is set not less than 90 degree
It is fixed, and surface effect is good, and permeability is good.
6, product utilization of the invention water-based hydroxyl acrylic emulsion and one-component acrylic emulsion blending, cost is more
It is cheap, it can be widely used on a variety of substrates such as glass reinforced plastic, PC, ABS/PC, ABS, PC/BS, in game equipment of travelling, automobile
Successful application is all obtained on gadget.
Specific embodiment
Below with reference to embodiment, further description of the technical solution of the present invention, and however, it is not limited to this, all right
Technical solution of the present invention is modified or replaced equivalently, and without departing from the spirit and scope of the technical solution of the present invention, should all be contained
Lid is within the protection scope of the present invention.
Embodiment 1
A kind of double-component aqueous PU plastic paint of scintilla water dispersion is present embodiments provided, composition and ratio are such as
Under:
Component A: 40 parts of acrylic emulsion of scintilla water-based hydroxyl (solid content 45wt.%), scintilla aqueous one-component
16 parts of acrylic emulsion (solid content 46wt.%), 0.8 part of coalescing agent dipropylene glycol methyl ether, type siloxane aqueous wetting agent
0.3 part, 0.2 part of dispersing agent of block propylene acid copolymer type, 0.3 part of Siloxane-Oxyalkylene Copolymers levelling agent, 28 parts of stock white, pH
DMEA0.2 parts of regulator, 0.6 part of alkali swelling type agent for polyacrylic acid thickening, 0.2 part of organic silicon defoamer, scintilla water 13.4
Part;
B component: 13 parts of isocyanide ester curing agent.
Specific preparation process is as follows:
(1) preparation of component A
First in a mixing bowl, under conditions of low whipping speed is 400r/min, it is separately added into 13.4 parts of scintilla water, embedding
0.2 part of section acrylic copolymer type dispersing agent, 0.2 part of organic silicon defoamer, 0.3 part of type siloxane aqueous wetting agent, it is to be mixed
After uniformly, then it is separately added into 40 parts of acrylic emulsion of scintilla water-based hydroxyl (solid content 45wt.%), scintilla one-component third
16 parts of olefin(e) acid lotion (solid content 46wt.%), 0.8 part of coalescing agent dipropylene glycol methyl ether, Siloxane-Oxyalkylene Copolymers levelling
0.3 part of agent, DMEA0.2 parts of pH adjusting agent, it is to be mixed uniformly after, add 0.6 part of alkali swelling type agent for polyacrylic acid thickening, white
It 28 parts of mill base, after uniform stirring, is filtered and packaged after passed examination.
(2) preparation of B component
Check whether the state of isocyanates is normal, it is filling 13 parts direct after normal.
(3) spraying application
Before coating decoration, first component A and B component are uniformly mixed, further according to viscosity requirement, is added and is used for diluted differential
Sub- water carries out spraying application.Air drying can be carried out, carries out drying and processing after surface dryings can also be waited.
Testing result: adhesion 1 grade, surface hardness H (Mitsubishi's pencil), do not see the bottom for alcohol resistance 300 times by 62 ° of gloss, resistance to
Aqueous 48h is not blistering not to be fallen off.
Embodiment 2
A kind of double-component aqueous PU plastic paint of scintilla water dispersion is present embodiments provided, composition and ratio are such as
Under:
Component A: 32 parts of acrylic emulsion of scintilla water-based hydroxyl (solid content 44wt.%), scintilla aqueous one-component
24 parts of acrylic emulsion (solid content 45wt.%), 1.2 parts of coalescing agent dipropylene glycol methyl ether, type siloxane aqueous wetting agent
0.3 part, 0.2 part of dispersing agent of block propylene acid copolymer type, 0.3 part of Siloxane-Oxyalkylene Copolymers levelling agent, 24 parts of bright red mill base,
DMEA0.2 parts of pH adjusting agent, 0.4 part of alkali swelling type agent for polyacrylic acid thickening, 0.2 part of phyllosilicate auxiliary rheological agents are organic
0.2 part of silicon defoaming agent, 17 parts of scintilla water;
B component: 10 parts of isocyanide ester curing agent.
Specific preparation process is as follows:
(1) preparation of component A
First in a mixing bowl, under conditions of low whipping speed is 300r/min, it is separately added into 17 parts of scintilla water, block
0.2 part of acrylic copolymer type, 0.2 part of organic silicon defoamer, 0.3 part of type siloxane aqueous wetting agent, it is to be mixed uniformly after, then
It is separately added into 32 parts of acrylic emulsion of scintilla water-based hydroxyl (solid content 44wt.%), scintilla aqueous one-component acrylic acid
24 parts of lotion (solid content 45wt.%), 1.2 parts of coalescing agent dipropylene glycol methyl ether, Siloxane-Oxyalkylene Copolymers levelling agent 0.3
Part, DMEA0.2 part of pH adjusting agent, it is to be mixed it is uniform after, add 0.4 part of alkali swelling type agent for polyacrylic acid thickening, stratiform silicon
0.2 part of hydrochlorate auxiliary rheological agents, 24 parts of bright red mill base, filter and package after passed examination.
(2) preparation of B component
Check whether the state of isocyanates is normal, it is filling 10 parts direct after normal.
(3) spraying application
Before coating decoration, first component A and B component are uniformly mixed, further according to viscosity requirement, is added and is used for diluted differential
Sub- water carries out spraying application.Air drying can be carried out, carries out drying and processing after surface dryings can also be waited.
Testing result: adhesion 1 grade, surface hardness H (Mitsubishi's pencil), do not see the bottom for alcohol resistance 200 times by 33 ° of gloss, resistance to
Aqueous 48h is not blistering not to be fallen off.
Embodiment 3
A kind of double-component aqueous PU plastic paint of scintilla water dispersion is present embodiments provided, composition and ratio are such as
Under:
Component A: 36 parts of acrylic emulsion of scintilla water-based hydroxyl (solid content 46wt.%), scintilla aqueous one-component
20 parts of acrylic emulsion (solid content 47wt.%), 1 part of coalescing agent dipropylene, siloxane aqueous wetting agent 0.3
Part, 0.2 part of dispersing agent of block propylene acid copolymer type, 0.3 part of Siloxane-Oxyalkylene Copolymers levelling agent, 24 parts of bright red mill base, pH
DMEA0.2 parts of regulator, 0.3 part of alkali swelling type agent for polyacrylic acid thickening, 0.3 part of phyllosilicate auxiliary rheological agents, organosilicon
0.2 part of defoaming agent, 15.2 parts of scintilla water;
B component: 11.3 parts of isocyanide ester curing agent.
Specific preparation process is as follows:
(1) preparation of component A
First in a mixing bowl, under conditions of low whipping speed is 500r/min, it is separately added into 15. parts of scintilla water, embedding
0.2 part of section acrylic copolymer type, 0.2 part of organic silicon defoamer, 0.3 part of siloxane aqueous wetting agent, it is to be mixed uniformly after, then
It is separately added into 36 parts of acrylic emulsion of scintilla water-based hydroxyl (solid content 46wt.%), scintilla one-component acrylic emulsion
20 parts (solid content 47wt.%), 1 part of coalescing agent dipropylene, 0.3 part of Siloxane-Oxyalkylene Copolymers levelling agent, pH
0.2 part of regulator DMEA, it is to be mixed uniformly after, add 0.3 part of alkali swelling type agent for polyacrylic acid thickening, phyllosilicate
0.3 part of auxiliary rheological agents, 26 parts of sapphire blue mill base, after uniform stirring, filter and package after passed examination.
(2) preparation of B component
Check whether the state of isocyanates is normal, it is filling 11.3 parts direct after normal.
(3) spraying application
Before coating decoration, first component A and B component are uniformly mixed, further according to viscosity requirement, is added and is used for diluted differential
Sub- water carries out spraying application.Air drying can be carried out, carries out drying and processing after surface dryings can also be waited.
Testing result: adhesion 1 grade, surface hardness F (Mitsubishi's pencil), do not see the bottom for alcohol resistance 300 times by 49 ° of gloss, resistance to
Aqueous 48h is not blistering not to be fallen off.
Embodiment 4
A kind of double-component aqueous PU plastic paint of scintilla water dispersion is present embodiments provided, composition and ratio are such as
Under:
Component A: 50 parts of acrylic emulsion of scintilla water-based hydroxyl (solid content 45wt.%), scintilla aqueous one-component
20 parts of acrylic emulsion (solid content 45wt.%), 1 part of filming aid propylene glycol phenyl ether, 0.2 part of siloxane aqueous wetting agent,
0.2 part of dispersing agent of block propylene acid copolymer type, 0.3 part of Siloxane-Oxyalkylene Copolymers levelling agent, DMEA0.2 parts of pH adjusting agent,
0.2 part of alkali swelling type agent for polyacrylic acid thickening, 0.2 part of phyllosilicate auxiliary rheological agents, 0.2 part of organic silicon defoamer, differential
27.5 parts of sub- water;
B component: 16 parts of isocyanide ester curing agent.
Specific preparation process is as follows:
(1) preparation of component A
First in a mixing bowl, under conditions of low whipping speed is 400r/min, it is separately added into 27.5 parts of scintilla water, embedding
0.2 part of section acrylic copolymer type dispersing agent, 0.2 part of organic silicon defoamer, 0.3 part of Siloxane-Oxyalkylene Copolymers levelling agent, silicon
0.2 part of oxygen alkane aqueous wetting agent, DMEA0.2 parts of pH adjusting agent, it is to be mixed uniformly after, then be separately added into scintilla water-based hydroxyl third
(solid content is for 50 parts of olefin(e) acid lotion (solid content 45wt.%), 20 parts of scintilla aqueous one-component acrylic emulsion
45wt.%), 1 part of filming aid propylene glycol phenyl ether, it is to be mixed uniformly after, add alkali swelling type agent for polyacrylic acid thickening 0.2
Part, 0.2 part of phyllosilicate auxiliary rheological agents, after uniform stirring, filter and package after passed examination.
(2) preparation of B component
Check whether the state of isocyanates is normal, it is filling 16 parts direct after normal.
(3) spraying application
Before coating decoration, first component A and B component are uniformly mixed, further according to viscosity requirement, is added and is used for diluted differential
Sub- water carries out spraying application.Air drying can be carried out, carries out drying and processing after surface dryings can also be waited.
Testing result:, not seeing the bottom for alcohol resistance 500 times by 0 grade of adhesive force, surface hardness 2H (Mitsubishi's pencil), 93 ° of gloss,
Water resistance 48h is not blistering not to be fallen off.
The double-component aqueous PU plastic paint of the scintilla water dispersion prepared according to the present invention has excellent adhesive force, surface
Hardness, good gloss, alcohol resistance etc., indices comply fully with the requirements of national standard.In the process actually promoted
In, also receive the approval of client.If being intended to green plastic paint in the present invention, green slurry can be added, if it is desired to middle Huang plastic cement
Paint, can be added in yellow pulp, no matter which kind of color, can be carried out by adjusting the type and dosage of mill base debugging can obtain
It arrives, both can be made solid color enamel, also can be made gloss oil, be not limited to the above embodiment.
Claims (10)
1. a kind of double-component aqueous PU plastic paint of scintilla water dispersion, it is characterised in that the double-component aqueous PU plastic paint by
A, two kinds of components of B are prepared, in which:
The component A is by mass percentage, raw materials used as follows: scintilla water-based hydroxyl acrylic emulsion 20~50%, micro-
Molecule aqueous one-component acrylic emulsion 10~30%, coalescing agent 0.5~1.5%, aqueous wetting agent 0.3~0.5%, dispersion
Agent 0.2~0.4%, levelling agent 0.3~0.5%, mill base 0~30%, pH adjusting agent 0.1~0.2%, thickener 0.4~
0.8%, defoaming agent 0.1~0.2%, surplus is scintilla water;
The B component is isocyanide ester curing agent;
The mass ratio of the component A and B component is 100:8~20.
2. the double-component aqueous PU plastic paint of scintilla water dispersion according to claim 1, it is characterised in that the differential
Sub- water-based hydroxyl acrylic emulsion is to be scattered in the hydroxyl acrylic emulsion synthesized in a manner of emulsifier-free emulsion polymerization in scintilla water,
Solid content is 44~46wt.%.
3. the double-component aqueous PU plastic paint of scintilla water dispersion according to claim 1, it is characterised in that the differential
Sub- one-component acrylic emulsion be scattered in the one-component acrylic emulsion synthesized in scintilla water with homopolymerization or copolymerized form, Gu
Content is 45~47wt.%.
4. the double-component aqueous PU plastic paint of scintilla water dispersion according to claim 1, it is characterised in that the film forming
Auxiliary agent is propylene glycol phenylate, propandiol butyl ether, diethylene glycol dimethyl ether acetate, butyl acetate, dipropylene glycol fourth
One or more of ether, dipropylene glycol methyl ether, butyl.
5. the double-component aqueous PU plastic paint of scintilla water dispersion according to claim 1, it is characterised in that the thickening
Agent is one or both of alkali swelling type agent for polyacrylic acid thickening, phyllosilicate auxiliary rheological agents.
6. the double-component aqueous PU plastic paint of scintilla water dispersion according to claim 1, it is characterised in that the dispersion
Agent is block propylene acid copolymer type dispersing agent.
7. the double-component aqueous PU plastic paint of scintilla water dispersion according to claim 1, it is characterised in that the defoaming
Agent is organic silicon defoamer.
8. the double-component aqueous PU plastic paint of scintilla water dispersion according to claim 1, it is characterised in that the pH tune
Section agent is one or more of dimethylethanolamine, AMP-95, ammonium hydroxide.
9. the double-component aqueous PU plastic paint of scintilla water dispersion according to claim 1, it is characterised in that the mill base
For resin-free color paste.
10. a kind of system of the double-component aqueous PU plastic paint of scintilla water dispersion described in claim 1-9 any claim
Standby technique, it is characterised in that specific step is as follows by the preparation process:
(1) preparation of component A
It is separately added into scintilla water, aqueous wetting agent, dispersing agent, defoaming agent according to the ratio first in a mixing bowl, it is to be mixed uniform
Afterwards, then according to the ratio scintilla water-based hydroxyl acrylic emulsion, scintilla aqueous one-component acrylic emulsion, film forming is separately added into help
Agent, levelling agent, pH adjusting agent, it is to be mixed uniformly after, add thickener and mill base, after uniform stirring, filtered after passed examination
Packaging;
(2) preparation of B component
Check whether the state of isocyanates is normal, it is directly filling according to the ratio after normal.