CN109054537A - A kind of iron-powder coating - Google Patents
A kind of iron-powder coating Download PDFInfo
- Publication number
- CN109054537A CN109054537A CN201810775090.XA CN201810775090A CN109054537A CN 109054537 A CN109054537 A CN 109054537A CN 201810775090 A CN201810775090 A CN 201810775090A CN 109054537 A CN109054537 A CN 109054537A
- Authority
- CN
- China
- Prior art keywords
- parts
- iron
- agent
- powder coating
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of iron-powder coatings; it is prepared from the following materials: acrylic emulsion, phenylpropyl alcohol modified emulsion, dipropylene, dipropylene glycol methyl ether, ferroso-ferric oxide, antirusting powder, dispersing agent, gas silicon (white carbon black), water, ethyl cellulose, antirust agent, preservative, defoaming agent, wetting agent, thickener; the iron-powder coating has magnetic adsorptive power; it being capable of the magnetic substance of the tool such as adsorption magnet; stapling on the wall is avoided the need for paste the trouble of paper, metope is protected not to be damaged.Even closer, the viscosity height of product is combined between molecule, and safe ingredients are nontoxic, entire manufacturing process Environmentally-frielow-energy-consumptipolycarboxylic low-energy-consumptipolycarboxylic, preparation method is simple, is suitble to industrialized production, high financial profit.
Description
Technical field
The invention belongs to technical field of coatings, especially a kind of iron-powder coating.
Background technique
Coating is to be coated in the body surface protected or decorated, and can form the continuous of firm attachment with coated article
Film addition or does not add pigment, filler usually based on resin or oil or lotion, adds corresponding additive, with organic molten
The thick liquid that agent or water are formulated.More authoritative " coating process " book of Chinese paint industry is defined as: " coating is one
Kind of material, this material can be coated in object surface with different construction technologies, formed adherency securely, with some strength,
Continuous solid film.But the problems such as present coating cohesion is poor, and time long coated article surface will appear cracking, and repair
Get up cumbersome.
Nowadays the works of student or notice etc. can all be attached on wall and open up by many schools, kindergarten etc.
It lookes at, but traditional exhibition mode is that stapling hangs photo frame processed on the wall mostly, destroys metope, absorption works are difficult, therefore send out
A kind of bright iron-powder coating is very necessary.
Summary of the invention
To solve the problems, such as that the deficiencies in the prior art, the present invention provide a kind of iron-powder coating, which has
Adsorbability, and it is environment-protecting and non-poisonous, cohesive force is good, and not easy to crack, preparation method is convenient and simple, is suitable for large industrialized and produces.
Specific technical solution is as follows:
A kind of iron-powder coating is prepared by the raw material of following mass fraction: 10-17 parts of acrylic emulsion, phenylpropyl alcohol are modified
5-10 parts of lotion, 1-5 parts of dipropylene, 1-5 parts of dipropylene glycol methyl ether, 40-60 parts of ferroso-ferric oxide, antirusting powder 8-14
Part, 0.5-1.5 parts of dispersing agent, 1-2 parts of gas silicon (white carbon black), 1-5 parts of water, 0.3-0.8 parts of ethyl cellulose, 1-2 parts of antirust agent,
0.3-0.8 parts of preservative, 0.5-1.5 parts of defoaming agent, 0.5-1.5 parts of wetting agent, 0.5-1.5 parts of thickener.
Preferably, it is prepared by the raw material of following mass fraction: 15 parts of acrylic emulsion, 8 parts of phenylpropyl alcohol modified emulsion, two
3 parts of propandiol butyl ether, 3 parts of dipropylene glycol methyl ether, 50 parts of ferroso-ferric oxide, 10 parts of antirusting powder, 1 part of dispersing agent, gas silicon (hard charcoal
It is black) 1.5 parts, 3 parts of water, 0.5 part of ethyl cellulose, 1.5 parts of antirust agent, 0.5 part of preservative, 1 part of defoaming agent, 1 part of wetting agent, increase
Thick dose 1 part.
Preferably, the fineness of the ferroso-ferric oxide is 1700 mesh or more.
Preferably, the defoaming agent is polypropylene glycerol aether, polyoxyethylene polyoxypropylene glycerin ether or poly dimethyl silicon
One of oxygen alkane.
Preferably, production method the following steps are included:
A. physical dispersion and mixed process: using vane type high speed disperser, and by acrylic emulsion, phenylpropyl alcohol modified emulsion is the same as two
Propandiol butyl ether, dipropylene glycol methyl ether mixing, is made glue;
B. plus auxiliary material: water, dispersing agent, antirust agent, antirusting powder, gas silicon (white carbon black), ethyl cellulose, preservative are added
It is mixed in glue;
C. into step b, ferroso-ferric oxide and wetting agent is added in mixed system, and mixing dispersion adds defoaming agent,
Defoaming;
D. it grinds: using blue formula sand mill, grinding 3 hours;
E. thickener is added, is uniformly mixed;
F. after the examination and test of products is qualified, filtering, filling and package storage.
Preferably, the speed of vane type high speed disperser is 400 turns per minute in the step a, jitter time 10-15
Minute.
Preferably, the mixing velocity in the step b is 900 turns per minute, and jitter time is 20-25 minutes.
Preferably, mixing velocity is 900 turns per minute in the step c, and mixing jitter time is 20-25 minutes.
The utility model has the advantages that
The present invention provides a kind of iron-powder coating, ferroso-ferric oxide joined in raw material, so that the iron-powder coating tool of preparation
Be magnetic adsorption capacity, can the tool such as adsorption magnet magnetic substance, avoid the need for stapling on the wall and paste paper
Trouble, protects metope not to be damaged.In the production process, using different mixing velocities and time, so that raw material is continuous
It mixes, the uniformity in raising system, the combination between molecule is even closer, the viscosity of product is improved, in addition, adding in raw material
Entered preservative and antirust agent, can anticorrosion, make product have excellent performance.Meanwhile use fineness be 1700 mesh with
On ferroso-ferric oxide, surface is fine and smooth, is applied to more smooth when metope.It is safe and non-toxic, and entire manufacturing process environmental protection low energy
Consumption, preparation method is simple, is suitble to industrialized production, high financial profit.
Specific embodiment
The present invention is specifically described in detail with reference to embodiments.
Embodiment 1:
A kind of iron-powder coating is prepared by the raw material of following mass fraction: 10 parts of acrylic emulsion, phenylpropyl alcohol modified emulsion
7 parts, 2 parts of dipropylene, 1 part of dipropylene glycol methyl ether, 60 parts of ferroso-ferric oxide, 8 parts of antirusting powder, 0.5 part of dispersing agent, gas silicon
1 part of (white carbon black), 1 part of water, 0.3 part of ethyl cellulose, 1 part of antirust agent, 0.3 part of preservative, 0.8 part of defoaming agent, wetting agent 0.5
Part, 1.5 parts of thickener.
The preparation method is as follows:
A. physical dispersion and mixed process: using vane type high speed disperser, and by acrylic emulsion, phenylpropyl alcohol modified emulsion is the same as two
Propandiol butyl ether, dipropylene glycol methyl ether mixing, the speed of vane type high speed disperser are 400 turns per minute, jitter time 10
Minute, glue is made;
B. plus auxiliary material: water, dispersing agent, antirust agent, antirusting powder, gas silicon (white carbon black), ethyl cellulose, preservative are added
It is mixed in glue, mixing velocity is 900 turns per minute, and jitter time is 20 minutes;
C. into step b, ferroso-ferric oxide and wetting agent, mixing dispersion is added in mixed system, and mixing velocity is every point
900 turns of clock, mixing jitter time is 20 minutes, adds polypropylene glycerol aether, is defoamed;
D. it grinds: using blue formula sand mill, grinding 3 hours;
E. thickener is added, is uniformly mixed;
F. after the examination and test of products is qualified, filtering, filling and package storage.
Embodiment 2:
A kind of iron-powder coating is prepared by the raw material of following mass fraction: 15 parts of acrylic emulsion, phenylpropyl alcohol modified emulsion
8 parts, 3 parts of dipropylene, 3 parts of dipropylene glycol methyl ether, 50 parts of ferroso-ferric oxide, 10 parts of antirusting powder, 1 part of dispersing agent, gas silicon
1.5 parts of (white carbon black), 3 parts of water, 0.5 part of ethyl cellulose, 1.5 parts of antirust agent, 0.5 part of preservative, 1 part of defoaming agent, wetting agent 1
Part, 1 part of thickener.
The preparation method is as follows:
A. physical dispersion and mixed process: using vane type high speed disperser, and by acrylic emulsion, phenylpropyl alcohol modified emulsion is the same as two
Propandiol butyl ether, dipropylene glycol methyl ether mixing, the speed of vane type high speed disperser are 400 turns per minute, jitter time 13
Minute, glue is made;
B. plus auxiliary material: water, dispersing agent, antirust agent, antirusting powder, gas silicon (white carbon black), ethyl cellulose, preservative are added
It is mixed in glue, mixing velocity is 900 turns per minute, and jitter time is 25 minutes;
C. into step b, ferroso-ferric oxide and wetting agent, mixing dispersion is added in mixed system, and mixing velocity is every point
900 turns of clock, mixing jitter time is 18 minutes, adds polypropylene glycerol aether, is defoamed;
D. it grinds: using blue formula sand mill, grinding 3 hours;
E. thickener is added, is uniformly mixed;
F. after the examination and test of products is qualified, filtering, filling and package storage.
Embodiment 3:
A kind of iron-powder coating is prepared by the raw material of following mass fraction: 17 parts of acrylic emulsion, phenylpropyl alcohol modified emulsion
5 parts, 1 part of dipropylene, 5 parts of dipropylene glycol methyl ether, 40 parts of ferroso-ferric oxide, 14 parts of antirusting powder, 1.5 parts of dispersing agent, gas
2 parts of silicon (white carbon black), 4 parts of water, 0.7 part of ethyl cellulose, 2 parts of antirust agent, 0.8 part of preservative, 0.9 part of defoaming agent, wetting agent
1.2 parts, 0.5 part of thickener.
The preparation method is as follows:
A. physical dispersion and mixed process: using vane type high speed disperser, and by acrylic emulsion, phenylpropyl alcohol modified emulsion is the same as two
Propandiol butyl ether, dipropylene glycol methyl ether mixing, the speed of vane type high speed disperser are 400 turns per minute, jitter time 15
Minute, glue is made;
B. plus auxiliary material: water, dispersing agent, antirust agent, antirusting powder, gas silicon (white carbon black), ethyl cellulose, preservative are added
It is mixed in glue, mixing velocity is 900 turns per minute, and jitter time is 23 minutes;
C. into step b, ferroso-ferric oxide and wetting agent, mixing dispersion is added in mixed system, and mixing velocity is every point
900 turns of clock, mixing jitter time is 21 minutes, adds polypropylene glycerol aether, is defoamed;
D. it grinds: using blue formula sand mill, grinding 3 hours;
E. thickener is added, is uniformly mixed;
F. after the examination and test of products is qualified, filtering, filling and package storage.
Embodiment 4:
A kind of iron-powder coating is prepared by the raw material of following mass fraction: 16 parts of acrylic emulsion, phenylpropyl alcohol modified emulsion
10 parts, 5 parts of dipropylene, 2 parts of dipropylene glycol methyl ether, 55 parts of ferroso-ferric oxide, 13 parts of antirusting powder, 0.8 part of dispersing agent, gas
1.8 parts of silicon (white carbon black), 5 parts of water, 0.8 part of ethyl cellulose, 1.7 parts of antirust agent, 0.4 part of preservative, 1.5 parts of defoaming agent, profit
1.5 parts of humectant, 1.1 parts of thickener.
The preparation method is as follows:
A. physical dispersion and mixed process: using vane type high speed disperser, and by acrylic emulsion, phenylpropyl alcohol modified emulsion is the same as two
Propandiol butyl ether, dipropylene glycol methyl ether mixing, the speed of vane type high speed disperser are 400 turns per minute, jitter time 11
Minute, glue is made;
B. plus auxiliary material: water, dispersing agent, antirust agent, antirusting powder, gas silicon (white carbon black), ethyl cellulose, preservative are added
It is mixed in glue, mixing velocity is 900 turns per minute, and jitter time is 21 minutes;
C. into step b, ferroso-ferric oxide and wetting agent, mixing dispersion is added in mixed system, and mixing velocity is every point
900 turns of clock, mixing jitter time is 25 minutes, adds polypropylene glycerol aether, is defoamed;
D. it grinds: using blue formula sand mill, grinding 3 hours;
E. thickener is added, is uniformly mixed;
F. after the examination and test of products is qualified, filtering, filling and package storage.
By iron-powder coating produced by the present invention, adhesive force is stronger, is all larger than 3.5MPa;Cracking resistance extension rate is high, can prolong
Stretch 5-6 times;Waterproof performance is superior, environment friendly and pollution-free;Preparation method is simple, is suitble to industrialized production, high financial profit.
Claims (8)
1. a kind of iron-powder coating, it is characterised in that: be prepared by the raw material of following mass fraction: 10-17 parts of acrylic emulsion,
5-10 parts of phenylpropyl alcohol modified emulsion, 1-5 parts of dipropylene, 1-5 parts of dipropylene glycol methyl ether, 40-60 parts of ferroso-ferric oxide, antirust
8-14 parts of powder, 0.5-1.5 parts of dispersing agent, 1-2 parts of gas silicon (white carbon black), 1-5 parts of water, 0.3-0.8 parts of ethyl cellulose, antirust agent
1-2 parts, 0.3-0.8 parts of preservative, 0.5-1.5 parts of defoaming agent, 0.5-1.5 parts of wetting agent, 0.5-1.5 parts of thickener.
2. iron-powder coating as described in claim 1, it is characterised in that: be prepared by the raw material of following mass fraction: propylene
15 parts of yogurt liquid, 3 parts of dipropylene, 3 parts of dipropylene glycol methyl ether, 50 parts of ferroso-ferric oxide, is prevented 8 parts of phenylpropyl alcohol modified emulsion
Become rusty 10 parts of powder, 1 part of dispersing agent, 1.5 parts of gas silicon (white carbon black), 3 parts of water, 0.5 part of ethyl cellulose, 1.5 parts of antirust agent, preservative
0.5 part, 1 part of defoaming agent, 1 part of wetting agent, 1 part of thickener.
3. iron-powder coating as claimed in claim 1 or 2, it is characterised in that: the fineness of the ferroso-ferric oxide be 1700 mesh with
On.
4. iron-powder coating as claimed in claim 3, it is characterised in that: the defoaming agent is polypropylene glycerol aether, polyoxy third
One of alkene polyoxyethylene glycerol ether or dimethyl silicone polymer.
5. the iron-powder coating as described in claim 1 or 4, which is characterized in that production method the following steps are included:
A. physical dispersion and mixed process: vane type high speed disperser is used, by acrylic emulsion, phenylpropyl alcohol modified emulsion is the same as dipropyl two
Alcohol butyl ether, dipropylene glycol methyl ether mixing, is made glue;
B. plus auxiliary material: glue is added in water, dispersing agent, antirust agent, antirusting powder, gas silicon (white carbon black), ethyl cellulose, preservative
In mixed;
C. into step b, ferroso-ferric oxide and wetting agent is added in mixed system, and mixing dispersion adds defoaming agent, defoams;
D. it grinds: using blue formula sand mill, grinding 3 hours;
E. thickener is added, is uniformly mixed;
F. after the examination and test of products is qualified, filtering, filling and package storage.
6. the iron-powder coating as claimed in claim 5, which is characterized in that vane type high speed disperser in the step a
Speed be 400 turns per minute, jitter time be 10-15 minutes.
7. the iron-powder coating as claimed in claim 5, which is characterized in that the mixing velocity in the step b is every point
900 turns of clock, jitter time is 20-25 minutes.
8. the iron-powder coating as claimed in claim 5, which is characterized in that mixing velocity is per minute in the step c
900 turns, mixing jitter time is 20-25 minutes.