CN109017099A - A kind of gold stamping dedicated gilding film and its technological process of production after crossing UV - Google Patents
A kind of gold stamping dedicated gilding film and its technological process of production after crossing UV Download PDFInfo
- Publication number
- CN109017099A CN109017099A CN201810815265.5A CN201810815265A CN109017099A CN 109017099 A CN109017099 A CN 109017099A CN 201810815265 A CN201810815265 A CN 201810815265A CN 109017099 A CN109017099 A CN 109017099A
- Authority
- CN
- China
- Prior art keywords
- layer
- gold stamping
- dedicated
- coating
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses excessively a kind of gold stamping dedicated gilding film and its technological process of productions after crossing UV, cross gold stamping dedicated gilding film after UV, including substrate layer, peeling layer, Information Level, metal layer, mucigel, the peeling layer coating is arranged in substrate layer upper end, the Information Level coating is arranged in peeling layer upper end, the metal layer is held on an information layer by plating setting, and the mucigel coating setting is held on the metal layer, then cuts molding gilding film, packs.It crosses gold stamping dedicated gilding film and preparation method thereof after UV the object of the present invention is to provide a kind of and mainly solved the problems, such as after UV or gold stamping adhesive force after the printing of UV ink, with adhesive force height, reach the excellent effect that 3M test tape pulls gold repeatedly, solves a large amount of advanced printed matters, high-grade material needs gold stamping technical problem.
Description
Technical field
The present invention relates to gold stamping technical field of membrane, and in particular to excessively a kind of gold stamping dedicated gilding film and its production work after crossing UV
Skill process.
Background technique
UV printing is a kind of by UV curing, a kind of printing technology of cured printing ink, by UV cure lamp with contain
The ink of photosensitizer matches.The UV that traditional printing refers in the industry is printed matter effect process, and the UV that crosses in the present invention refers to
General property crosses UV, needs the technique general name of UV-light photocuring including crossing after UV gloss oil and the printing of UV ink etc., i.e. this invention is warp
Crossed UV treated the dedicated gilding film in surface.Due to UV ink, UV gloss oil etc. after UV-light photocuring to tradition it is gold stamping have compared with
Strong repellency, so that the modeling class gilding film excessively of the overwhelming majority on a surface can not thermoprint or ineffective.
Summary of the invention
The object of the present invention is to provide gold stamping dedicated gilding films after a kind of UV excessively and preparation method thereof mainly to solve UV
Afterwards or after the printing of UV ink the problem of gold stamping adhesive force, has adhesive force high, reach 3M test tape and pull gold repeatedly
Excellent effect solves a large amount of advanced printed matters, high-grade material needs gold stamping technical problem.
To achieve the goals above, the technical solution adopted by the present invention is that:
A kind of gold stamping dedicated gilding film after crossing UV, including substrate layer, peeling layer, Information Level, aluminium coated, mucigel, it is described
Peeling layer coating setting is in substrate layer upper end, and the Information Level coating setting is in peeling layer upper end, and the metal layer is by plating
Setting is held on an information layer, and the mucigel coating setting is held on the metal layer, and the substrate layer is to use BOPET film for basement membrane
Manufactured film.
The present invention is further arranged to, and embossed plies are equipped between the Information Level and metal layer.
The present invention is further arranged to, the substrate layer with a thickness of 12-15 microns.
It is a kind of cross UV after gold stamping dedicated gilding film the technological process of production the following steps are included:
Peeling layer and Information Level are successively coated with coating machine on substrate layer, makes to increase on Information Level using high-precision press
Add embossed plies, i.e., increase laser effect on an information layer, so that surface has the flowing cangiante lustre of metal-like, then passes through
After the mode of outer processing is added with one layer of aluminium coated made of metal foil in embossed plies 4, finished film is formed.
Then according to customer demand, finished film is cut into corresponding specification, cutting while carries out quality inspection work, will apply
The bad part ejects such as holiday, race side, the dead wrinkle that may occur during cloth.
Finally the finished film cut is packed, with case be put into product using briefly explain and identification label after to
Hair.
Wherein peeling layer is made of water wax stripping method or OP wax stripping method any of them stripping method, the water wax removing
Method is mixed 99.9% or more pure ethanol and deionized water in the ratio of 1:1, and coating setting exists after the stirring sufficiently of water wax is added
Substrate layer upper end, wherein water wax is anodized aluminium mould release 101-5017, and the water wax solid content is less than 8%.
Butanone, ether are added coating after OP wax melts stirring in 2:1 ratio and are arranged in substrate layer by the OP wax stripping method
Upper end, for the OP wax solid content less than 6%, the OP wax has splendid lubrication and release property.
Wherein Information Level is made of acrylic resin, butanone, toluene, wherein effective acrylic resin solid content is
15%-25%, butanone content are 20%-47%, toluene level 15%-30%.
The wherein processing method of aluminium coated are as follows: high-purity aluminium wire is flashed into gaseous state at high temperature, substrate layer passes through later
When being evaporated in vacuo room, gaseous aluminium molecule is deposited in information layer surface, forms bright metal color.
Wherein mucigel is equal according to different proportions using polyurethane resin and butanone, ethyl ester, toluene and modifying agent HY-B
Coating setting is held on the metal layer after even stirring, and the polyurethane resin solid content is between 15%-25%, modifying agent HY-B
Content is 15%-20%, and urethane resin content is 10%-20%, and butanone content is 7%-15%, and ethyl ester content is 10-
30%, toluene level 20%-25%.
The present invention is further arranged to, and adds cyclohexanone on demand in the Information Level.
The present invention is further arranged to, and the aluminum layer thickness is 25-35 nanometers.
Beneficial effects of the present invention: gold stamping dedicated gilding film provided by the present invention after crossing UV, not only color developing effect is good, aobvious
Color is lasting, and low manufacture cost；And the cyclohexanone added in Information Level is colourless transparent liquid, itself has poor volatilization
Property, be adjustable the evaporation rate of solvent in coating procedure, avoid because butanone, ethyl ester equal solvent it is quick volatilization caused by be coated with produce
Shape effect is atomized, after misty effect is generated when so as to cause coating, seriously affects the photochromism of gilding film finished product, so that producing
Quality decline；Because the main function of peeling layer be exactly enable gilding film transfer when peeling layer completely with substrate layer be detached from,
Therefore the production method (material selection) for the peeling layer selected is extremely important, and OP wax stripping method and water wax stripping method all have preferably
Peeling effect, and the peeling layer made of water wax stripping method has the characteristics that micro-perfume, nontoxic, non-flammable.
Detailed description of the invention
Fig. 1 is the structural diagram of the present invention.
Wherein: 1- substrate layer；2- peeling layer；3- Information Level；4- embossed plies；5- aluminium coated；6- mucigel.
Specific embodiment
With reference to the accompanying drawings and examples, specific embodiments of the present invention will be described in further detail.Implement below
Example is not intended to limit the scope of the invention for illustrating the present invention.
Below with reference to Fig. 1, the present invention will be described.
A kind of gold stamping dedicated gilding film after crossing UV, including substrate layer 1, peeling layer 2, Information Level 3, aluminium coated 5, mucigel
6, the coating of peeling layer 2 setting is arranged in 1 upper end of substrate layer, the coating of Information Level 3 in 2 upper end of peeling layer, the metal
Layer is held on the information layer 3 by plating setting, and the coating of mucigel 6 setting is held on the metal layer, and the substrate layer 1 is to use
BOPET film is film made of basement membrane.
The present invention is further arranged to, and embossed plies 4 are equipped between the Information Level 3 and metal layer.
The present invention is further arranged to, the substrate layer 1 with a thickness of 12-15 microns.
It is a kind of cross UV after gold stamping dedicated gilding film the technological process of production the following steps are included:
Peeling layer 2 and Information Level 3 are successively coated with coating machine on substrate layer 1, makes Information Level 3 using high-precision press
Upper increase embossed plies 4, i.e., increase laser effect on the information layer 3, so that surface has the flowing cangiante lustre of metal-like, so
After being added with one layer of aluminium coated 5 made of metal foil in embossed plies 4 by the mode of outer processing afterwards, finished film is formed.
Then according to customer demand, finished film is cut into corresponding specification, cutting while carries out quality inspection work, will apply
The bad part ejects such as holiday, race side, the dead wrinkle that may occur during cloth.
Finally the finished film cut is packed, with case be put into product using briefly explain and identification label after to
Hair.
Wherein peeling layer 2 is made of water wax stripping method or OP wax stripping method any of them stripping method, the water wax stripping
99.9% or more pure ethanol and deionized water are mixed in the ratio of 1:1 from method, coating setting after the stirring sufficiently of water wax is added
In 1 upper end of substrate layer, wherein water wax is anodized aluminium mould release 101-5017, and the water wax solid content is less than 8%.
Butanone, ether are added coating after OP wax melts stirring in 2:1 ratio and are arranged in substrate layer 1 by the OP wax stripping method
Upper end, for the OP wax solid content less than 6%, the OP wax has splendid lubrication and release property.
Wherein Information Level 3 is made of acrylic resin, butanone, toluene, wherein effective acrylic resin solid content is
15%-25%, butanone content are 20%-47%, toluene level 15%-30%.
The wherein processing method of aluminium coated 5 are as follows: high-purity aluminium wire is flashed into gaseous state at high temperature, substrate layer 1 passes through later
When crossing vacuum evaporation room, gaseous aluminium molecule is deposited in 3 surface of Information Level, forms bright metal color.
Wherein mucigel 6 is equal according to different proportions using polyurethane resin and butanone, ethyl ester, toluene and modifying agent HY-B
Coating setting is held on the metal layer after even stirring, and the polyurethane resin solid content is between 15%-25%, modifying agent HY-
B content is 15%-20%, and urethane resin content is 10%-20%, and butanone content is 7%-15%, and ethyl ester content is 10-
30%, toluene level 20%-25%.
The present invention is further arranged to, and adds cyclohexanone on demand in the Information Level 3.
The present invention is further arranged to, and the aluminium coated 5 is with a thickness of 25-35 nanometers.
The above is only a preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For member, without departing from the technical principles of the invention, several improvements and modifications can also be made, above-mentioned hypothesis these
Improvement and modification also should be regarded as protection scope of the present invention.
Claims (6)
1. a kind of gold stamping dedicated gilding film after crossing UV, it is characterised in that: including substrate layer, peeling layer, Information Level, aluminium coated, stick
Glue-line, the peeling layer coating setting are arranged in substrate layer upper end, the Information Level coating in peeling layer upper end, the metal layer
It is held on an information layer by plating setting, the mucigel coating setting is held on the metal layer, and the substrate layer is using BOPET
Film is film made of basement membrane.
2. a kind of gold stamping dedicated gilding film after crossing UV according to claim 1, it is characterised in that: the Information Level and metal
Embossed plies are equipped between layer.
3. a kind of gold stamping dedicated gilding film after crossing UV according to claim 1, it is characterised in that: the thickness of the substrate layer
It is 12-15 microns.
4. it is a kind of cross UV after gold stamping dedicated gilding film the technological process of production, it is characterised in that: the technological process of production include with
Lower step:
Peeling layer and Information Level are successively coated with coating machine on substrate layer, makes to increase mould on Information Level using high-precision press
Pressurized layer increases laser effect on an information layer, so that surface has the flowing cangiante lustre of metal-like, then by additional
After the mode of work is added with one layer of aluminium coated made of metal foil in embossed plies 4, finished film is formed；
Then according to customer demand, finished film is cut into corresponding specification, cutting while carries out quality inspection work, will be coated
The bad part ejects such as holiday, race side, the dead wrinkle that may occur in journey；
Finally the finished film cut is packed, with case be put into product using briefly explain and identification label after it is pending；
Wherein peeling layer is made of water wax stripping method or OP wax stripping method any of them stripping method, and the water wax stripping method will
99.9% or more pure ethanol and deionized water are mixed in the ratio of 1:1, and coating is arranged in substrate after the stirring sufficiently of water wax is added
Layer upper end, wherein water wax is anodized aluminium mould release 101-5017, and the water wax solid content is less than 8%；
Butanone, ether are added coating after OP wax melts stirring in 2:1 ratio and are arranged in substrate layer upper end by the OP wax stripping method,
For the OP wax solid content less than 6%, the OP wax has splendid lubrication and release property；
Wherein Information Level is made of acrylic resin, butanone, toluene, wherein effective acrylic resin solid content is 15%-
25%, butanone content is 20%-47%, toluene level 15%-30%；
The wherein processing method of aluminium coated are as follows: high-purity aluminium wire is flashed into gaseous state at high temperature, substrate layer passes through vacuum later
When vaporization chamber, gaseous aluminium molecule is deposited in information layer surface, forms bright metal color.
Wherein mucigel is uniformly stirred using polyurethane resin and butanone, ethyl ester, toluene and modifying agent HY-B according to different proportions
Coating setting is held on the metal layer after mixing, and the polyurethane resin solid content is between 15%-25%, modifying agent HY-B content
For 15%-20%, urethane resin content is 10%-20%, and butanone content is 7%-15%, and ethyl ester content is 10-30%, toluene
Content is 20%-25%.
5. the technological process of production of gold stamping dedicated gilding film after a kind of UV excessively according to claim 4, it is characterised in that: institute
It states and adds cyclohexanone in Information Level on demand.
6. the technological process of production of gold stamping dedicated gilding film after a kind of UV excessively according to claim 4, it is characterised in that: institute
Stating aluminum layer thickness is 25-35 nanometers.