CN108854870A - 一种高纯度硅铝溶胶的制备方法 - Google Patents
一种高纯度硅铝溶胶的制备方法 Download PDFInfo
- Publication number
- CN108854870A CN108854870A CN201710327914.2A CN201710327914A CN108854870A CN 108854870 A CN108854870 A CN 108854870A CN 201710327914 A CN201710327914 A CN 201710327914A CN 108854870 A CN108854870 A CN 108854870A
- Authority
- CN
- China
- Prior art keywords
- aluminum sol
- high purity
- preparation
- sol
- purity silicon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高纯度硅铝溶胶的制备方法,以异丙醇铝为铝源,以正硅酸乙酯为硅源,采用水解法分别制备得到铝溶胶和硅溶胶。通过添加表面活性剂,显著改善了溶胶的稳定性,从而可以长时间存放溶胶和提高溶胶的浓度。在此基础上,采用水解法以制备好的铝溶胶为溶剂,按照步骤二的方法制备硅溶胶。在硅溶胶形成过程中溶胶粒子与溶液中的铝溶胶粒子结合形成硅铝溶胶。以该方法制备得到的硅铝溶胶纯度高,稳定性好,具有广泛的应用前景。
Description
技术领域
本发明属于纳米材料技术领域,涉及一种高纯度硅铝溶胶的制备方法。
背景技术
铝溶胶是一水合氧化铝微细粒子分散在水中形成的胶体溶液,具有易分散性、稳定性、水溶可逆性、带正电性、胶粘性、触变性、吸附性等诸多特性,可被广泛应用于无机纤维、搪瓷、日用品、活性高纯氧化铝、石油化工催化剂、造纸等多种行业。硅溶胶是多元活性硅酸的共聚物,是一种由二氧化硅粒子形成的胶体溶液,具有高分散性、高吸附性,大的比表面积等优良的性能,从而广泛应用在造纸、涂料、精密铸造、催化和纺织等工业领域。
铝溶胶和硅溶胶的结构和应用十分相似,因此可混合使用,从而发挥出更加优异的性能。由于酸性硅溶胶不稳定,市场上很少有酸性硅溶胶与铝溶胶混合使用的案例。本专利以正硅酸乙酯和异丙醇铝为原料,采用水解法制备出性质稳定,纯度高的铝溶胶和硅溶胶,并将两者按一定方法混合,得到一种工艺简单、纯度高、应用广泛的硅铝溶胶前驱体。
发明内容
本发明针对现有技术的上述问题,提供一种高纯度硅铝溶胶的制备方法。
为达到上述发明目的,本发明采用的技术方案是:一种高纯度硅铝溶胶的制备方法,可分别按下述步骤制得。
步骤一:在三口烧瓶中加入一定量的水,在恒温水浴锅中水浴加热到一定的温度,然后缓慢加入研磨好的异丙醇铝,边加边搅拌,再缓慢滴加一定量的异丙醇。之后水解反应1.5h,水解完成后,升温至95℃,敞口搅拌1h,蒸去大部分的异丙醇,得到白色勃姆石沉淀,补充损失的水分后,加入一定量的硝酸进行胶溶,控制溶胶的pH在一定的范围,然后加入表面活性剂A和少量螯合剂,回流陈化12h,制得稳定透明的铝溶胶。
步骤二:将正硅酸乙酯倒入烧杯中,先于室温下预水解,搅拌至澄清,溶于乙醇中,加入去离子水,然后加入少量硝酸和表面活性剂A,在70℃下搅拌反应60min。在此温度下必须严格控制搅拌时间,如果时间过长会使颗粒团聚,稳定性降低,导致溶胶凝胶时间过短,不能长时间存放。
步骤三:以步骤一所制备的铝溶胶作为溶剂,将正硅酸乙酯预水解后加入到铝溶胶中。根据溶胶中所需要的硅铝比来确定铝溶胶和正硅酸乙酯的用量。然后加入一定比例的硝酸和少量表面活性剂A,用乙醇稀释后,缓慢搅拌15分钟,之后在70℃下搅拌反应60min。调节混合溶胶的pH在一定范围内,然后在超声波清洗机中经T=25℃,F=32000Hz条件下超声30min使溶胶充分混合,粒子均匀分散,从而制备得到硅铝溶胶。
步骤一中所述异丙醇铝与异丙醇的摩尔比优选为1:1~1:3。
步骤一中异丙醇铝/硝酸/去离子水的摩尔比为1:0.2:150。
步骤一、二、三中表面活性剂A可选聚乙烯醇、十六烷基三甲基溴化铵、十二烷基苯磺酸钠中的一种;步骤一中的螯合剂B可选择乙酰乙酸乙酯、二乙胺四乙酸、柠檬酸、乙二胺中的一种。
步骤一中异丙醇铝与表面活性剂和螯合剂的质量比优选为1:0.001~1:0.001,步骤二正硅酸乙酯与表面活性剂的摩尔比优选为1:0.1~1:0.01。
步骤二和步骤三中正硅酸乙酯/去离子水/硝酸/乙醇的摩尔比为1:10:0.005:10。
步骤一中的水解温度优选为85℃~92℃。
步骤一和步骤三中溶胶的pH采用氨水和稀硝酸控制在2~4之间;步骤三中溶胶所含Al2O3和SiO2的比值优选为4:1~1:4。
本发明公开了一种高纯度硅铝溶胶的制备方法,以异丙醇铝为铝源,以正硅酸乙酯为硅源,采用水解法分别制备得到铝溶胶和硅溶胶。通过添加表面活性剂,显著改善了溶胶的稳定性,从而可以长时间存放溶胶和提高溶胶的浓度。在此基础上,采用水解法以制备好的铝溶胶为溶剂,按照步骤二的方法制备硅溶胶。在硅溶胶形成过程中溶胶粒子与溶液中的铝溶胶粒子结合形成硅铝溶胶。以该方法制备得到的硅铝溶胶纯度高,稳定性好,具有广泛的应用前景。
附图说明
附图1为制备的铝溶胶凝胶后经1100℃高温处理的XRD谱图。
附图2是硅铝溶胶凝胶后在不同温度下处理后的XRD谱图。
具体实施方式
实施例1
在三口烧瓶中加入374.22ml去离子水,在恒温水浴锅中水浴加热至92℃,然后缓慢加入研磨好的异丙醇铝28.3g,再缓慢滴加20mL异丙醇。水解反应1.5h,水解完成后,敞口搅拌1h,蒸去大部分醇,得白色勃姆石沉淀,补充损失的水分后,加入27.72ml硝酸(浓度为1mol/L)进行胶溶,反应一段时间后加入0.03g十六烷基三甲基溴化铵,升温至95℃,回流反应12h。制备得到铝溶胶。铝溶胶的平均粒径在10nm左右。
所得到的铝溶胶凝胶后经过1100℃高温处理的XRD谱图如图1所示。
实施例2
以制备好的铝溶胶为溶剂,加入预水解后的正硅酸乙酯44.6ml,乙醇10ml,以及1mol/L硝酸,搅拌60min。待形成溶胶后,加入0.7g十六烷基三甲基溴化铵,恢复至室温,。用氨水和稀硝酸调节混合溶胶的pH为3。将反应得到的溶胶经T=25℃,F=32000Hz超声30min使溶胶充分混合,粒子均匀分散。
所得到的硅铝溶胶凝胶后经过不同温度处理的XRD谱图如图2所示。
以上已对本发明的较佳实施例进行了具体说明,但本发明并不限于所述实施例,熟悉本领域的技术人员在不违背本发明精神的前提下还可作出种种的等同的变型或替换,这些等同的变型或替换均包含在本申请权利要求所限定的范围内。
Claims (9)
1.一种高纯度硅铝溶胶的制备方法,其特征在于按下述步骤进行制备:
步骤一:在三口烧瓶中加入一定量的水,在恒温水浴锅中水浴加热到一定的温度,然后缓慢加入研磨好的异丙醇铝,边加边搅拌,再缓慢滴加一定量的异丙醇,之后水解反应1.5h,水解完成后,升温至95℃,敞口搅拌1h,蒸去大部分的异丙醇,得到白色勃姆石沉淀,补充损失的水分后,加入一定量的硝酸进行胶溶,控制溶胶的pH在一定的范围,然后加入表面活性剂A和少量螯合剂,回流陈化12h,制得稳定透明的铝溶胶;
步骤二:将正硅酸乙酯倒入烧杯中,先于室温下预水解,搅拌至澄清,溶于乙醇中,加入去离子水,然后加入少量硝酸和表面活性剂A,在70℃下搅拌反应60min,在此温度下必须严格控制搅拌时间,如果时间过长会使颗粒团聚,稳定性降低,导致溶胶凝胶时间过短,不能长时间存放;
步骤三:以步骤一所制备的铝溶胶作为溶剂,将正硅酸乙酯预水解后加入到铝溶胶中,根据溶胶中所需要的硅铝比来确定铝溶胶和正硅酸乙酯的用量,然后加入一定比例的硝酸和少量表面活性剂A,用乙醇稀释后,缓慢搅拌15分钟,之后在70℃下搅拌反应60min,调节混合溶胶的pH在一定范围内,然后在超声波清洗机中经T=25℃,F=32000Hz条件下超声30min使溶胶充分混合,粒子均匀分散,从而制备得到硅铝溶胶。
2.根据权利要求1所述的一种高纯度硅铝溶胶的制备方法,其特征在于,所述步骤一中所述异丙醇铝与异丙醇的摩尔比优选为1:1~1:3。
3.根据权利要求1所述的一种高纯度硅铝溶胶的制备方法,其特征在于,所述步骤一中异丙醇铝/硝酸/去离子水的摩尔比为1:0.2:150。
4.根据权利要求1所述的一种高纯度硅铝溶胶的制备方法,其特征在于,所述步骤一、二、三中表面活性剂A可选聚乙烯醇、十六烷基三甲基溴化铵、十二烷基苯磺酸钠中的一种;步骤一中的螯合剂B可选择乙酰乙酸乙酯、二乙胺四乙酸、柠檬酸、乙二胺中的一种。
5.根据权利要求1所述的一种高纯度硅铝溶胶的制备方法,其特征在于,所述步骤一中异丙醇铝与表面活性剂和螯合剂的质量比优选为1:0.001~1:0.001,步骤二正硅酸乙酯与表面活性剂的摩尔比优选为1:0.1~1:0.01。
6.根据权利要求1所述的一种高纯度硅铝溶胶的制备方法,其特征在于,所述步骤二和步骤三中正硅酸乙酯/去离子水/硝酸/乙醇的摩尔比为1:10:0.005:10。
7.根据权利要求1所述的一种高纯度硅铝溶胶的制备方法,其特征在于,所述步骤一中的水解温度优选为85℃~92℃。
8.根据权利要求1所述的一种高纯度硅铝溶胶的制备方法,其特征在于,所述步骤一和步骤三中溶胶的pH采用氨水和稀硝酸控制在2~4之间。
9.根据权利要求1所述的一种高纯度硅铝溶胶的制备方法,其特征在于,所述步骤三中溶胶所含Al2O3和SiO2的比值优选为4:1~1:4。