CN108774027A - 一种防水瓷砖胶黏剂 - Google Patents
一种防水瓷砖胶黏剂 Download PDFInfo
- Publication number
- CN108774027A CN108774027A CN201810552415.8A CN201810552415A CN108774027A CN 108774027 A CN108774027 A CN 108774027A CN 201810552415 A CN201810552415 A CN 201810552415A CN 108774027 A CN108774027 A CN 108774027A
- Authority
- CN
- China
- Prior art keywords
- parts
- ceramic tile
- tile adhesive
- mineral wool
- modified silicon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种防水瓷砖胶黏剂，包括如下重量份的原料：硅酸盐水泥30～40份，石英砂30～40份，改性粉煤灰15～20份，改性硅灰石纤维10～15份，羧甲基维生素5～10份，木棉纤维5～10份，海菜胶粉1～5份，乳胶粉0.5～1份，增稠剂0.1～0.5份，交联剂0.1～0.5；其中，改性硅灰石纤维通过如下方法制备所得：将硅灰石纤维与环糊精、石墨烯混合搅拌，加入到阳离子表面活性剂溶液中超声混合10～20min，即得所述改性硅灰石纤维。本发明产品具有良好的柔性和粘结强度，有效的阻碍水分通过砖缝向基材的渗透，保护了瓷砖的牢固性，又提高了装饰体系的稳定性和防水性能。
Description
技术领域
本发明属于瓷砖胶粘剂领域，特别涉及一种防水瓷砖胶黏剂。
背景技术
瓷砖胶粘剂，是一种粘结度高、耐水、耐冻、耐老化的胶粘剂，主要用于粘贴普通瓷砖、陶砖、釉面砖、地砖、大理石、花岗石、石膏板等墙体装饰材料。目前，市场上的瓷砖胶粘剂的种类繁多，不同的应用对瓷砖胶粘剂的性能要求不同，如长期应用在碱性环境中的，要求瓷砖胶抗碱性能强；粘贴大尺寸砖在立面的，要求抗滑移性能强的瓷砖胶；粘贴低吸水率大尺寸玻化砖的，要求瓷砖胶具备较好的润湿性能；长期遇水的环境，要求使用具有一定防水性能的瓷砖胶。
目前，常用的瓷砖胶粘剂对防水性能的要求比较低，只对浸水后的粘结强度进行了限定，而对吸水率和抗渗性能没有任何要求，但在实际使用过程中，瓷砖胶的防水性能很关键，例如浴室，经常迎水面遇水，若瓷砖胶不具有防水抗渗性能，水会顺着瓷砖缝隙渗透到瓷砖胶层，在瓷砖胶层横向扩散到下面的防水层，使防水层造成了长期潮湿遇水的环境，导致防水层柔韧性、粘结力、防水性能都会有所下降，长此以往会有潮气甚至水透过墙体，影响墙面的装修和居住舒适度。因此，研究具有防水抗渗性能的瓷砖胶黏剂具有重要的现实意义。
发明内容
本发明的目的是针对现有技术存在的缺陷，提供了一种具有防水抗渗性能的瓷砖胶黏剂。
本发明解决上述技术问题的技术方案如下：
一种防水瓷砖胶黏剂，包括如下重量份的原料：硅酸盐水泥30～40份，石英砂30～40份，改性粉煤灰15～20份，改性硅灰石纤维10～15份，羧甲基维生素5～10份，木棉纤维5～10份，海菜胶粉1～5份，乳胶粉0.5～1份，增稠剂0.1～0.5份，交联剂0.1～0.5份。
优选的，一种防水瓷砖胶黏剂，包括如下重量份的原料：硅酸盐水泥40份，石英砂30份，粉煤灰15份，硅灰石纤维10份，羧甲基维生素8份，木棉纤维5份，海菜胶粉3份，乳胶粉1份，增稠剂0.5份，交联剂0.3份。
优选的，所述改性硅灰石纤维通过如下方法制备所得：将硅灰石纤维与环糊精、石墨烯混合搅拌，加入到阳离子表面活性剂溶液中超声混合10～20min，即得所述改性硅灰石纤维。
优选的，所述硅灰石纤维与环糊精、石墨烯的重量比为1:0.1～0.5:0.05～0.1。
优选的，所述阳离子表面活性剂溶液的质量分数为15～30％。
优选的，所述增稠剂为纤维素醚及其衍生物类、缔合型碱溶胀增稠剂、聚氨酯增稠剂、聚丙烯酸类增稠剂中的一种或多种。
优选的，所述交联剂为三聚磷酸钠、三氯氧磷、三偏磷酸钠、硼酸钠中的一种或多种。
本发明与现有技术相比的有益效果：
(1)本发明瓷砖胶黏剂利用矿物材料和乳胶粉末的有机结合，提高其粘附力，使材料具有较高的粘结性能；材料中添加改性硅灰石纤维降低了胶黏剂的孔隙率，极大地改善和提高了瓷砖粘结材料的密实和防水抗渗性能，同时改性硅灰石纤维具有较强的柔韧性，避免了材料因变形引起开裂，提高了粘结材料的抗拉强度，避免了瓷砖脱落的隐患。
(2)本发明瓷砖胶黏剂添加改性粉煤灰与改性硅灰石纤维，提高胶黏剂的柔性和粘结强度，有效的阻碍水分通过砖缝向基材的渗透，保护了瓷砖的牢固性，又提高了装饰体系的稳定性和防水性能。
(3)本发明瓷砖胶黏剂无毒，环保，复合绿色建材的要求。
具体实施方式
以下对本发明的原理和特征进行描述，所举实例只用于解释本发明，并非用于限定本发明的范围。
实施例1
一种防水瓷砖胶黏剂，包括如下重量份的原料：硅酸盐水泥30份，石英砂30份，改性粉煤灰15份，改性硅灰石纤维10份，羧甲基维生素5份，木棉纤维5份，海菜胶粉1份，乳胶粉0.5份，纤维素醚及其衍生物类0.1份，三聚磷酸钠0.1份；
其中，改性硅灰石纤维通过如下方法制备所得：将硅灰石纤维与环糊精、石墨烯按重量比为1:0.1:0.05混合搅拌，加入到质量分数为15％的阳离子表面活性剂溶液中超声混合20min，即得所述改性硅灰石纤维。
实施例2
一种防水瓷砖胶黏剂，包括如下重量份的原料：硅酸盐水泥40份，石英砂30份，粉煤灰15份，硅灰石纤维10份，羧甲基维生素8份，木棉纤维5份，海菜胶粉3份，乳胶粉1份，缔合型碱溶胀增稠剂0.5份，三氯氧磷0.3份；
其中，改性硅灰石纤维通过如下方法制备所得：将硅灰石纤维与环糊精、石墨烯按重量比为1:0.3:0.08混合搅拌，加入到质量分数为20％的阳离子表面活性剂溶液中超声混合15min，即得所述改性硅灰石纤维。
实施例3
一种防水瓷砖胶黏剂，包括如下重量份的原料：硅酸盐水泥40份，石英砂40份，改性粉煤灰20份，改性硅灰石纤维15份，羧甲基维生素10份，木棉纤维10份，海菜胶粉5份，乳胶粉1份，聚氨酯增稠剂0.5份，三偏磷酸钠0.5份；
其中，改性硅灰石纤维通过如下方法制备所得：将硅灰石纤维与环糊精、石墨烯按重量比为1:0.5:0.1混合搅拌，加入到质量分数为30％的阳离子表面活性剂溶液中超声混合10min，即得所述改性硅灰石纤维。
实施例4
一种防水瓷砖胶黏剂，包括如下重量份的原料：硅酸盐水泥35份，石英砂35份，改性粉煤灰20份，改性硅灰石纤维15份，羧甲基维生素10份，木棉纤维8份，海菜胶粉5份，乳胶粉0.8份，聚丙烯酸类增稠剂0.3份，硼酸钠0.3份；
其中，改性硅灰石纤维通过如下方法制备所得：将硅灰石纤维与环糊精、石墨烯按重量比为1:0.5:0.05混合搅拌，加入到质量分数为25％的阳离子表面活性剂溶液中超声混合15min，即得所述改性硅灰石纤维。
对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其它的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。
以上所述仅为本发明的较佳实施例，并不用以限制本发明，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (7)
1.一种防水瓷砖胶黏剂，其特征在于，包括如下重量份的原料：硅酸盐水泥30～40份，石英砂30～40份，改性粉煤灰15～20份，改性硅灰石纤维10～15份，羧甲基维生素5～10份，木棉纤维5～10份，海菜胶粉1～5份，乳胶粉0.5～1份，增稠剂0.1～0.5份，交联剂0.1～0.5份。
2.根据权利要求1所述的防水瓷砖胶黏剂，其特征在于，包括如下重量份的原料：硅酸盐水泥40份，石英砂30份，粉煤灰15份，硅灰石纤维10份，羧甲基维生素8份，木棉纤维5份，海菜胶粉3份，乳胶粉1份，增稠剂0.5份，交联剂0.3份。
3.根据权利要求1所述的防水瓷砖胶黏剂，其特征在于，所述改性硅灰石纤维通过如下方法制备所得：将硅灰石纤维与环糊精、石墨烯混合搅拌，加入到阳离子表面活性剂溶液中超声混合10～20min，即得所述改性硅灰石纤维。
4.根据权利要求3所述的防水瓷砖胶黏剂，其特征在于，所述硅灰石纤维与环糊精、石墨烯的重量比为1:0.1～0.5:0.05～0.1。
5.根据权利要求3所述的防水瓷砖胶黏剂，其特征在于，所述阳离子表面活性剂溶液的质量分数为15～30％。
6.根据权利要求1所述的防水瓷砖胶黏剂，其特征在于，所述增稠剂为纤维素醚及其衍生物类、缔合型碱溶胀增稠剂、聚氨酯增稠剂、聚丙烯酸类增稠剂中的一种或多种。
7.根据权利要求1所述的防水瓷砖胶黏剂，其特征在于，所述交联剂为三聚磷酸钠、三氯氧磷、三偏磷酸钠、硼酸钠中的一种或多种。