CN108752884A - 一种高抗菌性pla/pbat材料及其制备方法与应用 - Google Patents
一种高抗菌性pla/pbat材料及其制备方法与应用 Download PDFInfo
- Publication number
- CN108752884A CN108752884A CN201810547264.7A CN201810547264A CN108752884A CN 108752884 A CN108752884 A CN 108752884A CN 201810547264 A CN201810547264 A CN 201810547264A CN 108752884 A CN108752884 A CN 108752884A
- Authority
- CN
- China
- Prior art keywords
- pla
- pbat
- inorganic filler
- antibiotic property
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于高分子材料制备技术领域,具体涉及一种高抗菌性PLA/PBAT材料及其制备方法与应用。该方法将无机填料在负压条件下与锌盐水溶液混合,再碱化,热处理,偶联,可获得ZnO均匀分布的抗菌性填料,最后与PLA和PBAT混合得到高抗菌性PLA/PBAT材料,可提高材料的抗菌效率,并避免由于直接填充纳米ZnO导致的材料力学性能下降。偶联剂的负载可提高抗菌性无机填料在PLA/PBAT基体中的分散性及粘合力。当抗菌剂无机填料的添加量达到1phr时,PLA/PBAT材料对大肠杆菌和金黄色葡萄球菌的抑菌率即可达100%;当添加量达到20phr时,PLA/PBAT材料的拉伸强度和冲击强度没有下降现象,同时弯曲强度得以提高。由此制备的高抗菌性PLA/PBAT材料可被用于包装薄膜、无纺布、管材或片材等领域中。
Description
技术领域
本发明属于高分子材料制备技术领域,具体涉及一种高抗菌性PLA/PBAT 材料及其制备方法与应用。
背景技术
聚乳酸(PLA)和己二酸/对苯二甲酸-丁二酯共聚物(PBAT)是目前较为 成熟的生物可降解树脂,具有透明、易加工和原料天然等特点,是替代石油基 树脂的理想材料。然而,当替代聚乙烯来制备保鲜膜、包装薄膜或农膜时,PLA 虽然拉伸强度高,但却具有抗冲击强度、抗撕裂能力差,热变形温度低的缺点, 难以达到聚乙烯薄膜的技术性能指标;而PBAT虽然具有良好的柔韧性和成膜 性,但其强度和模量较低,阻隔性能差,且价格高,因此其推广与应用也受到 限制。为克服上述缺点,现有研究将两者共混制备PLA/PBAT基包装材料,以 实现两者性能互补的目的。但是,将PLA/PBAT用作食品包装材料时,其还具 有抗菌性能差的缺点,不能满足食品级包装材料的要求。
发明内容
为克服现有技术的缺点和不足,本发明的首要目的在于提供一种高抗菌性 PLA/PBAT材料的制备方法。
本发明的另一目的在于提供由上述制备方法得到的高抗菌性PLA/PBAT材 料。
本发明的再一目的在于提供上述高抗菌性PLA/PBAT材料的应用。
为实现上述目的,本发明采用的技术方案如下:
一种高抗菌性PLA/PBAT材料的制备方法,包括以下步骤:
(1)将无机填料置于容器中,抽真空,加入锌盐水溶液,搅拌,使无机填 料达到吸附平衡,过滤,干燥,得到锌离子化填料;
(2)向锌离子化填料中添加稀碱溶液,直至锌离子化填料所在溶液的 pH=8~10,震荡,过滤得到沉淀,洗涤,干燥,得到表面覆盖有Zn(OH)2的无 机填料;
(3)将表面覆盖有Zn(OH)2的无机填料进行煅烧,得到负载ZnO的无机填 料;
(4)将负载ZnO的无机填料与偶联剂混合均匀,干燥,得到抗菌性无机填 料;
(5)将聚乳酸(PLA)、己二酸/对苯二甲酸-丁二酯共聚物(PBAT)和抗 菌性无机填料在室温下混合,熔融挤出或混炼造粒,得到所述的高抗菌性 PLA/PBAT材料;
所述的PLA、PBAT和抗菌性无机填料的混合按质量份数配比为:PLA 50~ 100份、PBAT 0~50份和抗菌性无机填料1~20份。
优选的,步骤(1)中所述的无机填料为硅藻土、麦饭石粉、纳米二氧化硅、 高岭土或蒙脱土。
优选的,首先将步骤(1)中所述的无机填料在70~90℃下进行干燥处理, 然后置于容器中,抽真空,进行后续处理。
优选的,步骤(1)中所述的抽真空的条件为在0.05~0.1MPa下抽真空0.5~ 3h。
优选的,步骤(1)中所述的锌盐水溶液为醋酸锌水溶液、氯化锌水溶液或 硝酸锌水溶液。
优选的,步骤(1)中所述的锌盐水溶液的浓度为0.01~0.5mol/L。
优选的,步骤(1)中所述的加入锌盐水溶液的量按锌盐水溶液:无机填料 =1:6~1:3的质量配比。
优选的,步骤(1)中所述的搅拌的方法为在50~200r/min下磁力搅拌3h。
优选的,步骤(1)中所述的干燥的温度为160~200℃。
优选的,步骤(2)中所述的稀碱溶液为氨水溶液、氢氧化钠溶液或氢氧化 钾溶液。
优选的,步骤(2)中所述的稀碱溶液的浓度为0.01~0.5mol/L。
优选的,步骤(2)中所述的添加稀碱溶液的方法为逐步滴加。
优选的,步骤(2)中所述的震荡的方式为在30~80℃下超声震荡30min。
优选的,步骤(2)中所述的干燥的温度为80~200℃。
优选的,步骤(3)中所述的煅烧的温度为80~200℃。
优选的,步骤(4)中所述的偶联剂为钛酸酯偶联剂和硅烷偶联剂。
优选的,步骤(4)中所述的偶联剂的用量为负载ZnO的无机填料的质量的 1~3%。
优选的,步骤(4)中所述的混合均匀的方法为采用高速混合机干法。
优选的,步骤(5)中所述的熔融挤出或混炼造粒的温度为160~200℃。
优选的,步骤(5)中所述的PLA、PBAT和抗菌性无机填料的混合按质量 份数配比为:聚乳酸85份、己二酸/对苯二甲酸-丁二酯共聚物15份和抗菌性 无机填料1~20份。
本发明进一步提供由上述制备方法得到的高抗菌性PLA/PBAT材料。
本发明进一步提供上述高抗菌性PLA/PBAT材料的应用,将所述的高抗菌 性PLA/PBAT材料用作包装薄膜、无纺布、管材或片材。
本发明与现有技术相比,具有如下的优点和有益效果:
(1)本发明中制备的抗菌性无机填料为负载ZnO和偶联剂的无机填料, 通过将无机填料在负压条件下与锌盐水溶液混合,达到吸附平衡,再碱化,热 处理,偶联得到的抗菌性无机填料,可使ZnO均匀分布在填料表面,一方面可 利用填料的高比表面积提高ZnO抗菌剂的比表面积,进而提高材料的抗菌效率, 另一方面可充分避免向PLA/PBAT材料中直接添加ZnO而产生的团聚现象,抑 制由于ZnO团聚而导致的PLA/PBAT材料力学性能下降的问题。
(2)本发明中的抗菌性无机填料在负载ZnO后还负载了偶联剂,因此可 提高抗菌性无机填料在PLA/PBAT基体中的分散性及粘合力,强化PLA/PBAT 材料不会因抗菌性无机填料的加入而发生力学性能下降的问题。
(3)本发明制备的PLA/PBAT材料兼具高抗菌性和高力学性能,当抗菌 剂无机填料的添加量达到1phr时,其对大肠杆菌和金黄色葡萄球菌的抑菌率可 达100%。当抗菌剂无机填料的添加量达到20phr时,PLA/PBAT材料的拉伸强 度和冲击强度没有下降现象,同时弯曲强度得以提高。
具体实施方式
下面结合实施例对本发明作进一步的详细说明,但本发明的实施方式不限 于此。对于未特别注明的工艺参数,可参照常规技术进行。
实施例1
本实施例提供25种高抗菌性PLA/PBAT材料及其制备方法与应用,并提供 相应对照例。
(一)高抗菌性PLA/PBAT材料的制备:
(1)将表1中实验2~26所示的无机填料(包括硅藻土、麦饭石粉、蒙 脱土、高岭土、二氧化硅)于80℃下干燥处理12h,然后置于三口烧瓶中,于0.1MPa下抽真空0.5h,然后分别与0.5mol/L的硝酸锌水溶液混合,在200r/min 下磁力搅拌3h,过滤,在160℃下干燥,得到锌离子化填料。
(2)向锌离子化填料中加入浓度为0.1mol/L的NaOH水溶液至pH=8, 在80℃下超声震荡30min,洗涤,过滤,得到表面覆盖有Zn(OH)2的无机填料。
(3)将表面覆盖有Zn(OH)2的无机填料在180℃下煅烧,得到负载ZnO 的无机填料。
(4)将负载ZnO的无机填料与钛酸酯偶联剂(质量为无机粒子的1wt%) 采用高速混合机混合均匀,在80℃下干燥,得到抗菌性无机填料。
(5)按照表1中实验2~26所示的质量比,将PLA、PBAT分别与上述抗 菌性无机填料混合,在160℃下熔融挤出造粒,得到25种高抗菌性PLA/PBAT 材料。
(二)对照例1:无填料的PLA/PBAT材料的制备:
按照表1中实验1所示的质量比,将PLA和PBAT混合,在160℃下熔融 挤出造粒,得到无填料的PLA/PBAT材料。
(三)对照例2:添加非抗菌性填料的PLA/PBAT材料的制备:
按照表2中对比例1~25所示的质量比,将PLA、PBAT和无机填料混合, 在160℃下熔融挤出造粒,得到添加非抗菌性填料的PLA/PBAT材料。
(四)对照例3:添加偶联剂处理的纳米ZnO的PLA/PBAT材料的制备:
按照表3中对比例26~28所示质量比,将PLA、PBAT和经过钛酸酯偶联 剂(质量为纳米ZnO的1wt%)处理的纳米ZnO(粒径约为30nm)混合,在 160℃下熔融挤出造粒,得到添加偶联剂处理的纳米ZnO的PLA/PBAT材料。
采用光密度测量法和标准力学测试方法(GB/T 1040.3–2006),对上述高抗 菌性PLA/PBAT材料、无填料的PLA/PBAT材料、添加非抗菌性填料的 PLA/PBAT材料和添加偶联剂处理的纳米ZnO的PLA/PBAT材料进行抗菌性能 和力学性能测试,结果如表1、表2和表3所示。可见抗菌性无机填料的添加可 显著提高PLA/PBAT材料的抗菌性,尤其对于大肠杆菌和金黄色葡萄球菌的抑 菌率高达100%,同时,添加抗菌性无机填料后,PLA/PBAT材料的力学性能, 如拉伸强度、弯曲强度、抗冲击强度没有出现降低的现象。而直接采用偶联剂 处理的纳米ZnO填充会造成PLA/PBAT材料力学性能显著下降。 表1实验条件参数及其产品的抑菌率和力学性能
表2对照例2的条件参数及其产品的抑菌率和力学性能
表3对照例3的条件参数及其产品的抑菌率和力学性能
上述实施例为本发明较佳的实施方式,但本发明的实施方式并不受上述实 施例的限制,其它的任何未背离本发明的精神实质与原理下所作的改变、修饰、 替代、组合、简化,均应为等效的置换方式,都包含在本发明的保护范围之内。
Claims (10)
1.一种高抗菌性PLA/PBAT材料的制备方法,其特征在于,包括以下步骤:
(1)将无机填料置于容器中,抽真空,加入锌盐水溶液,搅拌,使无机填料达到吸附平衡,过滤,干燥,得到锌离子化填料;
(2)向锌离子化填料中添加稀碱溶液,直至锌离子化填料所在溶液的pH=8~10,震荡,过滤得到沉淀,洗涤,干燥,得到表面覆盖有Zn(OH)2的无机填料;
(3)将表面覆盖有Zn(OH)2的无机填料进行煅烧,得到负载ZnO的无机填料;
(4)将负载ZnO的无机填料与偶联剂混合均匀,干燥,得到抗菌性无机填料;
(5)将PLA、PBAT和抗菌性无机填料在室温下混合,熔融挤出或混炼造粒,得到所述的高抗菌性PLA/PBAT材料;
所述的PLA、PBAT和抗菌性无机填料的混合按质量份数配比为:聚乳酸50~100份、己二酸/对苯二甲酸-丁二酯共聚物0~50份和抗菌性无机填料1~20份。
2.根据权利要求1所述的高抗菌性PLA/PBAT材料的制备方法,其特征在于,步骤(5)中所述的聚乳酸、己二酸/对苯二甲酸-丁二酯共聚物和抗菌性无机填料的混合按质量份数配比为:聚乳酸85份、己二酸/对苯二甲酸-丁二酯共聚物15份和抗菌性无机填料1~20份。
3.根据权利要求1或2所述的高抗菌性PLA/PBAT材料的制备方法,其特征在于:
步骤(1)中所述的无机填料为硅藻土、麦饭石粉、纳米二氧化硅、高岭土或蒙脱土;
所述的锌盐水溶液为醋酸锌水溶液、氯化锌水溶液或硝酸锌水溶液;
所述的锌盐水溶液的浓度为0.01~0.5mol/L;
所述的加入锌盐水溶液的量按锌盐水溶液:无机填料=1:6~1:3的质量配比。
4.根据权利要求1或2所述的高抗菌性PLA/PBAT材料的制备方法,其特征在于:
步骤(1)中所述的抽真空的条件为在0.05~0.1MPa下抽真空0.5~3h;
所述的搅拌的方法为在50~200r/min下磁力搅拌3h;
所述的干燥的温度为160~200℃。
5.根据权利要求1或2所述的高抗菌性PLA/PBAT材料的制备方法,其特征在于:
步骤(2)中所述的稀碱溶液为氨水溶液、氢氧化钠溶液或氢氧化钾溶液;
所述的稀碱溶液的浓度为0.01~0.5mol/L;
所述的添加稀碱溶液的方法为逐步滴加。
6.根据权利要求1或2所述的高抗菌性PLA/PBAT材料的制备方法,其特征在于:步骤(3)中所述的煅烧的温度为80~200℃。
7.根据权利要求1或2所述的高抗菌性PLA/PBAT材料的制备方法,其特征在于:
步骤(4)中所述的偶联剂为钛酸酯偶联剂和硅烷偶联剂;
所述的偶联剂的用量为负载ZnO的无机填料的质量的1~3%。
8.根据权利要求1或2所述的高抗菌性PLA/PBAT材料的制备方法,其特征在于:步骤(5)中所述的熔融挤出或混炼造粒的温度为160~200℃。
9.一种高抗菌性PLA/PBAT材料,其特征在于:由权利要求1~8所述的制备方法得到。
10.权利要求9所述的高抗菌性PLA/PBAT材料的应用,其特征在于:将所述的高抗菌性PLA/PBAT材料用作包装薄膜、无纺布、管材或片材。