CN108751962A - A kind of white jade porcelain pot and preparation method thereof for rotation of soaring aloft - Google Patents
A kind of white jade porcelain pot and preparation method thereof for rotation of soaring aloft Download PDFInfo
- Publication number
- CN108751962A CN108751962A CN201810679086.3A CN201810679086A CN108751962A CN 108751962 A CN108751962 A CN 108751962A CN 201810679086 A CN201810679086 A CN 201810679086A CN 108751962 A CN108751962 A CN 108751962A
- Authority
- CN
- China
- Prior art keywords
- parts
- pot
- green body
- mud
- bottle body
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A kind of a kind of white jade porcelain pot and preparation method thereof for rotation of soaring aloft, white jade porcelain pot for rotation of soaring aloft, is made of the raw material of following parts by weight：20-25 parts of potassium feldspar, 25-30 parts of kaolin, it is 50-60 parts quartzy, 20-25 parts of granite, 10-15 parts of muscovite, 8-12 parts of diopside, 6-10 parts of the tremolite, 1-3 parts of solonchak, 12-16 parts of aluminium oxide, 6-8 parts of boron carbide, 5-8 parts of silicon nitride, 0.8-1.2 parts of zirconium oxide, 0.5-0.8 parts of lanthana, 0.2-0.5 parts of vanadic anhydride, 0.15-0.3 parts of beryllium oxide, 0.6-0.8 parts of sodium carboxymethylcellulose, 0.1-0.3 parts of titanium oxide, the present invention is with potassium feldspar, quartz and kaolin are basic raw material, granite is added, solonchak, muscovite, the tremolite, the auxiliary materials such as diopside, make white jade porcelain pot obtained can be in the case of not glazing, its surface can also reach smooth.
Description
Technical field
The invention belongs to domestic ceramics preparation fields, and in particular to it is a kind of soar aloft rotation white jade porcelain pot and its preparation
Method.
Background technology
Porcelain pot is the general designation for the container for storing liquid, and porcelain pot in the prior art generally comprises bottle body and pot lid, system
Bottle body and pot lid are all to have glazing, and the compactness between bottle body and pot lid is bad, when pouring or serving the tea, is easy to cause water when standby
Or gap outflow of the tea between bottle body and pot lid, keep the dynamics that spout was discharged or went out tea inadequate, and existing porcelain pot is general
The function of just only storing liquid, it is interesting low without other functions, it is further improved.
Invention content
The purpose of the present invention is overcoming the prior art, a kind of bottle body and pot lid good airproof performance are provided, can soar aloft to revolve
The white jade porcelain pot turned, another object make a kind of method preparing above-mentioned white jade porcelain pot of offer.
The present invention adopts the following technical scheme that：
A kind of white jade porcelain pot for rotation of soaring aloft, is made of the raw material of following parts by weight：20-25 parts of potassium feldspar, kaolinite
25-30 parts native, 50-60 parts of quartz, 20-25 parts of granite, 10-15 parts of muscovite, 8-12 parts of diopside, 6-10 parts of the tremolite,
1-3 parts of solonchak, 12-16 parts of aluminium oxide, 6-8 parts of boron carbide, 5-8 parts of silicon nitride, 0.8-1.2 parts of zirconium oxide, lanthana 0.5-0.8
Part, 0.2-0.5 parts of vanadic anhydride, 0.15-0.3 parts of beryllium oxide, 0.6-0.8 parts of sodium carboxymethylcellulose, titanium oxide 0.1-0.3
Part.
Further, including bottle body and pot lid, spout and pot handle, the opposite face of the bottle body and pot lid are provided in bottle body
It can mutually coincide, can agree under the action of water tight.
Further, the opposite face of the bottle body and pot lid is burnishing surface.
A kind of preparation method of the white jade porcelain pot of above-described rotation of soaring aloft, includes the following steps：
(1), by potassium feldspar, kaolin, quartz, granite, muscovite, diopside and tremolite weathering 5-7 days；
(2), by after weathering potassium feldspar, kaolin, quartz, granite, muscovite, diopside, the tremolite and its
Remaining raw material mixing is broken, and mud is made in sieving, wet ball mill；
(3), by mud aging 24-36h at a temperature of 30-45 DEG C made from step (2), then to the mud after aging
It beaten, squeezed repeatedly in sequence, can see that mud section is shinny after being streaked with knife；
(4), by step (3) treated mud injection plaster mold, bottle body green body and pot lid green body is made in injection forming；
(5), bottle body green body and pot lid green body are sent into kiln, biscuiting is carried out at a temperature of 700-750 DEG C；
(6), the bottle body green body after biscuiting and pot lid green body are cooled to room temperature, and are polished it, are then re-fed into kiln
In stove, reoxidizing in atmosphere and fire, firing temperature is 1320-1380 DEG C, sintering time 11-13h, heat preservation 1-2h, cooling room temperature,
White jade porcelain pot is made.
Further, in the step (4), the initial pressure of injection forming is 0.13-0.15MPa, and mud is allowed fully to fill out
After mold filling chamber, pressure is increased to 0.3-0.5MPa, a part of adherence of mud fluid made to reach required thickness on mud, then to
Charged pressure is the compressed air of 0.3-0.5MPa in die cavity, allows the extra mud of attachment to be discharged, continues to pressurize, make in mud
Moisture is filtered out, and bottle body green body and pot lid green body are made respectively, is finally applied respectively to bottle body green body and pot lid billet surface
Plus-pressure, pressure 0.2-0.3MPa make bottle body green body and pot lid green body be detached from die cavity respectively, you can take out bottle body green body and pot
Lid green body.
Further, in the step (2), in wet ball mill, by material：Ball：Water=1:1.5-1.8:The weight ratio of 0.8-1.2
It carries out, Ball-milling Time 32-36h.
By the above-mentioned description of this invention it is found that compared with prior art, the beneficial effects of the invention are as follows：The present invention is with potassium
Feldspar, quartz and kaolin are basic raw material, and the auxiliary materials such as granite, solonchak, muscovite, the tremolite, diopside are added, make
White jade porcelain pot obtained can be in the case of not glazing, and surface can also reach smooth, and color is white in fat, and can be such as suet
White jade is glittering and translucent like that, improves aesthetics；The opposite face of the white jade porcelain pot being prepared, bottle body and pot lid can mutually be kissed
It closes, in use, water can be enclosed in the pot mouth edge coated one of bottle body, because the bottle body of white jade porcelain pot and the opposite face of pot lid are light
Sliding, the tension of water will not be destroyed, so when covering pot lid, hydrone is filled with the gap between pot lid and bottle body, reduces
The distance between hydrone, and under atmospheric pressure, molecular attraction enhancing makes bottle body be mutually sucked with pot lid, agrees with
Tightly, the rotation high up in the air of white jade porcelain pot can be driven by hand-held pot lid, increases the practical value and art of white jade porcelain pot
Value, and the leakproofness enhancing between bottle body and pot lid, tea are not easy the outflow of the gap between bottle body and pot lid, enhance suet
The water outlet dynamics of beautiful porcelain pot.
Description of the drawings
Fig. 1 is the concrete structure schematic diagram of white jade porcelain pot；
Fig. 2 is the status diagram of white jade porcelain pot rotation high up in the air；
1- bottle bodies, 2- pot lids, 11- spouts, 12- pots handle, 13- openings, 14- stage portions, 21- pot buttons.
Specific implementation mode
Below by way of specific implementation mode, the invention will be further described.
Shown in Fig. 2, a kind of white jade porcelain pot for rotation of soaring aloft, including bottle body 1 and pot lid 2；
Bottle body 1 is provided with spout 11 and pot 12, and the top of bottle body 1 is provided with opening 13, is provided with and is used at opening 13
Place the stage portion 14 of pot lid 2；
Pot lid 2 is used for sealed opening 13, and top is provided with for hand-held pot button 21, specifically, bottle body 1 and pot lid 2
Opposite face can mutually coincide, under the action of water, bottle body 1 and pot lid 2 can agree with tightly, achieve the effect that it is high up in the air rotate, into
One step, the opposite face of bottle body 1 and pot lid 2 is burnishing surface；
Specifically, white jade porcelain pot, is made of the raw material of following parts by weight：20-25 parts of potassium feldspar, 25-30 parts of kaolin,
50-60 parts quartzy, 20-25 parts of granite, 10-15 parts of muscovite, 8-12 parts of diopside, 6-10 parts of the tremolite, 1-3 parts of solonchak,
12-16 parts of aluminium oxide, 6-8 parts of boron carbide, 5-8 parts of silicon nitride, 0.8-1.2 parts of zirconium oxide, 0.5-0.8 parts of lanthana, five oxidations
Two 0.2-0.5 parts of vanadium, 0.15-0.3 parts of beryllium oxide, 0.6-0.8 parts of sodium carboxymethylcellulose, 0.1-0.3 parts of titanium oxide；
Further, a kind of preparation method of the white jade porcelain pot for rotation of soaring aloft, includes the following steps：
(1), by potassium feldspar, kaolin, quartz, granite, muscovite, diopside and tremolite weathering 5-7 days；
(2), by after weathering potassium feldspar, kaolin, quartz, granite, muscovite, diopside, the tremolite and its
Remaining raw material mixing is broken, and mud is made in sieving, wet ball mill, wherein in wet ball mill, by material：Ball：Water=1:1.5-1.8:0.8-
1.2 weight ratio carries out, Ball-milling Time 32-36h；
(3), by mud aging 24-36h at a temperature of 30-45 DEG C made from step (2), then to the mud after aging
It beaten, squeezed repeatedly in sequence, can see that mud section is shinny after being streaked with knife；
(4), by step (3) treated mud injection plaster mold, bottle body green body and pot lid green body is made in injection forming,
Specifically, the initial pressure of injection forming is 0.13-0.15MPa, after allowing mud to be sufficient filling with die cavity, 0.3- pressure is increased to
0.5MPa makes a part of adherence of mud fluid reach required thickness on mud, and then into die cavity, charged pressure is 0.3-
The compressed air of 0.5MPa allows the extra mud of attachment to be discharged, continues to pressurize, the moisture in mud is made to be filtered out, respectively
Bottle body green body and pot lid green body is made, finally applies pressure, pressure 0.2- to bottle body green body and pot lid billet surface respectively
0.3MPa makes bottle body green body and pot lid green body be detached from die cavity respectively, you can takes out bottle body green body and pot lid green body；
(5), bottle body green body and pot lid green body are sent into kiln, biscuiting is carried out at a temperature of 700-750 DEG C；
(6), the bottle body green body after biscuiting and pot lid green body are cooled to room temperature, and are polished it, are then re-fed into kiln
In stove, reoxidizing in atmosphere and fire, firing temperature is 1320-1380 DEG C, sintering time 11-13h, heat preservation 1-2h, cooling room temperature,
White jade porcelain pot is made.
Embodiment 1
A kind of white jade porcelain pot for rotation of soaring aloft, is made of the raw material of following parts by weight：20 parts of potassium feldspar, kaolin 30
Part, 50 parts of quartz, 25 parts of granite, 10 parts of muscovite, 12 parts of diopside, 10 parts of the tremolite, 1 part of solonchak, 16 parts of aluminium oxide, carbon
Change 6 parts of boron, 5 parts of silicon nitride, 1.2 parts of zirconium oxide, 0.8 part of lanthana, 0.2 part of vanadic anhydride, 0.3 part of beryllium oxide, carboxymethyl
0.6 part of sodium cellulosate, 0.3 part of titanium oxide；
Preparation method includes the following steps：
(1), by potassium feldspar, kaolin, quartz, granite, muscovite, diopside and tremolite weathering 7 days；
(2), by after weathering potassium feldspar, kaolin, quartz, granite, muscovite, diopside, the tremolite and its
Remaining raw material mixing is broken, and mud is made in sieving, wet ball mill, wherein in wet ball mill, by material：Ball：Water=1:1.5:1.2 weight
Than carrying out, Ball-milling Time 36h；
(3), by mud made from step (2) at a temperature of 45 DEG C it is aging for 24 hours, then to the mud after aging by certain
Sequence beaten, squeezed repeatedly, can see that mud section is shinny after being streaked with knife；
(4), by step (3) treated mud injection plaster mold, bottle body green body and pot lid green body is made in injection forming,
Specifically, the initial pressure of injection forming is 0.15MPa, after allowing mud to be sufficient filling with die cavity, 0.3MPa is pressure is increased to, is made
A part of adherence of mud fluid reaches required thickness on mud, the compressed air that then charged pressure is 0.5MPa into die cavity,
It allows the extra mud of attachment to be discharged, continues to pressurize, the moisture in mud is made to be filtered out, bottle body green body and pot lid are made respectively
Green body, finally applies pressure to bottle body green body and pot lid billet surface respectively, and pressure 0.2MPa makes bottle body green body and pot lid base
Body is detached from die cavity respectively, you can takes out bottle body green body and pot lid green body；
(5), bottle body green body and pot lid green body are sent into kiln, biscuiting is carried out at a temperature of 700 DEG C；
(6), the bottle body green body after biscuiting and pot lid green body are cooled to room temperature, and are polished it, are then re-fed into kiln
It in stove, reoxidizes in atmosphere and fires, firing temperature is 1320 DEG C, sintering time 13h, keeps the temperature 1h, and white jade is made in cooling room temperature
Porcelain pot.
Embodiment 2
A kind of white jade porcelain pot for rotation of soaring aloft, is made of the raw material of following parts by weight：25 parts of potassium feldspar, kaolin 25
Part, 60 parts of quartz, 20 parts of granite, 15 parts of muscovite, 8 parts of diopside, 6 parts of the tremolite, 3 parts of solonchak, 12 parts of aluminium oxide, carbonization
8 parts of boron, 8 parts of silicon nitride, 0.8 part of zirconium oxide, 0.5 part of lanthana, 0.5 part of vanadic anhydride, 0.15 part of beryllium oxide, carboxymethyl are fine
Plain 0.8 part of the sodium of dimension, 0.1 part of titanium oxide；
Preparation method includes the following steps：
(1), by potassium feldspar, kaolin, quartz, granite, muscovite, diopside and tremolite weathering 5 days；
(2), by after weathering potassium feldspar, kaolin, quartz, granite, muscovite, diopside, the tremolite and its
Remaining raw material mixing is broken, and mud is made in sieving, wet ball mill, wherein in wet ball mill, by material：Ball：Water=1:1.8:0.8 weight
Than carrying out, Ball-milling Time 32h；
(3), by mud made from step (2) at a temperature of 30 DEG C aging 36h, then to the mud after aging by certain
Sequence beaten, squeezed repeatedly, can see that mud section is shinny after being streaked with knife；
(4), by step (3) treated mud injection plaster mold, bottle body green body and pot lid green body is made in injection forming,
Specifically, the initial pressure of injection forming is 0.13MPa, after allowing mud to be sufficient filling with die cavity, 0.5MPa is pressure is increased to, is made
A part of adherence of mud fluid reaches required thickness on mud, the compressed air that then charged pressure is 0.3MPa into die cavity,
It allows the extra mud of attachment to be discharged, continues to pressurize, the moisture in mud is made to be filtered out, bottle body green body and pot lid are made respectively
Green body, finally applies pressure to bottle body green body and pot lid billet surface respectively, and pressure 0.3MPa makes bottle body green body and pot lid base
Body is detached from die cavity respectively, you can takes out bottle body green body and pot lid green body；
(5), bottle body green body and pot lid green body are sent into kiln, biscuiting is carried out at a temperature of 750 DEG C；
(6), the bottle body green body after biscuiting and pot lid green body are cooled to room temperature, and are polished it, are then re-fed into kiln
It in stove, reoxidizes in atmosphere and fires, firing temperature is 1380 DEG C, sintering time 11h, keeps the temperature 2h, and white jade is made in cooling room temperature
Porcelain pot.
Embodiment 3
A kind of white jade porcelain pot for rotation of soaring aloft, is made of the raw material of following parts by weight：23 parts of potassium feldspar, kaolin 27
Part, 55 parts of quartz, 22 parts of granite, 12 parts of muscovite, 10 parts of diopside, 8 parts of the tremolite, 2 parts of solonchak, 14 parts of aluminium oxide, carbon
It is fine to change 7 parts of boron, 7 parts of silicon nitride, 1 part of zirconium oxide, 0.6 part of lanthana, 0.3 part of vanadic anhydride, 0.24 part of beryllium oxide, carboxymethyl
Plain 0.7 part of the sodium of dimension, 0.2 part of titanium oxide；
Preparation method includes the following steps：
(1), by potassium feldspar, kaolin, quartz, granite, muscovite, diopside and tremolite weathering 6 days；
(2), by after weathering potassium feldspar, kaolin, quartz, granite, muscovite, diopside, the tremolite and its
Remaining raw material mixing is broken, and mud is made in sieving, wet ball mill, wherein in wet ball mill, by material：Ball：Water=1:1.6:1 weight ratio
It carries out, Ball-milling Time 34h；
(3), by mud made from step (2) at a temperature of 40 DEG C aging 30h, then to the mud after aging by certain
Sequence beaten, squeezed repeatedly, can see that mud section is shinny after being streaked with knife；
(4), by step (3) treated mud injection plaster mold, bottle body green body and pot lid green body is made in injection forming,
Specifically, the initial pressure of injection forming is 0.14MPa, after allowing mud to be sufficient filling with die cavity, 0.4MPa is pressure is increased to, is made
A part of adherence of mud fluid reaches required thickness on mud, the compressed air that then charged pressure is 0.4MPa into die cavity,
It allows the extra mud of attachment to be discharged, continues to pressurize, the moisture in mud is made to be filtered out, bottle body green body and pot lid are made respectively
Green body, finally applies pressure to bottle body green body and pot lid billet surface respectively, and pressure 0.25MPa makes bottle body green body and pot lid
Green body is detached from die cavity respectively, you can takes out bottle body green body and pot lid green body；
(5), bottle body green body and pot lid green body are sent into kiln, biscuiting is carried out at a temperature of 720 DEG C；
(6), the bottle body green body after biscuiting and pot lid green body are cooled to room temperature, and are polished it, are then re-fed into kiln
It in stove, reoxidizes in atmosphere and fires, firing temperature is 1350 DEG C, sintering time 12h, keeps the temperature 1.5h, and suet is made in cooling room temperature
Beautiful porcelain pot.
In use, the one circle water of coating in stage portion, covers pot lid, it, will not because pot lid and the opposite face of bottle body are smooth
Destroy the surface tension of hydrone so that hydrone is filled with the gap between pot lid and bottle body, reduce between hydrone away from
From, and under atmospheric pressure, molecular attraction enhancing makes bottle body be mutually sucked with pot lid, agrees with tightly, passes through and hold pot
Button rotates, you can drives bottle body rotation high up in the air, when rotation finishes, is used to open pot lid, you can add water into pot, make tea；
The present invention is basic raw material with potassium feldspar, quartz and kaolin, be added granite, solonchak, muscovite, the tremolite,
The auxiliary materials such as diopside make white jade porcelain pot obtained can be in the case of not glazing, and surface can also reach smooth, color
In fat white, and can be glittering and translucent as fine white tallow jade, improve aesthetics；The white jade porcelain pot being prepared, bottle body and
The opposite face of pot lid can mutually coincide, in use, water can be enclosed in the pot mouth edge coated one of bottle body, because of the pot of white jade porcelain pot
The opposite face of body and pot lid is smooth, will not destroy the tension of water, so when covering pot lid, hydrone be filled with pot lid with
Gap between bottle body reduces the distance between hydrone, and under atmospheric pressure, and molecular attraction enhancing makes bottle body
It is mutually sucked, agrees with tightly with pot lid, the rotation high up in the air of white jade porcelain pot can be driven by hand-held pot lid, increase white jade porcelain
The practical value and artistic value of pot, and the leakproofness enhancing between bottle body and pot lid, tea are not easy between bottle body and pot lid
Gap outflow, enhance white jade porcelain pot water outlet dynamics.
The foregoing is only a preferred embodiment of the present invention, therefore cannot be limited the scope of implementation of the present invention with this, i.e.,
According to equivalent changes and modifications made by scope of the present invention patent and description, it all should still belong to what patent of the present invention covered
In range.
Claims (6)
1. a kind of white jade porcelain pot for rotation of soaring aloft, it is characterised in that：It is made of the raw material of following parts by weight：Potassium feldspar 20-
25 parts, 25-30 parts of kaolin, 50-60 parts of quartz, 20-25 parts of granite, 10-15 parts of muscovite, 8-12 parts of diopside, thoroughly dodge
6-10 parts of stone, 1-3 parts of solonchak, 12-16 parts of aluminium oxide, 6-8 parts of boron carbide, 5-8 parts of silicon nitride, 0.8-1.2 parts of zirconium oxide, oxidation
0.5-0.8 parts of lanthanum, 0.2-0.5 parts of vanadic anhydride, 0.15-0.3 parts of beryllium oxide, 0.6-0.8 parts of sodium carboxymethylcellulose, oxidation
0.1-0.3 parts of titanium.
2. a kind of white jade porcelain pot of rotation high up in the air according to claim 1, it is characterised in that：Including bottle body and pot lid,
It is provided with spout and pot handle in bottle body, the opposite face of the bottle body and pot lid can mutually coincide, and can agree under the action of water tight
It is close.
3. a kind of white jade porcelain pot of rotation high up in the air according to claim 2, it is characterised in that：The bottle body and pot lid
Opposite face is burnishing surface.
4. a kind of preparation method of the white jade porcelain pot of rotation of soaring aloft according to claim 1, it is characterised in that：Including
Following steps：
(1), by potassium feldspar, kaolin, quartz, granite, muscovite, diopside and tremolite weathering 5-7 days；
(2), by potassium feldspar, kaolin, quartz, granite, muscovite, diopside, the tremolite and remaining original after weathering
Material mixing is broken, and mud is made in sieving, wet ball mill；
(3), by mud aging 24-36h at a temperature of 30-45 DEG C made from step (2), one then is pressed to the mud after aging
Fixed sequence is beaten, is squeezed repeatedly, can see that mud section is shinny after being streaked with knife；
(4), by step (3) treated mud injection plaster mold, bottle body green body and pot lid green body is made in injection forming；
(5), bottle body green body and pot lid green body are sent into kiln, biscuiting is carried out at a temperature of 700-750 DEG C；
(6), the bottle body green body after biscuiting and pot lid green body are cooled to room temperature, and are polished it, are then re-fed into kiln,
It reoxidizes in atmosphere and fires, firing temperature is 1320-1380 DEG C, sintering time 11-13h, keeps the temperature 1-2h, and cooling room temperature is made
White jade porcelain pot.
5. a kind of preparation method of the white jade porcelain pot of rotation of soaring aloft according to claim 4, it is characterised in that：It is described
In step (4), the initial pressure of injection forming is 0.13-0.15MPa, after allowing mud to be sufficient filling with die cavity, be pressure is increased to
0.3-0.5MPa makes a part of adherence of mud fluid reach required thickness on mud, and then into die cavity, charged pressure is 0.3-
The compressed air of 0.5MPa allows the extra mud of attachment to be discharged, continues to pressurize, the moisture in mud is made to be filtered out, respectively
Bottle body green body and pot lid green body is made, finally applies pressure, pressure 0.2- to bottle body green body and pot lid billet surface respectively
0.3MPa makes bottle body green body and pot lid green body be detached from die cavity respectively, you can takes out bottle body green body and pot lid green body.
6. a kind of preparation method of the white jade porcelain pot of rotation of soaring aloft according to claim 4, it is characterised in that：It is described
In step (2), in wet ball mill, by material：Ball：Water=1:1.5-1.8:The weight ratio of 0.8-1.2 carries out, Ball-milling Time 32-
36h。