CN108411307A - A kind of environmental protection quick-dry type water-based antirust agent and preparation method thereof - Google Patents
A kind of environmental protection quick-dry type water-based antirust agent and preparation method thereof Download PDFInfo
- Publication number
- CN108411307A CN108411307A CN201810411025.9A CN201810411025A CN108411307A CN 108411307 A CN108411307 A CN 108411307A CN 201810411025 A CN201810411025 A CN 201810411025A CN 108411307 A CN108411307 A CN 108411307A
- Authority
- CN
- China
- Prior art keywords
- parts
- content
- agent
- water
- thickener
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of environmentally friendly quick-dry type water-based antirust agents and preparation method thereof, including main corrosion inhibiter, auxiliary corrosion inhibiter, film forming agent, thickener, bleeding agent, antifoaming agent, wherein, in terms of mass fraction, the film former content is 3~10 parts, the infiltration agent content is 10~30 parts, the amount of thickener is 2~5 parts, the auxiliary inhibition agent content is 30~45 parts, the main inhibition agent content is 30~50 parts, the antifoam content is 1~3 part.After the water-based antirust agent of the present invention is distributed in metal surface, quickly, about 20min can dry under room temperature, far faster than the drying time (about 3~8h) of water-based antirust agent in the market for volatilization；It is in colorless and transparent film shape after drying, therefore suitable for the metal of a variety of colors；It is very fast due to volatilizing, therefore be evenly distributed in metal surface, no sag phenomenon, be not easy in metal storage or transportational process because also it is unseasoned it is complete just scratched etc. caused by active ingredient situation unevenly distributed.
Description
Technical field
The invention belongs to water-based antirust agent technical fields, and in particular to a kind of environmental protection quick-dry type water-based antirust agent and its preparation
Method.
Background technology
Anti-corrosion of metal is to take various means, protects the metal for being easy corrosion, extends its storage or use to reach
The purpose in service life.Metal erosion is huge to the direct losses that human society is brought, and many industrially developed country have carried out phase
Statistics is closed, as a result shows that the loss of metal erosion accounts for 1% to the 5% of national GNP；China was shown in data in 2014, was corroded
Caused by annual loss fail to keep an appointment as 2,000,000,000,000 RMB, account for the 3% of current year GDP.Therefore metal erosion should attract great attention.
The measure of common anti-corrosion of metal currently on the market is antirust agent, antirust agent be then divided into antirust oil, antirust emulsion and
Water-based antirust agent etc..After application antirust oil or antirust emulsion, the surface of metal tools and instrument etc. can cover thickness thickness
Oil film, can not use immediately, need leading oil removing that could continue to operate, increase treatment process；And water-based antirust agent is then several
Metallic surface appearance and sense of touch are not influenced, in addition the raising of people's environmental consciousness and the considerations of economic interests, so being more prone to
And processing convenient water-based antirust agent friendly in use environment.Common environmentally-friewater-borne water-borne antirusting agent has multiple using ethanol amine and acid
Match or is prepared by the substances such as polyol ester, has certain rust-proof effect, but mostly short-term rust prevention (about 20 days) or cost are higher；
During use, there is also volatile dry is not easy, it is unfavorable for subsequent processing and film forming is uniform.
Therefore, how to prepare one kind having medium-term and long-term antirust effect and lower-cost quick-dry type water-based antirust agent, and matches
Making simple for process, environmentally protective antirust agent, to be this field have technical problem to be solved.
Invention content
The purpose of this part is to summarize some aspects of the embodiment of the present invention and briefly introduce some preferably to implement
Example.It may do a little simplified or be omitted to avoid our department is made in this section and the description of the application and the title of the invention
Point, the purpose of abstract of description and denomination of invention it is fuzzy, and this simplification or omit and cannot be used for limiting the scope of the invention.
In view of above-mentioned technological deficiency, it is proposed that the present invention.
Therefore, as one aspect of the present invention, the present invention overcomes the deficiencies in the prior art, provides a kind of water
Property antirust agent.
In order to solve the above technical problems, the present invention provides following technical solutions：A kind of water-based antirust agent comprising, it is main
Corrosion inhibiter, auxiliary corrosion inhibiter, film forming agent, thickener, bleeding agent, antifoaming agent, wherein in terms of mass fraction, the film former content
For 3~10 parts, the infiltration agent content be 10~30 parts, the amount of thickener is 2~5 parts, the auxiliary inhibition agent content is
30~45 parts, the main inhibition agent content be 30~50 parts, the antifoam content is 1~3 part.
A kind of preferred embodiment as water-based antirust agent of the present invention：Further include solvent, the solvent includes water, second
Alcohol, acetone, ether, wherein ethanol content is 130~210 parts, content of acetone is 15~25 parts, ether content is 5~15 parts,
Water content is 600~700 parts.
A kind of preferred embodiment as water-based antirust agent of the present invention：The main corrosion inhibiter include petroleum sodium sulfonate,
Triethanolamine borate, the auxiliary corrosion inhibiter include di-o-tolyl-thiourea, sodium benzoate, EDTA-2Na, sodium citrate, phytic acid,
Triethanolamine, the film forming agent include polyvinyl alcohol, rosin, aqueous lanolin, aqueous polyurethane, and the thickener includes bright
Glue, guar gum, the bleeding agent include oleic acid, enuatrol, alkali-resistant penetrant AEP98, fast penetrant T, the antifoaming agent packet
Include Byfuel L85.
A kind of preferred embodiment as water-based antirust agent of the present invention：In terms of mass fraction, the petroleum sodium sulfonate
Content is 20~30 parts, the triethanolamine borate content is 20~30 parts, the di-o-tolyl-thiourea content is 4~5 parts,
The sodium benzoate content is 4~6 parts, the EDTA-2Na contents are 4~6 parts, the content of sodium citrate is 8~10 parts,
The phytic acid content is 4~5 parts, the triethanolamine content is 14~15 parts, the polyvinyl alcohol content is 2~3 parts, described
Rosin content is 2~3 parts, the aqueous lanolin content is 1.5~2 parts, the aqueous polyurethane content is 1~3 part, described
Gelatine content is 2~4 parts, the guar gum content is 1~3 part, the oleic acid content is 6~8 parts, the oleic acid sodium content is
7~10 parts, the alkali-resistant penetrant AEP98 contents be 6~8 parts, the fast penetrant T content is 4~6 parts, described
Byfuel L85 contents are 1~3, the ethanol content is 130~210 parts, content of acetone is 15~25 parts, ether content is 5
~15 parts, water content be 600~700 parts.
As another aspect of the present invention, the present invention overcomes the deficiencies in the prior art, provide claim 1~
The preparation method of 4 any water-based antirust agents.
In order to solve the above technical problems, the present invention provides following technical solutions：Any water of Claims 1 to 4
The preparation method of property antirust agent comprising,
Prepare film forming agent：In terms of mass fraction, 3~10 parts of film forming agent is mixed with 90~97 parts of water, prepares film forming agent
Aqueous solution；
Prepare thickener：In terms of mass fraction, 2~5 parts of thickener is mixed with 95~98 parts of water, prepares thickener water
Solution；
The first step is reacted：After 10~30 parts of bleeding agents are mixed with 170~190 parts of water, 30~45 parts of auxiliary corrosion inhibiter are added,
Add the film forming agent aqueous solution；
Second step reacts：After first step reaction, 30~50 parts of main corrosion inhibiter are added, the aqueous thickener solution is added later
And 130~210 parts of ethyl alcohol of solvent, 15~25 parts of acetone, 5~15 parts of ether, 180~270 parts of water mixing.
A kind of preferred embodiment of preparation method as water-based antirust agent of the present invention：In terms of mass fraction, it is described at
The component of film includes 3 parts of polyvinyl alcohol, 3 parts of rosin, 2 parts of aqueous lanolin, 2 parts of aqueous polyurethanes, the group of the thickener
It includes 3 parts of gelatin, 2 parts of guar gums to divide.
A kind of preferred embodiment of preparation method as water-based antirust agent of the present invention：The first step reaction, with matter
Number meter is measured, the bleeding agent includes 8 parts of oleic acid, 10 parts of enuatrols, 7 parts of alkali-resistant penetrant AEP98,5 parts of fast penetrant Ts,
The auxiliary corrosion inhibiter includes 5 parts of di-o-tolyl-thioureas, 5 sodium benzoates, 5 parts of EDTA-2Na, 10 parts of sodium citrates, 5 parts of phytic acid, 15
Part triethanolamine.
A kind of preferred embodiment of preparation method as water-based antirust agent of the present invention：The second step reaction, with matter
Number meter is measured, the main corrosion inhibiter includes 30 parts of petroleum sodium sulfonates, 20 parts of triethanolamine borates, and the solvent includes 210 parts
Ethyl alcohol, 25 parts of acetone, 15 parts of ether and 180 parts of deionized waters.
A kind of preferred embodiment of preparation method as water-based antirust agent of the present invention：Further include,
Homogeneous：After carrying out the second step reaction, carries out homogeneous and antifoaming agent is added.
A kind of preferred embodiment of preparation method as water-based antirust agent of the present invention：Including carrying out the second step
Homogeneous 12min, 72 parts of deionized waters of addition continue homogeneous 2min at 7200rpm after reaction, and 3 parts of Byfuel L85 are added and disappear
Infusion, homogeneous 1min.
Beneficial effects of the present invention：After the water-based antirust agent of the present invention is distributed in metal surface, volatilize quickly, under room temperature about
20min can dry, far faster than the drying time (about 3~8h) of water-based antirust agent in the market；It is in colorless and transparent film after drying
Shape, therefore suitable for the metal of a variety of colors；It is very fast due to volatilizing, therefore be evenly distributed in metal surface, no sag phenomenon is not easy
Metal store or transportational process in because also it is unseasoned it is complete just scratched etc. caused by active ingredient situation unevenly distributed.
Suitable bleeding agent, film forming agent and thickener are added in the present invention, due to the effect of specific bleeding agent, the present invention
The good dispersion of water-based antirust agent, stability are long, mobility is good, therefore can preferably penetrate into the deep layer pore defect of metal surface
In, and drive the source of corrosion such as the air in micropore and microgroove, moisture away.Other products are compared, which is significantly improved from principle
Its rust-proof effect.On this basis, film forming agent is that water-based antirust agent has been still further provided in adhesive force with thickener, and film can
It is completely covered in each corner of metal surface, completely fine and close package is carried out, active ingredient can be made to maintain metal watch
The face longer time, to substantially extend antirust time.
The water-based antirust agent antirust time of the present invention is long, it is recommended that using the resistance to neutrality of minimum concentration i.e. 5% dilution
Salt fog was up to 36 hours, can antirust 18 months or more in practical application far above the antirust time of water-based antirust agent in the market.
The water-based antirust agent of the present invention contains main corrosion inhibiter and auxiliary corrosion inhibiter, if individually with main corrosion inhibiter, resistance to neutral salt spray
Time is only 9~12 hours；If individually with auxiliary corrosion inhibiter, the resistance to neutral salt spray time is only 5~8 hours；But two class corrosion inhibiter are matched
It closes and uses, not simple adduction of resistance to neutral salt spray time, but be unexpectedly obviously improved 60 hours, this is embodied
Has fabulous compatibility synergistic effect between major-minor corrosion inhibiter.
The water-based antirust agent of the present invention is pH controllable types.Its pH value can be by the organic acids such as citric acid and sodium bicarbonate etc. no
The buffer of this kind of safe green of strong base-weak acid salt of chloride ion-containing regulates and controls, and meets different rust-proof effects：This product exists
Between 8.6~8.8, the resistance to neutral salt spray time reaches 60 hours pH value when undiluted；If adjusting pH value between 8.1~8.6,
The resistance to neutral salt spray time is then at 48~60 hours；If adjusting pH value between 7.5~8.1, the resistance to neutral salt spray time 36~
48 hours；If adjusting pH value between 7.0~7.5, the resistance to neutral salt spray time was at 26~36 hours；If adjusting pH value 6.5
Between~7.0, the resistance to neutral salt spray time is then at 16~26 hours.To sum up, the present invention can be expired by the height of control ph
The different antirust requirement of foot, being diluted with water for the prior art excessive can cause (more than 20 times) that film is too thin and rust-proof effect is unstable
Fixed situation, the present invention can be solved directly by adjusting pH value, meet the customization demand of user.
The water-based antirust agent of the present invention is different from other manner of formulation in preparation process and is to need to quantify several times
Solvent is added, proves that the method for the present invention can make water-based antirust agent disperse more stable, appearance and be more fully apparent from through a large number of experiments, it is long-term to protect
Deposit no Precipitation.Raw materials used green safe, nontoxic, preparation process is easy to operate, and SOLUTION PROPERTIES is stablized.
Specific implementation mode
In order to make the foregoing objectives, features and advantages of the present invention clearer and more comprehensible, with reference to specific embodiment pair
The specific implementation mode of the present invention is described in detail.
Many details are elaborated in the following description to facilitate a thorough understanding of the present invention, still the present invention can be with
Implemented different from other manner described here using other, those skilled in the art can be without prejudice to intension of the present invention
In the case of do similar popularization, therefore the present invention is not limited by following public specific embodiment.
Secondly, " one embodiment " or " embodiment " referred to herein refers to that may be included at least one realization side of the present invention
A particular feature, structure, or characteristic in formula." in one embodiment " that different places occur in the present specification not refers both to
The same embodiment, nor the individual or selective embodiment mutually exclusive with other embodiment.
Embodiment 1：
1, first add 3 parts of polyvinyl alcohol, 3 parts of rosin, 2 parts of aqueous lanolin, 2 parts of aqueous polyurethanes, then add 90 parts thereto
Deionized water is formulated as film forming agent dilute aqueous solution；Separately add 3 parts of gelatin, 2 parts of guar gums, then add 95 parts of deionized waters thereto, matches
It is made as thickener dilute aqueous solution, preservative film sealing is for use；
2, add 8 parts of oleic acid, 10 parts of enuatrols, 7 parts of alkali-resistant penetrant AEP98,5 parts of fast penetrant Ts in a kettle, then
The deionized water for adding 170 parts is stirred continuously until it is substantially dissolved；
3, continuously add 5 parts of di-o-tolyl-thioureas, 5 sodium benzoates, 5 parts of EDTA-2Na, 10 parts of sodium citrates, 5 parts of phytic acid,
15 parts of triethanolamines add step 1 gained film forming agent dilute aqueous solution, and are stirred continuously until it is substantially dissolved；
4,30 parts of petroleum sodium sulfonates, 20 parts of triethanolamine borates are continuously added, it is dilute water-soluble that step 1 gained thickener is added
Liquid adds 210 parts of ethyl alcohol, 25 parts of acetone, 15 parts of ether and 180 parts of deionized waters, is stirred continuously until it is almost dissolved；
5, after homogeneous 12min, 72 parts of deionized waters are added at 7200rpm in solution；Continue homogeneous 2min, is added 3 parts
Byfuel L85 antifoaming agent；Waterborne anti-rust agent solution can be obtained after last homogeneous 1min.It tests (experimental result is shown in Table 1)：
Water-based antirust agent stoste processing through sand paper polished light without iron mold blade 5min, test resistance to neutral salt spray when
Between be 60h, spontaneously dry time 10min, pH=8.8；
According to 1:5 dilution, test the resistance to neutral salt spray time be 48h, spontaneously dry time 15min, pH=8.1；
According to 1:20 dilution, test the neutral salt spray time be 36h, spontaneously dry time 20min, pH=7.5.
Embodiment 2：
1, first add 2 parts of polyvinyl alcohol, 2.5 parts of rosin, 1.5 parts of aqueous lanolin, 2 parts of aqueous polyurethanes, then add thereto
92 parts of deionized waters prepare film forming agent dilute aqueous solution；Separately add 2 parts of gelatin, 2 parts of guar gums, then add 96 parts of deionized waters thereto,
It is configured to thickener dilute aqueous solution, preservative film sealing is for use；
2, add 6 parts of oleic acid, 7.5 parts of enuatrols, 7 parts of alkali-resistant penetrant AEP98,5 parts of fast penetrant Ts in a kettle,
Again plus 174.5 parts of deionized water, it is stirred continuously until it is substantially dissolved；
3, continuously add 4 parts of di-o-tolyl-thioureas, 5 sodium benzoates, 5 parts of EDTA-2Na, 8 parts of sodium citrates, 4 parts of phytic acid,
14 parts of triethanolamines add 1 gained film forming agent dilute aqueous solution, and are stirred continuously until it is substantially dissolved；
4,30 parts of petroleum sodium sulfonates, 20 parts of triethanolamine borates are continuously added, 1 gained thickener dilute aqueous solution is added,
210 parts of ethyl alcohol, 20 parts of acetone, 10 parts of ether and 180 parts of deionized waters are added, are stirred continuously until it is almost dissolved；
5, after homogeneous 12min, 87 parts of deionized waters are added at 7200rpm in solution；Continue homogeneous 2min, is added 3 parts
Byfuel L85 antifoaming agent；Waterborne anti-rust agent solution can be obtained after last homogeneous 1min.It tests (experimental result is shown in Table 1)：
Water-based antirust agent stoste processing through sand paper polished light without iron mold blade 5min, test resistance to neutral salt spray when
Between be 56h, spontaneously dry time 15min, pH=8.6；
According to 1:5 dilution, test the resistance to neutral salt spray time be 44h, spontaneously dry time 22min, pH=7.9；
According to 1:20 dilution, test the neutral salt spray time be 32h, spontaneously dry time 30min, pH=7.3.
Reference examples 1：
1,2 parts of polyvinyl alcohol, 2.5 parts of rosin, 1.5 parts of aqueous lanolin, 2 parts of aqueous poly- ammonia are first added in a kettle
Ester, 2 parts of gelatin, 2 parts of guar gums, 6 parts of oleic acid, 7.5 parts of enuatrols, 7 parts of alkali-resistant penetrant AEP98,5 parts of fast penetrant Ts, 4
Part di-o-tolyl-thiourea, 5 sodium benzoates, 5 parts of EDTA-2Na, 8 parts of sodium citrates, 4 parts of phytic acid, 14 parts of triethanolamines, 30 parts of stones
Oily sodium sulfonate, 20 parts of triethanolamine borates add 210 parts of ethyl alcohol, 20 parts of acetone, 10 parts of ether and 629.5 parts of deionizations
Water is stirred continuously until it is almost dissolved；
2, after homogeneous 15min, 3 parts of Byfuel L85 antifoaming agent are added at 8000rpm in solution；After last homogeneous 2min
Waterborne anti-rust agent solution can be obtained.
(raw materials used and its dosage is same as Example 2, but preparation method is different, i.e., solvent is disposable addition completely)
It tests (experimental result is shown in Table 1)：
Water-based antirust agent stoste processing through sand paper polished light without iron mold blade 5min, test resistance to neutral salt spray when
Between be 40h, spontaneously dry time 18min, pH=8.6；
According to 1:5 dilution, test the resistance to neutral salt spray time be 28h, spontaneously dry time 25min, pH=7.9；
According to 1:20 dilution, test the neutral salt spray time be 16h, spontaneously dry time 45min, pH=7.3.
Reference examples 2：
1, first add 2 parts of polyvinyl alcohol, 2.5 parts of rosin, 1.5 parts of aqueous lanolin, 2 parts of aqueous polyurethanes, then add thereto
192 parts of deionized waters, prepare film forming agent dilute aqueous solution, and preservative film sealing is for use；
2, add 6 parts of oleic acid, 7.5 parts of enuatrols, 7 parts of alkali-resistant penetrant AEP98,5 parts of fast penetrant Ts in a kettle,
Again plus 174.5 parts of deionized water, it is stirred continuously until it is substantially dissolved；
3, continuously add 4 parts of di-o-tolyl-thioureas, 5 sodium benzoates, 5 parts of EDTA-2Na, 8 parts of sodium citrates, 4 parts of phytic acid,
14 parts of triethanolamines add 1 gained film forming agent dilute aqueous solution, and are stirred continuously until it is substantially dissolved；
4,30 parts of petroleum sodium sulfonates, 20 parts of triethanolamine borates are continuously added, 1 gained thickener dilute aqueous solution is added,
210 parts of ethyl alcohol, 20 parts of acetone, 10 parts of ether and 180 parts of deionized waters are added, are stirred continuously until it is almost dissolved；
5, after homogeneous 12min, 87 parts of deionized waters are added at 7200rpm in solution；Continue homogeneous 2min, is added 3 parts
Byfuel L85 antifoaming agent；Waterborne anti-rust agent solution can be obtained after last homogeneous 1min.It tests (experimental result is shown in Table 1)：
Water-based antirust agent stoste processing through sand paper polished light without iron mold blade 5min, test resistance to neutral salt spray when
Between be 36h, spontaneously dry time 15min, pH=8.6；
According to 1:5 dilution, test the resistance to neutral salt spray time be for 24 hours, spontaneously dry time 30min, pH=7.9；
According to 1:20 dilution, test the neutral salt spray time be 12h, spontaneously dry time 1h, pH=7.3.
The preparation method of reference examples 3~10 is identical as embodiment 1,2, specific experiment result data such as 1~table of table 3：
1 Examples 1 to 2 of table and 1~2 antirust agent of reference examples are with when test result
2 reference examples of table, 3~6 antirust agent is with when test result
3 reference examples of table, 7~14 antirust agent is with when test result
Salt spray test standard：Standard GB/T 6458-86 neutral salt spray tests are neutral：5% sodium chloride solution spontaneously dries
Condition：Light is immersed in water-based antirust agent without iron mold blade after 5min and is taken out, 25 DEG C ± 2 DEG C of temperature, humidity 40%~
50%.
To sum up, after water-based antirust agent of the invention is distributed in metal surface, quickly, about 20min can dry in the air under room temperature for volatilization
It is dry, far faster than the drying time (about 3~8h) of water-based antirust agent in the market；It is in colorless and transparent film shape after drying, therefore is suitable for
The metal of a variety of colors；It is very fast due to volatilizing, therefore be evenly distributed in metal surface, no sag phenomenon, be not easy in metal storage or
In transportational process because also it is unseasoned just scratched etc. completely caused by active ingredient situation unevenly distributed.
Suitable bleeding agent, film forming agent and thickener are added in the present invention, due to the effect of specific bleeding agent, the present invention
The good dispersion of water-based antirust agent, stability are long, mobility is good, therefore can preferably penetrate into the deep layer pore defect of metal surface
In, and drive the source of corrosion such as the air in micropore and microgroove, moisture away.Other products are compared, which is significantly improved from principle
Its rust-proof effect.On this basis, film forming agent is that water-based antirust agent has been still further provided in adhesive force with thickener, and film can
It is completely covered in each corner of metal surface, completely fine and close package is carried out, active ingredient can be made to maintain metal watch
The face longer time, to substantially extend antirust time.
The water-based antirust agent antirust time of the present invention is long, it is recommended that using the resistance to neutrality of minimum concentration i.e. 5% dilution
Salt fog was up to 36 hours, can antirust 18 months or more in practical application far above the antirust time of water-based antirust agent in the market.
The water-based antirust agent of the present invention contains main corrosion inhibiter and auxiliary corrosion inhibiter, if individually with main corrosion inhibiter, resistance to neutral salt spray
Time is only 9~12 hours；If individually with auxiliary corrosion inhibiter, the resistance to neutral salt spray time is only 5~8 hours；But two class corrosion inhibiter are matched
It closes and uses, not simple adduction of resistance to neutral salt spray time, but be unexpectedly obviously improved 60 hours, this is embodied
Has fabulous compatibility synergistic effect between major-minor corrosion inhibiter.
The water-based antirust agent of the present invention is pH controllable types.Its pH value can be by the organic acids such as citric acid and sodium bicarbonate etc. no
The buffer of this kind of safe green of strong base-weak acid salt of chloride ion-containing regulates and controls, and meets different rust-proof effects：This product exists
Between 8.6~8.8, the resistance to neutral salt spray time reaches 60 hours pH value when undiluted；If adjusting pH value between 8.1~8.6,
The resistance to neutral salt spray time is then at 48~60 hours；If adjusting pH value between 7.5~8.1, the resistance to neutral salt spray time 36~
48 hours；If adjusting pH value between 7.0~7.5, the resistance to neutral salt spray time was at 26~36 hours；If adjusting pH value 6.5
Between~7.0, the resistance to neutral salt spray time is then at 16~26 hours.To sum up, the present invention can be expired by the height of control ph
The different antirust requirement of foot, being diluted with water for the prior art excessive can cause (more than 20 times) that film is too thin and rust-proof effect is unstable
Fixed situation, the present invention can be solved directly by adjusting pH value, meet the customization demand of user.
The water-based antirust agent of the present invention is different from other manner of formulation in preparation process and is to need to quantify several times
Solvent is added, proves that the method for the present invention can make water-based antirust agent disperse more stable, appearance and be more fully apparent from through a large number of experiments, it is long-term to protect
Deposit no Precipitation.Raw materials used green safe, nontoxic, preparation process is easy to operate, and SOLUTION PROPERTIES is stablized.
It should be noted that the above examples are only used to illustrate the technical scheme of the present invention and are not limiting, although with reference to preferable
Embodiment describes the invention in detail, it will be understood by those of ordinary skill in the art that, it can be to the technology of the present invention
Scheme is modified or replaced equivalently, and without departing from the spirit of the technical scheme of the invention and range, should all be covered in this hair
In bright right.
Claims (10)
1. a kind of water-based antirust agent, it is characterised in that：Including, main corrosion inhibiter, auxiliary corrosion inhibiter, film forming agent, thickener, bleeding agent,
Antifoaming agent, wherein in terms of mass fraction, the film former content is 3~10 parts, the infiltration agent content is 10~30 parts, institute
State that amount of thickener is 2~5 parts, the auxiliary inhibition agent content is 30~45 parts, the main inhibition agent content is 30~50 parts, institute
It is 1~3 part to state antifoam content.
2. water-based antirust agent as described in claim 1, it is characterised in that：Further include solvent, the solvent include water, ethyl alcohol,
Acetone, ether, wherein ethanol content is 130~210 parts, content of acetone is 15~25 parts, ether content is 5~15 parts, water contains
Amount is 600~700 parts.
3. water-based antirust agent as claimed in claim 1 or 2, it is characterised in that：The main corrosion inhibiter includes petroleum sodium sulfonate, three
Ethanol amine borate, the auxiliary corrosion inhibiter include di-o-tolyl-thiourea, sodium benzoate, EDTA-2Na, sodium citrate, phytic acid, three
Ethanol amine, the film forming agent include polyvinyl alcohol, rosin, aqueous lanolin, aqueous polyurethane, the thickener include gelatin,
Guar gum, the bleeding agent include oleic acid, enuatrol, alkali-resistant penetrant AEP98, fast penetrant T, and the antifoaming agent includes
Byfuel L85。
4. water-based antirust agent as claimed in claim 3, it is characterised in that：In terms of mass fraction, the mahogany acid sodium content
For 20~30 parts, the triethanolamine borate content be 20~30 parts, the di-o-tolyl-thiourea content is 4~5 parts, described
Sodium benzoate content is 4~6 parts, the EDTA-2Na contents are 4~6 parts, the content of sodium citrate is 8~10 parts, described
Phytic acid content is 4~5 parts, the triethanolamine content is 14~15 parts, the polyvinyl alcohol content is 2~3 parts, the rosin
Content is 2~3 parts, the aqueous lanolin content is 1.5~2 parts, the aqueous polyurethane content is 1~3 part, the gelatin
Content is 2~4 parts, the guar gum content is 1~3 part, the oleic acid content is 6~8 parts, the oleic acid sodium content be 7~
10 parts, the alkali-resistant penetrant AEP98 contents be 6~8 parts, the fast penetrant T content is 4~6 parts, the Byfuel
L85 contents are 1~3, the ethanol content is 130~210 parts, content of acetone is 15~25 parts, ether content is 5~15 parts,
Water content is 600~700 parts.
5. the preparation method of any water-based antirust agent of Claims 1 to 4, it is characterised in that：Including,
Prepare film forming agent：In terms of mass fraction, 3~10 parts of film forming agent is mixed with 90~97 parts of water, it is water-soluble to prepare film forming agent
Liquid；
Prepare thickener：In terms of mass fraction, 2~5 parts of thickener is mixed with 95~98 parts of water, it is water-soluble to prepare thickener
Liquid；
The first step is reacted：After 10~30 parts of bleeding agents are mixed with 170~190 parts of water, 30~45 parts of auxiliary corrosion inhibiter are added, then add
Enter the film forming agent aqueous solution；
Second step reacts：The first step reaction after, be added 30~50 parts of main corrosion inhibiter, be added later the aqueous thickener solution and
130~210 parts of ethyl alcohol of solvent, 15~25 parts of acetone, 5~15 parts of ether, 180~270 parts of water mixing.
6. preparation method as claimed in claim 5, it is characterised in that：In terms of mass fraction, the component of the film forming agent includes 3
The component of part polyvinyl alcohol, 3 parts of rosin, 2 parts of aqueous lanolin, 2 parts of aqueous polyurethanes, the thickener includes 3 parts of gelatin, 2
Part guar gum.
7. such as preparation method described in claim 5 or 6, it is characterised in that：The first step reaction, in terms of mass fraction, institute
It includes 8 parts of oleic acid, 10 parts of enuatrols, 7 parts of alkali-resistant penetrant AEP98,5 parts of fast penetrant Ts, the auxiliary corrosion inhibiter to state bleeding agent
Including 5 parts of di-o-tolyl-thioureas, 5 sodium benzoates, 5 parts of EDTA-2Na, 10 parts of sodium citrates, 5 parts of phytic acid, 15 parts of triethanolamines.
8. such as preparation method described in claim 5 or 6, it is characterised in that：The second step reaction, in terms of mass fraction, institute
State main corrosion inhibiter include 30 parts of petroleum sodium sulfonates, 20 parts of triethanolamine borates, the solvent include 210 parts of ethyl alcohol, 25 part third
Ketone, 15 parts of ether and 180 parts of deionized waters.
9. such as preparation method described in claim 5 or 6, it is characterised in that：Further include,
Homogeneous：After carrying out the second step reaction, carries out homogeneous and antifoaming agent is added.
10. preparation method as claimed in claim 9, it is characterised in that：Including, carry out after the second step reaction
72 parts of deionized waters are added in homogeneous 12min under 7200rpm, continue homogeneous 2min, and 3 parts of Byfuel L85 antifoaming agent, homogeneous is added
1min。