CN108395652A - 一种具有高阻隔抗拉伸性能的包装膜及其制备方法 - Google Patents

一种具有高阻隔抗拉伸性能的包装膜及其制备方法 Download PDF

Info

Publication number
CN108395652A
CN108395652A CN201810344277.4A CN201810344277A CN108395652A CN 108395652 A CN108395652 A CN 108395652A CN 201810344277 A CN201810344277 A CN 201810344277A CN 108395652 A CN108395652 A CN 108395652A
Authority
CN
China
Prior art keywords
parts
packaging film
barrier
tensile resistance
nano
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201810344277.4A
Other languages
English (en)
Inventor
武行峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hefei Jintongwei Low-Temperature Technology Co Ltd
Original Assignee
Hefei Jintongwei Low-Temperature Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hefei Jintongwei Low-Temperature Technology Co Ltd filed Critical Hefei Jintongwei Low-Temperature Technology Co Ltd
Priority to CN201810344277.4A priority Critical patent/CN108395652A/zh
Publication of CN108395652A publication Critical patent/CN108395652A/zh
Withdrawn legal-status Critical Current

Abstract

本发明公开了一种具有高阻隔抗拉伸性能的包装膜，包括以下重量份的原料：聚乙烯醇树脂36‑42份、ABS树脂28‑32份、松香22‑26份、复合纳米纤维10‑16份、纳米石墨烯18‑22份、纳米硫酸钡5‑9份、羟丙基纤维素4‑8份、抗冲改性剂3‑5份、矿物土填料1‑3份。本发明的目的是提供一种具有高阻隔抗拉伸性能的包装膜，该包装膜不仅阻隔性能好，抗拉性能同样优异，此外二者能够很好的协调，使包装膜阻隔性、抗拉性能兼备，具有较高的使用价值和良好的应用前景。

Description

一种具有高阻隔抗拉伸性能的包装膜及其制备方法
技术领域
本发明涉及包装膜技术领域，具体涉及一种具有高阻隔抗拉伸性能的包装膜及其制备方法。
背景技术
随着人们对物质文化需求的日益增长，对日常用品的安全性提出了更高的要求，包装为了保护、提高商品的安全性并且促销商品的关键，目前高阻隔包装塑料薄膜的生产及技术逐渐进入公众的视野，引起了广泛的关注，包装膜采用收缩包装的优点是：1、适应于包装各种形状的商品，增加产品外观吸引力；2、薄膜能够紧贴商品，具有透明性，外形美观，清洁亮丽；3、包装好的商品具有卫生性、保洁性，密封包装，防尘阻湿；4、收缩包装具有良好的防震撞性、防冲击性、以及良好的保护性能;；5、被包装的商品具有紧密性和固定性，小部件不会在包装中东倒西歪；6、热收缩膜也可用于代替各类纸盒，尤其是在不规则形体物品或商品的组合式包装方面，不但节约包装成本，而且符合包装潮流。
现有技术中，包装膜虽具有降解功能，但阻隔性和抗拉性能还不是很好，同时二者不能很好的达到协调，使包装膜技术受到了限制。
发明内容
针对现有技术的缺陷，本发明的目的是提供一种具有高阻隔抗拉伸性能的包装膜，该包装膜不仅阻隔性能好，抗拉性能同样优异，此外二者能够很好的协调，使包装膜阻隔性、抗拉性能兼备。
本发明解决技术问题采用如下技术方案：
本发明提供了一种具有高阻隔抗拉伸性能的包装膜，包括以下重量份的原料：
聚乙烯醇树脂36-42份、ABS树脂28-32份、松香22-26份、复合纳米纤维10-16份、纳米石墨烯18-22份、纳米硫酸钡5-9份、羟丙基纤维素4-8份、抗冲改性剂3-5份、矿物土填料1-3份。
优选地，所述具有高阻隔抗拉伸性能的包装膜包括以下重量份的原料：
聚乙烯醇树脂39份、ABS树脂30份、松香24份、复合纳米纤维13份、纳米石墨烯20份、纳米硫酸钡7份、羟丙基纤维素6份、抗冲改性剂4份、矿物土填料2份。
优选地，所述复合纳米纤维为二氧化硅纳米纤维、壳聚糖纳米纤维按照重量比（2-6）:1进行复合。
优选地，所述复合纳米纤维为二氧化硅纳米纤维、壳聚糖纳米纤维按照重量比4:1进行复合。
优选地，所述抗冲改性剂为抗冲改性剂ACR。
优选地，所述矿物土填料为角闪石粉、地开石粉、方解石粉、孔雀石粉中的一种或多种的组合。
本发明还提供了一种具有高阻隔抗拉伸性能的包装膜的制备方法，包括以下步骤：
步骤一，按要求称量各组分原料；
步骤二，将聚乙烯醇树脂、ABS树脂、松香、复合纳米纤维加入高速搅拌机中混合，温度保持115-125℃，搅拌速度135-155r/min，搅拌时间25-35min，得到混合物A；
步骤三，将步骤二得到混合物A、纳米石墨烯、纳米硫酸钡、羟丙基纤维素、抗冲改性剂、矿物土填料加入高速混合机中混合，搅拌速度1550-1650r/min，搅拌时间为55-65min，随后送入双螺旋挤出机中，挤出，造粒，冷却即得本发明的具有高阻隔抗拉伸性能的包装膜。
优选地，所述具有高阻隔抗拉伸性能的包装膜的制备步骤为：
步骤一，按要求称量各组分原料；
步骤二，将聚乙烯醇树脂、ABS树脂、松香、复合纳米纤维加入高速搅拌机中混合，温度保持120℃，搅拌速度140r/min，搅拌时间30min，得到混合物A；
步骤三，将步骤二得到混合物A、纳米石墨烯、纳米硫酸钡、羟丙基纤维素、抗冲改性剂、矿物土填料加入高速混合机中混合，搅拌速度1600r/min，搅拌时间为60min，随后送入双螺旋挤出机中，挤出，造粒，冷却即得本发明的具有高阻隔抗拉伸性能的包装膜。
与现有技术相比，本发明具有如下的有益效果：
（1）本发明的一种具有高阻隔抗拉伸性能的包装膜，聚乙烯醇树脂具有可降解性，同时阻隔性能好，ABS树脂强度高，韧性好，且容易加工，松香具有很好的黏性，能够提高粘接强度，将三者作为主要基料，能够使薄膜拉伸强度、阻隔性兼备，同时性能好，此外加入的矿物土填料能够在拉伸、阻隔性能基础上提高包装膜的强度。
（2）本发明的一种具有高阻隔抗拉伸性能的包装膜，添加的复合纳米纤维以及羟丙基纤维素能够提高包装膜的韧性，加入的抗冲改性剂为抗冲改性剂ACR，可进一步的提高包装膜的拉伸性能，纳米石墨烯、纳米硫酸钡可在原有基础上更进一步的提高材料的韧性。
（3）本发明的一种具有高阻隔抗拉伸性能的包装膜，该包装膜不仅阻隔性能好，抗拉性能同样优异，此外二者能够很好的协调，使包装膜阻隔性、抗拉性能兼备。
具体实施方式
下面结合具体实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1.
本实施例的一种具有高阻隔抗拉伸性能的包装膜，包括以下重量份的原料：
聚乙烯醇树脂36份、ABS树脂28份、松香22份、复合纳米纤维10份、纳米石墨烯18份、纳米硫酸钡5份、羟丙基纤维素4份、抗冲改性剂3份、矿物土填料1份。
本实施例的复合纳米纤维为二氧化硅纳米纤维、壳聚糖纳米纤维按照重量比2:1进行复合。
本实施例的抗冲改性剂为抗冲改性剂ACR。
本实施例的矿物土填料为角闪石粉。
本实施例的一种具有高阻隔抗拉伸性能的包装膜的制备方法，包括以下步骤：
步骤一，按要求称量各组分原料；
步骤二，将聚乙烯醇树脂、ABS树脂、松香、复合纳米纤维加入高速搅拌机中混合，温度保持115℃，搅拌速度135r/min，搅拌时间25min，得到混合物A；
步骤三，将步骤二得到混合物A、纳米石墨烯、纳米硫酸钡、羟丙基纤维素、抗冲改性剂、矿物土填料加入高速混合机中混合，搅拌速度1550r/min，搅拌时间为55min，随后送入双螺旋挤出机中，挤出，造粒，冷却即得本发明的具有高阻隔抗拉伸性能的包装膜。
实施例2.
本实施例的一种具有高阻隔抗拉伸性能的包装膜，包括以下重量份的原料：
聚乙烯醇树脂42份、ABS树脂32份、松香26份、复合纳米纤维16份、纳米石墨烯22份、纳米硫酸钡9份、羟丙基纤维素8份、抗冲改性剂5份、矿物土填料3份。
本实施例的复合纳米纤维为二氧化硅纳米纤维、壳聚糖纳米纤维按照重量比6:1进行复合。
本实施例的抗冲改性剂为抗冲改性剂ACR。
本实施例的矿物土填料为方解石粉。
本实施例的一种具有高阻隔抗拉伸性能的包装膜的制备方法，包括以下步骤：
步骤一，按要求称量各组分原料；
步骤二，将聚乙烯醇树脂、ABS树脂、松香、复合纳米纤维加入高速搅拌机中混合，温度保持125℃，搅拌速度155r/min，搅拌时间35min，得到混合物A；
步骤三，将步骤二得到混合物A、纳米石墨烯、纳米硫酸钡、羟丙基纤维素、抗冲改性剂、矿物土填料加入高速混合机中混合，搅拌速度1650r/min，搅拌时间为65min，随后送入双螺旋挤出机中，挤出，造粒，冷却即得本发明的具有高阻隔抗拉伸性能的包装膜。
实施例3.
本实施例的一种具有高阻隔抗拉伸性能的包装膜，包括以下重量份的原料：
聚乙烯醇树脂39份、ABS树脂30份、松香24份、复合纳米纤维13份、纳米石墨烯20份、纳米硫酸钡7份、羟丙基纤维素6份、抗冲改性剂4份、矿物土填料2份。
本实施例的复合纳米纤维为二氧化硅纳米纤维、壳聚糖纳米纤维按照重量比4:1进行复合。
本实施例的抗冲改性剂为抗冲改性剂ACR。
本实施例的矿物土填料为地开石粉。
本实施例的一种具有高阻隔抗拉伸性能的包装膜的制备方法，包括以下步骤：
步骤一，按要求称量各组分原料；
步骤二，将聚乙烯醇树脂、ABS树脂、松香、复合纳米纤维加入高速搅拌机中混合，温度保持120℃，搅拌速度140r/min，搅拌时间30min，得到混合物A；
步骤三，将步骤二得到混合物A、纳米石墨烯、纳米硫酸钡、羟丙基纤维素、抗冲改性剂、矿物土填料加入高速混合机中混合，搅拌速度1600r/min，搅拌时间为60min，随后送入双螺旋挤出机中，挤出，造粒，冷却即得本发明的具有高阻隔抗拉伸性能的包装膜。
本发明的目的是提供一种具有高阻隔抗拉伸性能的包装膜，该包装膜不仅阻隔性能好，抗拉性能同样优异，此外二者能够很好的协调，使包装膜阻隔性、抗拉性能兼备，具有较高的使用价值和良好的应用前景。
对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。
此外，应当理解，虽然本说明书按照实施方式加以描述，但并非每个实施方式仅包含一个独立的技术方案，说明书的这种叙述方式仅仅是为清楚起见，本领域技术人员应当将说明书作为一个整体，各实施例中的技术方案也可以经适当组合，形成本领域技术人员可以理解的其他实施方式。

Claims (8)

1.一种具有高阻隔抗拉伸性能的包装膜，其特征在于，包括以下重量份的原料：
聚乙烯醇树脂36-42份、ABS树脂28-32份、松香22-26份、复合纳米纤维10-16份、纳米石墨烯18-22份、纳米硫酸钡5-9份、羟丙基纤维素4-8份、抗冲改性剂3-5份、矿物土填料1-3份。
2.根据权利要求1所述的一种具有高阻隔抗拉伸性能的包装膜，其特征在于，所述具有高阻隔抗拉伸性能的包装膜包括以下重量份的原料：
聚乙烯醇树脂39份、ABS树脂30份、松香24份、复合纳米纤维13份、纳米石墨烯20份、纳米硫酸钡7份、羟丙基纤维素6份、抗冲改性剂4份、矿物土填料2份。
3.根据权利要求1或2所述的一种具有高阻隔抗拉伸性能的包装膜，其特征在于，所述复合纳米纤维为二氧化硅纳米纤维、壳聚糖纳米纤维按照重量比（2-6）:1进行复合。
4.根据权利要求3所述的一种具有高阻隔抗拉伸性能的包装膜，其特征在于，所述复合纳米纤维为二氧化硅纳米纤维、壳聚糖纳米纤维按照重量比4:1进行复合。
5.根据权利要求1所述的一种具有高阻隔抗拉伸性能的包装膜，其特征在于，所述抗冲改性剂为抗冲改性剂ACR。
6.根据权利要求1所述的一种具有高阻隔抗拉伸性能的包装膜，其特征在于，所述矿物土填料为角闪石粉、地开石粉、方解石粉、孔雀石粉中的一种或多种的组合。
7.一种制备如权利要求1或2所述具有高阻隔抗拉伸性能的包装膜的方法，其特征在于，包括以下步骤：
步骤一，按要求称量各组分原料；
步骤二，将聚乙烯醇树脂、ABS树脂、松香、复合纳米纤维加入高速搅拌机中混合，温度保持115-125℃，搅拌速度135-155r/min，搅拌时间25-35min，得到混合物A；
步骤三，将步骤二得到混合物A、纳米石墨烯、纳米硫酸钡、羟丙基纤维素、抗冲改性剂、矿物土填料加入高速混合机中混合，搅拌速度1550-1650r/min，搅拌时间为
55-65min，随后送入双螺旋挤出机中，挤出，造粒，冷却即得本发明的具有高阻隔抗拉伸性能的包装膜。
8.根据权利要求7所述的一种具有高阻隔抗拉伸性能的包装膜的制备方法，其特征在于，所述制备步骤为：
步骤一，按要求称量各组分原料；
步骤二，将聚乙烯醇树脂、ABS树脂、松香、复合纳米纤维加入高速搅拌机中混合，温度保持120℃，搅拌速度140r/min，搅拌时间30min，得到混合物A；
步骤三，将步骤二得到混合物A、纳米石墨烯、纳米硫酸钡、羟丙基纤维素、抗冲改性剂、矿物土填料加入高速混合机中混合，搅拌速度1600r/min，搅拌时间为60min，随后送入双螺旋挤出机中，挤出，造粒，冷却即得本发明的具有高阻隔抗拉伸性能的包装膜。
CN201810344277.4A 2018-04-17 2018-04-17 一种具有高阻隔抗拉伸性能的包装膜及其制备方法 Withdrawn CN108395652A (zh)