CN108250962A - 非固化耐根穿刺防水卷材及其生产工艺 - Google Patents
非固化耐根穿刺防水卷材及其生产工艺 Download PDFInfo
- Publication number
- CN108250962A CN108250962A CN201810045767.4A CN201810045767A CN108250962A CN 108250962 A CN108250962 A CN 108250962A CN 201810045767 A CN201810045767 A CN 201810045767A CN 108250962 A CN108250962 A CN 108250962A
- Authority
- CN
- China
- Prior art keywords
- parts
- uncured
- waterproof roll
- root
- resistant waterproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种非固化耐根穿刺防水卷材及其生产工艺，属于防水材料领域。这种非固化耐根穿刺防水卷材，其包括依次设置的面层、非固化防水涂料层、底层，面层为高分子膜，底层为隔离膜，非固化防水涂料层包括：改性石油沥青、热熔胶、松香树脂、附着力促进剂、聚异丁烯、阻根剂、滑石粉、软化剂。其生产工艺包括：将改性石油沥青、热熔胶、松香树脂和附着力促进剂混合，得到混合基质；再将混合基质与其他原料混合，得到非固化防水涂料；再将非固化防水涂料涂覆于底层之上，在再其面层覆盖高分子膜。这种防水卷材具有长效的耐植物根穿刺的性能，同时又不影响植物的正常生长，适用于建筑绿化，其粘结力强，稳定性好，还具有很好的抗腐蚀性能。
Description
技术领域
本发明涉及防水材料领域，具体而言，涉及一种非固化耐根穿刺防水卷材及其生产工艺。
背景技术
将沥青类或高分子类防水材料浸渍在胎体上，制作成的防水材料产品，以卷材形式提供，称为防水卷材。根据主要组成材料不同，分为沥青防水卷材、高聚物改性沥青防水卷材和合成高分子防水卷材；根据胎体的不同分为无胎体卷材、纸胎卷材、玻璃纤维胎卷材、玻璃布胎卷材和聚乙烯胎卷材。
非固化橡胶沥青防水涂料是一种比较经典的液体橡胶防水涂料，其产品的特点已受防水行业的认可，具有自愈性、蠕变性和自修复功能，其广泛用于防水卷材的制备中。
然而，目前这类非固化橡胶沥青防水涂料，都不具有抗根性能，很容易被植物的根尖穿透，造成建筑体破坏和渗漏，无法满足建筑种植***的需要。
发明内容
本发明的第一目的在于提供一种非固化耐根穿刺防水卷材，这种防水卷材具有长效的耐植物根穿刺的性能，同时又不影响植物的正常生长，适用于建筑绿化，其粘结力强，稳定性好，还具有很好的抗腐蚀性能。
本发明的第二目的在于提供一种非固化耐根穿刺防水卷材的生产工艺，该制备方法简单，容易实现精细化控制，所得到的防水卷材的耐根穿刺性能好。
为了实现本发明的上述目的，特采用以下技术方案：
一种非固化耐根穿刺防水卷材，其包括依次设置的面层、非固化防水涂料层、底层，面层为高分子膜，底层为隔离膜，非固化防水涂料层按重量份数计包括：改性石油沥青60～80份、热熔胶20～30份、松香树脂15～30份、附着力促进剂10～18份、聚异丁烯5～12份、阻根剂10～18份、滑石粉15～20份、软化剂14～20份。
进一步的，在本发明较佳的实施例中，按重量份数计，改性石油沥青为64～76份、热熔胶为23～28份、松香树脂为19～26份、附着力促进剂为12～16份、聚异丁烯为7～10份、阻根剂为12～16份、滑石粉为16～18份、软化剂为16～19份。
进一步的，在本发明较佳的实施例中，按重量份数计，改性石油沥青为68～73份、热熔胶为25～27份、松香树脂为22～24份、附着力促进剂为14～15份、聚异丁烯为8～9份、阻根剂为14～15份、滑石粉为17～18份、软化剂为17～18份。
进一步的，在本发明较佳的实施例中，阻根剂选自氧化铝、氧化钛和氧化铁中的至少一种。
进一步的，在本发明较佳的实施例中，软化剂选自环烷油或芳烃油。
进一步的，在本发明较佳的实施例中，热熔胶为苯乙烯-异戊二烯-苯乙烯嵌段共聚物。
进一步的，在本发明较佳的实施例中，隔离层包括聚乙烯膜层或黄沙层。
进一步的，在本发明较佳的实施例中，附着力促进剂包括醛酮树脂或聚苯乙烯丁二烯橡胶。
一种非固化耐根穿刺防水卷材的生产工艺，其包括：
按重量份数，将改性石油沥青、热熔胶、松香树脂和附着力促进剂混合，于130～150℃下加热1～2h，得到混合基质；
再将冷却后的混合基质与聚异丁烯、阻根剂和软化剂于90～110℃下加热2～3h后，加入软化剂，在室温下搅拌30～50min，得到非固化防水涂料；
再将非固化防水涂料涂覆于底层之上，在再其面层覆盖高分子膜。
进一步的，在本发明较佳的实施例中，在将改性石油沥青、热熔胶、松香树脂和附着力促进剂混合得到熔融基质的过程中，以3～5℃/min的升温速率进行梯度升温。
与现有技术相比，本发明的有益效果例如包括：
本发明提供的这种非固化耐根穿刺防水卷材及其生产工艺，通过将改性石油沥青、热熔胶、松香树脂和附着力促进剂混合，实现改性石油沥青与松香树脂之间的化学交联反应，使得非固化防水卷材在使用年限内保持弹性膏状体性能的基础上，还具有耐热性和低粘度等特性。
同时，在得到混合基质后，将其与聚异丁烯、阻根剂和软化剂，使其具有具有长效的耐植物根穿刺的性能，同时又不影响植物的正常生长，适用于建筑物绿化。随后再加入软化剂，使得得到的非固化涂料具有较好的流变性，增强该防水卷的软化性能。
具体实施方式
下面将结合实施例对本发明的实施方案进行详细描述，但是本领域技术人员将会理解，下列实施例仅用于说明本发明，而不应视为限制本发明的范围。实施例中未注明具体条件者，按照常规条件或制造商建议的条件进行。所用试剂或仪器未注明生产厂商者，均为可以通过市售购买获得的常规产品。
以下结合实施例对本发明的特征和性能作进一步的详细描述：
实施例1
本实施例提供一种非固化耐根穿刺防水卷材，其包括依次设置的面层、非固化防水涂料层和底层。
其中，非固化防水涂料层按重量份数计包括：
改性石油沥青60份、热熔胶30份、松香树脂15份、附着力促进剂18份、聚异丁烯5份、阻根剂18份、滑石粉15份、软化剂14份。
这种非固化耐根穿刺防水卷材的生产工艺包括：
按重量份数，将改性石油沥青、热熔胶、松香树脂和附着力促进剂混合，于130℃下加热2h，得到混合基质；
再将冷却后的混合基质与聚异丁烯、阻根剂和软化剂于110℃下加热2h后，加入软化剂，在室温下搅拌50min，得到非固化防水涂料；
再将非固化防水涂料涂覆于底层之上，在再其面层覆盖高分子膜。
实施例2
本实施例提供一种非固化耐根穿刺防水卷材，其包括依次设置的面层、非固化防水涂料层和底层。
其中，非固化防水涂料层按重量份数计包括：
改性石油沥青80份、热熔胶20份、松香树脂30份、附着力促进剂10份、聚异丁烯12份、阻根剂10份、滑石粉20份、软化剂20份。
这种非固化耐根穿刺防水卷材的生产工艺包括：
按重量份数，将改性石油沥青、热熔胶、松香树脂和附着力促进剂混合，于150℃下加热1h，得到混合基质；
再将冷却后的混合基质与聚异丁烯、阻根剂和软化剂于90℃下加热3h后，加入软化剂，在室温下搅拌30min，得到非固化防水涂料；
再将非固化防水涂料涂覆于底层之上，在再其面层覆盖高分子膜。
实施例3
本实施例提供一种非固化耐根穿刺防水卷材，其包括依次设置的面层、非固化防水涂料层和底层。
其中，非固化防水涂料层按重量份数计包括：
改性石油沥青70份、热熔胶25份、松香树脂22份、附着力促进剂15份、聚异丁烯8份、阻根剂14份、滑石粉17份、软化剂16份。
这种非固化耐根穿刺防水卷材的生产工艺包括：
按重量份数，将改性石油沥青、热熔胶、松香树脂和附着力促进剂混合，于140℃下加热1.5h，得到混合基质；
再将冷却后的混合基质与聚异丁烯、阻根剂和软化剂于100℃下加热2.5h后，加入软化剂，在室温下搅拌40min，得到非固化防水涂料；
再将非固化防水涂料涂覆于底层之上，在再其面层覆盖高分子膜。
实施例4
本实施例提供一种非固化耐根穿刺防水卷材，其包括依次设置的面层、非固化防水涂料层和底层。
其中，非固化防水涂料层按重量份数计包括：
改性石油沥青64份、热熔胶23份、松香树脂19份、附着力促进剂16份、聚异丁烯10份、阻根剂16份、滑石粉16份、软化剂19份。
这种非固化耐根穿刺防水卷材的生产工艺包括：
按重量份数，将改性石油沥青、热熔胶、松香树脂和附着力促进剂混合，以3℃/min的升温速率梯度升温至135℃下加热1.2h，得到混合基质；
再将冷却后的混合基质与聚异丁烯、阻根剂和软化剂于95℃下加热2.7h后，加入软化剂，在室温下搅拌40min，得到非固化防水涂料；
再将非固化防水涂料涂覆于底层之上，在再其面层覆盖高分子膜。
实施例5
本实施例提供一种非固化耐根穿刺防水卷材，其包括依次设置的面层、非固化防水涂料层和底层。
其中，非固化防水涂料层按重量份数计包括：
改性石油沥青73份、热熔胶27份、松香树脂24份、附着力促进剂15份、聚异丁烯9份、阻根剂14份、滑石粉18份、软化剂17份。
这种非固化耐根穿刺防水卷材的生产工艺包括：
按重量份数，将改性石油沥青、热熔胶、松香树脂和附着力促进剂混合，以5℃/min的升温速率梯度升温至145℃下加热1.8h，得到混合基质；
再将冷却后的混合基质与聚异丁烯、阻根剂和软化剂于105℃下加热2.3h后，加入软化剂，在室温下搅拌35min，得到非固化防水涂料；
再将非固化防水涂料涂覆于底层之上，在再其面层覆盖高分子膜。
综上所述，本实施方式提供的这种非固化耐根穿刺防水卷材，具有长效的耐植物根穿刺的性能，同时又不影响植物的正常生长，适用于建筑绿化，其粘结力强，稳定性好，还具有很好的抗腐蚀性能。
尽管已用具体实施例来说明和描述了本发明，然而应意识到，在不背离本发明的精神和范围的情况下可以作出许多其它的更改和修改。因此，这意味着在所附权利要求中包括属于本发明范围内的所有这些变化和修改。
Claims (10)
1.一种非固化耐根穿刺防水卷材，其特征在于，其包括依次设置的面层、非固化防水涂料层、底层，所述面层为高分子膜，所述底层为隔离膜，所述非固化防水涂料层按重量份数计包括：改性石油沥青60～80份、热熔胶20～30份、松香树脂15～30份、附着力促进剂10～18份、聚异丁烯5～12份、阻根剂10～18份、滑石粉15～20份、软化剂14～20份。
2.根据权利要求1所述的非固化耐根穿刺防水卷材，其特征在于，按重量份数计，所述改性石油沥青为64～76份、所述热熔胶为23～28份、所述松香树脂为19～26份、所述附着力促进剂为12～16份、所述聚异丁烯为7～10份、所述阻根剂为12～16份、所述滑石粉为16～18份、所述软化剂为16～19份。
3.根据权利要求1所述的非固化耐根穿刺防水卷材，其特征在于，按重量份数计，所述改性石油沥青为68～73份、所述热熔胶为25～27份、所述松香树脂为22～24份、所述附着力促进剂为14～15份、所述聚异丁烯为8～9份、所述阻根剂为14～15份、所述滑石粉为17～18份、所述软化剂为17～18份。
4.根据权利要求1所述的非固化耐根穿刺防水卷材，其特征在于，所述阻根剂选自氧化铝、氧化钛和氧化铁中的至少一种。
5.根据权利要求1所述的非固化耐根穿刺防水卷材，其特征在于，所述软化剂选自环烷油或芳烃油。
6.根据权利要求1所述的非固化耐根穿刺防水卷材，其特征在于，所述热熔胶为苯乙烯-异戊二烯-苯乙烯嵌段共聚物。
7.根据权利要求1所述的非固化耐根穿刺防水卷材，其特征在于，所述隔离层包括聚乙烯膜层或黄沙层。
8.根据权利要求1所述的非固化耐根穿刺防水卷材，其特征在于，所述附着力促进剂包括醛酮树脂或聚苯乙烯丁二烯橡胶。
9.一种根据权利要求1～8任一项所述的非固化耐根穿刺防水卷材的生产工艺，其特征在于，其包括：
按重量份数，将所述改性石油沥青、所述热熔胶、所述松香树脂和所述附着力促进剂混合，于130～150℃下加热1～2h，得到混合基质；
再将冷却后的所述混合基质与所述聚异丁烯、阻根剂和软化剂于90～110℃下加热2～3h后，加入软化剂，在室温下搅拌30～50min，得到非固化防水涂料；
再将所述非固化防水涂料涂覆于所述底层之上，在再其面层覆盖所述高分子膜。
10.根据权利要求9所述的非固化耐根穿刺防水卷材的生产工艺，其特征在于，在将所述改性石油沥青、所述热熔胶、所述松香树脂和所述附着力促进剂混合得到熔融基质的过程中，以3～5℃/min的升温速率进行梯度升温。