CN108151913A - A kind of heat-sensitive material of sensor - Google Patents
A kind of heat-sensitive material of sensor Download PDFInfo
- Publication number
- CN108151913A CN108151913A CN201711439179.0A CN201711439179A CN108151913A CN 108151913 A CN108151913 A CN 108151913A CN 201711439179 A CN201711439179 A CN 201711439179A CN 108151913 A CN108151913 A CN 108151913A
- Authority
- CN
- China
- Prior art keywords
- oxide
- manganese
- nickel
- heat
- sensitive material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
A kind of heat-sensitive material of sensor, the plastic cement are grouped as by each group of the quality for following percentage:Manganese:12%~15%, cobalt oxide:1%~5%, nickel oxide:3%~7%, titanium:11%~13%, nickel:1%~5%, silicon:3%~5%, silicon carbide:5%~8%, surplus is manganese oxide.The invention has the beneficial effects that:For product made of the present invention for sensing body temperature range, and precision is higher, precision can reach 0.01 DEG C.
Description
First, technical field
The present invention relates to a kind of new material, more particularly to a kind of heat-sensitive material of sensor.
2nd, background technology
Thermo-sensitive material refers to PTC, NTC, CTR etc..It means positive temperature coefficient, refers to that positive temperature coefficient is very big partly to be led
Body material or component.NTC means negative temperature coefficient, refers to negative temperature coefficient very big semi-conducting material or component.
In recent years, with the development of society, thermoinduction sensor is widely used, and core is exactly the heat-sensitive material of itself.Temperature-sensitive material
Material is a kind of semiconductor sensitive element.Research at this stage is a kind of to be used to sense body temperature range, and the temperature-sensitive that precision is higher
It is particularly significant to feel material.
3rd, invention content
In order to overcome the shortcoming of existing new material, the present invention provides a kind of heat-sensitive materials of sensor.
The technical proposal of the invention is realized in this way.
A kind of heat-sensitive material of sensor of this programme, the plastic cement are grouped by each group of the quality for following percentage
Into:Manganese:12%~15%, cobalt oxide:1%~5%, nickel oxide:3%~7%, titanium:11%~13%, nickel:1%~5%,
Silicon:3%~5%, silicon carbide:5%~8%, surplus is manganese oxide.
The plastic cement is grouped as by each group of the quality for following percentage:Manganese:12%, cobalt oxide:3%, nickel oxide:4%,
Titanium:13%, nickel:2%, silicon:5%, silicon carbide:6%, surplus is manganese oxide.
The plastic cement is grouped as by each group of the quality for following percentage:Manganese:13%, cobalt oxide:4%, nickel oxide:5%,
Titanium:12%, nickel:3%, silicon:4%, silicon carbide:7%, surplus is manganese oxide.
The plastic cement is grouped as by each group of the quality for following percentage:Manganese:14%, cobalt oxide:5%, nickel oxide:6%,
Titanium:11%, nickel:4%, silicon:3%, silicon carbide:8%, surplus is manganese oxide.
The invention has the beneficial effects that:Product made of the present invention for sensing body temperature range, and precision compared with
Height, precision can reach 0.01 DEG C.
4th, specific embodiment
Embodiment 1
A kind of heat-sensitive material of sensor, by manganese:12kg, cobalt oxide:3kg, nickel oxide:4kg, titanium:13kg, nickel:
2kg, silicon:5kg, silicon carbide:6kg, surplus are mixed and made into material described in 100kg for manganese oxide, and product made of the present invention is used for
Sense body temperature range, and precision is higher, precision can reach 0.01 DEG C.
Embodiment 2
A kind of heat-sensitive material of sensor, by manganese:13kg, cobalt oxide:4kg, nickel oxide:5kg, titanium:12kg, nickel:
3kg, silicon:4kg, silicon carbide:7kg, surplus are mixed and made into material described in 100kg for manganese oxide, and product made of the present invention is used for
Sense body temperature range, and precision is higher, precision can reach 0.01 DEG C.
Embodiment 3
A kind of heat-sensitive material of sensor, by manganese:14kg, cobalt oxide:5kg, nickel oxide:6kg, titanium:11kg, nickel:
4kg, silicon:3kg, silicon carbide:8kg, surplus are mixed and made into material described in 100kg for manganese oxide, and product made of the present invention is used for
Sense body temperature range, and precision is higher, precision can reach 0.01 DEG C.
One embodiment of the present of invention is described in detail above, but the content is only the preferable implementation of the present invention
Example, it is impossible to be construed as limiting the practical range of the present invention.All all the changes and improvements made according to the present patent application range
Deng, should all still belong to the present invention patent covering scope within.
Claims (4)
1. a kind of heat-sensitive material of sensor, it is characterised in that:The plastic cement is by each component of the quality for following percentage
Composition:Manganese:12%~15%, cobalt oxide:1%~5%, nickel oxide:3%~7%, titanium:11%~13%, nickel:1%~5%,
Silicon:3%~5%, silicon carbide:5%~8%, surplus is manganese oxide.
2. a kind of heat-sensitive material of sensor according to claim 1, it is characterised in that:The plastic cement is by quality
The each group of following percentage is grouped as:Manganese:12%, cobalt oxide:3%, nickel oxide:4%, titanium:13%, nickel:2%, silicon:5%, carbon
SiClx:6%, surplus is manganese oxide.
3. a kind of heat-sensitive material of sensor according to claim 1, it is characterised in that:The plastic cement is by quality
The each group of following percentage is grouped as:Manganese:13%, cobalt oxide:4%, nickel oxide:5%, titanium:12%, nickel:3%, silicon:4%, carbon
SiClx:7%, surplus is manganese oxide.
4. a kind of heat-sensitive material of sensor according to claim 1, it is characterised in that:The plastic cement is by quality
The each group of following percentage is grouped as:Manganese:14%, cobalt oxide:5%, nickel oxide:6%, titanium:11%, nickel:4%, silicon:3%, carbon
SiClx:8%, surplus is manganese oxide.