CN108130721B - 瘦身保健女装及其制备方法 - Google Patents
瘦身保健女装及其制备方法 Download PDFInfo
- Publication number
- CN108130721B CN108130721B CN201711381233.0A CN201711381233A CN108130721B CN 108130721 B CN108130721 B CN 108130721B CN 201711381233 A CN201711381233 A CN 201711381233A CN 108130721 B CN108130721 B CN 108130721B
- Authority
- CN
- China
- Prior art keywords
- fabric
- parts
- titanium dioxide
- care
- health
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种瘦身保健女装及其制备方法,所述瘦身保健女装的制备方法包括以下步骤:(1)制备整理液;(2)浸渍;(3)洗涤烘干;(4)裁剪缝制。本发明瘦身保健女装及其制备方法,工艺简单,得到的瘦身保健面料具有抗菌、防紫外的功能,还能够释放远红外线,远红外线能使体内热能提高,细胞活化,促进人体血液循环,因此促进脂肪组织代谢,燃烧分解,将多余脂肪消耗掉,进而有效瘦身,促进人体健康,具有保健功效。
Description
技术领域
本发明涉及一种女装,具体涉及一种瘦身保健女装及其制备方法。
背景技术
随着大众生活水平的提高,人们更注重对生活品质的追求。高档服饰、家用面料成为当前中产阶级的主要消费群,该消费群已逐渐形成了独特的消费品味,但当下的服饰、家纺产品,已无法满足人们快速增长的个性化需求。
传统的面料具有保暖、遮盖和美化功能,功能性面料则是超出以上三种基本作用外还具有其他一些特殊性质,例如我们生活工作中现在比较流行的阻燃、抗菌、防紫外线、防辐射。
功能性面料的功能一般会根据应用需求的不同而赋予其不同的特性,制备方式也比较多,范围涉及多个领域。其制备的途径主要有两种:一种是利用一些具有特殊功能的纤维来生产;另一种是在织物上进行处理,通过各种化学、物理手段使织物具有一些我们所需要的特殊功能。
常规纤维制成的面料,采用后整理的加工方法使面料具有功能性来满足实际生产的需求,通过这种方法获得的功能性面料具有以下几个优点:整理目的性明确、效果突出、附加值较高、且操作相对简单。后整理的功能性面料要求环保、无毒、操作简单方便及特殊功能具有持久性。
现有技术中面料功能相对单一,且缺乏瘦身保健功能的面料。本发明提供了一种瘦身保健女装,工艺简单,具有抗菌、防紫外、瘦身和保健功效,能够完美修饰女性身材。
发明内容
为实现上述目的,本发明采用如下技术方案:
一种瘦身保健女装的制备方法,包括以下步骤:
(1)制备整理液;
(2)浸渍;
(3)洗涤烘干;
(4)裁剪缝制。
优选地,一种瘦身保健女装的制备方法,包括以下步骤:
(1)制备整理液:按重量份称取渗透剂0.2-2份,粘合剂0.2-2份、电气石1-3份、二氧化钛1-3份、氨基硅油1-3份、六偏磷酸钠1-3份、水95-105份,将上述渗透剂、粘合剂、电气石、二氧化钛、氨基硅油、六偏磷酸钠依次加入到水中,在30-40℃以100-300转/分搅拌10-20分钟,得到整理液;
(2)浸渍:将面料在整理液中浸渍,浸渍时间15-25min,浸渍液温度30-40℃,浴比1:(10-20),浸渍后将面料在90-100℃干燥20分钟,得到浸渍后的面料;
(3)洗涤烘干:将浸渍后的面料水洗1-3次,40-60℃干燥5-10小时,得到瘦身保健面料;
(4)裁剪缝制:将瘦身保健面料进行裁剪,并按常规女装制备工艺缝制得到瘦身保健女装。
优选地,一种瘦身保健女装的制备方法,包括以下步骤:
(1)制备整理液:按重量份称取渗透剂0.2-2份,粘合剂0.2-2份、改性电气石1-3份、改性二氧化钛1-3份、氨基硅油1-3份、六偏磷酸钠1-3份、水95-105份,将上述渗透剂、粘合剂、改性电气石、改性二氧化钛、氨基硅油、六偏磷酸钠依次加入到水中,在30-40℃以100-300转/分搅拌10-20分钟,得到整理液;
(2)浸渍:将面料在整理液中浸渍,浸渍时间15-25min,浸渍液温度30-40℃,浴比1:(10-20),浸渍后将面料在90-100℃干燥20分钟,得到浸渍后的面料;
(3)洗涤烘干:将浸渍后的面料水洗1-3次,40-60℃干燥5-10小时,得到瘦身保健面料;
(4)裁剪缝制:将瘦身保健面料进行裁剪,并按常规女装制备工艺缝制得到瘦身保健女装。
所述改性电气石由下述方法制备而成:将电气石和水按固液比1g:(5-10)mL混合,在65-75℃以100-300转/分搅拌10-20分钟,加入电气石质量0.2-2%的改性剂,在65-75℃以100-300转/分继续搅拌2-3小时,以3000-5000转/分离心5-10分钟,将下层沉淀在85-95℃干燥5-10小时,得到改性电气石。
所述改性剂为吐温60和/或聚丙烯酸钠。
所述改性剂为吐温60和聚丙烯酸钠的混合物,所述吐温60和聚丙烯酸铵的质量比为1:(1-5)。
所述改性二氧化钛由下述方法制备而成:将二氧化钛与去离子水按固液比1g:(10-20)mL混合,在20-30℃以300-600转/分搅拌10-20分钟,加入二氧化钛质量0.1-1%的蔗糖单硬脂酸酯,在20-30℃以300-600转/分搅拌40-60分钟,升温至65-75℃,加入二氧化钛质量25-35%的单体,以300-600转/分搅拌5-10分钟,再以1滴/秒的速度滴加二氧化钛质量0.5-1.5%的过硫酸铵,滴加完毕后在65-75℃以300-600转/分搅拌6-10小时,以3000-5000转/分离心5-10分钟,沉淀在65-75℃干燥10-15小时,得到改性二氧化钛。
所述单体为苯乙烯和丙烯酸丁酯按质量比(1-5):1的混合物或苯乙烯和甲基丙烯酸甲酯按质量比(1-5):1的混合物或苯乙烯和丙烯酸甲酯按质量比(1-5):1的混合物。
优选地,所述单体为苯乙烯和丙烯酸丁酯按质量比(1-5):1的混合物或苯乙烯和丙烯酸甲酯按质量比(1-5):1的混合物。
更优选地,所述单体为苯乙烯和丙烯酸甲酯按质量比(1-5):1的混合物。
优选地,所述面料由60-70wt%棉纤维、25-35wt%尼龙和3-7%氨纶制备而成。
本发明还提供了一种瘦身保健女装,采用上述方法制备而成。
本发明瘦身保健女装及其制备方法,工艺简单,得到的瘦身保健面料具有抗菌、防紫外的功能,还能够释放远红外线,远红外线能使体内热能提高,细胞活化,促进人体血液循环,因此促进脂肪组织代谢,燃烧分解,将多余脂肪消耗掉,进而有效瘦身,促进人体健康,具有保健功效。
具体实施方式
电气石,采用德通矿产品加工厂生产的粒径为4000目的电气石粉。
二氧化钛,采用南京天行新材料有限公司提供的型号为TTP-A10的纳米二氧化钛,粒径10nm。
渗透剂,采用江苏省海安石油化工厂生产的渗透剂JFC,渗透力≤60秒(0.1%水溶液)。
粘合剂,采用常州旭杰纺织材料有限公司生产的自交联聚丙烯酸酯粘合剂SHW。
氨基硅油,采用道康宁公司的OFX8040A。
吐温60,即失水山梨醇脂肪酸酯,采用江苏省海安石油化工厂生产的S-60。
聚丙烯酸钠,采用北京东方澳汉有限公司生产的SC-860。
蔗糖单硬脂酸酯,武汉拉那白医药化工有限公司生产。
苯乙烯(St),上海试剂一厂生产。
丙烯酸丁酯(BA),上海试剂一厂生产。
甲基丙烯酸甲酯(MMA),上海试剂一厂生产。
丙烯酸甲酯(MA),上海试剂一厂生产。
棉纤维,采用细棉绒,规格1.8dtex×30mm。
尼龙,采用诸暨市海超化纤丝经营部生产的70D/24F尼龙高弹丝。
氨纶,采用汕头市洪发色纱纺织有限公司生产的70D氨纶纤维。
远红外发射率测试:利用远红外发射率测试仪(EMS302远红外发射率测试仪,深圳市万科仪器有限公司)对面料的远红外发射率进行测试,控制其在温度为20℃,相对湿度为65%的恒温恒湿的环境内进行测试。将每种试样裁剪成直径约为7cm的圆(每个试样准备5块)后,在仪器上测试其在4-14μm的远红外发射率取平均值。
抗菌性能测试:采用国家标准GB/T20944.3-2008《面料抗菌性能的评价第3部分:振荡法》进行抗菌性定量测试,采用耐洗色牢度试验机洗涤方法,测试水洗30次后织物的抑菌率。所测试的微生物:大肠杆菌(Escherichia coli)AS.1.90;白色念珠菌(Candidaalbicance)AS.2.2086。
实施例1
瘦身保健女装的制备方法,包括以下步骤:
(1)制备整理液:按重量份称取渗透剂1份,粘合剂1份、电气石2份、二氧化钛2份、氨基硅油2份、六偏磷酸钠2份、水100份,将上述渗透剂、粘合剂、电气石、二氧化钛、氨基硅油、六偏磷酸钠依次加入到水中,在35℃以200转/分搅拌15分钟,得到整理液;
(2)浸渍:将面料在整理液中浸渍,浸渍时间20min,浸渍液温度35℃,浴比1:15,浸渍后将面料在95℃干燥20分钟,得到浸渍后的面料;
(3)洗涤烘干:将浸渍后的面料水洗2次,50℃干燥8小时,得到瘦身保健面料;
(4)裁剪缝制:将瘦身保健面料进行裁剪,并按常规女装制备工艺缝制得到瘦身保健女装。
所述面料由65wt%棉纤维、30wt%尼龙和5%氨纶制备而成。
所述面料由下述方法制备而成:将棉纤维与尼龙混纺成混纺纱线,再用混纺纱线与氨纶使用针织纬编大圆机进行针织织造,得到面料,平纹织物,面料克重为200克/平方米。
实施例2
瘦身保健女装的制备方法,包括以下步骤:
(1)制备整理液:按重量份称取渗透剂1份,粘合剂1份、电气石2份、改性二氧化钛2份、氨基硅油2份、六偏磷酸钠2份、水100份,将上述渗透剂、粘合剂、电气石、改性二氧化钛、氨基硅油、六偏磷酸钠依次加入到水中,在35℃以200转/分搅拌15分钟,得到整理液;
(2)浸渍:将面料在整理液中浸渍,浸渍时间20min,浸渍液温度35℃,浴比1:15,浸渍后将面料在95℃干燥20分钟,得到浸渍后的面料;
(3)洗涤烘干:将浸渍后的面料水洗2次,50℃干燥8小时,得到瘦身保健面料;
(4)裁剪缝制:将瘦身保健面料进行裁剪,并按常规女装制备工艺缝制得到瘦身保健女装。
所述改性二氧化钛由下述方法制备而成:将二氧化钛与去离子水按固液比1g:15mL混合,在25℃以400转/分搅拌15分钟,加入二氧化钛质量0.5%的蔗糖单硬脂酸酯,在25℃以400转/分搅拌50分钟,升温至70℃,加入二氧化钛质量30%的单体,以400转/分搅拌8分钟,再以1滴/秒的速度滴加二氧化钛质量1%的过硫酸铵,滴加完毕后在70℃以400转/分搅拌8小时,以4000转/分离心8分钟,沉淀在70℃干燥12小时,得到改性二氧化钛。
所述单体为苯乙烯和丙烯酸丁酯按质量比3:1的混合物。
所述面料由65wt%棉纤维、30wt%尼龙和5%氨纶制备而成。
所述面料由下述方法制备而成:将棉纤维与尼龙混纺成混纺纱线,再用混纺纱线与氨纶使用针织纬编大圆机进行针织织造,得到面料,平纹织物,面料克重为200克/平方米。
实施例3
与实施例2基本相同,区别仅在于:
所述改性二氧化钛由下述方法制备而成:将二氧化钛与去离子水按固液比1g:15mL混合,在25℃以400转/分搅拌15分钟,加入二氧化钛质量0.5%的蔗糖单硬脂酸酯,在25℃以400转/分搅拌50分钟,升温至70℃,加入二氧化钛质量30%的单体,以400转/分搅拌8分钟,再以1滴/秒的速度滴加二氧化钛质量1%的过硫酸铵,滴加完毕后在70℃以400转/分搅拌8小时,以4000转/分离心8分钟,沉淀在70℃干燥12小时,得到改性二氧化钛。
所述单体为苯乙烯和甲基丙烯酸甲酯按质量比3:1的混合物。
实施例4
与实施例2基本相同,区别仅在于:
所述改性二氧化钛由下述方法制备而成:将二氧化钛与去离子水按固液比1g:15mL混合,在25℃以400转/分搅拌15分钟,加入二氧化钛质量0.5%的蔗糖单硬脂酸酯,在25℃以400转/分搅拌50分钟,升温至70℃,加入二氧化钛质量30%的单体,以400转/分搅拌8分钟,再以1滴/秒的速度滴加二氧化钛质量1%的过硫酸铵,滴加完毕后在70℃以400转/分搅拌8小时,以4000转/分离心8分钟,沉淀在70℃干燥12小时,得到改性二氧化钛。
所述单体为苯乙烯和丙烯酸甲酯按质量比3:1的混合物。
对比例1
与实施例4基本相同,区别仅在于:
所述改性二氧化钛由下述方法制备而成:将二氧化钛与去离子水按固液比1g:15mL混合,在25℃以400转/分搅拌65分钟,升温至70℃,加入二氧化钛质量30%的单体,以400转/分搅拌8分钟,再以1滴/秒的速度滴加二氧化钛质量1%的过硫酸铵,滴加完毕后在70℃以400转/分搅拌8小时,以4000转/分离心8分钟,沉淀在70℃干燥12小时,得到改性二氧化钛。
所述单体为苯乙烯和丙烯酸甲酯按质量比3:1的混合物。
对比例2
与实施例4基本相同,区别仅在于:
所述改性二氧化钛由下述方法制备而成:将二氧化钛与去离子水按固液比1g:15mL混合,在25℃以400转/分搅拌15分钟,加入二氧化钛质量0.5%的十二烷基苯磺酸钠,在25℃以400转/分搅拌50分钟,升温至70℃,加入二氧化钛质量30%的单体,以400转/分搅拌8分钟,再以1滴/秒的速度滴加二氧化钛质量1%的过硫酸铵,滴加完毕后在70℃以400转/分搅拌8小时,以4000转/分离心8分钟,沉淀在70℃干燥12小时,得到改性二氧化钛。
所述单体为苯乙烯和丙烯酸甲酯按质量比3:1的混合物。
实施例5
瘦身保健女装的制备方法,包括以下步骤:
(1)制备整理液:按重量份称取渗透剂1份,粘合剂1份、改性电气石2份、改性二氧化钛2份、氨基硅油2份、六偏磷酸钠2份、水100份,将上述渗透剂、粘合剂、改性电气石、改性二氧化钛、氨基硅油、六偏磷酸钠依次加入到水中,在35℃以200转/分搅拌15分钟,得到整理液;
(2)浸渍:将面料在整理液中浸渍,浸渍时间20min,浸渍液温度35℃,浴比1:15,浸渍后将面料在95℃干燥20分钟,得到浸渍后的面料;
(3)洗涤烘干:将浸渍后的面料水洗2次,50℃干燥8小时,得到瘦身保健面料;
(4)裁剪缝制:将瘦身保健面料进行裁剪,并按常规女装制备工艺缝制得到瘦身保健女装。
所述改性电气石由下述方法制备而成:将电气石和水按固液比1g:8mL混合,在70℃以200转/分搅拌15分钟,加入电气石质量1%的改性剂,在70℃以200转/分继续搅拌2.5小时,以4000转/分离心8分钟,将下层沉淀在90℃干燥8小时,得到改性电气石。
所述改性剂为吐温60。
所述改性二氧化钛由下述方法制备而成:将二氧化钛与去离子水按固液比1g:15mL混合,在25℃以400转/分搅拌15分钟,加入二氧化钛质量0.5%的蔗糖单硬脂酸酯,在25℃以400转/分搅拌50分钟,升温至70℃,加入二氧化钛质量30%的单体,以400转/分搅拌8分钟,再以1滴/秒的速度滴加二氧化钛质量1%的过硫酸铵,滴加完毕后在70℃以400转/分搅拌8小时,以4000转/分离心8分钟,沉淀在70℃干燥12小时,得到改性二氧化钛。
所述单体为苯乙烯和丙烯酸甲酯按质量比3:1的混合物。
所述面料由65wt%棉纤维、30wt%尼龙和5%氨纶制备而成。
所述面料由下述方法制备而成:将棉纤维与尼龙混纺成混纺纱线,再用混纺纱线与氨纶使用针织纬编大圆机进行针织织造,得到面料,平纹织物,面料克重为200克/平方米。
得到的瘦身保健面料的远红外发射率测试结果:0.865;抗菌性能测试结果:大肠杆菌抑菌率95.8%,白色念珠菌抑菌率96.9%。
实施例6
瘦身保健女装的制备方法,包括以下步骤:
(1)制备整理液:按重量份称取渗透剂1份,粘合剂1份、改性电气石2份、改性二氧化钛2份、氨基硅油2份、六偏磷酸钠2份、水100份,将上述渗透剂、粘合剂、改性电气石、改性二氧化钛、氨基硅油、六偏磷酸钠依次加入到水中,在35℃以200转/分搅拌15分钟,得到整理液;
(2)浸渍:将面料在整理液中浸渍,浸渍时间20min,浸渍液温度35℃,浴比1:15,浸渍后将面料在95℃干燥20分钟,得到浸渍后的面料;
(3)洗涤烘干:将浸渍后的面料水洗2次,50℃干燥8小时,得到瘦身保健面料;
(4)裁剪缝制:将瘦身保健面料进行裁剪,并按常规女装制备工艺缝制得到瘦身保健女装。
所述改性电气石由下述方法制备而成:将电气石和水按固液比1g:8mL混合,在70℃以200转/分搅拌15分钟,加入电气石质量1%的改性剂,在70℃以200转/分继续搅拌2.5小时,以4000转/分离心8分钟,将下层沉淀在90℃干燥8小时,得到改性电气石。
所述改性剂为聚丙烯酸钠。
所述改性二氧化钛由下述方法制备而成:将二氧化钛与去离子水按固液比1g:15mL混合,在25℃以400转/分搅拌15分钟,加入二氧化钛质量0.5%的蔗糖单硬脂酸酯,在25℃以400转/分搅拌50分钟,升温至70℃,加入二氧化钛质量30%的单体,以400转/分搅拌8分钟,再以1滴/秒的速度滴加二氧化钛质量1%的过硫酸铵,滴加完毕后在70℃以400转/分搅拌8小时,以4000转/分离心8分钟,沉淀在70℃干燥12小时,得到改性二氧化钛。
所述单体为苯乙烯和丙烯酸甲酯按质量比3:1的混合物。
所述面料由65wt%棉纤维、30wt%尼龙和5%氨纶制备而成。
所述面料由下述方法制备而成:将棉纤维与尼龙混纺成混纺纱线,再用混纺纱线与氨纶使用针织纬编大圆机进行针织织造,得到面料,平纹织物,面料克重为200克/平方米。
得到的瘦身保健面料的远红外发射率测试结果:0.869;抗菌性能测试结果:大肠杆菌抑菌率96.5%,白色念珠菌抑菌率97.7%。
实施例7
瘦身保健女装的制备方法,包括以下步骤:
(1)制备整理液:按重量份称取渗透剂1份,粘合剂1份、改性电气石2份、改性二氧化钛2份、氨基硅油2份、六偏磷酸钠2份、水100份,将上述渗透剂、粘合剂、改性电气石、改性二氧化钛、氨基硅油、六偏磷酸钠依次加入到水中,在35℃以200转/分搅拌15分钟,得到整理液;
(2)浸渍:将面料在整理液中浸渍,浸渍时间20min,浸渍液温度35℃,浴比1:15,浸渍后将面料在95℃干燥20分钟,得到浸渍后的面料;
(3)洗涤烘干:将浸渍后的面料水洗2次,50℃干燥8小时,得到瘦身保健面料;
(4)裁剪缝制:将瘦身保健面料进行裁剪,并按常规女装制备工艺缝制得到瘦身保健女装。
所述改性电气石由下述方法制备而成:将电气石和水按固液比1g:8mL混合,在70℃以200转/分搅拌15分钟,加入电气石质量1%的改性剂,在70℃以200转/分继续搅拌2.5小时,以4000转/分离心8分钟,将下层沉淀在90℃干燥8小时,得到改性电气石。
所述改性剂为吐温60和聚丙烯酸钠的混合物,所述吐温60和聚丙烯酸铵的质量比为1:4。
所述改性二氧化钛由下述方法制备而成:将二氧化钛与去离子水按固液比1g:15mL混合,在25℃以400转/分搅拌15分钟,加入二氧化钛质量0.5%的蔗糖单硬脂酸酯,在25℃以400转/分搅拌50分钟,升温至70℃,加入二氧化钛质量30%的单体,以400转/分搅拌8分钟,再以1滴/秒的速度滴加二氧化钛质量1%的过硫酸铵,滴加完毕后在70℃以400转/分搅拌8小时,以4000转/分离心8分钟,沉淀在70℃干燥12小时,得到改性二氧化钛。
所述单体为苯乙烯和丙烯酸甲酯按质量比3:1的混合物。
所述面料由65wt%棉纤维、30wt%尼龙和5%氨纶制备而成。
所述面料由下述方法制备而成:将棉纤维与尼龙混纺成混纺纱线,再用混纺纱线与氨纶使用针织纬编大圆机进行针织织造,得到面料,平纹织物,面料克重为200克/平方米。
得到的瘦身保健面料的远红外发射率测试结果:0.886;抗菌性能测试结果:大肠杆菌抑菌率98.9%,白色念珠菌抑菌率99.3%。
测试例1
对实施例1-4和对比例1-2的步骤(3)制备的瘦身保健面料的远红外发射率进行测试。具体结果见表1。
表1:远红外发射率测试结果表
远红外发射率 | |
实施例1 | 0.829 |
实施例2 | 0.848 |
实施例3 | 0.837 |
实施例4 | 0.854 |
对比例1 | 0.842 |
对比例2 | 0.846 |
实施例2-4采用了改性二氧化钛,得到的面料的远红外发射率优于实施例1。这是因为二氧化钛为纳米级,不经改性的二氧化钛极易发生团聚或沉淀,经过改性的二氧化钛的表面被聚合物包覆,提高了在整理液的中的稳定性。
实施例2-4采用不同单体对二氧化钛进行改性,发现实施例2和实施例4的单体改性效果较好,尤其实施例4采用苯乙烯和丙烯酸甲酯按质量比3:1的混合物作为单体,改性效果较好。
对比例1在二氧化钛的制备过程中没有添加蔗糖单硬脂酸酯,对比例2将蔗糖单硬脂酸酯替换为十二烷基苯磺酸钠,得到的面料的远红外发射率均不如实施例4。
测试例2
对实施例1-4和对比例1-2的步骤(3)制备的瘦身保健面料的抗菌性能进行测试。具体结果见表2。
表2抗菌性能测试表
大肠杆菌抑菌率,% | 白色念珠菌抑菌率,% | |
实施例1 | 87.4 | 89.2 |
实施例2 | 93.2 | 94.7 |
实施例3 | 89.6 | 92.4 |
实施例4 | 94.6 | 95.6 |
对比例1 | 91.3 | 93.3 |
对比例2 | 92.4 | 93.8 |
Claims (5)
1.一种瘦身保健女装的制备方法,其特征在于,包括以下步骤:
(1)制备整理液:按重量份称取渗透剂0.2-2份,粘合剂0.2-2份、改性电气石1-3份、改性二氧化钛1-3份、氨基硅油1-3份、六偏磷酸钠1-3份、水95-105份,将上述渗透剂、粘合剂、改性电气石、改性二氧化钛、氨基硅油、六偏磷酸钠依次加入到水中,在30-40℃以100-300转/分搅拌10-20分钟,得到整理液;
(2)浸渍:将面料在整理液中浸渍,浸渍时间15-25min,浸渍液温度30-40℃,浴比1:(10-20),浸渍后将面料在90-100℃干燥20分钟,得到浸渍后的面料;
(3)洗涤烘干:将浸渍后的面料水洗1-3次,40-60℃干燥5-10小时,得到瘦身保健面料;
(4)裁剪缝制:将瘦身保健面料进行裁剪,并按常规女装制备工艺缝制得到瘦身保健女装;
所述改性二氧化钛由下述方法制备而成:将二氧化钛与去离子水按固液比1g:(10-20)mL混合,在20-30℃以300-600转/分搅拌10-20分钟,加入二氧化钛质量0.1-1%的蔗糖单硬脂酸酯,在20-30℃以300-600转/分搅拌40-60分钟,升温至65-75℃,加入二氧化钛质量25-35%的单体,以300-600转/分搅拌5-10分钟,再以1滴/秒的速度滴加二氧化钛质量0.5-1.5%的过硫酸铵,滴加完毕后在65-75℃以300-600转/分搅拌6-10小时,以3000-5000转/分离心5-10分钟,沉淀在65-75℃干燥10-15小时,得到改性二氧化钛;
所述单体为苯乙烯和丙烯酸甲酯按质量比(1-5):1的混合物。
2.如权利要求1所述的瘦身保健女装的制备方法,其特征在于,所述改性电气石由下述方法制备而成:将电气石和水按固液比1g:(5-10)mL混合,在65-75℃以100-300转/分搅拌10-20分钟,加入电气石质量0.2-2%的改性剂,在65-75℃以100-300转/分继续搅拌2-3小时,以3000-5000转/分离心5-10分钟,将下层沉淀在85-95℃干燥5-10小时,得到改性电气石。
3.如权利要求2所述的瘦身保健女装的制备方法,其特征在于,所述改性剂为吐温60和聚丙烯酸钠的混合物,所述吐温60和聚丙烯酸铵的质量比为1:(1-5)。
4.根据权利要求1所述的瘦身保健女装的制备方法,其特征在于,所述面料由60-70wt%棉纤维、25-35wt%尼龙和3-7%氨纶制备而成。
5.一种瘦身保健女装,其特征在于,采用权利要求1-4中任一项方法制备而成。