CN108030592B - 一种易撕医用胶布 - Google Patents
一种易撕医用胶布 Download PDFInfo
- Publication number
- CN108030592B CN108030592B CN201711348654.3A CN201711348654A CN108030592B CN 108030592 B CN108030592 B CN 108030592B CN 201711348654 A CN201711348654 A CN 201711348654A CN 108030592 B CN108030592 B CN 108030592B
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- mixture
- rubber
- drying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开一种易撕医用胶布，以无纺布为基底材料，首先将无纺布漂白处理，通过装有改性液的上浆机的滚筒轧液，进行锡林预烘，再通过烘道进行干燥，得到改性无纺布；接着制备胶浆，用炼胶机把片状天然橡胶块制成萝卜丝状或者薄片状，然后浸于汽油和甲苯的混合液中充分溶胀，加入三硬脂酸甘油酯和古马隆树脂，搅拌均匀，再加入各种助剂，即可得到橡胶型的压敏胶浆，最后用涂布机将压敏胶浆涂到改性基布上，然后进行干燥收卷等处理，即可制得成品；本发明制出的易撕医用胶布，不仅容易撕开，撕开时病人不会产生疼痛感，而且经过长时间粘附后，依然具有很好的皮肤粘附性，不会自动与皮肤相分离，保证了该胶布能起到固定作用，发挥其应有的作用。
Description
技术领域
本发明涉及一种医用胶布，更具体的说是涉及一种易撕医用胶布。
背景技术
胶布是一种有粘性的塑料制品胶布，常见的胶布包括有医用胶布，绝缘胶布等，其中医用胶布具有良好的透气性能，且无毒无刺激性，性质比较温和，有良好的粘性，常用于固定注射针头、包扎等等；但现有的医用胶布从成人身上揭下时，往往都会感受到一阵“撕裂的痛楚”，若然这种胶布从宝宝娇嫩的肌肤上揭下时，很可能会损伤皮肤，还可能会引起医疗投诉和纠纷事件时，给医疗单位造成一定的负面影响。
在现有技术中,也存在很多容易撕开的胶布,如申请号为CN201510781909.X的中国专利一种新型医用胶布，这样的胶布透气性好,绿色环保，而且贴在人体上后容易撕开，不会对人体产生一点疼痛感。
但现有的易撕开医用胶布随着时间变化，粘性会有大幅度的降低，等到一定时间后，由于胶布粘性过小，它会自动与人体相脱离，就无法起到固定作用，常常需要多次粘贴，既费时又费力，甚至影响治疗结果。
发明内容
针对现有技术存在的不足，本发明的目的在于提供一种易撕医用胶布，该医用胶布黏贴在人体上后，很容易撕开，而且在较长时间内保持较强的粘性，不会自动与人体相脱离。
为实现上述目的，本发明提供了如下技术方案：一种易撕医用胶布，包括下列重量份组成：
无纺布：90份；
炭黑：2份；
氧化镁：2份；
偶联剂：3份；
交联剂：5份；
乳化剂：1份；
增溶剂：1份；
抗菌剂：3份；
增塑剂:2份；
防水剂：1份；
防老剂：2份；
稳定剂：5份；
改性工作液：10-30份；
所述稳定剂为双[3-(三乙氧基硅烷)丙基]胺、硬脂酸镁、十二烷基硫酸钠、月桂亚氨基二丙酸二钠和亚磷酸三(2-乙基己基)酯的混合物，其质量比为3:1:2:2:2；
所述改性工作液包括下述重量份物质组成：
丙烯酸酯共聚乳液：15份；
叔戊醇铋：2份；
N,N-二丁基-1,3-丙二胺：3份；
羟甲基纤维素钠：1份；
氧化锌：2份；
水：50份。
所述偶联剂为3-氨基丙基三乙氧基硅烷。
所述交联剂为过氧化二异丙苯。
所述乳化剂为二(2-乙基己基)胺。
所述增溶剂为月桂醇聚氧乙烯醚和环氧乙烷的混合物，其质量比为1:1。
所述抗菌剂为单硬脂酸甘油酯、山梨酸钾和聚维酮碘的混合物，其质量比为2:1:2。
所述增塑剂为邻苯二甲酸二辛脂。
所述防水剂为(3,3,3-三氟丙基)三甲氧基硅烷。
所述防老剂为N-N'-二苯基-对苯二胺和4-叔丁基邻苯二酚的混合物，其质量比为1:2。
一种易撕医用胶布的制备方法：
第一步：布材处理，首先将无纺布进行漂白处理得到漂布，然后将改性工作液倒入上浆机的浆槽内，控制轧点压力为3500～4500公斤，使上述漂布以每分钟8～18米速度通过滚筒轧液，轧液率为60～80％，然后经过锡林90～110°预烘约半分钟，经扩幅机扩幅至原幅宽，入烘道，在170～195℃下通过烘道，干燥时间约为1-5分钟，即得到用作基布的改性无纺布；
第二步，制备胶浆，将20-50份片状生天然橡胶块经炼胶机轧制成萝卜丝状或薄片状，浸于30-80份质量比为2:1的汽油和甲苯的混合液中使之溶胀充分，得到生胶溶胀物，然后加入3-5份作为软化剂的三硬脂酸甘油酯，再加入5-20份古马隆树脂，搅拌5-20min，然后依次加入炭黑、氧化镁、偶联剂、交联剂、乳化剂、增溶剂、抗菌剂、增塑剂、防水剂、防老剂和稳定剂，继续搅拌30-60min，从而得到橡胶型压敏胶浆；
第三步，胶浆涂覆，将第二步中得到的胶浆放置在涂布机涂布滚筒前的胶浆槽内，控制滚筒间隙为0.1～0.25mm，使基布缓缓通过滚筒，经干燥、收卷、切断制得成品。
本发明的有益效果：一种易撕医用胶布，以无纺布作为基底材料，首先将无纺布进行漂白处理得到漂布，然后让漂布通过装有改性工作液的上浆机的滚筒轧液，再进行锡林预烘，然后通过烘道进行干燥，即可得到改性无纺布；接着制备胶浆，用炼胶机把片状的生的天然橡胶块制成萝卜丝状或者薄片状，然后浸于汽油和甲苯的混合液中，汽油和甲苯的质量为2：1，这样配置而成的混合液能使生橡胶充分的溶胀，溶胀完全后，加入三硬脂酸甘油酯作为软化剂和古马隆树脂作为增粘剂，古马隆树脂除了起到增粘作用，还能起到塑化、软化和补强的作用，先搅拌一定时间，再加入各种助剂，即可得到橡胶型的压敏胶浆，最后用涂布机将压敏胶浆涂到改性基布上，涂层的厚度为0.1-0.25mm，然后进行干燥收卷等处理，即可制得成品；本发明制出的易撕医用胶布，不仅容易撕开，撕开时病人不会产生疼痛感，而且在经过3小时的粘附后，依然具有很好的皮肤粘附性，不会自动与皮肤相分离，保证了该胶布能起到固定作用，发挥其应有的作用。
作为本发明的创新点之一，进行漂白过得无纺布用改性液处理，改性工作液以水为溶剂，通过加入丙烯酸乳液、叔戊醇铋、N,N-二丁基-1,3-丙二胺、羟甲基纤维素钠和氧化锌这几种物质，在这几种物质的共同作用下能对无纺布进行很好的改性处理，使得最终制得的易撕医用胶布容易撕开，不会使病人产生疼痛感，更不会对皮肤造成损伤；另一个创新点是稳定剂选择了双[3-(三乙氧基硅烷)丙基]胺、硬脂酸镁、十二烷基硫酸钠、月桂亚氨基二丙酸二钠和亚磷酸三(2-乙基己基)酯这5种物质；在这些物质的相互协调下，保证了易撕医用胶布具有较好的粘性，而且粘性随时间的变化较小，即使在皮肤上粘附3小时后，粘性依然较强，能起到很好的固定作用。
抗菌剂选择了单硬脂酸甘油酯、山梨酸钾和聚维酮碘这3种物质，在这3种物质的共同作用下，制得的易撕医用胶带具有很好的抗菌性，减少对病人二次伤害的可能性，更加安全健康；防老剂上选择了N-N'-二苯基-对苯二胺和4-叔丁基邻苯二酚这2种物质，这2种物质的共同作用下，能起到很好的抗老化作用，保证本发明不容易老化，能放置很长时间，便于生产、运输以及存放。
具体实施方式
实施例1：一种易撕医用胶布，包括下列重量份组成：
无纺布：90份；
炭黑：2份；
氧化镁：2份；
偶联剂：3份；
交联剂：5份；
乳化剂：1份；
增溶剂：1份；
抗菌剂：3份；
增塑剂:2份；
防水剂：1份；
防老剂：2份；
稳定剂：5份；
改性工作液：10-30份；
所述稳定剂为双[3-(三乙氧基硅烷)丙基]胺、硬脂酸镁、十二烷基硫酸钠、月桂亚氨基二丙酸二钠和亚磷酸三(2-乙基己基)酯的混合物，其质量比为3:1:2:2:2；
所述改性工作液包括下述重量份物质组成：
丙烯酸酯共聚乳液：15份；
叔戊醇铋：2份；
N,N-二丁基-1,3-丙二胺：3份；
羟甲基纤维素钠：1份；
氧化锌：2份；
水：50份。
所述偶联剂为3-氨基丙基三乙氧基硅烷。
所述交联剂为过氧化二异丙苯。
所述乳化剂为二(2-乙基己基)胺。
所述增溶剂为月桂醇聚氧乙烯醚和环氧乙烷的混合物，其质量比为1:1。
所述抗菌剂为单硬脂酸甘油酯、山梨酸钾和聚维酮碘的混合物，其质量比为2:1:2。
所述增塑剂为邻苯二甲酸二辛脂。
所述防水剂为(3,3,3-三氟丙基)三甲氧基硅烷。
所述防老剂为N-N'-二苯基-对苯二胺和4-叔丁基邻苯二酚的混合物，其质量比为1:2。
一种易撕医用胶布的制备方法：
第一步：布材处理，首先将无纺布进行漂白处理得到漂布，然后将改性工作液倒入上浆机的浆槽内，控制轧点压力为3500～4500公斤，使上述漂布以每分钟8～18米速度通过滚筒轧液，轧液率为60～80％，然后经过锡林90～110°预烘约半分钟，经扩幅机扩幅至原幅宽，入烘道，在170～195℃下通过烘道，干燥时间约为1-5分钟，即得到用作基布的改性无纺布；
第二步，制备胶浆，将20-50份片状生天然橡胶块经炼胶机轧制成萝卜丝状或薄片状，浸于30-80份质量比为2:1的汽油和甲苯的混合液中使之溶胀充分，得到生胶溶胀物，然后加入3-5份作为软化剂的三硬脂酸甘油酯，再加入5-20份古马隆树脂，搅拌5-20min，然后依次加入炭黑、氧化镁、偶联剂、交联剂、乳化剂、增溶剂、抗菌剂、增塑剂、防水剂、防老剂和稳定剂，继续搅拌30-60min，从而得到橡胶型压敏胶浆；
第三步，胶浆涂覆，将第二步中得到的胶浆放置在涂布机涂布滚筒前的胶浆槽内，控制滚筒间隙为0.1～0.25mm，使基布缓缓通过滚筒，经干燥、收卷、切断制得成品。
对比例1：一种易撕医用胶布，包括下列重量份组成：
一种易撕医用胶布，包括下列重量份组成：
无纺布：90份；
炭黑：2份；
氧化镁：2份；
偶联剂：3份；
交联剂：5份；
乳化剂：1份；
增溶剂：1份；
抗菌剂：3份；
增塑剂:2份；
防水剂：1份；
防老剂：2份；
稳定剂：5份；
改性工作液：10-30份；
所述稳定剂为硬脂酸镁、十二烷基硫酸钠、月桂亚氨基二丙酸二钠和亚磷酸三(2-乙基己基)酯的混合物，其质量比为1:2:2:2；
所述改性工作液包括下述重量份物质组成：
丙烯酸酯共聚乳液：15份；
叔戊醇铋：2份；
N,N-二丁基-1,3-丙二胺：3份；
羟甲基纤维素钠：1份；
氧化锌：2份；
水：50份。
所述偶联剂为3-氨基丙基三乙氧基硅烷。
所述交联剂为过氧化二异丙苯。
所述乳化剂为二(2-乙基己基)胺。
所述增溶剂为月桂醇聚氧乙烯醚和环氧乙烷的混合物，其质量比为1:1。
所述抗菌剂为单硬脂酸甘油酯、山梨酸钾和聚维酮碘的混合物，其质量比为2:1:2。
所述增塑剂为邻苯二甲酸二辛脂。
所述防水剂为(3,3,3-三氟丙基)三甲氧基硅烷。
所述防老剂为N-N'-二苯基-对苯二胺和4-叔丁基邻苯二酚的混合物，其质量比为1:2。
一种易撕医用胶布的制备方法：
第一步：布材处理，首先将无纺布进行漂白处理得到漂布，然后将改性工作液倒入上浆机的浆槽内，控制轧点压力为3500～4500公斤，使上述漂布以每分钟8～18米速度通过滚筒轧液，轧液率为60～80％，然后经过锡林90～110°预烘约半分钟，经扩幅机扩幅至原幅宽，入烘道，在170～195℃下通过烘道，干燥时间约为1-5分钟，即得到用作基布的改性无纺布；
第二步，制备胶浆，将20-50份片状生天然橡胶块经炼胶机轧制成萝卜丝状或薄片状，浸于30-80份质量比为2:1的汽油和甲苯的混合液中使之溶胀充分，得到生胶溶胀物，然后加入3-5份作为软化剂的三硬脂酸甘油酯，再加入5-20份古马隆树脂，搅拌5-20min，然后依次加入炭黑、氧化镁、偶联剂、交联剂、乳化剂、增溶剂、抗菌剂、增塑剂、防水剂、防老剂和稳定剂，继续搅拌30-60min，从而得到橡胶型压敏胶浆；
第三步，胶浆涂覆，将第二步中得到的胶浆放置在涂布机涂布滚筒前的胶浆槽内，控制滚筒间隙为0.1～0.25mm，使基布缓缓通过滚筒，经干燥、收卷、切断制得成品。
对比例2：一种易撕医用胶布，包括下列重量份组成：
无纺布：90份；
炭黑：2份；
氧化镁：2份；
偶联剂：3份；
交联剂：5份；
乳化剂：1份；
增溶剂：1份；
抗菌剂：3份；
增塑剂:2份；
防水剂：1份；
防老剂：2份；
稳定剂：5份；
改性工作液：10-30份；
所述稳定剂为双[3-(三乙氧基硅烷)丙基]胺、月桂亚氨基二丙酸二钠和亚磷酸三(2-乙基己基)酯的混合物，其质量比为3:2:2；
所述改性工作液包括下述重量份物质组成：
丙烯酸酯共聚乳液：15份；
叔戊醇铋：2份；
N,N-二丁基-1,3-丙二胺：3份；
羟甲基纤维素钠：1份；
氧化锌：2份；
水：50份。
所述偶联剂为3-氨基丙基三乙氧基硅烷。
所述交联剂为过氧化二异丙苯。
所述乳化剂为二(2-乙基己基)胺。
所述增溶剂为月桂醇聚氧乙烯醚和环氧乙烷的混合物，其质量比为1:1。
所述抗菌剂为单硬脂酸甘油酯、山梨酸钾和聚维酮碘的混合物，其质量比为2:1:2。
所述增塑剂为邻苯二甲酸二辛脂。
所述防水剂为(3,3,3-三氟丙基)三甲氧基硅烷。
所述防老剂为N-N'-二苯基-对苯二胺和4-叔丁基邻苯二酚的混合物，其质量比为1:2。
一种易撕医用胶布的制备方法：
第一步：布材处理，首先将无纺布进行漂白处理得到漂布，然后将改性工作液倒入上浆机的浆槽内，控制轧点压力为3500～4500公斤，使上述漂布以每分钟8～18米速度通过滚筒轧液，轧液率为60～80％，然后经过锡林90～110°预烘约半分钟，经扩幅机扩幅至原幅宽，入烘道，在170～195℃下通过烘道，干燥时间约为1-5分钟，即得到用作基布的改性无纺布；
第二步，制备胶浆，将20-50份片状生天然橡胶块经炼胶机轧制成萝卜丝状或薄片状，浸于30-80份质量比为2:1的汽油和甲苯的混合液中使之溶胀充分，得到生胶溶胀物，然后加入3-5份作为软化剂的三硬脂酸甘油酯，再加入5-20份古马隆树脂，搅拌5-20min，然后依次加入炭黑、氧化镁、偶联剂、交联剂、乳化剂、增溶剂、抗菌剂、增塑剂、防水剂、防老剂和稳定剂，继续搅拌30-60min，从而得到橡胶型压敏胶浆；
第三步，胶浆涂覆，将第二步中得到的胶浆放置在涂布机涂布滚筒前的胶浆槽内，控制滚筒间隙为0.1～0.25mm，使基布缓缓通过滚筒，经干燥、收卷、切断制得成品。
对比例3：一种易撕医用胶布，包括下列重量份组成：
无纺布：90份；
炭黑：2份；
氧化镁：2份；
偶联剂：3份；
交联剂：5份；
乳化剂：1份；
增溶剂：1份；
抗菌剂：3份；
增塑剂:2份；
防水剂：1份；
防老剂：2份；
稳定剂：5份；
改性工作液：10-30份；
所述稳定剂为双[3-(三乙氧基硅烷)丙基]胺、硬脂酸镁、十二烷基硫酸钠的混合物，其质量比为3:1:2；
所述改性工作液包括下述重量份物质组成：
丙烯酸酯共聚乳液：15份；
叔戊醇铋：2份；
N,N-二丁基-1,3-丙二胺：3份；
羟甲基纤维素钠：1份；
氧化锌：2份；
水：50份。
所述偶联剂为3-氨基丙基三乙氧基硅烷。
所述交联剂为过氧化二异丙苯。
所述乳化剂为二(2-乙基己基)胺。
所述增溶剂为月桂醇聚氧乙烯醚和环氧乙烷的混合物，其质量比为1:1。
所述抗菌剂为单硬脂酸甘油酯、山梨酸钾和聚维酮碘的混合物，其质量比为2:1:2。
所述增塑剂为邻苯二甲酸二辛脂。
所述防水剂为(3,3,3-三氟丙基)三甲氧基硅烷。
所述防老剂为N-N'-二苯基-对苯二胺和4-叔丁基邻苯二酚的混合物，其质量比为1:2。
一种易撕医用胶布的制备方法：
第一步：布材处理，首先将无纺布进行漂白处理得到漂布，然后将改性工作液倒入上浆机的浆槽内，控制轧点压力为3500～4500公斤，使上述漂布以每分钟8～18米速度通过滚筒轧液，轧液率为60～80％，然后经过锡林90～110°预烘约半分钟，经扩幅机扩幅至原幅宽，入烘道，在170～195℃下通过烘道，干燥时间约为1-5分钟，即得到用作基布的改性无纺布；
第二步，制备胶浆，将20-50份片状生天然橡胶块经炼胶机轧制成萝卜丝状或薄片状，浸于30-80份质量比为2:1的汽油和甲苯的混合液中使之溶胀充分，得到生胶溶胀物，然后加入3-5份作为软化剂的三硬脂酸甘油酯，再加入5-20份古马隆树脂，搅拌5-20min，然后依次加入炭黑、氧化镁、偶联剂、交联剂、乳化剂、增溶剂、抗菌剂、增塑剂、防水剂、防老剂和稳定剂，继续搅拌30-60min，从而得到橡胶型压敏胶浆；
第三步，胶浆涂覆，将第二步中得到的胶浆放置在涂布机涂布滚筒前的胶浆槽内，控制滚筒间隙为0.1～0.25mm，使基布缓缓通过滚筒，经干燥、收卷、切断制得成品。
对比例4：一种易撕医用胶布，包括下列重量份组成：
无纺布：90份；
炭黑：2份；
氧化镁：2份；
偶联剂：3份；
交联剂：5份；
乳化剂：1份；
增溶剂：1份；
抗菌剂：3份；
增塑剂:2份；
防水剂：1份；
防老剂：2份；
稳定剂：5份；
改性工作液：10-30份；
所述稳定剂为双[3-(三乙氧基硅烷)丙基]胺、硬脂酸镁、十二烷基硫酸钠、月桂亚氨基二丙酸二钠和亚磷酸三(2-乙基己基)酯的混合物，其质量比为3:1:2:2:2；
所述改性工作液包括下述重量份物质组成：
丙烯酸酯共聚乳液：15份；
N,N-二丁基-1,3-丙二胺：3份；
氧化锌：2份；
水：50份。
所述偶联剂为3-氨基丙基三乙氧基硅烷。
所述交联剂为过氧化二异丙苯。
所述乳化剂为二(2-乙基己基)胺。
所述增溶剂为月桂醇聚氧乙烯醚和环氧乙烷的混合物，其质量比为1:1。
所述抗菌剂为单硬脂酸甘油酯、山梨酸钾和聚维酮碘的混合物，其质量比为2:1:2。
所述增塑剂为邻苯二甲酸二辛脂。
所述防水剂为(3,3,3-三氟丙基)三甲氧基硅烷。
所述防老剂为N-N'-二苯基-对苯二胺和4-叔丁基邻苯二酚的混合物，其质量比为1:2。
一种易撕医用胶布的制备方法：
第一步：布材处理，首先将无纺布进行漂白处理得到漂布，然后将改性工作液倒入上浆机的浆槽内，控制轧点压力为3500～4500公斤，使上述漂布以每分钟8～18米速度通过滚筒轧液，轧液率为60～80％，然后经过锡林90～110°预烘约半分钟，经扩幅机扩幅至原幅宽，入烘道，在170～195℃下通过烘道，干燥时间约为1-5分钟，即得到用作基布的改性无纺布；
第二步，制备胶浆，将20-50份片状生天然橡胶块经炼胶机轧制成萝卜丝状或薄片状，浸于30-80份质量比为2:1的汽油和甲苯的混合液中使之溶胀充分，得到生胶溶胀物，然后加入3-5份作为软化剂的三硬脂酸甘油酯，再加入5-20份古马隆树脂，搅拌5-20min，然后依次加入炭黑、氧化镁、偶联剂、交联剂、乳化剂、增溶剂、抗菌剂、增塑剂、防水剂、防老剂和稳定剂，继续搅拌30-60min，从而得到橡胶型压敏胶浆；
第三步，胶浆涂覆，将第二步中得到的胶浆放置在涂布机涂布滚筒前的胶浆槽内，控制滚筒间隙为0.1～0.25mm，使基布缓缓通过滚筒，经干燥、收卷、切断制得成品。
对比例5：一种易撕医用胶布，包括下列重量份组成：
无纺布：90份；
炭黑：2份；
氧化镁：2份；
偶联剂：3份；
交联剂：5份；
乳化剂：1份；
增溶剂：1份；
抗菌剂：3份；
增塑剂:2份；
防水剂：1份；
防老剂：2份；
稳定剂：5份；
改性工作液：10-30份；
所述稳定剂为双[3-(三乙氧基硅烷)丙基]胺、硬脂酸镁、十二烷基硫酸钠、月桂亚氨基二丙酸二钠和亚磷酸三(2-乙基己基)酯的混合物，其质量比为3:1:2:2:2；
所述改性工作液包括下述重量份物质组成：
丙烯酸酯共聚乳液：15份；
叔戊醇铋：2份；
羟甲基纤维素钠：1份；
水：50份。
所述偶联剂为3-氨基丙基三乙氧基硅烷。
所述交联剂为过氧化二异丙苯。
所述乳化剂为二(2-乙基己基)胺。
所述增溶剂为月桂醇聚氧乙烯醚和环氧乙烷的混合物，其质量比为1:1。
所述抗菌剂为单硬脂酸甘油酯、山梨酸钾和聚维酮碘的混合物，其质量比为2:1:2。
所述增塑剂为邻苯二甲酸二辛脂。
所述防水剂为(3,3,3-三氟丙基)三甲氧基硅烷。
所述防老剂为N-N'-二苯基-对苯二胺和4-叔丁基邻苯二酚的混合物，其质量比为1:2。
一种易撕医用胶布的制备方法：
第一步：布材处理，首先将无纺布进行漂白处理得到漂布，然后将改性工作液倒入上浆机的浆槽内，控制轧点压力为3500～4500公斤，使上述漂布以每分钟8～18米速度通过滚筒轧液，轧液率为60～80％，然后经过锡林90～110°预烘约半分钟，经扩幅机扩幅至原幅宽，入烘道，在170～195℃下通过烘道，干燥时间约为1-5分钟，即得到用作基布的改性无纺布；
第二步，制备胶浆，将20-50份片状生天然橡胶块经炼胶机轧制成萝卜丝状或薄片状，浸于30-80份质量比为2:1的汽油和甲苯的混合液中使之溶胀充分，得到生胶溶胀物，然后加入3-5份作为软化剂的三硬脂酸甘油酯，再加入5-20份古马隆树脂，搅拌5-20min，然后依次加入炭黑、氧化镁、偶联剂、交联剂、乳化剂、增溶剂、抗菌剂、增塑剂、防水剂、防老剂和稳定剂，继续搅拌30-60min，从而得到橡胶型压敏胶浆；
第三步，胶浆涂覆，将第二步中得到的胶浆放置在涂布机涂布滚筒前的胶浆槽内，控制滚筒间隙为0.1～0.25mm，使基布缓缓通过滚筒，经干燥、收卷、切断制得成品。
对比例6：由青岛海氏海诺医疗用品有限公司生产的医用胶布。
对比例7：按照申请号为CN201510781909.X的中国专利制备的一种新型医用胶布。
将实施例1和对比例1-7制得的试样切成宽15mm、长40mm大小的胶带粘附到志愿者的前臂内侧的皮肤表面上。从粘附起3小时后，评价皮肤粘附性、剥离时的痛感情况。
180°剥离强度测试：将实施1和对比例1-7按GB2792-81标准制成相应试样，采用LANGUANG电子剥离试验机测量。
本发明的易撕医用胶布，以无纺布作为基底材料，首先将无纺布进行漂白处理得到漂布，然后让漂布通过装有改性工作液的上浆机的滚筒轧液，再进行锡林预烘，然后通过烘道进行干燥，即可得到改性无纺布；接着制备胶浆，用炼胶机把片状的生的天然橡胶块制成萝卜丝状或者薄片状，然后浸于汽油和甲苯的混合液中，汽油和甲苯的质量为2：1，这样配置而成的混合液能使生橡胶充分的溶胀，溶胀完全后，加入三硬脂酸甘油酯作为软化剂和古马隆树脂作为增粘剂，古马隆树脂除了起到增粘作用，还能起到塑化、软化和补强的作用，先搅拌一定时间，再加入各种助剂，即可得到橡胶型的压敏胶浆，最后用涂布机将压敏胶浆涂到改性基布上，涂层的厚度为0.1-0.25mm，然后进行干燥收卷等处理，即可制得成品；本发明制出的易撕医用胶布，不仅容易撕开，撕开时病人不会产生疼痛感，而且在经过3小时的粘附后，依然具有很好的皮肤粘附性，不会自动与皮肤相分离，保证了该胶布能起到固定作用，发挥其应有的作用。
作为本发明的创新点之一，进行漂白过得无纺布用改性液处理，改性工作液以水为溶剂，通过加入丙烯酸乳液、叔戊醇铋、N,N-二丁基-1,3-丙二胺、羟甲基纤维素钠和氧化锌这几种物质，在这几种物质的共同作用下能对无纺布进行很好的改性处理，使得最终制得的易撕医用胶布容易撕开，不会使病人产生疼痛感，更不会对皮肤造成损伤；另一个创新点是稳定剂选择了双[3-(三乙氧基硅烷)丙基]胺、硬脂酸镁、十二烷基硫酸钠、月桂亚氨基二丙酸二钠和亚磷酸三(2-乙基己基)酯这5种物质；在这些物质的相互协调下，保证了易撕医用胶布具有较好的粘性，而且粘性随时间的变化较小，即使在皮肤上粘附3小时后，粘性依然较强，能起到很好的固定作用。
抗菌剂选择了单硬脂酸甘油酯、山梨酸钾和聚维酮碘这3种物质，在这3种物质的共同作用下，制得的易撕医用胶布具有很好的抗菌性，减少对病人二次伤害的可能性，更加安全健康；防老剂上选择了N-N'-二苯基-对苯二胺和4-叔丁基邻苯二酚这2种物质，这2种物质的共同作用下，能起到很好的抗老化作用，保证本发明不容易老化，能放置很长时间，便于生产、运输以及存放。
以上所述仅是本发明的优选实施方式，本发明的保护范围并不仅局限于上述实施例，凡属于本发明思路下的技术方案均属于本发明的保护范围。应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理前提下的若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。
Claims (1)
1.一种易撕医用胶布，其特征在于：包括下列重量份组成：
无纺布：90 份；
炭黑：2 份；
氧化镁：2 份；
偶联剂：3 份；
交联剂：5 份；
乳化剂：1 份；
增溶剂：1 份；
抗菌剂：3 份；
增塑剂：2 份；
防水剂：1 份；
防老剂：2 份；
稳定剂：5 份；
改性工作液：10-30 份；
所述偶联剂为3-氨基丙基三乙氧基硅烷；
所述交联剂为过氧化二异丙苯；
所述乳化剂为二(2-乙基己基)胺；
所述增溶剂为月桂醇聚氧乙烯醚和环氧乙烷的混合物，其质量比为 1:1；
所述抗菌剂为单硬脂酸甘油酯、山梨酸钾和聚维酮碘的混合物，其质量比为 2:1:2；
所述增塑剂为邻苯二甲酸二辛脂；
所述防水剂为(3,3,3-三氟丙基)三甲氧基硅烷；
所述防老剂为N-N'-二苯基-对苯二胺和 4-叔丁基邻苯二酚的混合物，其质量比为 1:2；
所述稳定剂为双[3-(三乙氧基硅烷)丙基]胺、硬脂酸镁、十二烷基硫酸钠、 月桂亚氨基二丙酸二钠和亚磷酸三 (2- 乙基己基) 酯的混合物， 其质量比为 3:1:2:2:2；
所述改性工作液包括下述重量份物质组成：
丙烯酸酯共聚乳液：15 份；
叔戊醇铋：2 份；
N,N-二丁基-1,3-丙二胺：3 份；
羟甲基纤维素钠：1 份；
氧化锌：2 份；
水：50 份；
所述易撕医用胶布的制备方法包括步骤：
第一步：布材处理，首先将无纺布进行漂白处理得到漂布，然后将改性工作液倒入上浆机的浆槽内，控制轧点压力为 3500～4500 公斤，使上述漂布以每分钟 8～18 米速度通过滚筒轧液，轧液率为 60～80%，然后经过锡林 90～110℃预烘半分钟，经扩幅机扩幅至原幅宽，入烘道，在170～195℃下通过烘道，干燥时间为 1-5 分钟，即得到用作基布的改性无纺布；
第二步，制备胶浆，将 20-50 份片状生天然橡胶块经炼胶机轧制成萝卜丝状或薄片状，浸于 30-80 份质量比为 2:1 的汽油和甲苯的混合液中使之溶胀充分，得到生胶溶胀物，然后加入 3-5 份作为软化剂的三硬脂酸甘油酯，再加入 5-20 份古马隆树脂，搅拌 5-20min，然后依次加入炭黑、氧化镁、偶联剂、交联剂、 乳化剂、增溶剂、抗菌剂、增塑剂、防水剂、防老剂和稳定剂，继续搅拌 30-60min， 从而得到橡胶型压敏胶浆；
第三步，胶浆涂覆，将第二步中得到的橡胶型压敏胶浆放置在涂布机涂布滚筒前的胶浆槽内，控制滚筒间隙为 0.1～0.25mm，使基布缓缓通过滚筒，经干燥、收卷、切断制得成品。