CN107962658A - A kind of production method of the three ability teabowls with a cover to fit together perfectly - Google Patents
A kind of production method of the three ability teabowls with a cover to fit together perfectly Download PDFInfo
- Publication number
- CN107962658A CN107962658A CN201711263277.3A CN201711263277A CN107962658A CN 107962658 A CN107962658 A CN 107962658A CN 201711263277 A CN201711263277 A CN 201711263277A CN 107962658 A CN107962658 A CN 107962658A
- Authority
- CN
- China
- Prior art keywords
- teacup
- base substrate
- ability
- cover
- teabowls
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention discloses a kind of production method of the three ability teabowls with a cover to fit together perfectly, and three ability teabowls with a cover include teacup, tea lid and saucer, manufacturing process and comprise the following steps：Teacup the rim of a bowl opening and the rim of a bowl radian are adjusted by throwing, processing time is 5 to 10 minutes；After base substrate reaches partial desiccation state, teacup thickness is repaired to 2.5~3mm according to global shape irony Fettling knife；Base substrate is put into electrical kiln and carries out 800 DEG C of heating, 2~3 hours of used time, allows kiln temperature natural cooling after heating, color modification is carried out to base substrate after taking out base substrate；The lower edge of tea lid is uniformly wiped with round sponge body, makes to form an arc convex on the outside of its edge, the radius R5 of arc convex is 1.4mm, and radian Q5 is 80 °；Teacup, tea lid and saucer are put into 1320 DEG C of hot environment to be fired.The present invention can be achieved to reach air-tight state between teacup and tea lid, can effectively keep tea perfume when making tea here, lift original tea flavour entrance mouthfeel.
Description
Technical field
The present invention relates to teabowl with a cover technical field, more particularly, to a kind of production method of the three ability teabowls with a cover to fit together perfectly.
Background technology
Teabowl with a cover be have in one kind lid, under have support, in have Han nationality's tea set of bowl.Also known as " three ability bowls ", " three ability cups ", Gai Wei
My god, support be ground, bowl be people, the meaning of people from world sum in secret." saucer " is also known as " tea ship ".Cover bowl tea, must use boiling hot boiling water punching one
Lower bowl, is then placed in tealeaves and is filled with water capping, and the time for the tea that oozes is determined by tealeaves value volume and range of product, about 20 seconds to 3 minutes.Clear
It is prevailing to use teabowl with a cover between Yongzheng year.Existing teabowl with a cover, is unable to reach the air-tight state to fit together perfectly, makes between teacup and tea lid
Tea perfume is obtained to be not easy to retain, it is necessary to improve.
The content of the invention
It is an object of the invention to overcome above-mentioned the deficiencies in the prior art, there is provided a kind of system of the three ability teabowls with a cover to fit together perfectly
Make method.
To achieve these goals, the present invention adopts the following technical scheme that：
A kind of production method of the three ability teabowls with a cover to fit together perfectly, the three ability teabowl with a cover include teacup, tea lid and saucer, make
Process comprises the following steps：
The first step, the rim of a bowl openings of sizes and the rim of a bowl radian of teacup are adjusted by throwing, and processing time is 5 to 10 minutes,
The size d2 of the rim of a bowl is 99mm after adjustment, and the exterior radius R3 of the rim of a bowl is 27mm, and radian Q3 is 55 °, the inner wall radius R4 of the rim of a bowl
For 27.4mm, radian Q4 is 58 °, while it is 82mm to control the lower end size d1 of tea lid, and the lower end outer wall radius R1 of tea lid is
44mm, radian Q1 are 45 °, and the lower end inner wall radius R2 of tea lid is 56mm, and radian Q2 is 95 °；
Second step：After base substrate reaches partial desiccation state, teacup thickness is repaired to 2.5 according to global shape irony Fettling knife
~3mm；
3rd step：Base substrate is put into electrical kiln and carries out 8000C heating, 2~3 hours of used time, after heating, allow kiln temperature certainly
It is right to cool down, glaze is soaked with reference to outside, glaze is swung in inside, part fills out the enameling method of glaze to base substrate progress color modification after taking-up base substrate；
4th step：Uniformly wiped with round sponge body for the lower edge of tea lid, make to form one on the outside of its edge
A arc convex, the radius R5 of the arc convex is 1.4mm, and radian Q5 is 80 °；
5th step：Teacup, tea lid and saucer are put into 1320 DEG C of hot environment to be fired.
The condition that base substrate reaches partial desiccation state is set to be in the second step：Open air has sunlight to continue direct projection, mean temperature
Higher than 30 DEG C, continue 12 it is small when.
The condition that base substrate reaches partial desiccation state is set to be in the second step：In the environment of 26 DEG C~36 DEG C, indoor nothing
Continue in the case of wind 24 it is small when.
The condition that base substrate reaches partial desiccation state is set to be in the second step：0 DEG C~25 DEG C in the environment of, it is indoor calm
In the case of continue 48 it is small when.
The water content of the cavernous body is 30%~40%.
In the sintering procedure of 5th step, using oxidation aluminium backing, left-hand thread pad burning is carried out to teacup and tea lid.
The component of the base substrate includes the high clay wash that mass percent is 95%, three oxidations that mass percent is 3%
Two aluminium powders and the paper pulp that mass percent is 2%.
The beneficial effects of the invention are as follows：By the dimensional fits between tea lid and teacup, arc convex is set to prop up teacup
The rim of a bowl inner wall is poured into after tea, lifts tea Gai Keling, it can be achieved that reach the air-tight state to fit together perfectly between tea lid and teacup
Teacup lifts at the same time not to drop.Tea perfume can effectively be kept here by sampling tea when people is made tea with this teabowl with a cover, lift original tea flavour entrance mouthfeel.
Brief description of the drawings
Fig. 1 is the structure diagram of the present invention；
Fig. 2 is the structure diagram of the tea lid of the present invention；
Fig. 3 is the structure diagram of the teacup of the present invention.
In figure：Teacup 1, tea lid 2, saucer 3.
Embodiment
The invention will be further described with reference to the accompanying drawings and detailed description：
As shown in FIG. 1 to 3, a kind of production method of the three ability teabowls with a cover to fit together perfectly, the three ability teabowl with a cover include teacup
1st, tea lid 2 and saucer 3, tea lid 2 are covered in 1 upper port of teacup, and teacup 1 is held in the upper surface center fitting of saucer 3, and (these are existing
Have technology, do not describe in detail), manufacturing process comprises the following steps：
The first step, the rim of a bowl openings of sizes and the rim of a bowl radian of teacup 1 are adjusted by throwing, and processing time is 5 to 10 minutes,
The size d2 of the rim of a bowl is 99mm after adjustment, and the exterior radius R3 of the rim of a bowl is 27mm, and radian Q3 is 55 °, the inner wall radius R4 of the rim of a bowl
For 27.4mm, radian Q4 is 58 °, while it is 82mm to control the lower end size d1 of tea lid 2, and the lower end outer wall radius R1 of tea lid 2 is
44mm, radian Q1 are 45 °, and the lower end inner wall radius R2 of tea lid 2 is 56mm, and radian Q2 is 95 °；
Second step：After base substrate reaches partial desiccation state, 1 thickness of teacup is repaired extremely according to global shape irony Fettling knife
2.5~3mm；Can there is sunlight to continue direct projection outdoors, mean temperature is higher than 30 DEG C, continue 12 it is small when.Can also be 26
DEG C~36 DEG C in the environment of, it is indoor it is calm in the case of continue 24 it is small when.0 DEG C~25 DEG C be can also be in the environment of, indoor nothing
Continue in the case of wind 48 it is small when.Should avoid less than 0 DEG C has the drying of regimen condition, and mud mixture can influence body drying as frozen
Firmness afterwards, is unfavorable for post-processing, the dry time will be different according to actual external temperature wind-force difference, half-dried
State is not required to excessively accurately judge, as long as reaching certain degree of hardness, such as repaired biscuit again after the dry moistening that excessively can also soak.
3rd step：Base substrate is put into electrical kiln and carries out 800 DEG C of heating, 2~3 hours of used time, after heating, allow kiln temperature certainly
It is right to cool down, glaze is soaked with reference to outside, glaze is swung in inside, part fills out the enameling method of glaze to base substrate progress color modification after taking-up base substrate；
4th step：Uniformly wiped with round sponge body for the lower edge of tea lid 2, make to form one on the outside of its edge
A arc convex, the radius R5 of the arc convex is 1.4mm, and radian Q5 is 80 °；The water content of the cavernous body for 30%~
40%, i.e., mild crush makes cavernous body not drip voluntarily when stretching after cavernous body water suction.The teacup 1 and tea lid 2 of the present invention
Combined with Radiotherapy postpones, and the rim of a bowl inner wall of teacup 1 is propped up by arc convex, realizes both fit together perfectly, is filled at this time in teacup 1
Lift tea lid 2 after water, can reach teacup 1 and tea lid 2 lifts and unseparated effect together.
5th step：The hot environment that teacup 1, tea lid 2 and saucer 3 are put into 13200C is fired.
In the sintering procedure of 5th step, using oxidation aluminium backing, left-hand thread pad burning is carried out to teacup 1 and tea lid 2, can
Prevent the deformation of teacup 1 and tea lid 2.
The component of the base substrate includes the high clay wash that mass percent is 95%, three oxidations that mass percent is 3%
Two aluminium powders and the paper pulp that mass percent is 2%.The injection of aluminium oxide powder in order to increase fire in base substrate hardness, reduce
Burn till rear deformation rate；The addition of paper pulp can reduce burn till that the quality of rear totality makes teabowl with a cover be affectedly bashful feel lifting.
The foregoing is merely presently preferred embodiments of the present invention, is not intended to limit the invention, it is all the present invention spirit and
Within principle, any modification, equivalent replacement, improvement and so on, should all be included in the protection scope of the present invention.
Claims (7)
1. a kind of production method of the three ability teabowls with a cover to fit together perfectly, the three ability teabowl with a cover include teacup, tea lid and saucer, its feature
It is, manufacturing process comprises the following steps：
The first step, the rim of a bowl openings of sizes and the rim of a bowl radian of teacup are adjusted by throwing, and processing time is 5 to 10 minutes, adjustment
The size d2 of the rim of a bowl is 99mm afterwards, and the exterior radius R3 of the rim of a bowl is 27mm, and radian Q3 is 55 °, and the inner wall radius R4 of the rim of a bowl is
27.4mm, radian Q4 are 58 °, while it is 82mm to control the lower end size d1 of tea lid, and the lower end outer wall radius R1 of tea lid is 44mm,
Radian Q1 is 45 °, and the lower end inner wall radius R2 of tea lid is 56mm, and radian Q2 is 95 °；
Second step：After base substrate reaches partial desiccation state, according to global shape with irony Fettling knife repair teacup thickness to 2.5~
3mm；
3rd step：Base substrate is put into electrical kiln and carries out 800 DEG C of heating, 2~3 hours of used time, after heating, makes kiln temperature naturally cold
But, glaze is soaked with reference to outside, glaze is swung in inside, part fills out the enameling method of glaze to base substrate progress color modification after taking-up base substrate；
4th step：Uniformly wiped with round sponge body for the lower edge of tea lid, make to form an arc on the outside of its edge
Shape is raised, and the radius R5 of the arc convex is 1.4mm, and radian Q5 is 80 °；
5th step：Teacup, tea lid and saucer are put into 1320 DEG C of hot environment to be fired.
2. a kind of production method of the three ability teabowls with a cover to fit together perfectly as claimed in claim 1, it is characterised in that in the second step
The condition that base substrate reaches partial desiccation state is set to be：Open air has sunlight to continue direct projection, and mean temperature is higher than 30 DEG C, continue 12 it is small when.
3. a kind of production method of the three ability teabowls with a cover to fit together perfectly as claimed in claim 1, it is characterised in that in the second step
The condition that base substrate reaches partial desiccation state is set to be：In the environment of 26 DEG C~36 DEG C, it is indoor it is calm in the case of continue 24 it is small when.
4. a kind of production method of the three ability teabowls with a cover to fit together perfectly as claimed in claim 1, it is characterised in that in the second step
The condition that base substrate reaches partial desiccation state is set to be：0 DEG C~25 DEG C in the environment of, it is indoor it is calm in the case of continue 48 it is small when.
A kind of 5. production method of the three ability teabowls with a cover to fit together perfectly as described in Claims 1 to 4 any one, it is characterised in that
The water content of the cavernous body is 30%~40%.
6. a kind of production method of the three ability teabowls with a cover to fit together perfectly as claimed in claim 5, it is characterised in that the 5th step
In sintering procedure, using oxidation aluminium backing, left-hand thread pad burning is carried out to teacup and tea lid.
A kind of 7. production method of the three ability teabowls with a cover to fit together perfectly as claimed in claim 6, it is characterised in that the base substrate into
Point include aluminium oxide powder that high clay wash, mass percent that mass percent is 95% are 3% and mass percent is
2% paper pulp.