CN101288542A - Pottery-porcelain double-layer congou tea set and preparation method thereof - Google Patents
Pottery-porcelain double-layer congou tea set and preparation method thereof Download PDFInfo
- Publication number
- CN101288542A CN101288542A CNA2008100283912A CN200810028391A CN101288542A CN 101288542 A CN101288542 A CN 101288542A CN A2008100283912 A CNA2008100283912 A CN A2008100283912A CN 200810028391 A CN200810028391 A CN 200810028391A CN 101288542 A CN101288542 A CN 101288542A
- Authority
- CN
- China
- Prior art keywords
- tea
- teacup
- layer
- pottery
- porcelain
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a congou tea set with a pottery layer and a porcelain layer and a preparation method thereof. The tea set comprises a covered bowl, a tea board, a tea board bracket and a plurality of cups; wherein, the covered bowl consists of a tea cover, a tea bowl and a tea bracket; the tea cups and the tea bowl take on two-layered structure, an outer layer is white porcelain, an inner layer is purple sand ceramics, and port edges of the inner layer and the outer layer are bonded into a whole; the middle of the tea board is engraved with a through hole. The preparation comprises the following technological steps: selecting purple sand petuntse for manufacturing inner-layer green bodies of the tea board, the tea cover and the tea bowl, glazing and baking; selecting high-temperature white petuntse for manufacturing outer-layer green bodies of the tray, the tea bracket, the tea cups and the tea bowl, glazing and baking; nesting and bonding the inner layers and the outer layers of the tea cups and the tea bowl and braking. The tea set prepared by the invention has good heat preservation and heat insulation effect; the hands can not be burnt when making tea or drinking tea; by skillfully combining the purple sand with the white porcelain, the texture and the color has intense comparison and the lasting appeal is boundless, wherein, the purple sand is polished and refined, which not only absorbs tea aroma, but contains a plurality of beneficial elements, thus having healthcare function on human body; a triangular basic pattern is adopted, the unique pattern not only inherits the lasting appeal of the traditional congou tea set, but also increases fashion elements, thus having the advantages of enjoyment performance and collection value, etc.
Description
Technical field
The present invention relates to a kind of apparatus and preparation method thereof of drinking tea, relate in particular to a kind of pottery, porcelain double-layer tea set time and preparation method thereof.
Background technology
In occasions such as family or friend's party, particularly in Guangdong of China, southern provinces and cities such as Fujian, a lot of people have the custom of drinking " kung fu tea ", the tea set that generally uses when drinking " kung fu tea " is generally made by pottery, its shape also mostly is circular single layer structure.Used teacup and teacup are single layer structure owing to make tea and have tea, and insulation and effect of heat insulation are relatively poor, when making tea or have tea, often scald very much hand because of tea, and pottery does not have the health-care effect to human body yet simultaneously.Along with the raising of people's living standard, more and more higher to the requirement of material and cultural life, the dull circular tea set of tradition also incompatibility people is pursued the demand of material and cultural life.
Summary of the invention
For overcoming above-mentioned deficiency, the object of the present invention is to provide a kind of tea set and preparation method thereof, this tea set insulation and effect of heat insulation are better, do not scald hand when making tea or having tea, and also have the health-care effect to human body simultaneously; And the moulding uniqueness had both passed on the charm of traditional time of tea set, had increased the fashion element again, and was elegant and graceful.
The technical solution adopted for the present invention to solve the technical problems is: a kind of pottery, porcelain double-layer tea set time, comprise teabowl with a cover, tea tray, tea tray holder and some teacups, teabowl with a cover is made up of tea lid, teacup and saucer, described teacup, teacup are double-decker, skin is a ceramic whiteware, internal layer is an electrothermal dark-red pottery, outside anti-limit, internal layer oral area edge, and the anti-limit of internal layer and outer field peristoma adopt cadmium piece glaze bonding and be bonded into one through burning till; Described tea tray, tea lid are made for electrothermal dark-red pottery, and pallet, saucer are that ceramic whiteware is made; The outer bottom of teacup is provided with an aperture, and the middle part of tea tray is carved with through hole.
Described teacup, teabowl with a cover, tea tray and tea tray holder structure triangular in shape.
The through hole of the middle part engraving of described tea tray can be " tea " or other literal, pattern.
The preparation method of above-mentioned pottery, porcelain double-layer tea set time, its processing step comprises:
(1) select the clay internal layer base substrate of making tea tray, Cha Gai, teacup and teacup of boccaro porcelain for use, glazing, burn till, firing temperature is 1050~1120 ℃, and firing time is 6~7 hours, and all the other are by the common process flow operations of making the electrothermal dark-red pottery device;
(2) select the clay outer base substrate of making pallet, saucer, teacup and teacup of high temperature ceramic whiteware for use, glazing, burn till, firing temperature is 1300~1350 ℃, and firing time is 12~13 hours, and all the other are by the common process flow operations of making the ceramic whiteware device;
(3) with the inside and outside layer fit of teacup, teacup, select for use special cadmium piece glaze that inside and outside layer is bonded together;
(4) above-mentioned steps (3) is bonding teacup, teacup burn till in 780~820 ℃ temperature, and firing time is 1.5~2 hours.
Use the tea set that the present invention makes, because teacup and teacup adopt double-decker, insulation and effect of heat insulation are better, do not scald hand when making tea or having tea, and adopt boccaro to combine with the ingenious of ceramic whiteware simultaneously, and quality and Se Cai contrast are strong, implication of endless appeal; The gentle grace of boccaro can absorb tea perfume (or spice), and contains the element of multiple beneficial, and is with health role to human body; And adopting leg-of-mutton basic styling, the moulding uniqueness had both passed on the charm of traditional time of tea set, had increased the fashion element again, and was elegant and graceful, had advantages such as sight and reserve value.
Description of drawings
Fig. 1 is the schematic perspective view of pottery of the present invention, porcelain double-layer tea set time;
Fig. 2 is the cutaway view of the teacup of pottery of the present invention, porcelain double-layer tea set time;
Fig. 3 is the cutaway view of the teabowl with a cover of pottery of the present invention, porcelain double-layer tea set time.
The specific embodiment
Embodiment 1: a kind of pottery, porcelain double-layer tea set time, comprise teabowl with a cover, tea tray 1, tea tray holder 2 and four teacups 3 of structure triangular in shape, and teabowl with a cover is made up of tea lid 4, teacup 5 and saucer 6; Described teacup 3, teacup 5 are double-decker, teacup outer 31 is made for ceramic whiteware, internal layer 32 is made for electrothermal dark-red pottery, teacup outer 51 is made for ceramic whiteware, internal layer 52 is made for electrothermal dark-red pottery, outside anti-limit 33, the oral area edge of teacup 3 internal layers 32, outside anti-limit 53, teacup 5 internal layers 52 oral area edges, the anti-limit 33 of the internal layer of teacup 3 and teacup 5 and 53 adopt cadmium piece glaze 7 bonding and be bonded into one through burning till with teacup 3 and teacup 5 outer field peristomas 311 and 511 respectively; Described tea tray 1, tea lid 4 is made for electrothermal dark-red pottery, and tea tray holder 2, saucer 6 are made for ceramic whiteware; Skin 31 bottoms of teacup 3 are provided with an aperture 34, and the middle part of tea tray 1 is carved with the through hole 11 of " tea " font.
The preparation method of above-mentioned pottery, porcelain double-layer tea set time, its processing step comprises:
(1) select the clay internal layer base substrate 32 and 52 of making tea tray 1, tea lid 4, teacup 3 and teacup 5 of boccaro porcelain for use, glazing, burn till, firing temperature is 1100 ℃, and firing time is 7 hours, all the other technological process operations routinely;
(2) select the clay outer base substrate 31 and 51 of making tea tray holder 2, saucer 6, teacup 3 and teacup 5 of high temperature ceramic whiteware for use, glazing, burn till, firing temperature is 1350 ℃, and firing time is 13 hours, all the other technological process operations routinely;
(3) with the inside and outside layer fit of teacup 3, teacup 5, select for use special cadmium piece glaze that inside and outside layer is bonded together;
(4) above-mentioned steps (3) is bonding teacup 3, teacup 5 burn till in 800 ℃ temperature, and firing time is 2 hours.
Claims (4)
1, a kind of pottery, porcelain double-layer tea set time, comprise teabowl with a cover, tea tray, tea tray holder and some teacups, teabowl with a cover is made up of tea lid, teacup and saucer, it is characterized in that: described teacup, teacup are double-decker, skin is a ceramic whiteware, internal layer is an electrothermal dark-red pottery, outside anti-limit, internal layer oral area edge, and the anti-limit of internal layer and outer field peristoma adopt cadmium piece glaze bonding and be bonded into one through burning till; Described tea tray, tea lid are made for electrothermal dark-red pottery, and pallet, saucer are that ceramic whiteware is made; The outer bottom of teacup is provided with an aperture, and the middle part of tea tray is carved with through hole.
2, pottery according to claim 1, porcelain double-layer tea set time is characterized in that: described teacup, teabowl with a cover, tea tray and tea tray holder structure triangular in shape.
3, pottery according to claim 1, porcelain double-layer tea set time is characterized in that: the through hole of the middle part engraving of described tea tray can be " tea " or other literal, pattern form.
4, the preparation method of a kind of pottery, porcelain double-layer tea set time, it is characterized in that: its processing step comprises:
(1) select the clay internal layer base substrate of making tea tray, Cha Gai, teacup and teacup of boccaro porcelain for use, glazing, burn till, firing temperature is 1050~1120 ℃, and firing time is 6~7 hours, and all the other are by the common process flow operations of making the electrothermal dark-red pottery device;
(2) select the clay outer base substrate of making pallet, saucer, teacup and teacup of high temperature ceramic whiteware for use, glazing, burn till, firing temperature is 1300~1350 ℃, and firing time is 12~13 hours, and all the other are by the common process flow operations of making the ceramic whiteware device;
(3) with the inside and outside layer fit of teacup, teacup, select for use special cadmium piece glaze that inside and outside layer is bonded together;
(4) above-mentioned steps (3) is bonding teacup, teacup burn till in 780~820 ℃ temperature, and firing time is 1.5~2 hours.