CN107954600A - Crackle crystal glaze and preparation method thereof - Google Patents
Crackle crystal glaze and preparation method thereof Download PDFInfo
- Publication number
- CN107954600A CN107954600A CN201711263823.3A CN201711263823A CN107954600A CN 107954600 A CN107954600 A CN 107954600A CN 201711263823 A CN201711263823 A CN 201711263823A CN 107954600 A CN107954600 A CN 107954600A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- crackle
- crystal
- component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of crackle crystal glaze and preparation method thereof, the component of glaze used in crackle crystal glaze and each component mass parts are as follows：50 parts~60 parts of clues mud；6 parts~8 parts of calcite；6 parts~8 parts of zinc oxide；10 parts~12 parts of lithium carbonate；3 parts~5 parts of kaolin；10 parts~12 parts of zirconium silicate.The crackle crystal glaze of the present invention is transparent, and has superfine greasy crackle, has bubble in crackle, has the crystal of white, glaze body surface face is smooth, and artistry is stronger.
Description
Technical field
The present invention relates to a kind of crackle crystal glaze and preparation method thereof.
Background technology
At present, occur crystalline glaze on existing market, but its glaze paint is relatively simple, artistry is not strong enough.
The content of the invention
The technical problems to be solved by the invention are the defects of overcoming the prior art, there is provided a kind of crackle crystal glaze, it is in
Transparence, has superfine greasy crackle, has bubble in crackle, has the crystal of white, glaze body surface face is smooth, and artistry is stronger.
In order to solve the above technical problems, the technical scheme is that：A kind of crackle crystal glaze, glaze used in it
Component and each component mass parts it is as follows：50 parts~60 parts of clues mud；6 parts~8 parts of calcite；6 parts~8 parts of zinc oxide；Carbonic acid
10 parts~12 parts of lithium；3 parts~5 parts of kaolin；10 parts~12 parts of zirconium silicate.
Present invention also offers a kind of preparation method of crackle crystal glaze, the step of method in contain：
A) stock up according to each component and each component mass parts：
B) according to 1.6 ︰ 0.6 of mass ratio=1 ︰ of glaze material ︰ ball ︰ water, when wet ball grinding 12~14 is small, the glaze mistake after ball milling
After 200 mesh sieves, 53~54 Baume concentration are modulated into, take clean base substrate leaching glaze,
C) base substrate for having soaked glaze is put into down-draft kiln to form to fire in 1270 DEG C of oxidizing atmospheres.
After employing above-mentioned technical proposal, the research and development of the glaze are by base glaze coefficient of expansion constantly regulate, and combine knot
Brilliant glaze handicraft, constantly continuous cross-beta, adjustment, the glaze are transparent, have superfine greasy crackle, have bubble in crackle, have
The crystal of white, glaze body surface face is smooth, which is the stronger glaze of artistry, is adapted to domestic market, meets the aesthetic of domestic correspondent.
Embodiment
In order that the present invention can be more clearly and readily understood, below according to specific embodiment, the present invention is made into
One step is described in detail.
Embodiment one
A kind of crackle crystal glaze, the component of glaze and each component mass parts are as follows used in it：50 parts of clues mud；Fang Xie
6 parts of stone；6 parts of zinc oxide；10 parts of lithium carbonate；3 parts of kaolin；10 parts of zirconium silicate.
Contain in a kind of the step of preparation method of crackle crystal glaze, method：
A) stock up according to each component and each component mass parts：
B) according to 1.6 ︰ 0.6 of mass ratio=1 ︰ of glaze material ︰ ball ︰ water, when wet ball grinding 12 is small, the glaze after ball milling crosses 200
After mesh sieve, 53~54 Baume concentration are modulated into, take clean base substrate leaching glaze,
C) base substrate for having soaked glaze is put into down-draft kiln to form to fire in 1270 DEG C of oxidizing atmospheres.
Embodiment two
A kind of crackle crystal glaze, the component of glaze and each component mass parts are as follows used in it：60 parts of clues mud；Fang Xie
8 parts of stone；8 parts of zinc oxide；12 parts of lithium carbonate；5 parts of kaolin；12 parts of zirconium silicate.
Contain in a kind of the step of preparation method of crackle crystal glaze, method：
A) stock up according to each component and each component mass parts：
B) according to 1.6 ︰ 0.6 of mass ratio=1 ︰ of glaze material ︰ ball ︰ water, when wet ball grinding 14 is small, the glaze after ball milling crosses 200
After mesh sieve, 53~54 Baume concentration are modulated into, take clean base substrate leaching glaze,
C) base substrate for having soaked glaze is put into down-draft kiln to form to fire in 1270 DEG C of oxidizing atmospheres.
Embodiment three
A kind of crackle crystal glaze, the component of glaze and each component mass parts are as follows used in it：55 parts of clues mud；Fang Xie
7 parts of stone；7 parts of zinc oxide；11 parts of lithium carbonate；4 parts of kaolin；11 parts of zirconium silicate.
Contain in a kind of the step of preparation method of crackle crystal glaze, method：
A) stock up according to each component and each component mass parts：
B) according to 1.6 ︰ 0.6 of mass ratio=1 ︰ of glaze material ︰ ball ︰ water, when wet ball grinding 13 is small, the glaze after ball milling crosses 200
After mesh sieve, 53~54 Baume concentration are modulated into, take clean base substrate leaching glaze,
C) base substrate for having soaked glaze is put into down-draft kiln to form to fire in 1270 DEG C of oxidizing atmospheres.
Crackle crystal glaze prepared by three above embodiment, process have bubble, have it has been observed that crackle is fine and smooth in crackle
The crystal of white, glaze body surface face is smooth, and artistry is stronger, meets the requirements.
Particular embodiments described above, has carried out the purpose of the present invention, technical solution and beneficial effect further in detail
Describe in detail it is bright, it should be understood that the foregoing is merely the present invention specific embodiment, be not intended to limit the invention, it is all
Within the spirit and principles in the present invention, any modification, equivalent substitution, improvement and etc. done, should be included in the guarantor of the present invention
Within the scope of shield.
Claims (2)
- A kind of 1. crackle crystal glaze, it is characterised in that：The component of glaze and each component mass parts are as follows used in it：Clues mud 50 parts~60 parts；6 parts~8 parts of calcite；6 parts~8 parts of zinc oxide；10 parts~12 parts of lithium carbonate；3 parts~5 parts of kaolin；Silicic acid 10 parts~12 parts of zirconium.
- 2. a kind of preparation method of crackle crystal glaze as claimed in claim 1, it is characterised in that contain in the step of method：A) stock up according to each component and each component mass parts：B) according to 1.6 ︰ 0.6 of mass ratio=1 ︰ of glaze material ︰ ball ︰ water, when wet ball grinding 12~14 is small, the glaze after ball milling crosses 200 After mesh sieve, 53~54 Baume concentration are modulated into, take clean base substrate leaching glaze,C) base substrate for having soaked glaze is put into down-draft kiln to form to fire in 1270 DEG C of oxidizing atmospheres.