CN109912207A - Brown bottom white coral coloured glaze and preparation method thereof - Google Patents
Brown bottom white coral coloured glaze and preparation method thereof Download PDFInfo
- Publication number
- CN109912207A CN109912207A CN201711328096.4A CN201711328096A CN109912207A CN 109912207 A CN109912207 A CN 109912207A CN 201711328096 A CN201711328096 A CN 201711328096A CN 109912207 A CN109912207 A CN 109912207A
- Authority
- CN
- China
- Prior art keywords
- parts
- component
- coloured glaze
- bottom white
- glaze
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of brown bottom white coral coloured glaze, the palm fibre bottom white coral coloured glaze ground coat enamel each component and each component quality are as follows: 35 parts~42 parts of feldspar;14 parts~23 parts of dolomite;10 parts~12 parts of Jiepai clay;3 parts~6 parts of zinc oxide;8 parts~13 parts of spodumene;7 parts~11 parts of kaolin;13 parts~16 parts of iron oxide;5 parts~7 parts of manganese carbonate;The each component and each component content of overglaze are as follows: 30 parts~35 parts of potassium feldspar;10 parts~12 parts of calcite;14 parts~16 parts of dolomite;4 parts~6 parts of Guizhou clay;4 parts~5 parts of lithium carbonate;15 parts~16 parts of zinc oxide;8 parts~13 parts of titanium oxide;5 parts~10 parts of zirconium silicate.The palm fibre bottom white coral coloured glaze is to flow the raw coralliform reaction effect of movable property on ground coat enamel by overglaze at high temperature, which fires in 1270 DEG C of down-draft kiln, deep to be liked by customers.
Description
Technical field
The invention discloses a kind of brown bottom white coral coloured glazes and preparation method thereof.
Background technique
Currently, all kinds of furniture of life, tableware for daily use is all as enthusiasm of the people to ceramic process demand constantly increases
Gradually level off to more special fairly simple beautiful ceramic, which is by overglaze at high temperature
The raw coralliform reaction effect of movable property is flowed on ground coat enamel, which fires in 1270 DEG C of down-draft kiln, deep by customers
Like.
Summary of the invention
The technical problem to be solved by the present invention is to overcome the deficiencies of existing technologies, glazing effect is improved, keeps it more beautiful
It sees, the invention discloses a kind of brown bottom white coral coloured glaze, the palm fibre bottom white coral coloured glaze ground coat enamel each component and each component quality are as follows:
35 parts~42 parts of feldspar;14 parts~23 parts of dolomite;10 parts~12 parts of Jiepai clay;3 parts~6 parts of zinc oxide;Spodumene 8 parts~13
Part;7 parts~11 parts of kaolin;13 parts~16 parts of iron oxide;5 parts~7 parts of manganese carbonate;The each component and each component content of overglaze are such as
Under: 30 parts~35 parts of potassium feldspar;10 parts~12 parts of calcite;14 parts~16 parts of dolomite;4 parts~6 parts of Guizhou clay;Lithium carbonate 4
Part~5 parts;15 parts~16 parts of zinc oxide;8 parts~13 parts of titanium oxide;5 parts~10 parts of zirconium silicate.
The step of brown bottom white coral coloured glaze production method, this method, is as follows:
A) brown bottom white coral coloured glaze ground coat enamel, overglaze are stocked up according to each component and each component mass parts;
B) 1.6 ︰ 0.7 of You Liao ︰ Qiu ︰ water=1 ︰, wet ball grinding 15~17 hours, after the glaze after ball milling crosses 200 meshes, bottom
It is stand-by that glaze is modulated into 51~53 Baume concentration;Overglaze is modulated into 53~55 Baume concentration;
C) clean green body is taken, is dried after upper ground coat enamel, then the overglaze on interior glaze;
D) above-mentioned palm fibre bottom white coral coloured glaze of carrying out is burnt into 1270 DEG C of down-draft kiln.
After above-mentioned technical proposal, by the control of mobile performance, reaction effect to brown bottom white coral coloured glaze, make
It is more suitable for volume production, deep to be liked by users.
Specific embodiment
In order that the present invention can be more clearly and readily understood, below according to specific embodiment, to the present invention make into
One step detailed description.
Embodiment one:
The invention discloses a kind of brown bottom white coral coloured glaze, the palm fibre bottom white coral coloured glaze ground coat enamel each component and each component quality
It is as follows: 35 parts~42 parts of feldspar;14 parts~23 parts of dolomite;10 parts~12 parts of Jiepai clay;3 parts~6 parts of zinc oxide;Spodumene 8
Part~13 parts;7 parts~11 parts of kaolin;13 parts~16 parts of iron oxide;5 parts~7 parts of manganese carbonate;The each component and each component of overglaze
Content is as follows: 30 parts~35 parts of potassium feldspar;10 parts~12 parts of calcite;14 parts~16 parts of dolomite;4 parts~6 parts of Guizhou clay;
7 parts~9 parts of lithium carbonate;10 parts~13 parts of zinc oxide;5 parts~10 parts of titanium oxide;5 parts~10 parts of zirconium silicate.
The step of brown bottom white coral coloured glaze production method, this method, is as follows:
A) brown bottom white coral coloured glaze ground coat enamel, overglaze are stocked up according to each component and each component mass parts;
B) 1.6 ︰ 0.7 of You Liao ︰ Qiu ︰ water=1 ︰, wet ball grinding 15~17 hours, after the glaze after ball milling crosses 200 meshes, bottom
It is stand-by that glaze is modulated into 51~53 Baume concentration;Overglaze is modulated into 53~55 Baume concentration;
C) clean green body is taken, is dried after upper ground coat enamel, then the overglaze on interior glaze;
D) above-mentioned palm fibre bottom white coral coloured glaze of carrying out is burnt into 1270 DEG C of down-draft kiln.
Embodiment two:
The invention discloses a kind of brown bottom white coral coloured glaze, the palm fibre bottom white coral coloured glaze ground coat enamel each component and each component quality
It is as follows: 35 parts~42 parts of feldspar;14 parts~23 parts of dolomite;10 parts~12 parts of Jiepai clay;3 parts~6 parts of zinc oxide;Spodumene 8
Part~13 parts;7 parts~11 parts of kaolin;13 parts~16 parts of iron oxide;5 parts~7 parts of manganese carbonate;The each component and each component of overglaze
Content is as follows: 30 parts~35 parts of potassium feldspar;10 parts~12 parts of calcite;14 parts~16 parts of dolomite;4 parts~6 parts of Guizhou clay;
4 parts~5 parts of lithium carbonate;15 parts~16 parts of zinc oxide;8 parts~13 parts of titanium oxide;5 parts~10 parts of zirconium silicate.
The step of brown bottom white coral coloured glaze production method, this method, is as follows:
A) brown bottom white coral coloured glaze ground coat enamel, overglaze are stocked up according to each component and each component mass parts;
B) 1.6 ︰ 0.7 of You Liao ︰ Qiu ︰ water=1 ︰, wet ball grinding 15~17 hours, after the glaze after ball milling crosses 200 meshes, bottom
It is stand-by that glaze is modulated into 51~53 Baume concentration;Overglaze is modulated into 53~55 Baume concentration;
C) clean green body is taken, is dried after upper ground coat enamel, then the overglaze on interior glaze;
D) above-mentioned palm fibre bottom white coral coloured glaze of carrying out is burnt into 1270 DEG C of down-draft kiln.
Embodiment three:
The invention discloses a kind of brown bottom white coral coloured glaze, the palm fibre bottom white coral coloured glaze ground coat enamel each component and each component quality
It is as follows: 35 parts~42 parts of feldspar;14 parts~23 parts of dolomite;10 parts~12 parts of Jiepai clay;3 parts~6 parts of zinc oxide;Spodumene 8
Part~13 parts;7 parts~11 parts of kaolin;13 parts~16 parts of iron oxide;5 parts~7 parts of manganese carbonate;The each component and each component of overglaze
Content is as follows: 38 parts~43 parts of potassium feldspar;10 parts~12 parts of calcite;14 parts~16 parts of dolomite;4 parts~6 parts of Guizhou clay;
4 parts~5 parts of lithium carbonate;15 parts~16 parts of zinc oxide;4 parts~7 parts of titanium oxide;3 parts~5 parts of zirconium silicate.
The step of brown bottom white coral coloured glaze production method, this method, is as follows:
A) brown bottom white coral coloured glaze ground coat enamel, overglaze are stocked up according to each component and each component mass parts;
B) 1.6 ︰ 0.7 of You Liao ︰ Qiu ︰ water=1 ︰, wet ball grinding 15~17 hours, after the glaze after ball milling crosses 200 meshes, bottom
It is stand-by that glaze is modulated into 51~53 Baume concentration;Overglaze is modulated into 53~55 Baume concentration;
C) clean green body is taken, is dried after upper ground coat enamel, then the overglaze on interior glaze;
D) above-mentioned palm fibre bottom white coral coloured glaze of carrying out is burnt into 1270 DEG C of down-draft kiln.
Conclusion: experiment one: white coral effect is weaker, and temperature be higher than 1270 white coral effects almost naked eyes difficulty is shown in.
Experiment two:: meet the purpose of this research and development, for the effect in ideal.
Experiment three: opaque effect is bad, causes white coral effect weak.
In summary 3 points to test three as ideal developmental achievement.
Particular embodiments described above, pair present invention solves the technical problem that, technical scheme and beneficial effects carry out
It is further described, it should be understood that the above is only a specific embodiment of the present invention, is not limited to this
Invention, all within the spirits and principles of the present invention, any modification, equivalent substitution, improvement and etc. done should be included in this hair
Within bright protection scope.
Claims (2)
1. the palm fibre bottom white coral coloured glaze ground coat enamel each component and each component quality are such as the invention discloses a kind of brown bottom white coral coloured glaze
Under: 35 parts~42 parts of feldspar;14 parts~23 parts of dolomite;10 parts~12 parts of Jiepai clay;3 parts~6 parts of zinc oxide;8 parts of spodumene
~13 parts;7 parts~11 parts of kaolin;13 parts~16 parts of iron oxide;5 parts~7 parts of manganese carbonate;The each component and each component of overglaze contain
It measures as follows: 30 parts~35 parts of potassium feldspar;10 parts~12 parts of calcite;14 parts~16 parts of dolomite;4 parts~6 parts of Guizhou clay;Carbonic acid
4 parts~5 parts of lithium;15 parts~16 parts of zinc oxide;8 parts~13 parts of titanium oxide;5 parts~10 parts of zirconium silicate.
2. the step of brown bottom white coral coloured glaze glaze production method described in, this method, is as follows:
A) brown bottom white coral coloured glaze ground coat enamel, overglaze are stocked up according to each component and each component mass parts:
B) 1.6 ︰ 0.7 of You Liao ︰ Qiu ︰ water=1 ︰, wet ball grinding 15~17 hours, after the glaze after ball milling crosses 200 meshes, ground coat enamel tune
It is stand-by that 51~53 Baume concentration are made;Overglaze is modulated into 53~55 Baume concentration;
C) clean green body is taken, is dried after upper ground coat enamel, then the overglaze on interior glaze.
D) above-mentioned palm fibre bottom white coral coloured glaze of carrying out is burnt into 1270 DEG C of down-draft kiln.