CN107938327A - A kind of special antibiotic finishing solution of wool cap - Google Patents
A kind of special antibiotic finishing solution of wool cap Download PDFInfo
- Publication number
- CN107938327A CN107938327A CN201711236359.9A CN201711236359A CN107938327A CN 107938327 A CN107938327 A CN 107938327A CN 201711236359 A CN201711236359 A CN 201711236359A CN 107938327 A CN107938327 A CN 107938327A
- Authority
- CN
- China
- Prior art keywords
- parts
- antibiotic finishing
- finishing solution
- wool cap
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of special antibiotic finishing solution of wool cap, its raw material includes by weight：5 20 parts of Nano silica sol, 1 3.8 parts of hexamethylolmelamine, 3 15 parts of zinc oxide colloidal sol, 5 20 parts attapulgite modified, 38 parts of ε polylysines, 12 parts of dimethylol urea, 300 500 parts of water.The special antibiotic finishing solution of wool cap proposed by the present invention, its can effectively eliminating bacteria and mould, assign wool cap excellent anti-microbial property.
Description
Technical field
The present invention relates to wool field of hat, more particularly to a kind of special antibiotic finishing solution of wool cap.
Background technology
Wool cap is prepared by raw material of wool, has the characteristics that cold-proof comfort, is favored by people.Wool is one
Kind protein fibre, is easy to absorption bacterium and mould, but existing wool cap is generally handled without antibacterial and mouldproof,
During wearing, it is easier to be corroded by bacterium and mould, has potential hazard to health.
The content of the invention
Based on technical problem existing for background technology, the present invention proposes a kind of special antibiotic finishing solution of wool cap, its
Can effectively eliminating bacteria and mould, assign wool cap excellent anti-microbial property.
A kind of special antibiotic finishing solution of wool cap proposed by the present invention, its raw material include by weight：Nano silica sol
5-20 parts, 1-3.8 parts of hexamethylolmelamine, 3-15 parts of zinc oxide colloidal sol, 5-20 parts attapulgite modified, epsilon-polylysine
3-8 parts, 1-2 parts of dimethylol urea, 300-500 parts of water.
Preferably, the solid content of the Nano silica sol is 20-25%.
Preferably, the solid content of the zinc oxide colloidal sol is 10-35%.
Preferably, it is described attapulgite modified to be prepared according to following technique：1,2- phenylpropyl alcohol isothiazoline -3- ketone is added
Enter in water, regulation system pH value is 9-10, then adds attapulgite aqueous solution, 5-9h is stirred at room temperature, is transferred to hydro-thermal
Hydro-thermal reaction 5-9h in kettle, centrifuges, washs, is dried to obtain material A after reaction；Material A, butyl titanate and ethanol are mixed
Close uniformly, 3-5h is stirred after adding water, washed after filtering, is dry, 120-150min is then calcined at 550-650 DEG C obtains thing
Expect B；Material B is added to the water and is stirred evenly, cetyl trimethylammonium bromide stirring 30-50min is then added, adds nitric acid
The ammonia solution of silver, stirs 5-8h, then filters, washs, is dry, and 100-150min is calcined at 550-650 DEG C and obtains described change
Property attapulgite.
Preferably, 1,2- phenylpropyl alcohols isothiazoline -3- ketone, the weight ratio of attapulgite are 1-5：15-30.
Preferably, material A, the weight ratio of butyl titanate are 1：2.5-3.
Preferably, material B, cetyl trimethylammonium bromide, the weight ratio of silver nitrate are 0.5-1.5：3.5-5：0.1-
0.35。
Preferably, its raw material includes by weight：18 parts of Nano silica sol, 2.5 parts of hexamethylolmelamine, zinc oxide
10 parts of colloidal sol, 17 parts attapulgite modified, 6 parts of epsilon-polylysine, 1.5 parts of dimethylol urea, 400 parts of water.
The ammonia solution of the silver nitrate is dissolved in stirring in concentrated ammonia liquor by silver nitrate and obtains.
The special antibiotic finishing solution of wool cap of the present invention, in its raw material, adds Nano silica sol, in wool after processing
The fiber surface of cap forms perforated membrane, has covered the scale structure of wool, and on the one hand imparting wool cap is excellent resists
Pilling tendency, on the other hand, coordinates with the zinc oxide colloidal sol in system, is keeping the situation of wool cap fracture strength and whiteness
Under, assign wool cap excellent antibiotic property and antistatic property, and durability is good；In attapulgite modified preparation process,
First with 1,2- phenylpropyl alcohols isothiazoline -3- ketone and attapulgite for raw material, by controlling the condition of reaction, make the different thiophene of 1,2- phenylpropyl alcohols
Oxazoline -3- ketone is inserted into the piece interlayer of attapulgite, is reacted afterwards with butyl titanate, makes titanium dichloride load in bumps
The surface of rod soil, after being mixed with the ammonia solution of cetyl trimethylammonium bromide and silver nitrate, and bears on the surface of attapulgite
Silver chlorate has been carried, so that 1 has been obtained, the attapulgite that 2- phenylpropyl alcohol isothiazoline -3- ketone, titanium dioxide and silver chlorate are modified, together
When have 1,2- phenylpropyl alcohol isothiazoline -3- ketone, titanium dioxide and silver chlorate property, be added into system, with hexamethylol
Melamine, epsilon-polylysine and dimethylol urea coordinate, and the absorption for enhancing dressing liquid arranges ability, is not damaging fiber
Under the conditions of, make the function adhesion-tight, lasting, the excellent antibiotic property of imparting wool cap.
Embodiment
In the following, technical scheme is described in detail by specific embodiment.
Embodiment 1
A kind of special antibiotic finishing solution of wool cap proposed by the present invention, its raw material include by weight：Nano silica sol
20 parts, 1 part of hexamethylolmelamine, 15 parts of zinc oxide colloidal sol, 5 parts attapulgite modified, 8 parts of epsilon-polylysine, dihydroxy first
1 part of base urea, 500 parts of water.
Embodiment 2
A kind of special antibiotic finishing solution of wool cap proposed by the present invention, its raw material include by weight：Nano silica sol 5
Part, 3.8 parts of hexamethylolmelamine, 3 parts of zinc oxide colloidal sol, 20 parts attapulgite modified, 3 parts of epsilon-polylysine, dihydroxy first
2 parts of base urea, 300 parts of water.
Embodiment 3
A kind of special antibiotic finishing solution of wool cap proposed by the present invention, its raw material include by weight：Nano silica sol
16 parts, 1.6 parts of hexamethylolmelamine, 13 parts of zinc oxide colloidal sol, 9 parts attapulgite modified, 7 parts of epsilon-polylysine, dihydroxy
1.3 parts of methylurea, 430 parts of water；
Wherein, the solid content of the Nano silica sol is 20%；
The solid content of the zinc oxide colloidal sol is 35%；
It is described attapulgite modified to be prepared according to following technique：1,2- phenylpropyl alcohol isothiazoline -3- ketone is added to the water,
Regulation system pH value is 9, then adds attapulgite aqueous solution, wherein, 1,2- phenylpropyl alcohol isothiazoline -3- ketone, attapulgite
Weight ratio is 5：15,9h is stirred at room temperature, is transferred to hydro-thermal reaction 5h in water heating kettle, centrifuges, wash after reaction, is dry
Obtain material A；Material A, butyl titanate and ethanol are uniformly mixed, wherein, material A, the weight ratio of butyl titanate are 1：
3,3h is stirred after adding water, is washed after filtering, is dry, 120min is then calcined at 650 DEG C obtains material B；Material B is added
Stirred evenly in water, then add cetyl trimethylammonium bromide stirring 50min, add the ammonia solution of silver nitrate, wherein, thing
Expect that B, cetyl trimethylammonium bromide, the weight ratio of silver nitrate are 0.5：5：0.1,8h is stirred, then filters, wash, is dry,
Calcining 150min is obtained described attapulgite modified at 550 DEG C.
Embodiment 4
A kind of special antibiotic finishing solution of wool cap proposed by the present invention, its raw material include by weight：Nano silica sol 7
Part, 3.2 parts of hexamethylolmelamine, 6 parts of zinc oxide colloidal sol, 16 parts attapulgite modified, 4.3 parts of epsilon-polylysine, dihydroxy
1.8 parts of methylurea, 350 parts of water；
Wherein, the solid content of the Nano silica sol is 25%；
The solid content of the zinc oxide colloidal sol is 10%；
It is described attapulgite modified to be prepared according to following technique：1,2- phenylpropyl alcohol isothiazoline -3- ketone is added to the water,
Regulation system pH value is 10, then adds attapulgite aqueous solution, wherein, 1,2- phenylpropyl alcohol isothiazoline -3- ketone, attapulgite
Weight ratio is 1：30,5h is stirred at room temperature, is transferred to hydro-thermal reaction 9h in water heating kettle, centrifuges, wash after reaction, is dry
Obtain material A；Material A, butyl titanate and ethanol are uniformly mixed, wherein, material A, the weight ratio of butyl titanate are 1：
2.5,5h is stirred after adding water, is washed after filtering, is dry, 150min is then calcined at 550 DEG C obtains material B；Material B is added
Enter in water and stir evenly, then add cetyl trimethylammonium bromide stirring 30min, add the ammonia solution of silver nitrate, wherein,
Material B, cetyl trimethylammonium bromide, the weight ratio of silver nitrate are 1.5：3.5：0.35,5h is stirred, then filter, wash,
Dry, calcining 100min is obtained described attapulgite modified at 650 DEG C.
Embodiment 5
A kind of special antibiotic finishing solution of wool cap proposed by the present invention, its raw material include by weight：Nano silica sol
18 parts, 2.5 parts of hexamethylolmelamine, 10 parts of zinc oxide colloidal sol, 17 parts attapulgite modified, 6 parts of epsilon-polylysine, dihydroxy
1.5 parts of methylurea, 400 parts of water；
Wherein, the solid content of the Nano silica sol is 22%；
The solid content of the zinc oxide colloidal sol is 31%；
It is described attapulgite modified to be prepared according to following technique：1,2- phenylpropyl alcohol isothiazoline -3- ketone is added to the water,
Regulation system pH value is 9.5, then adds attapulgite aqueous solution, wherein, 1,2- phenylpropyl alcohol isothiazoline -3- ketone, attapulgite
Weight ratio be 3：22,7h is stirred at room temperature, is transferred to hydro-thermal reaction 6h in water heating kettle, centrifuges, wash after reaction, is dry
It is dry to obtain material A；Material A, butyl titanate and ethanol are uniformly mixed, wherein, material A, the weight ratio of butyl titanate are
1：2.7,4h is stirred after adding water, is washed after filtering, is dry, 130min is then calcined at 600 DEG C obtains material B；By material B
It is added to the water and stirs evenly, then add cetyl trimethylammonium bromide stirring 40min, adds the ammonia solution of silver nitrate, its
In, material B, cetyl trimethylammonium bromide, the weight ratio of silver nitrate are 1：4：0.3,6h is stirred, then filters, wash, is dry
Dry, calcining 130min is obtained described attapulgite modified at 600 DEG C.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art the invention discloses technical scope in, technique according to the invention scheme and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (8)
1. a kind of special antibiotic finishing solution of wool cap, it is characterised in that its raw material includes by weight：Nano silica sol 5-20
Part, 1-3.8 parts of hexamethylolmelamine, 3-15 parts of zinc oxide colloidal sol, 5-20 parts attapulgite modified, epsilon-polylysine 3-8
Part, 1-2 parts of dimethylol urea, 300-500 parts of water.
2. the special antibiotic finishing solution of wool cap according to claim 1, it is characterised in that consolidating for the Nano silica sol contains
Measure as 20-25%.
3. the special antibiotic finishing solution of wool cap according to claim 1 or claim 2, it is characterised in that the zinc oxide colloidal sol
Solid content is 10-35%.
4. according to the special antibiotic finishing solution of wool cap any one of claim 1-3, it is characterised in that the modification is recessed
Convex rod soil is prepared according to following technique：1,2- phenylpropyl alcohol isothiazoline -3- ketone is added to the water, regulation system pH value is 9-
10, attapulgite aqueous solution is then added, 5-9h is stirred at room temperature, is transferred to hydro-thermal reaction 5-9h in water heating kettle, reaction knot
Centrifuged after beam, wash, be dried to obtain material A；Material A, butyl titanate and ethanol are uniformly mixed, 3- is stirred after adding water
5h, washs after filtering, is dry, and 120-150min is then calcined at 550-650 DEG C obtains material B；Material B is added to the water and is stirred
Mix uniformly, then add cetyl trimethylammonium bromide stirring 30-50min, add the ammonia solution of silver nitrate, stir 5-8h,
Then filter, wash, is dry, calcining 100-150min is obtained described attapulgite modified at 550-650 DEG C.
5. the special antibiotic finishing solution of wool cap according to claim 4, it is characterised in that 1,2- phenylpropyl alcohol isothiazoline -3-
Ketone, the weight ratio of attapulgite are 1-5：15-30.
6. according to the special antibiotic finishing solution of wool cap of claim 4 or 5, it is characterised in that material A, butyl titanate
Weight ratio be 1：2.5-3.
7. according to the special antibiotic finishing solution of wool cap any one of claim 4-6, it is characterised in that material B, 16
Alkyl trimethyl ammonium bromide, the weight ratio of silver nitrate are 0.5-1.5：3.5-5：0.1-0.35.
8. according to the special antibiotic finishing solution of wool cap any one of claim 1-7, it is characterised in that its raw material is by weight
Amount part includes：18 parts of Nano silica sol, 2.5 parts of hexamethylolmelamine, 10 parts of zinc oxide colloidal sol, attapulgite modified 17
Part, 6 parts of epsilon-polylysine, 1.5 parts of dimethylol urea, 400 parts of water.