CN107903370A - 一种具备耐水解性能的复合聚酯 - Google Patents

一种具备耐水解性能的复合聚酯 Download PDF

Info

Publication number
CN107903370A
CN107903370A CN201711125946.0A CN201711125946A CN107903370A CN 107903370 A CN107903370 A CN 107903370A CN 201711125946 A CN201711125946 A CN 201711125946A CN 107903370 A CN107903370 A CN 107903370A
Authority
CN
China
Prior art keywords
polyester
parts
weight fraction
reagent bottle
hydrolytic performance
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711125946.0A
Other languages
English (en)
Inventor
龚伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHOU BOYUN PLASTIC CO Ltd
Original Assignee
SUZHOU BOYUN PLASTIC CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU BOYUN PLASTIC CO Ltd filed Critical SUZHOU BOYUN PLASTIC CO Ltd
Priority to CN201711125946.0A priority Critical patent/CN107903370A/zh
Publication of CN107903370A publication Critical patent/CN107903370A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种具备耐水解性能的复合聚酯，包括以下组合成分：聚酯混合物、阻燃剂和异氰酸酯，所述聚酯混合物包括聚酯多元醇、聚碳酸酯二醇、碳原子数44的二羧酸、一元醇、多元醇扩链剂、催化剂和水。本发明操作方便，通过聚酯混合物、阻燃剂和异氰酸酯合成的复合聚酯具有良好的耐水解性能和粘结性能，且耐水解性能和粘结性能对比常规的复合聚酯的耐水解性能和粘结性能有较大的提高。

Description

一种具备耐水解性能的复合聚酯
技术领域
本发明涉及耐水解材料领域，尤其涉及一种具备耐水解性能的复合聚酯。
背景技术
聚酯海绵具有优异的机械强度和独特的耐油、抗溶剂的特性，在耐磨性、耐磨蚀、耐高温、拉伸性强、弹性好、无不良气味,广泛应用于汽车、家电和电子电器等领域，近年来，随着中国经济的迅速发展，国内对聚酯海绵的表观消费量迅速增长，我国的聚酯海绵产能迅速发展。
专利号为CN 1040987533 A的专利文件提供了一种复合聚酯，其通过使用复合聚酯，使用聚酯多元醇、聚碳酸酯二醇作为树脂基体，在配合使用异氰酸酯、扩链剂、催化剂等，实现该复合聚酯具有良好的粘结性能，同时赋予复合聚酯优异的耐水解性能，但是其耐水解性能和粘结性能较差，所以我们提供了一种具备耐水解性能的复合聚酯用于解决上述提出的问题。
发明内容
基于背景技术存在的技术问题，本发明提出了一种具备耐水解性能的复合聚酯。
本发明提出的一种具备耐水解性能的复合聚酯，包括以下组合成分：聚酯混合物、阻燃剂和异氰酸酯，所述聚酯混合物包括聚酯多元醇、聚碳酸酯二醇、碳原子数44的二羧酸、一元醇、多元醇扩链剂、催化剂和水，所述催化剂由钛化合物、含磷化合物以及镁化合物组成，且钛化合物为金属化合物，所述金属化合物重金属为碱金属，所述碳原子数44的二羧酸为芥酸二聚物。
优选的，所述聚酯多元醇的重量分数为70-85份、聚碳酸酯二醇的重量分数为10-20份、碳原子数44的二羧酸的重量分数为2-3.5份、一元醇的重量分数为1-2份、多元醇扩链剂的重量分数为1-1.5份、催化剂的重量分数为1-1.5份、水的重量分数为0.5-2.5份。
优选的，所述多元醇扩连剂中的多元醇含有三个以上的羟基。
优选的，所述聚酯多元醇的重量分数为75份、聚碳酸酯二醇的重量分数为15份。
优选的，所述复合聚酯的制备方法包括以下步骤：
S1：以聚酯多元醇和聚碳酸酯二醇作为树脂基体；
S2：利用钛化合物、含磷化合物以及镁化合物制作出催化剂；
S3：取特定分量的聚酯多元醇和聚碳酸酯二醇放入试剂瓶中，然后在试剂瓶中依次加入重量分数为2-3.5份的碳原子数44的二羧酸、重量分数为1-2份的一元醇、重量分数为1-1.5份的多元醇扩链剂、重量分数为1-1.5份的催化剂以及重量分数为0.5-2.5份的水；
S4：利用搅拌器对试剂瓶中的材料进行搅拌，合成聚酯混合物，接着在试剂瓶中加入阻燃剂和异氰酸酯，并继续搅拌；
S5：对搅拌后的试剂瓶中材料进行静置，并得出复合聚酯。
优选的，所述S2中，钛化合物中的钛元素的添加量为22ppm,磷化合物的磷元素的添加量为10ppm，镁化合物中的镁元素的添加量为15ppm。
优选的，所述S3中，准备试剂瓶，然后取重量分数为75份的聚酯多元醇和重量分数为15份的聚碳酸酯二醇加入试剂瓶中。
优选的，所述S4中，准备搅拌器和加热器，利用加热器对试剂瓶内的材料进行加热，然后再利用搅拌器对试剂瓶中的材料进行充分搅拌，在搅拌的同时加入阻燃剂和异氰酸酯，并继续搅拌至粘稠状。
本发明的有益效果是：通过钛化合物、含磷化合物和镁化合物可以制作出催化剂，通过聚酯多元醇、聚碳酸酯二醇、碳原子数44的二羧酸、一元醇、多元醇扩链剂、催化剂和水，可以合成出聚酯混合物，通过聚酯混合物、阻燃剂和异氰酸酯可以合成出复合聚酯，本发明操作方便，通过聚酯混合物、阻燃剂和异氰酸酯合成的复合聚酯具有良好的耐水解性能和粘结性能，且耐水解性能和粘结性能对比常规的复合聚酯的耐水解性能和粘结性能有较大的提高。
具体实施方式
下面结合具体实施例对本发明作进一步解说。
实施例一
本发明提出的一种具备耐水解性能的复合聚酯，包括以下组合成分：聚酯混合物、阻燃剂和异氰酸酯，聚酯混合物包括聚酯多元醇、聚碳酸酯二醇、碳原子数44的二羧酸、一元醇、多元醇扩链剂、催化剂和水，催化剂由钛化合物、含磷化合物以及镁化合物组成，且钛化合物为金属化合物，金属化合物重金属为碱金属，碳原子数44的二羧酸为芥酸二聚物，聚酯多元醇的重量分数为70-85份、聚碳酸酯二醇的重量分数为10-20份、碳原子数44的二羧酸的重量分数为2-3.5份、一元醇的重量分数为1-2份、多元醇扩链剂的重量分数为1-1.5份、催化剂的重量分数为1-1.5份、水的重量分数为0.5-2.5份，多元醇扩连剂中的多元醇含有三个以上的羟基，聚酯多元醇的重量分数为75份、聚碳酸酯二醇的重量分数为15份，通过钛化合物、含磷化合物和镁化合物可以制作出催化剂，通过聚酯多元醇、聚碳酸酯二醇、碳原子数44的二羧酸、一元醇、多元醇扩链剂、催化剂和水，可以合成出聚酯混合物，通过聚酯混合物、阻燃剂和异氰酸酯可以合成出复合聚酯，本发明操作方便，通过聚酯混合物、阻燃剂和异氰酸酯合成的复合聚酯具有良好的耐水解性能和粘结性能，且耐水解性能和粘结性能对比常规的复合聚酯的耐水解性能和粘结性能有较大的提高。
一种具备耐水解性能的复合聚酯的制备方法包括以下步骤：
S1：以聚酯多元醇和聚碳酸酯二醇作为树脂基体；
S2：利用钛化合物、含磷化合物以及镁化合物制作出催化剂；
S3：取特定分量的聚酯多元醇和聚碳酸酯二醇放入试剂瓶中，然后在试剂瓶中依次加入重量分数为3.5份的碳原子数44的二羧酸、重量分数为1份的一元醇、重量分数为1.5份的多元醇扩链剂、重量分数为1.5份的催化剂以及重量分数为2.5份的水；
S4：利用搅拌器对试剂瓶中的材料进行搅拌，合成聚酯混合物，接着在试剂瓶中加入阻燃剂和异氰酸酯，并继续搅拌；
S5：对搅拌后的试剂瓶中材料进行静置，并得出复合聚酯。
本实施例中，S2中，钛化合物中的钛元素的添加量为22ppm,磷化合物的磷元素的添加量为10ppm，镁化合物中的镁元素的添加量为15ppm，先利用钛化合物、磷化合物和镁化合物合成出催化剂，S3中，准备试剂瓶，然后取重量分数为75份的聚酯多元醇和重量分数为15份的聚碳酸酯二醇加入试剂瓶中，并以此作为树脂基体，S4中，准备搅拌器和加热器，利用加热器对试剂瓶内的材料进行加热，然后再利用搅拌器对试剂瓶中的材料进行充分搅拌，在搅拌的同时加入阻燃剂和异氰酸酯，并继续搅拌至粘稠状，然后将试剂瓶进行静置，并得出复合聚酯。
实施例二
取重量分数为70份的聚酯多元醇和重量分数为20份的聚碳酸酯二醇，并以此作为树脂基体，然后将树脂基体加入试剂瓶中，并依次在试剂瓶中加入重量分数为3.5份的碳原子数44的二羧酸、重量分数为2份的一元醇、重量分数为1.5的多元醇扩链剂、重量分数为1.5份的催化剂以及重量分数为1.5份的水，然后对试剂瓶进行加热，并利用搅拌器对其进行搅拌，直至搅拌成粘稠状，然后将试剂瓶进行静置，并得出复合聚酯。
实施例三
取重量分数为80份的聚酯多元醇和重量分数为10份的聚碳酸酯二醇，并以此作为树脂基体，然后然后将树脂基体加入试剂瓶中，并依次在试剂瓶中加入重量分数为3份的碳原子数44的二羧酸、重量分数为2份的一元醇、重量分数为1.5的多元醇扩链剂、重量分数为1.5份的催化剂以及重量分数为2份的水，然后对试剂瓶进行加热，并利用搅拌器对其进行搅拌，直至搅拌成粘稠状，然后将试剂瓶进行静置，并得出复合聚酯。
对比常规的复合聚酯与实施例一至三的具备耐水解性能的复合聚酯，实施例一至三的具备耐水解性能的复合聚酯的提高百分比如下表：
从而得出实施例二中的制作出的复合聚酯，其耐水解性能和粘结性能最好，经过本发明制作出的复合聚酯，可以广泛应用于汽车、家电和电子电器等领域。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。

Claims (8)

1.一种具备耐水解性能的复合聚酯，其特征在于，包括以下组合成分：聚酯混合物、阻燃剂和异氰酸酯，所述聚酯混合物包括聚酯多元醇、聚碳酸酯二醇、碳原子数44的二羧酸、一元醇、多元醇扩链剂、催化剂和水，所述催化剂由钛化合物、含磷化合物以及镁化合物组成，且钛化合物为金属化合物，所述金属化合物重金属为碱金属，所述碳原子数44的二羧酸为芥酸二聚物。
2.根据权利要求1所述的一种具备耐水解性能的复合聚酯，其特征在于，所述聚酯多元醇的重量分数为70-85份、聚碳酸酯二醇的重量分数为10-20份、碳原子数44的二羧酸的重量分数为2-3.5份、一元醇的重量分数为1-2份、多元醇扩链剂的重量分数为1-1.5份、催化剂的重量分数为1-1.5份、水的重量分数为0.5-2.5份。
3.根据权利要求1所述的一种具备耐水解性能的复合聚酯，其特征在于，所述多元醇扩连剂中的多元醇含有三个以上的羟基。
4.根据权利要求2所述的一种具备耐水解性能的复合聚酯，其特征在于，所述聚酯多元醇的重量分数为75份、聚碳酸酯二醇的重量分数为15份。
5.根据权利要求1所述的一种具备耐水解性能的复合聚酯，其特征在于，所述复合聚酯的制备方法包括以下步骤：
S1：以聚酯多元醇和聚碳酸酯二醇作为树脂基体；
S2：利用钛化合物、含磷化合物、镁化合物制作出催化剂；
S3：取特定分量的聚酯多元醇和聚碳酸酯二醇放入试剂瓶中，然后在试剂瓶中依次加入重量分数为2-3.5份的碳原子数44的二羧酸、重量分数为1-2份的一元醇、重量分数为1-1.5份的多元醇扩链剂、重量分数为1-1.5份的催化剂以及重量分数为0.5-2.5份的水；
S4：利用搅拌器对试剂瓶中的材料进行搅拌，合成聚酯混合物，接着在试剂瓶中加入阻燃剂和异氰酸酯，并继续搅拌；
S5：对搅拌后的试剂瓶中材料进行静置，并得出复合聚酯。
6.根据权利要求5所述的一种具备耐水解性能的复合聚酯，其特征在于，所述S2中，钛化合物中的钛元素的添加量为22ppm,磷化合物的磷元素的添加量为10ppm，镁化合物中的镁元素的添加量为15ppm。
7.根据权利要求5所述的一种具备耐水解性能的复合聚酯，其特征在于，所述S3中，准备试剂瓶，然后取重量分数为75份的聚酯多元醇和重量分数为15份的聚碳酸酯二醇加入试剂瓶中。
8.根据权利要求5所述的一种具备耐水解性能的复合聚酯，其特征在于，所述S4中，准备搅拌器和加热器，利用加热器对试剂瓶内的材料进行加热，然后再利用搅拌器对试剂瓶中的材料进行充分搅拌，在搅拌的同时加入阻燃剂和异氰酸酯，并继续搅拌至粘稠状。
CN201711125946.0A 2017-11-15 2017-11-15 一种具备耐水解性能的复合聚酯 Pending CN107903370A (zh)