CN107903050A - A kind of preparation process for the Imitation Rock Porcelain Tiles for connecting grinding system based on five balls - Google Patents

A kind of preparation process for the Imitation Rock Porcelain Tiles for connecting grinding system based on five balls Download PDF

Info

Publication number
CN107903050A
CN107903050A CN201711317551.0A CN201711317551A CN107903050A CN 107903050 A CN107903050 A CN 107903050A CN 201711317551 A CN201711317551 A CN 201711317551A CN 107903050 A CN107903050 A CN 107903050A
Authority
CN
China
Prior art keywords
balls
system based
porcelain tiles
preparation process
imitation rock
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711317551.0A
Other languages
Chinese (zh)
Inventor
陈晓宣
黄大平
周海龙
洪敏�
周伟峰
薛细亮
吴谋胜
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangdong Crown Star Ceramic Enterprise Co Ltd
Original Assignee
Guangdong Crown Star Ceramic Enterprise Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangdong Crown Star Ceramic Enterprise Co Ltd filed Critical Guangdong Crown Star Ceramic Enterprise Co Ltd
Priority to CN201711317551.0A priority Critical patent/CN107903050A/en
Publication of CN107903050A publication Critical patent/CN107903050A/en
Pending legal-status Critical Current

Abstract

The present invention relates to ceramic field, specifically, is related to a kind of preparation process for the Imitation Rock Porcelain Tiles for connecting grinding system based on five balls, the technique includes：Step 1：Ball milling, feeds injection into five ball grinders of series connection and carries out ball milling；Step 2：Pressed compact, becomes default specification by the raw material pressed compact after ball milling；Step 3：It is dry, the brick body after pressed compact is dried by dry kiln；The Drying Technology Parameter is dry 40 60min at 160 200 DEG C.Step 4：Glazing, billet surface charity glaze layer after the drying and stamp；Step 5：Fire；Burning process is 1,190 1220 DEG C, 60 70min of firing time.Wherein, the raw material is composed of the following components：SiO265 68%；Al2O318 21%；Fe2O3≤1.0；CaO+MgO 1 2%；K2O+Na2O 5.5 7%；Loss on ignition 4 7%；The object of the present invention is to provide a kind of preparation process for the Imitation Rock Porcelain Tiles for connecting grinding system based on five balls, the Imitation Rock Porcelain Tiles water absorption rate being prepared by the technique can be controlled below 0.02%.

Description

A kind of preparation process for the Imitation Rock Porcelain Tiles for connecting grinding system based on five balls
Technical field
The present invention relates to ceramic field, specifically, is related to a kind of preparation work for the Imitation Rock Porcelain Tiles for connecting grinding system based on five balls Skill.
Background technology
Imitation Rock Porcelain Tiles have the texture of lithotome, and with more high photosensitiveness, high rigidity, high abrasion, high-dirt-resistance, water suction Rate is low, aberration is few and multi-size and it is rich in color the advantages of, be interior, kitchen, the common metope of bathroom and ground Material.
Existing Imitation Rock Porcelain Tiles national standard water absorption rate will be controlled below 0.5%, still, be directed to the water suction of Imitation Rock Porcelain Tiles Rate, the requirement of client are more harsh, if it is possible to control below 0.02%, then product competitiveness bigger.
The content of the invention
The object of the present invention is to provide a kind of preparation process for the Imitation Rock Porcelain Tiles for connecting grinding system based on five balls, pass through the technique system Standby obtained Imitation Rock Porcelain Tiles water absorption rate can be controlled below 0.02%.
Technical solution provided by the invention is：A kind of preparation process for the Imitation Rock Porcelain Tiles for connecting grinding system based on five balls, it is described Technique includes：
Step 1：Ball milling, feeds injection into five ball grinders of series connection and carries out ball milling；
Step 2：Pressed compact, becomes default specification by the raw material pressed compact after ball milling；
Step 3：It is dry, the brick body after pressed compact is dried by dry kiln；
Step 4：Glazing, billet surface charity glaze layer after the drying and stamp；
Step 5：Fire；
Wherein, the raw material is composed of the following components：
SiO265-68%；Al2O318-21%；Fe2O3≤1.0；CaO+MgO 1-2%；K2O+Na2O 5.5-7%；Burn Vector 4-7%.
In the preparation process of the above-mentioned Imitation Rock Porcelain Tiles for connecting grinding system based on five balls, the raw material is in five ball grinders Ball-milling Time is 1.4-1.8h.
In the preparation process of the above-mentioned Imitation Rock Porcelain Tiles for connecting grinding system based on five balls, the raw material is in five ball grinders Ball-milling Time is 1.5h
In the preparation process of the above-mentioned Imitation Rock Porcelain Tiles for connecting grinding system based on five balls, the drying temperature is 160-200 ℃。
In the preparation process of the above-mentioned Imitation Rock Porcelain Tiles for connecting grinding system based on five balls, the burning process is 1190- 1220 DEG C, firing time 60-70min.
Beneficial effect：
The present invention connects mill technology using five balls, is aided with the further preferred of raw material, and the Imitation Rock Porcelain Tiles for making to burn out absorb water Rate reaches less than 0.02%.
The present invention realizes the standardization of raw material, connects mill technology by five balls, is sufficiently mixed material, standardization level It is high.
And guarantee is provided for the raising of production capacity, and ensure that the constant of product quality, reduces floor space.
Embodiment
With reference to embodiment, technical scheme is described in further detail, but is not formed pair Any restrictions of the present invention.
Embodiment one
A kind of preparation process for the Imitation Rock Porcelain Tiles for being connected grinding system based on five balls, the technique are included：
Step 1：Ball milling, feeds injection into five ball grinders of series connection and carries out ball milling；
Step 2：Pressed compact, becomes default specification by the raw material pressed compact after ball milling；
Step 3：It is dry, the brick body after pressed compact is dried by dry kiln；The Drying Technology Parameter is 160-200 DEG C Lower dry 40-60min.
Step 4：Glazing, billet surface charity glaze layer after the drying and stamp；
Step 5：Fire；Burning process is 1190-1220 DEG C, firing time 70min.
Wherein, the raw material is composed of the following components：
SiO267.5%；Al2O319%；Fe2O3≤1.0；CaO+MgO 1.5%；K2O+Na2O 6%；Loss on ignition 5%.
The raw material is 1.5h in the Ball-milling Time of five ball grinders.
Embodiment two
A kind of preparation process for the Imitation Rock Porcelain Tiles for being connected grinding system based on five balls, the technique are included：
Step 1：Ball milling, feeds injection into five ball grinders of series connection and carries out ball milling；
Step 2：Pressed compact, becomes default specification by the raw material pressed compact after ball milling；
Step 3：It is dry, the brick body after pressed compact is dried by dry kiln；The Drying Technology Parameter is 160-200 DEG C Lower dry 40-60min.
Step 4：Glazing, billet surface charity glaze layer after the drying and stamp；
Step 5：Fire；Burning process is 1190-1220 DEG C, firing time 60min.
Wherein, the raw material is composed of the following components：
SiO265%；Al2O321%；Fe2O3≤1.0；CaO+MgO 2%；K2O+Na2O 7%；Loss on ignition 4%.
The raw material is 1.6h in the Ball-milling Time of five ball grinders.
Embodiment three
A kind of preparation process for the Imitation Rock Porcelain Tiles for being connected grinding system based on five balls, the technique are included：
Step 1：Ball milling, feeds injection into five ball grinders of series connection and carries out ball milling；
Step 2：Pressed compact, becomes default specification by the raw material pressed compact after ball milling；
Step 3：It is dry, the brick body after pressed compact is dried by dry kiln；The Drying Technology Parameter is 160-200 DEG C Lower dry 40-60min.
Step 4：Glazing, billet surface charity glaze layer after the drying and stamp；
Step 5：Fire；Burning process is 1190-1220 DEG C, firing time 64min.
Wherein, the raw material is composed of the following components：
SiO268%；Al2O319%；Fe2O3≤1.0；CaO+MgO 1%；K2O+Na2O 5.5%；Loss on ignition 6.5%.
The raw material is 1.4h in the Ball-milling Time of five ball grinders.
Test result
The water absorption rate of embodiment 1-3 is below 0.01%.Also, above-described embodiment 1-3 connects mill technology using five balls, also reaches Arrived raw material standardization, production stabilisation, floor space optimization purpose.
Above-described embodiment is the preferable embodiment of the present invention, but embodiments of the present invention and from above-described embodiment Limitation, other any Spirit Essences without departing from the present invention with made under principle change, modification, replacement, combine, simplification, Equivalent substitute mode is should be, is included within protection scope of the present invention.

Claims (5)

  1. A kind of 1. preparation process for the Imitation Rock Porcelain Tiles for connecting grinding system based on five balls, it is characterised in that：The technique includes：
    Step 1：Ball milling, feeds injection into five ball grinders of series connection and carries out ball milling；
    Step 2：Pressed compact, becomes default specification by the raw material pressed compact after ball milling；
    Step 3：It is dry, the brick body after pressed compact is dried by dry kiln；
    Step 4：Glazing, billet surface charity glaze layer after the drying and stamp；
    Step 5：Fire；
    Wherein, the raw material is composed of the following components：
    SiO265-68%；Al2O318-21%；Fe2O3≤1.0；CaO+MgO 1-2%；K2O+Na2O 5.5-7%；Loss on ignition 4-7%.
  2. 2. the preparation process of the Imitation Rock Porcelain Tiles according to claim 1 for connecting grinding system based on five balls, it is characterised in that：Described Raw material is 1.4-1.8h in the Ball-milling Time of five ball grinders.
  3. 3. the preparation process of the Imitation Rock Porcelain Tiles according to claim 1 for connecting grinding system based on five balls, it is characterised in that：Described Raw material is 1.5h in the Ball-milling Time of five ball grinders.
  4. 4. the preparation process of the Imitation Rock Porcelain Tiles according to claim 1 for connecting grinding system based on five balls, it is characterised in that：Described Drying temperature is 160-200 DEG C.
  5. 5. the preparation process of the Imitation Rock Porcelain Tiles according to claim 1 for connecting grinding system based on five balls, it is characterised in that：Described Burning process is 1190-1220 DEG C, firing time 60-70min.
CN201711317551.0A 2017-12-12 2017-12-12 A kind of preparation process for the Imitation Rock Porcelain Tiles for connecting grinding system based on five balls Pending CN107903050A (en)