CN107790357A - A kind of spraying coating process of compressor case protective coating - Google Patents
A kind of spraying coating process of compressor case protective coating Download PDFInfo
- Publication number
- CN107790357A CN107790357A CN201711033837.6A CN201711033837A CN107790357A CN 107790357 A CN107790357 A CN 107790357A CN 201711033837 A CN201711033837 A CN 201711033837A CN 107790357 A CN107790357 A CN 107790357A
- Authority
- CN
- China
- Prior art keywords
- parts
- sprayed
- protective coating
- spraying
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention provides a kind of spraying coating process of compression case protective coating, is related to double entry pump protection field, comprises the following steps:Blasting treatment:Sandblasting roughening is carried out to cabinet parts surface to be sprayed;Surface clean:Immerse in metal cleaner, deionized water and absolute ethyl alcohol and carry out ultrasonic cleaning processing, then vacuum drying;Anti-corrosion primer:Plasma spraying anti-corrosion primer is carried out to the cabinet parts surface of the drying, the anti-corrosion primer thickness is 0.05 0.15mm;Spray-on coating;Cabinet parts surface to be sprayed is sprayed with nonmetallic barrier material, protective coating is made, is solidified 6~8 hours;The invention provides a kind of spraying coating process of compression case protective coating, the Corrosion Protection of casing is improved, and material environment friendly, economic and practical, cost is low, can be sprayed repeatedly.
Description
Technical field
The present invention relates to double entry pump to protect field, and in particular to a kind of spraying coating process of compressor case protective coating.
Background technology
Compressor is a kind of driven fluid machinery that low-pressure gas is promoted to gases at high pressure, is the heart of refrigeration system
It is dirty.It is operated after being compressed with piston to it, to row from the refrigerant gas of air intake duct suction low-temp low-pressure by motor
Tracheae discharges the refrigerant gas of HTHP, and power is provided for kind of refrigeration cycle, so as to realize compression → condensation (heat release) → swollen
The kind of refrigeration cycle of swollen → evaporation (heat absorption).Compressor is divided into piston compressor, helical-lobe compressor, centrifugal compressor, straight line compression
Machine etc..Entry describes operation principle, classification, accessory, specification, running requirements, the production of compressor, the most common failure of compressor
And environmental requirement, Type Selection Principle, mounting condition and development trend.
Compressor is chronically in high temperature complex environment, and therefore, the anti-corrosion treatment of compressor case part is especially heavy
Will.
The content of the invention
In view of the shortcomings of the prior art, the invention provides a kind of spraying coating process of compressor case protective coating so that
Improve the Corrosion Protection of casing.
To realize object above, the present invention is achieved by the following technical programs:A kind of compressor case protective coating
Spraying coating process, comprise the following steps:
S1. blasting treatment:Sandblasting roughening is carried out to cabinet parts surface to be sprayed;
S2. surface clean:Immerse in metal cleaner, deionized water and absolute ethyl alcohol and carry out ultrasonic cleaning processing, then
Vacuum drying;
S3. anti-corrosion primer:Plasma spraying anti-corrosion primer, the anti-corrosion bottom are carried out to the cabinet parts surface of the drying
Paint thickness is 0.1-0.15mm;
S4. spray-on coating;Cabinet parts surface to be sprayed is sprayed with nonmetallic barrier material, is made anti-
Coating is protected, is solidified 6~8 hours.
Further, the S1 sandblastings operation is purity quartzite with sand grains.
Further, in parts by weight, its component includes the anti-corrosion primer in the S3:Deionized water 150~200
Part, 40~60 parts of alkyd emulsion, 70~90 parts of water-based fluorocarbon resin, 120~140 parts of pure-acrylic emulsion, organic silicon emulsion 10~20
Part, 20~35 parts of propane diols, 5~6 parts of levelling agent, 5~6 parts of defoamer, 4~6 parts of wetting agent, 4~8 parts of dispersant, film forming help
10~40 parts of agent.
Further, the nonmetallic barrier material in the S4 includes diamond dust and polyurethane rubber.
The invention provides a kind of spraying coating process of compressor case protective coating, the Corrosion Protection of casing is improved, and
And material environment friendly, economic and practical, cost is low, can be sprayed repeatedly.
Embodiment
To make the purpose, technical scheme and advantage of the embodiment of the present invention clearer, below in conjunction with the embodiment of the present invention
In, the technical scheme in the embodiment of the present invention is clearly and completely described, it is clear that described embodiment is the present invention
Part of the embodiment, rather than whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art are not having
The every other embodiment obtained under the premise of creative work is made, belongs to the scope of protection of the invention.
Embodiment 1:
A kind of spraying coating process of compressor case protective coating, comprises the following steps:
S1. blasting treatment:Sandblasting roughening is carried out to cabinet parts surface to be sprayed;
S2. surface clean:Immerse in metal cleaner, deionized water and absolute ethyl alcohol and carry out ultrasonic cleaning processing, then
Vacuum drying;
S3. anti-corrosion primer:Plasma spraying anti-corrosion primer, the anti-corrosion bottom are carried out to the cabinet parts surface of the drying
Paint thickness is 0.1mm;
S4. spray-on coating;Cabinet parts surface to be sprayed is sprayed with nonmetallic barrier material, is made anti-
Coating is protected, is solidified 6 hours.
Further, the S1 sandblastings operation is purity quartzite with sand grains.
Further, in parts by weight, its component includes the anti-corrosion primer in the S3:150 parts of deionized water, alcohol
40 parts of yogurt liquid, 70 parts of water-based fluorocarbon resin, 120 parts of pure-acrylic emulsion, 10 parts of organic silicon emulsion, 20 parts of propane diols, levelling agent 5
Part, 5 parts of defoamer, 6 parts of wetting agent, 8 parts of dispersant, 40 parts of coalescents.
Further, the nonmetallic barrier material in the S4 includes diamond dust and polyurethane rubber.
Embodiment 2:
A kind of spraying coating process of compressor case protective coating, comprises the following steps:
S1. blasting treatment:Sandblasting roughening is carried out to cabinet parts surface to be sprayed;
S2. surface clean:Immerse in metal cleaner, deionized water and absolute ethyl alcohol and carry out ultrasonic cleaning processing, then
Vacuum drying;
S3. anti-corrosion primer:Plasma spraying anti-corrosion primer, the anti-corrosion bottom are carried out to the cabinet parts surface of the drying
Paint thickness is 0.15mm;
S4. spray-on coating;Cabinet parts surface to be sprayed is sprayed with nonmetallic barrier material, is made anti-
Coating is protected, is solidified 8 hours.
Further, the S1 sandblastings operation is purity quartzite with sand grains.
Further, in parts by weight, its component includes the anti-corrosion primer in the S3:200 parts of deionized water, alcohol
60 parts of yogurt liquid, 90 parts of water-based fluorocarbon resin, 140 parts of pure-acrylic emulsion, 20 parts of organic silicon emulsion, 35 parts of propane diols, levelling agent 6
Part, 6 parts of defoamer, 6 parts of wetting agent, 8 parts of dispersant, 40 parts of coalescents.
Further, the nonmetallic barrier material in the S4 includes diamond dust and polyurethane rubber.
Coating made from embodiment 1,2 is tested, and contrasted with the common coating in market.Result of the test is as follows:
The invention provides a kind of spraying coating process of compressor case protective coating, the Corrosion Protection of casing is improved, and
And material environment friendly, economic and practical, cost is low, can be sprayed repeatedly.
It should be noted that herein, such as first and second or the like relational terms are used merely to a reality
Body or operation make a distinction with another entity or operation, and not necessarily require or imply and deposited between these entities or operation
In any this actual relation or order.Moreover, term " comprising ", "comprising" or its any other variant are intended to
Nonexcludability includes, so that process, method, article or equipment including a series of elements not only will including those
Element, but also the other element including being not expressly set out, or it is this process, method, article or equipment also to include
Intrinsic key element.In the absence of more restrictions, the key element limited by sentence "including a ...", it is not excluded that
Other identical element also be present in process, method, article or equipment including the key element.
The above embodiments are merely illustrative of the technical solutions of the present invention, rather than its limitations;Although with reference to the foregoing embodiments
The present invention is described in detail, it will be understood by those within the art that:It still can be to foregoing each implementation
Technical scheme described in example is modified, or carries out equivalent substitution to which part technical characteristic;And these modification or
Replace, the essence of appropriate technical solution is departed from the spirit and scope of various embodiments of the present invention technical scheme.
Claims (4)
1. a kind of spraying coating process of compression case protective coating, it is characterised in that comprise the following steps:
S1. blasting treatment:Sandblasting roughening is carried out to cabinet parts surface to be sprayed;
S2. surface clean:Immerse in metal cleaner, deionized water and absolute ethyl alcohol and carry out ultrasonic cleaning processing, then vacuum
Drying;
S3. anti-corrosion primer:Plasma spraying anti-corrosion primer is carried out to the cabinet parts surface of the drying, the anti-corrosion primer is thick
Spend for 0.05-0.15mm;
S4. spray-on coating;Cabinet parts surface to be sprayed is sprayed with nonmetallic barrier material, protection is made and applies
Layer, solidify 6~8 hours.
2. the spraying coating process of compression case protective coating as claimed in claim 1, it is characterised in that the S1 sandblastings operation is used
Sand grains is purity quartzite.
3. the spraying coating process of compression case protective coating as claimed in claim 1, it is characterised in that the anti-corrosion bottom in the S3
In parts by weight, its component includes paint:150~200 parts of deionized water, 40~60 parts of alkyd emulsion, water-based fluorocarbon resin
70~90 parts, 120~140 parts of pure-acrylic emulsion, 10~20 parts of organic silicon emulsion, 20~35 parts of propane diols, 5~6 parts of levelling agent, disappear
5~6 parts of infusion, 4~6 parts of wetting agent, 4~8 parts of dispersant, 10~40 parts of coalescents.
4. the spraying coating process of compression case protective coating as claimed in claim 1, it is characterised in that nonmetallic in the S4
Barrier material includes diamond dust and polyurethane rubber.