CN107739490A - 一种互感器复合磁性材料 - Google Patents

一种互感器复合磁性材料 Download PDF

Info

Publication number
CN107739490A
CN107739490A CN201711102716.2A CN201711102716A CN107739490A CN 107739490 A CN107739490 A CN 107739490A CN 201711102716 A CN201711102716 A CN 201711102716A CN 107739490 A CN107739490 A CN 107739490A
Authority
CN
China
Prior art keywords
parts
oxide
raw material
composite magnetic
dispersant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201711102716.2A
Other languages
English (en)
Inventor
黄健俊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201711102716.2A priority Critical patent/CN107739490A/zh
Publication of CN107739490A publication Critical patent/CN107739490A/zh
Withdrawn legal-status Critical Current

Abstract

本发明公开了一种互感器复合磁性材料，按照重量份有以下原料组成：丙烯酸树脂15‑18份、聚乙二醇4‑9份、氯酸钠2‑5份、三氧化二铬4‑7份、二氧化钛2‑5份、三氧化二铁1‑4份、原料钕粉8‑12份、粘合剂4‑8份、分散剂3‑6份、固化剂6‑9份和氧化物材料7‑10份。本发明具有很强的弹性和可拉伸性，且耐高温性能好，增强了磁性且不易消磁，更重要的是节能环保效果好等特点。

Description

一种互感器复合磁性材料
技术领域
本发明涉及互感器相关材料的技术研发领域，尤其涉及一种互感器复合磁性材料。
背景技术
众所周知，中国是世界上最先发现物质磁性现象和应用磁性材料的国家。磁性产品种类繁多，应用广泛，在军事装备电子化及高新技术产业发展中起着重要作用，磁功能复合材料仅是其中的一个分支。复合磁性材料的主要优点是：密度小、耐冲击强度大，制品可进行切割、钻孔、焊接、层压和压花纹等加工，而且使用时不会发生碎裂，易于加工成尺寸精度高、薄壁、复杂形状的制品，现在复合磁性材料越来越多为人们所重视，是一种很有前途的基础功能材料。随着磁性材料的广泛应用，越来越多的领域需要用到磁性材料，磁性材料的要求也就越来越高，但目前现有的磁性材料弹性和拉伸性很差，而且影响环境。
发明内容
本发明的目的是为了解决现有技术中存在的缺点，而提出的一种互感器复合磁性材料。
为了实现上述目的，本发明采用了如下技术方案：
一种互感器复合磁性材料，按照重量份有以下原料组成：丙烯酸树脂15-18份、聚乙二醇4-9份、氯酸钠2-5份、三氧化二铬4-7份、二氧化钛2-5份、三氧化二铁1-4份、原料钕粉8-12份、粘合剂4-8份、分散剂3-6份、固化剂6-9份和氧化物材料7-10份；
所述氧化物材料包括氧化镍3-7份、氧化锌5-9份、氧化铝4-8份和氧化钴2-5份。
上述的一种互感器复合磁性材料，按照重量份有以下原料组成：丙烯酸树脂15-17份、聚乙二醇4-8份、氯酸钠2-4份、三氧化二铬4-6份、二氧化钛2-4份、三氧化二铁1-3份、原料钕粉8-11份、粘合剂4-7份、分散剂3-5份、固化剂6-8份和氧化物材料7-9份；
所述氧化物材料包括氧化镍3-6份、氧化锌5-8份、氧化铝4-7份和氧化钴2-4份。
上述的一种互感器复合磁性材料，按照重量份有以下原料组成：丙烯酸树脂16-17份、聚乙二醇5-8份、氯酸钠3-4份、三氧化二铬5-6份、二氧化钛3-4份、三氧化二铁2-3份、原料钕粉9-11份、粘合剂5-7份、分散剂4-5份、固化剂7-8份和氧化物材料8-9份；
所述氧化物材料包括氧化镍4-6份、氧化锌6-8份、氧化铝5-7份和氧化钴3-4份。
上述的一种互感器复合磁性材料，按照重量份有以下原料组成：丙烯酸树脂16.5份、聚乙二醇6.5份、氯酸钠3.5份、三氧化二铬5.5份、二氧化钛3.5份、三氧化二铁2.5份、原料钕粉10份、粘合剂6份、分散剂4.5份、固化剂7.5份和氧化物材料8.5份；
所述氧化物材料包括氧化镍5份、氧化锌7份、氧化铝6份和氧化钴3.5份。
与现有技术相比，本发明的有益效果是：
本发明具有很强的弹性和可拉伸性，且耐高温性能好，增强了磁性且不易消磁，更重要的是节能环保效果好等有益效果。
具体实施方式
实施例1
一种互感器复合磁性材料，按照重量份有以下原料组成：丙烯酸树脂16.5份、聚乙二醇6.5份、氯酸钠3.5份、三氧化二铬5.5份、二氧化钛3.5份、三氧化二铁2.5份、原料钕粉10份、粘合剂6份、分散剂4.5份、固化剂7.5份和氧化物材料8.5份；
所述氧化物材料包括氧化镍5份、氧化锌7份、氧化铝6份和氧化钴3.5份。
实施例2
上述的一种互感器复合磁性材料，按照重量份有以下原料组成：丙烯酸树脂15份、聚乙二醇4份、氯酸钠2份、三氧化二铬4份、二氧化钛2份、三氧化二铁1份、原料钕粉8份、粘合剂4份、分散剂3份、固化剂6份和氧化物材料7份；
所述氧化物材料包括氧化镍3份、氧化锌5份、氧化铝4份和氧化钴2份。
实施例3
上述的一种互感器复合磁性材料，按照重量份有以下原料组成：丙烯酸树脂18份、聚乙二醇9份、氯酸钠5份、三氧化二铬7份、二氧化钛5份、三氧化二铁4份、原料钕粉12份、粘合剂8份、分散剂6份、固化剂9份和氧化物材料10份；
所述氧化物材料包括氧化镍7份、氧化锌9份、氧化铝8份和氧化钴5份。
上面对本专利的较佳实施方式作了详细说明，但是本专利并不限于上述实施方式，在本领域的普通技术人员所具备的知识范围内，还可以在不脱离本专利宗旨的前提下做出各种变化。

Claims (4)

1.一种互感器复合磁性材料，其特征在于，按照重量份有以下原料组成：丙烯酸树脂15-18份、聚乙二醇4-9份、氯酸钠2-5份、三氧化二铬4-7份、二氧化钛2-5份、三氧化二铁1-4份、原料钕粉8-12份、粘合剂4-8份、分散剂3-6份、固化剂6-9份和氧化物材料7-10份；
所述氧化物材料包括氧化镍3-7份、氧化锌5-9份、氧化铝4-8份和氧化钴2-5份。
2.根据权利要求1所述的一种互感器复合磁性材料，其特征在于，按照重量份有以下原料组成：丙烯酸树脂15-17份、聚乙二醇4-8份、氯酸钠2-4份、三氧化二铬4-6份、二氧化钛2-4份、三氧化二铁1-3份、原料钕粉8-11份、粘合剂4-7份、分散剂3-5份、固化剂6-8份和氧化物材料7-9份；
所述氧化物材料包括氧化镍3-6份、氧化锌5-8份、氧化铝4-7份和氧化钴2-4份。
3.根据权利要求1所述的一种互感器复合磁性材料，其特征在于，按照重量份有以下原料组成：丙烯酸树脂16-17份、聚乙二醇5-8份、氯酸钠3-4份、三氧化二铬5-6份、二氧化钛3-4份、三氧化二铁2-3份、原料钕粉9-11份、粘合剂5-7份、分散剂4-5份、固化剂7-8份和氧化物材料8-9份；
所述氧化物材料包括氧化镍4-6份、氧化锌6-8份、氧化铝5-7份和氧化钴3-4份。
4.根据权利要求1所述的一种互感器复合磁性材料，其特征在于，按照重量份有以下原料组成：丙烯酸树脂16.5份、聚乙二醇6.5份、氯酸钠3.5份、三氧化二铬5.5份、二氧化钛3.5份、三氧化二铁2.5份、原料钕粉10份、粘合剂6份、分散剂4.5份、固化剂7.5份和氧化物材料8.5份；
所述氧化物材料包括氧化镍5份、氧化锌7份、氧化铝6份和氧化钴3.5份。
CN201711102716.2A 2017-11-07 2017-11-07 一种互感器复合磁性材料 Withdrawn CN107739490A (zh)