CN107603199A - 一种抗压性能好耐磨型泡沫塑料包装盒及其生产工艺 - Google Patents
一种抗压性能好耐磨型泡沫塑料包装盒及其生产工艺 Download PDFInfo
- Publication number
- CN107603199A CN107603199A CN201710903441.6A CN201710903441A CN107603199A CN 107603199 A CN107603199 A CN 107603199A CN 201710903441 A CN201710903441 A CN 201710903441A CN 107603199 A CN107603199 A CN 107603199A
- Authority
- CN
- China
- Prior art keywords
- parts
- good wear
- resisting type
- compressive property
- bubble wrap
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种抗压性能好耐磨型泡沫塑料包装盒及其生产工艺，包括以下重量份的各组份制备而成：多亚甲基多苯基多异氰酸酯50‑90份、聚醚多元醇10‑60份、甘油三醋酸酯5‑15份、硫酸钡粉3‑17份、氯磺化聚乙烯5‑19份、椰糠5‑10份、改性蒙脱土3‑13份、聚丙烯酰胺10‑18份、羧甲基淀粉钠2‑8份、月桂醇聚氧乙烯醚5‑8份、石蜡1‑5份等。本发明质轻、强度高、可吸收冲击载荷性能好、隔热、隔音性能好、透气，可在工业、农业、建筑、交通运输等领域广泛应用。
Description
技术领域
本发明涉及一种抗压性能好耐磨型泡沫塑料包装盒及其生产工艺，属于泡沫塑料包装盒技术领域。
背景技术
泡沫塑料是由大量气体微孔分散于固体塑料中而形成的一类高分子材料，具有质轻、隔热、吸音、减震等特性，且介电性能优于基体树脂，用途很广；几乎各种塑料均可作成泡沫塑料，发泡成型已成为塑料加工中一个重要领域。
泡沫塑料整体布满无数互相连通或互不连通的微孔而使表观密度明显降低的塑料，具有质轻、绝热、吸音、防震、耐潮、耐腐蚀等优点。泡沫塑料是以塑料为基本组分并含有大量气泡的聚合物材料, 因此也可以说是以气体为填料的复合塑料。
目前市场上用于电器产品包装的泡沫塑料存在硬度高、柔软性较差、质重、绝热效果差、透气效果不佳、抗震性能欠缺、耐腐蚀效果不佳等缺陷。
发明内容
本发明的目的是针对上述现有技术的不足，提供一种抗压性能好耐磨型泡沫塑料包装盒及其生产工艺。
本发明的技术方案如下：一种抗压性能好耐磨型泡沫塑料包装盒，其特征是，包括以下重量份的各组份制备而成：多亚甲基多苯基多异氰酸酯50-90份、聚醚多元醇10-60份、甘油三醋酸酯5-15份、硫酸钡粉3-17份、氯磺化聚乙烯5-19份、椰糠5-10份、改性蒙脱土3-13份、聚丙烯酰胺10-18份、羧甲基淀粉钠2-8份、月桂醇聚氧乙烯醚5-8份、石蜡1-5份、硬脂酸钙5-8份、黄豆蛋白粉10-20份、引发剂15-25份、玻璃纤维3-8份、马来酸酐3-8份、异戊烷1-5份、稳定剂1-5份、发泡剂15-25份、抗老化剂1-8份、硼酸5-12份、交联剂1-3份。
所述稳定剂为有机锡稳定剂。
所述引发剂为过氧化二苯甲酰。
所述交联剂为甲基丙烯酰胺。
所述发泡剂是偶氮二甲酰胺。
一种抗压性能好耐磨型泡沫塑料包装盒的生产工艺，其特征是，将塑料物料加热至熔融状态中, 借助强烈搅拌，把大量空气或其他气体引入液态塑料中，产生微孔；使微孔增长到一定体积；放入剩余物料，继续搅拌并加热30-300分钟；然后所有物料放入注射成型机中，发泡剂在机筒中分解，物料离开机头时，压力降到常压，溶入气体即膨胀发泡，最后得到该泡沫制品。
聚醚多元醇（简称聚醚）是由起始剂（含活性氢基团的化合物）与环氧乙烷（EO）、环氧丙烷（PO）、环氧丁烷（BO）等在催化剂存在下经加聚反应制得。聚醚产量最大者为以甘油（丙三醇）作起始剂和环氧化物（一般是PO与EO并用），通过改变PO和EO的加料方式（混合加或分开加）、加量比、加料次序等条件，生产出各种通用的聚醚多元醇。
多苯基多亚甲基多异氰酸酯，浅黄色至褐色粘稠液体,有刺激性气味,升温时能发生自聚作用,溶于氯苯、邻二氯苯、甲苯等。PAPI的活性低，蒸气压低，只是TDI的百分之一，故毒性很低。用于制造聚氨脂胶粘剂，也可直接加入橡胶胶粘剂中，改善橡胶与尼龙或聚酯线的粘接性能。贮存于阴凉、通风、干燥的库房内，远离火种、热源。
氯磺化聚乙烯由低密度聚乙烯或高密度聚乙烯经过氯化和氯磺化反应制得。为白色或黄色弹性体，能溶解于芳香烃及氯代烃不溶于脂肪及醇中，在酮和醚中只能溶胀不能溶解，有优异的耐臭氧性、耐大气老化性、耐化学腐蚀性等，较好的物理机械性能、耐老化性能、耐热及耐低温性、耐油性、耐燃性、耐磨性及耐电绝缘性。
与现有电器包装用的泡沫塑料相比，本发明具有很多优良的性能：质轻、强度高、可吸收冲击载荷性能好、隔热、隔音性能好、透气，也可在工业、农业、建筑、交通运输等领域广泛应用。
具体实施方式
一种抗压性能好耐磨型泡沫塑料包装盒，包括以下重量份的各组份制备而成：多亚甲基多苯基多异氰酸酯50-90份、聚醚多元醇10-60份、甘油三醋酸酯5-15份、硫酸钡粉3-17份、氯磺化聚乙烯5-19份、椰糠5-10份、改性蒙脱土3-13份、聚丙烯酰胺10-18份、羧甲基淀粉钠2-8份、月桂醇聚氧乙烯醚5-8份、石蜡1-5份、硬脂酸钙5-8份、黄豆蛋白粉10-20份、引发剂15-25份、玻璃纤维3-8份、马来酸酐3-8份、异戊烷1-5份、稳定剂1-5份、发泡剂15-25份、抗老化剂1-8份、硼酸5-12份、交联剂1-3份。
稳定剂为有机锡稳定剂,引发剂为过氧化二苯甲酰,交联剂为甲基丙烯酰胺,发泡剂是偶氮二甲酰胺。
一种抗压性能好耐磨型泡沫塑料包装盒的生产工艺，将塑料物料加热至熔融状态中, 借助强烈搅拌，把大量空气或其他气体引入液态塑料中，产生微孔；使微孔增长到一定体积；放入剩余物料，继续搅拌并加热30-300分钟；然后所有物料放入注射成型机中，发泡剂在机筒中分解，物料离开机头时，压力降到常压，溶入气体即膨胀发泡，最后得到该泡沫制品。
Claims (6)
1.一种抗压性能好耐磨型泡沫塑料包装盒，其特征是，包括以下重量份的各组份制备而成：多亚甲基多苯基多异氰酸酯50-90份、聚醚多元醇10-60份、甘油三醋酸酯5-15份、硫酸钡粉3-17份、氯磺化聚乙烯5-19份、椰糠5-10份、改性蒙脱土3-13份、聚丙烯酰胺10-18份、羧甲基淀粉钠2-8份、月桂醇聚氧乙烯醚5-8份、石蜡1-5份、硬脂酸钙5-8份、黄豆蛋白粉10-20份、引发剂15-25份、玻璃纤维3-8份、马来酸酐3-8份、异戊烷1-5份、稳定剂1-5份、发泡剂15-25份、抗老化剂1-8份、硼酸5-12份、交联剂1-3份。
2.根据权利要求1所述的一种抗压性能好耐磨型泡沫塑料包装盒，其特征是，所述稳定剂为有机锡稳定剂。
3.根据权利要求1所述的一种抗压性能好耐磨型泡沫塑料包装盒，其特征是，所述引发剂为过氧化二苯甲酰。
4.根据权利要求1所述的一种抗压性能好耐磨型泡沫塑料包装盒，其特征是，所述交联剂为甲基丙烯酰胺。
5.根据权利要求1所述的一种抗压性能好耐磨型泡沫塑料包装盒，其特征是，所述发泡剂是偶氮二甲酰胺。
6. 根据权利要求1-5中任一项所述的一种抗压性能好耐磨型泡沫塑料包装盒的生产工艺，其特征是，将塑料物料加热至熔融状态中, 借助强烈搅拌，把大量空气或其他气体引入液态塑料中，产生微孔；使微孔增长到一定体积；放入剩余物料，继续搅拌并加热30-300分钟；然后所有物料放入注射成型机中，发泡剂在机筒中分解，物料离开机头时，压力降到常压，溶入气体即膨胀发泡，最后得到该泡沫制品。