CN107599720A - 天然环保工艺品及其制备方法 - Google Patents
天然环保工艺品及其制备方法 Download PDFInfo
- Publication number
- CN107599720A CN107599720A CN201710778965.7A CN201710778965A CN107599720A CN 107599720 A CN107599720 A CN 107599720A CN 201710778965 A CN201710778965 A CN 201710778965A CN 107599720 A CN107599720 A CN 107599720A
- Authority
- CN
- China
- Prior art keywords
- parts
- natural
- handicraft
- flower
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种天然环保工艺品,由以下重量份数的各组分组成:天然花卉40~50份,茶渣3~5份,中草药20~25份;所述天然花卉由以下重量份数的各组分组成:荷花5份,玫瑰花5份,茉莉花2份,梅花2份,康乃馨2份,金银花2份,玉兰花2份,油菜花5份,牡丹花5份,牵牛花2份,山茶花5份;所述茶渣由以下重量份数的各组分组成:茶梗2份,茶叶10份;所述中草药由以下重量份数的各组分组成:丁香3份,檀香3份,葛根1份,艾草5份,白芷1份,花椒2份,冰片1份,樟脑2份,灵香草5份。本发明还涉及所述天然环保工艺品的制备方法,制作工艺简单,使用天然的原材料,清洁环保,制备出来的工艺品具有自然的美感,且具有防虫防腐的效果。
Description
技术领域
本发明涉及工艺品领域,更具体地,涉及一种天然环保工艺品及其制备方法。
背景技术
随着生活生产水平的提高,工艺品逐渐成为人们生活中不可或缺的一部分,作为摆设来装点环境,提高品位。现今市面上的工艺品多为陶瓷、镀金产品等,其制作过程一般需要高温烧结或者焊接等工艺,制作过程复杂,需要消耗一定能源,且对环境造成污染。
发明内容
本发明的目的是针对上述的问题,提供一种天然环保工艺品及其制备方法。
本发明目的通过以下技术方案予以实现:
提供一种天然环保工艺品,由以下重量份数的各组分组成:天然花卉40~50份,茶渣3~5份,中草药20~25份。
优选地,所述天然环保工艺品由以下重量份数的各组分组成:天然花卉45份,茶渣4份,中草药22份。
其中,所述天然花卉由以下重量份数的各组分组成:荷花5份,玫瑰花5份,茉莉花2份,梅花2份,康乃馨2份,金银花2份,玉兰花2份,油菜花5份,牡丹花5份,牵牛花2份,山茶花5份。
所述茶渣由以下重量份数的各组分组成:茶梗2份,茶叶10份。
所述中草药由以下重量份数的各组分组成:丁香3份,檀香3份,葛根1份,艾草5份,白芷1份,花椒2份,冰片1份,樟脑2份,灵香草5份。
本发明还提供了所述天然环保工艺品的制备方法,包括以下步骤:
S1.将中草药加入2~3倍量的水,加热煎煮30~60min,过滤得到浸泡药液,备用;
S2.将天然花卉去除腐败、霉变及杂物,清洗干净,切成条状,在100℃高温蒸汽保温30min,起到对天然花卉消毒杀菌的作用。然后放入浸泡药液中浸泡3~5h,烘干得到干花条备用;
S3.将茶渣用蒸汽蒸软,烘干后粉碎过50目筛,与干花条混合均匀,得到干料备用;如使用冲泡过的茶渣,可直接烘干,步骤更为简便快捷,且进行废物利用,更加环保;
S4.按干料质量5~8%取松香熔化,加热至其充分熔解,加入干料并混合均匀,得到原料;松香起到粘合剂的作用,让原料粘结更加牢固。
S5.将原料用蒸汽蒸软并装入工艺品模具,在温度120~200℃、压力1~3MPa的环境下将原料压制成型,密度至少0.5g/cm³,静置10~15h后脱模,干燥,得到工艺品。干燥可以为烘干、晒干或自然风干。
与现有技术相比,本发明具有以下有益效果:
本发明提供了一种天然环保工艺品,无需耗费大量能源,制作工艺简单,使用天然的原材料,清洁环保,不会对环境造成负担,还使制备出来的工艺品具有独特自然的质感,带有花卉本身的清香和药香,且具有防虫防腐的效果。
具体实施方式
下面结合具体实施例对本发明作进一步的说明。
实施例1
本实施例公开了一种天然环保工艺品,由以下重量份数的各组分组成:天然花卉40份,茶渣3份,中草药20份。
其中,所述天然花卉由以下重量份数的各组分组成:荷花5份,玫瑰花5份,茉莉花2份,梅花2份,康乃馨2份,金银花2份,玉兰花2份,油菜花5份,牡丹花5份,牵牛花2份,山茶花5份。所述茶渣由以下重量份数的各组分组成:茶梗2份,茶叶10份。所述中草药由以下重量份数的各组分组成:丁香3份,檀香3份,葛根1份,艾草5份,白芷1份,花椒2份,冰片1份,樟脑2份,灵香草5份。
实施例2
本实施例公开了一种天然环保工艺品,由以下重量份数的各组分组成:天然花卉50份,茶渣5份,中草药25份。
其中,所述天然花卉由以下重量份数的各组分组成:荷花5份,玫瑰花5份,茉莉花2份,梅花2份,康乃馨2份,金银花2份,玉兰花2份,油菜花5份,牡丹花5份,牵牛花2份,山茶花5份。所述茶渣由以下重量份数的各组分组成:茶梗2份,茶叶10份。所述中草药由以下重量份数的各组分组成:丁香3份,檀香3份,葛根1份,艾草5份,白芷1份,花椒2份,冰片1份,樟脑2份,灵香草5份。
实施例3
本实施例公开了一种天然环保工艺品,由以下重量份数的各组分组成:天然花卉48份,茶渣4份,中草药24份。
其中,所述天然花卉由以下重量份数的各组分组成:荷花5份,玫瑰花5份,茉莉花2份,梅花2份,康乃馨2份,金银花2份,玉兰花2份,油菜花5份,牡丹花5份,牵牛花2份,山茶花5份。所述茶渣由以下重量份数的各组分组成:茶梗2份,茶叶10份。所述中草药由以下重量份数的各组分组成:丁香3份,檀香3份,葛根1份,艾草5份,白芷1份,花椒2份,冰片1份,樟脑2份,灵香草5份。
实施例4
本实施例公开了一种天然环保工艺品,由以下重量份数的各组分组成:天然花卉45份,茶渣4份,中草药22份。
其中,所述天然花卉由以下重量份数的各组分组成:荷花5份,玫瑰花5份,茉莉花2份,梅花2份,康乃馨2份,金银花2份,玉兰花2份,油菜花5份,牡丹花5份,牵牛花2份,山茶花5份。所述茶渣由以下重量份数的各组分组成:茶梗2份,茶叶10份。所述中草药由以下重量份数的各组分组成:丁香3份,檀香3份,葛根1份,艾草5份,白芷1份,花椒2份,冰片1份,樟脑2份,灵香草5份。
实施例5
取实施例1~4任意实施例的重量组分制备天然环保工艺品,制备步骤如下:
S1.将中草药加入2倍量的水,加热煎煮30min,过滤得到浸泡药液,备用;
S2.将天然花卉去除腐败、霉变及杂物,清洗干净,切成条状,在100℃高温蒸汽保温30min,然后放入浸泡药液中浸泡3h,烘干得到干花条备用;
S3.将茶渣用蒸汽蒸软,烘干后粉碎过50目筛,与干花条混合均匀,得到干料备用;
S4.按干料质量5%取松香熔化,加热至其充分熔解,加入干料并混合均匀,得到原料;
S5.将原料用蒸汽蒸软并装入工艺品模具,在温度120℃、压力1MPa的环境下将原料压制成型,静置10h后脱模,晒干后得到工艺品。
实施例6
取实施例1~4任意实施例的重量组分制备天然环保工艺品,制备步骤如下:
S1.将中草药加入3倍量的水,加热煎煮60min,过滤得到浸泡药液,备用;
S2.将天然花卉去除腐败、霉变及杂物,清洗干净,切成条状,在100℃高温蒸汽保温30min,然后放入浸泡药液中浸泡5h,烘干得到干花条备用;
S3.将茶渣用蒸汽蒸软,烘干后粉碎过50目筛,与干花条混合均匀,得到干料备用;
S4.按干料质量8%取松香熔化,加热至其充分熔解,加入干料并混合均匀,得到原料;
S5.将原料用蒸汽蒸软并装入工艺品模具,将模具放入温度200℃、压力3MPa的环境下将原料压制成型,密度为0.6g/cm³,在模具内静置15h后脱模,自然风干后得到工艺品。
实施例7
取实施例1~4任意实施例的重量组分制备天然环保工艺品,制备步骤如下:
S1.将中草药加入2.5倍量的水,加热煎煮45min,过滤得到浸泡药液,备用;
S2.将天然花卉去除腐败、霉变及杂物,清洗干净,切成条状,在100℃高温蒸汽保温30min,然后放入浸泡药液中浸泡4h,烘干得到干花条备用;
S3.将茶渣用蒸汽蒸软,烘干后粉碎过50目筛,与干花条混合均匀,得到干料备用;
S4.按干料质量7%取松香熔化,加热至其充分熔解,加入干料并混合均匀,得到原料;
S5.将原料用蒸汽蒸软并装入工艺品模具,在温度180℃、压力2MPa的环境下将原料压制成型,在模具内静置12h后脱模,烘干后得到工艺品。
Claims (6)
1.一种天然环保工艺品,其特征在于,由以下重量分数的各组分组成:天然花卉40~50份,茶渣3~5份,中草药20~25份。
2.根据权利要求1所述的天然环保工艺品,其特征在于,由以下重量份数的各组分组成:天然花卉45份,茶渣4份,中草药22份。
3.根据权利要求1或2所述的天然环保工艺品,其特征在于,所述天然花卉由以下重量份数的各组分组成:荷花5份,玫瑰花5份,茉莉花2份,梅花2份,康乃馨2份,金银花2份,玉兰花2份,油菜花5份,牡丹花5份,牵牛花2份,山茶花5份。
4.根据权利要求1或2或3所述的天然环保工艺品,其特征在于,所述茶渣由以下重量份数的各组分组成:茶梗2份,茶叶10份。
5.根据权利要求1所述的天然环保工艺品,其特征在于,所述中草药由以下重量份数的各组分组成:丁香3份,檀香3份,葛根1份,艾草5份,白芷1份,花椒2份,冰片1份,樟脑2份,灵香草5份。
6.根据权利要求1或2所述天然环保工艺品的制备方法,其特征在于,包括以下步骤:
S1.将中草药加入2~3倍量的水,加热煎煮30~60min,过滤得到浸泡药液,备用;
S2.将天然花卉去除腐败、霉变及杂物,清洗干净,切成条状,在100℃高温蒸汽保温30min,然后放入浸泡药液中浸泡3~5h,烘干得到干花条备用;
S3.将茶渣用蒸汽蒸软,烘干后粉碎过50目筛,与干花条混合均匀,得到干料备用;
S4.按干料质量5~8%取松香熔化,加热至其充分熔解,加入干料并混合均匀,得到原料;
S5.将原料用蒸汽蒸软并装入工艺品模具,在温度120~200℃、压力1~3MPa的环境下将原料压制成型,静置10~15h后脱模,干燥,得到工艺品。