CN107556799A - 防火涂料及其制备方法 - Google Patents
防火涂料及其制备方法 Download PDFInfo
- Publication number
- CN107556799A CN107556799A CN201710802227.1A CN201710802227A CN107556799A CN 107556799 A CN107556799 A CN 107556799A CN 201710802227 A CN201710802227 A CN 201710802227A CN 107556799 A CN107556799 A CN 107556799A
- Authority
- CN
- China
- Prior art keywords
- parts
- fireproof coating
- water
- foaming agent
- inorganic filler
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开一种防火涂料及其制备方法，其中，该防火涂料由包含无机填料、粘合剂、氢氧化铝、发泡剂及水制备，各成分的组分比如下：无机填料20～30份；粘合剂10～20份；氢氧化铝10～25份；发泡剂10～25份；水10～25份。本发明的技术方案防火涂料涂覆于物体表面后，具有较佳的阻燃效果，能够起到防火和延长阻燃时间，同时满足粘接的防火涂料具有结构稳定的特点。
Description
技术领域
本发明涉及涂料技术领域，特别涉及一种防火涂料及其制备方法。
背景技术
建筑防火已经是影响建筑安全性能的主要技术指标，最近几年全国各地均发生了中的火灾，造成了人员伤亡及大量的财产损失，因此开发一种具有防火性能的涂料，对建筑的安全性起到至关重要的作用。
优异的建筑的防火涂料目前均有国外的几个大的厂家所垄断，中国市场鱼龙混杂的，以次充好的现象屡禁不止，为此，有必要提出一种价格合理，性能优异的防火涂料供市场使用。
有鉴于此，有必要对防火涂料进行进一步的改进。
发明内容
为解决至少一上述技术问题，本发明的主要目的是提供防火涂料及其制备方法。
为实现上述目的，本发明提出的一种防火涂料，由包含无机填料、粘合剂、氢氧化铝、发泡剂及水制备，各成分的组分比如下：
无机填料 20～30份；
粘合剂 10～20份；
氢氧化铝 10～25份；
发泡剂 10～25份；
水 10～25份。
其中，所述防火涂料由包含无机填料、粘合剂、氢氧化铝、发泡剂及水制备，各成分的组分比如下：
无机填料 25份；
粘合剂 15份；
氢氧化铝 20份；
发泡剂 20份；
水 20份。
其中，所述发泡剂为三聚氰胺。
其中，所述无机填料为粉煤灰、重钙、高岭土按照配比为1：1：2混合而成。
为实现上述目的，本发明提出的一种防火涂料的制备方法，包括如下步骤：
称重10～25重量份的水，并将水加入制备器皿中；
依次将20～30重量份无机填料、10～20重量份粘合剂、10～25重量份氢氧化铝、10～2重量份发泡剂加入制备器皿中；
常温常压下，以搅拌速度为900-1100rpm/min，持续搅拌40min，使各组分分散均匀，制备得到防火涂料。
本发明的技术方案主要采用在水溶液中添加氢氧化铝和发泡剂，氢氧化铝和三聚氰胺均是阻燃剂，能够在涂覆有该防火涂料的物体表面形成阻燃层，从而起到阻燃及长效防火时间的特点；另外，本实施例中，通过粘合剂能够提高附着效果，通过水溶液能够使氢氧化铝和发泡剂混合均匀，使得阻燃层的厚度均匀，从而起到较佳的阻燃效果。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明的一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例一
本发明的实施例中，该防火涂料，由包含无机填料、粘合剂、氢氧化铝、发泡剂及水制备，各成分的组分比如下：
无机填料 20～30份；
粘合剂 10～20份；
氢氧化铝 10～25份；
发泡剂 10～25份；
水 10～25份。
本发明的实施例中，所述发泡剂为三聚氰胺。三聚氰胺为阻燃剂，通过将氢氧化铝和三聚氰胺混合，能够增加阻燃剂的重量比，起到较佳的阻燃效果。可以理解的，该三聚氰胺仅为本实施例一优选的方案，其他类型的发泡剂也是可行方案。
其中，所述无机填料为粉煤灰、重钙、高岭土按照配比为1：1：2混合而成。
本发明的技术方案主要采用在水溶液中添加氢氧化铝和发泡剂，氢氧化铝和三聚氰胺均是阻燃剂，能够在涂覆有该防火涂料的物体表面形成阻燃层，从而起到阻燃及长效防火时间的特点；另外，本实施例中，通过粘合剂能够提高附着效果，通过水溶液能够使氢氧化铝和发泡剂混合均匀，使得阻燃层的厚度均匀，从而起到较佳的阻燃效果。
上述实施例的防火涂料的制备方法，包括如下步骤：
称重10～25重量份的水，并将水加入制备器皿中；
依次将20～30重量份无机填料、10～20重量份粘合剂、10～25重量份氢氧化铝、10～2重量份发泡剂加入制备器皿中，；
常温常压下，以搅拌速度为900-1100rpm/min，持续搅拌40min，使各组分分散均匀，制备得到防火涂料。
实施例二
本发明的实施例中，该防火涂料由包含无机填料、粘合剂、氢氧化铝、发泡剂及水制备，各成分的组分比如下：
无机填料 25份；
粘合剂 15份；
氢氧化铝 20份；
发泡剂 20份；
水 20份。
本发明的实施例中，所述发泡剂为三聚氰胺。三聚氰胺为阻燃剂，通过将氢氧化铝和三聚氰胺混合，能够增加阻燃剂的重量比，起到较佳的阻燃效果。可以理解的，该三聚氰胺仅为本实施例一优选的方案，其他类型的发泡剂也是可行方案。
其中，所述无机填料为粉煤灰、重钙、高岭土按照配比为1：1：2混合而成。
本发明的技术方案主要采用在水溶液中添加氢氧化铝和发泡剂，氢氧化铝和三聚氰胺均是阻燃剂，能够在涂覆有该防火涂料的物体表面形成阻燃层，从而起到阻燃及长效防火时间的特点；另外，本实施例中，通过粘合剂能够提高附着效果，通过水溶液能够使氢氧化铝和发泡剂混合均匀，使得阻燃层的厚度均匀，从而起到较佳的阻燃效果。
上述实施例的防火涂料的制备方法，包括如下步骤：
称重10～25重量份的水，并将水加入制备器皿中；
依次将20～30重量份无机填料、10～20重量份粘合剂、10～25重量份氢氧化铝、10～2重量份发泡剂加入制备器皿中；
常温常压下，以搅拌速度为900-1100rpm/min，持续搅拌40min，使各组分分散均匀，制备得到防火涂料。
具体测试结果，请参照表1，表1为本防火涂料的测试效果表。
表1
| 项目 | 指标 | 结果 |
| 容器中状态 | 无硬块，搅拌后呈均匀状态 | 合格 |
| 施工性 | 刷涂二道无障碍 | 合格 |
| 低温稳定性 | 不变质 | 不变质 |
| 涂膜外观 | 正常 | 正常 |
| 干燥时间（表干） ≤ | 2h | 1h |
| 耐碱性b（48h） | 无异常 | 无异常 |
| 耐水性b（96h） | 无异常 | 无异常 |
| 涂层耐温变性b（3次循环） | 无异常 | 无异常 |
以上所述仅为本发明的优选实施例，并非因此限制本发明的专利范围，凡是在本发明的发明构思下，利用本发明说明书内容所作的等效变换，或直接/间接运用在其他相关的技术领域均包括在本发明的专利保护范围内。
Claims (5)
1.一种防火涂料，其特征在于：所述防火涂料由包含无机填料、粘合剂、氢氧化铝、发泡剂及水制备，各成分的组分比如下：
无机填料 20～30份；
粘合剂 10～20份；
氢氧化铝 10～25份；
发泡剂 10～25份；
水 10～25份。
2.如权利要求1所述的防火涂料，其特征在于：所述防火涂料由包含无机填料、粘合剂、氢氧化铝、发泡剂及水制备，各成分的组分比如下：
无机填料 25份；
粘合剂 15份；
氢氧化铝 20份；
发泡剂 20份；
水 20份。
3.如权利要求1或2所述的防火涂料，其特征在于，所述发泡剂为三聚氰胺。
4.如权利要求1或2所述的防火涂料，其特征在于，所述无机填料为粉煤灰、重钙、高岭土按照配比为1：1：2混合而成。
5.一种防火涂料的制备方法，其特征在于，所述防火涂料的制备方法的制备方法包括如下步骤：
称重10～25重量份的水，并将水加入制备器皿中；
依次将20～30重量份无机填料、10～20重量份粘合剂、10～25重量份氢氧化铝、10～2重量份发泡剂加入制备器皿中；
常温常压下，以搅拌速度为900-1100rpm/min，持续搅拌40min，使各组分分散均匀，制备得到防火涂料。