CN107556799A - Fireproof coating and preparation method thereof - Google Patents
Fireproof coating and preparation method thereof Download PDFInfo
- Publication number
- CN107556799A CN107556799A CN201710802227.1A CN201710802227A CN107556799A CN 107556799 A CN107556799 A CN 107556799A CN 201710802227 A CN201710802227 A CN 201710802227A CN 107556799 A CN107556799 A CN 107556799A
- Authority
- CN
- China
- Prior art keywords
- parts
- fireproof coating
- water
- foaming agent
- inorganic filler
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention discloses a kind of fireproof coating and preparation method thereof, wherein, for the fireproof coating by being prepared comprising inorganic filler, adhesive, aluminium hydroxide, foaming agent and water, the component ratio of each composition is as follows：20~30 parts of inorganic filler；10~20 parts of adhesive；10~25 parts of aluminium hydroxide；10~25 parts of foaming agent；10~25 parts of water.After technical scheme fireproof coating is coated on body surface, there is preferable flame retardant effect, fire prevention can be played and extend duration of fire resistance, while meet that the fireproof coating of bonding has the characteristics of Stability Analysis of Structures.
Description
Technical field
The present invention relates to technical field of coatings, more particularly to a kind of fireproof coating and preparation method thereof.
Background technology
Building Fire Protection be influence building safety performance the key technical indexes, recent years all parts of the country there occurs
In fire, casualties and substantial amounts of property loss are caused, therefore develop a kind of coating with fire protecting performance, to building
Security play vital effect.
Several big producers that the fireproof coating of excellent building has foreign countries at present are monopolized, and the good and bad jumbled together for Chinese market
, shoddy phenomenon remains incessant after repeated prohibition, for this reason, it is necessary to propose a kind of reasonable price, the fireproof coating of excellent performance supplies city
Field uses.
In view of this, it is necessary to which fireproof coating is further improved.
The content of the invention
It is to provide fireproof coating and preparation method thereof to solve an at least above-mentioned technical problem, the main object of the present invention.
To achieve the above object, a kind of fireproof coating proposed by the present invention, by including inorganic filler, adhesive, hydroxide
Prepared by aluminium, foaming agent and water, the component ratio of each composition is as follows：
20~30 parts of inorganic filler；
10~20 parts of adhesive；
10~25 parts of aluminium hydroxide；
10~25 parts of foaming agent；
10~25 parts of water.
Wherein, the fireproof coating comprising inorganic filler, adhesive, aluminium hydroxide, foaming agent and water by preparing, each composition
Component ratio it is as follows：
25 parts of inorganic filler；
15 parts of adhesive；
20 parts of aluminium hydroxide；
20 parts of foaming agent；
20 parts of water.
Wherein, the foaming agent is melamine.
Wherein, the inorganic filler is that flyash, coarse whiting, kaolin according to proportioning are 1：1：2 mix.
To achieve the above object, the preparation method of a kind of fireproof coating proposed by the present invention, comprises the following steps：
The water for 10~25 parts by weight of weighing, and add water to and prepare in vessel；
Successively by 20~30 parts by weight of inorganic fillers, 10~20 parts by weight of binder, 10~25 parts by weight aluminium hydroxides, 10~2
Parts by weight of blowing agent addition is prepared in vessel；
Under normal temperature and pressure, using mixing speed as 900-1100rpm/min, 40min is persistently stirred, each component is uniformly dispersed, made
It is standby to obtain fireproof coating.
Technical scheme is mainly using addition aluminium hydroxide and foaming agent, aluminium hydroxide and trimerization in aqueous
Cyanamide is fire retardant, can form flame-retardant layer in the body surface coated with the fireproof coating, fire-retardant and long-acting so as to play
The characteristics of fire prevention time；In addition, in the present embodiment, adhesion effect can be improved by adhesive, hydrogen can be made by the aqueous solution
Aluminum oxide and foaming agent are well mixed so that the thickness of flame-retardant layer is uniform, so as to play preferable flame retardant effect.
Embodiment
The technical scheme in the embodiment of the present invention will be clearly and completely described below, it is clear that described implementation
Example is only the part of the embodiment of the present invention, rather than whole embodiments.It is general based on the embodiment in the present invention, this area
The every other embodiment that logical technical staff is obtained under the premise of creative work is not made, belong to what the present invention protected
Scope.
Embodiment one
In embodiments of the invention, the fireproof coating, by including inorganic filler, adhesive, aluminium hydroxide, foaming agent and water system
Standby, the component ratio of each composition is as follows：
20~30 parts of inorganic filler；
10~20 parts of adhesive；
10~25 parts of aluminium hydroxide；
10~25 parts of foaming agent；
10~25 parts of water.
In embodiments of the invention, the foaming agent is melamine.Melamine is fire retardant, by by aluminium hydroxide
Mixed with melamine, by increasing capacitance it is possible to increase the weight ratio of fire retardant, play preferable flame retardant effect.It should be understood that the melamine
Amine is only one preferable scheme of the present embodiment, and other kinds of foaming agent is also feasible program.
Wherein, the inorganic filler is that flyash, coarse whiting, kaolin according to proportioning are 1：1：2 mix.
Technical scheme is mainly using addition aluminium hydroxide and foaming agent, aluminium hydroxide and trimerization in aqueous
Cyanamide is fire retardant, can form flame-retardant layer in the body surface coated with the fireproof coating, fire-retardant and long-acting so as to play
The characteristics of fire prevention time；In addition, in the present embodiment, adhesion effect can be improved by adhesive, hydrogen can be made by the aqueous solution
Aluminum oxide and foaming agent are well mixed so that the thickness of flame-retardant layer is uniform, so as to play preferable flame retardant effect.
The preparation method of the fireproof coating of above-described embodiment, comprises the following steps：
The water for 10~25 parts by weight of weighing, and add water to and prepare in vessel；
Successively by 20~30 parts by weight of inorganic fillers, 10~20 parts by weight of binder, 10~25 parts by weight aluminium hydroxides, 10~2
Parts by weight of blowing agent addition is prepared in vessel,；
Under normal temperature and pressure, using mixing speed as 900-1100rpm/min, 40min is persistently stirred, each component is uniformly dispersed, made
It is standby to obtain fireproof coating.
Embodiment two
In embodiments of the invention, the fireproof coating by comprising inorganic filler, adhesive, aluminium hydroxide, foaming agent and water prepare,
The component ratio of each composition is as follows：
25 parts of inorganic filler；
15 parts of adhesive；
20 parts of aluminium hydroxide；
20 parts of foaming agent；
20 parts of water.
In embodiments of the invention, the foaming agent is melamine.Melamine is fire retardant, by by aluminium hydroxide
Mixed with melamine, by increasing capacitance it is possible to increase the weight ratio of fire retardant, play preferable flame retardant effect.It should be understood that the melamine
Amine is only one preferable scheme of the present embodiment, and other kinds of foaming agent is also feasible program.
Wherein, the inorganic filler is that flyash, coarse whiting, kaolin according to proportioning are 1：1：2 mix.
Technical scheme is mainly using addition aluminium hydroxide and foaming agent, aluminium hydroxide and trimerization in aqueous
Cyanamide is fire retardant, can form flame-retardant layer in the body surface coated with the fireproof coating, fire-retardant and long-acting so as to play
The characteristics of fire prevention time；In addition, in the present embodiment, adhesion effect can be improved by adhesive, hydrogen can be made by the aqueous solution
Aluminum oxide and foaming agent are well mixed so that the thickness of flame-retardant layer is uniform, so as to play preferable flame retardant effect.
The preparation method of the fireproof coating of above-described embodiment, comprises the following steps：
The water for 10~25 parts by weight of weighing, and add water to and prepare in vessel；
Successively by 20~30 parts by weight of inorganic fillers, 10~20 parts by weight of binder, 10~25 parts by weight aluminium hydroxides, 10~2
Parts by weight of blowing agent addition is prepared in vessel；
Under normal temperature and pressure, using mixing speed as 900-1100rpm/min, 40min is persistently stirred, each component is uniformly dispersed, made
It is standby to obtain fireproof coating.
Specific test result, refer to table 1, and table 1 is the test effect table of this fireproof coating.
Table 1
| Project | Index | As a result |
| Condition in container | It is in uniform state after stirring without lump | It is qualified |
| Application property | It is accessible to brush two | It is qualified |
| Low-temperature stability | Never degenerate | Never degenerate |
| Appearance of film | Normally | Normally |
| Drying time（Surface drying） ≤ | 2h | 1h |
| Alkali resistance b（48h） | It is without exception | It is without exception |
| Water resistance b（96h） | It is without exception | It is without exception |
| Coating temperature-change resistance b（3 circulations） | It is without exception | It is without exception |
The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the scope of the invention, it is every in the present invention
Inventive concept under, the equivalent transformation made using present specification, or directly/be used in other related skills indirectly
Art field is included in the scope of patent protection of the present invention.
Claims (5)
- A kind of 1. fireproof coating, it is characterised in that：The fireproof coating is by including inorganic filler, adhesive, aluminium hydroxide, foaming Prepared by agent and water, the component ratio of each composition is as follows：20~30 parts of inorganic filler；10~20 parts of adhesive；10~25 parts of aluminium hydroxide；10~25 parts of foaming agent；10~25 parts of water.
- 2. fireproof coating as claimed in claim 1, it is characterised in that：The fireproof coating by comprising inorganic filler, adhesive, Prepared by aluminium hydroxide, foaming agent and water, the component ratio of each composition is as follows：25 parts of inorganic filler；15 parts of adhesive；20 parts of aluminium hydroxide；20 parts of foaming agent；20 parts of water.
- 3. fireproof coating as claimed in claim 1 or 2, it is characterised in that the foaming agent is melamine.
- 4. fireproof coating as claimed in claim 1 or 2, it is characterised in that the inorganic filler is flyash, coarse whiting, kaolinite Soil is 1 according to proportioning：1：2 mix.
- 5. a kind of preparation method of fireproof coating, it is characterised in that the preparation method of the preparation method of the fireproof coating includes Following steps：The water for 10~25 parts by weight of weighing, and add water to and prepare in vessel；Successively by 20~30 parts by weight of inorganic fillers, 10~20 parts by weight of binder, 10~25 parts by weight aluminium hydroxides, 10~2 Parts by weight of blowing agent addition is prepared in vessel；Under normal temperature and pressure, using mixing speed as 900-1100rpm/min, 40min is persistently stirred, each component is uniformly dispersed, made It is standby to obtain fireproof coating.