CN107324765A - A kind of floor tile for adjusting humidity - Google Patents
A kind of floor tile for adjusting humidity Download PDFInfo
- Publication number
- CN107324765A CN107324765A CN201710533564.5A CN201710533564A CN107324765A CN 107324765 A CN107324765 A CN 107324765A CN 201710533564 A CN201710533564 A CN 201710533564A CN 107324765 A CN107324765 A CN 107324765A
- Authority
- CN
- China
- Prior art keywords
- parts
- floor tile
- zeolite
- adobe
- humidity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of floor tile, and in particular to a kind of floor tile of regulation humidity.A kind of floor tile of regulation humidity of the present invention, is made up of the component of following parts by weight：20~25 parts of zeolite, 10~15 parts of allophane, 10~12 parts of sepiolite mixes 2~5 parts of silver zeolite, 15~18 parts of kaolinite, 10~15 parts of attapulgite.The floor tile of the present invention has the effect of regulation indoor humidity and sterilization.
Description
Technical field
The present invention relates to a kind of floor tile, and in particular to a kind of floor tile of regulation humidity.
Background technology
The Sichuan Basin belongs to gentle subtropical monsoon climate, with the winter is warm, spring drought, summer heat, autumn rain the characteristics of.It is same with China
The In Middle And Lower Reaches of Changjiang River of latitude is compared, and 1 monthly mean temperature is typically all higher by more than 3 DEG C, and extreme minimum temperature is typically higher by 10
More than DEG C, the features such as causing basin moisture weight.
Due to climate reasons, indoor clothing and other items often gets damp.For this reason, it may be necessary to which a kind of can adjust the floor tile of humidity
To solve this problem.
The content of the invention
The invention solves the problems that first technical problem be to provide it is a kind of adjust humidity floor tile.
A kind of floor tile for adjusting humidity, is made up of the component of following parts by weight：20~25 parts of zeolite, allophane 10~15
Part, 10~12 parts of sepiolite mixes 2~5 parts of silver zeolite, 15~18 parts of kaolinite, 10~15 parts of attapulgite.
It is preferred that, 25 parts of zeolite, 10 parts of allophane, 12 parts of sepiolite mixes 5 parts of silver zeolite, 15 parts of kaolinite, concave convex rod
10 parts of soil.
Second technical problem of the problem to be solved in the present invention is to provide a kind of preparation method for adjusting humidity floor tile.
A kind of preparation method for the floor tile for adjusting humidity, is prepared from according to the following steps：
A, kaolinite, attapulgite crushed with ball mill, cross 110~120 mesh sieves, add water obtained slurry, then by spray
Mist is dried and powder is made, standby；
B, by zeolite, allophane, sepiolite, mix silver zeolite, crush, cross 120~130 mesh sieves, add water obtained slurry, quiet
4~6h is put, the particle that water content is 6~8% is spray dried to, it is standby；
C, particle made from step a and step b mixed, be pressed into adobe, adobe is entered into kiln is drying to obtain a kind of regulation
The floor tile of humidity.
It is preferred that, adobe enters kiln drying drying method and is, adobe is warming up into 800~850 DEG C, guarantor with 5~9 DEG C/min speed
2~3h of temperature, then 1200~1220 DEG C are risen to 20~25 DEG C/min speed, it is incubated 4~6h.
Beneficial effects of the present invention：A kind of floor tile for adjusting humidity produced by the present invention, passes through zeolite, allophane, sea
Afrodite, the effect for mixing silver zeolite, adjust indoor humidity.Silver zeolite is mixed due to also added in floor tile, sterilization can also be played
Effect.
Embodiment
The invention solves the problems that first technical problem be to provide it is a kind of adjust humidity floor tile.
A kind of floor tile for adjusting humidity, is made up of the component of following parts by weight：20~25 parts of zeolite, allophane 10~15
Part, 10~12 parts of sepiolite mixes 2~5 parts of silver zeolite, 15~18 parts of kaolinite, 10~15 parts of attapulgite.
Zeolite, allophane, sepiolite have absorb-discharge humid, reach the purpose of damping.Sterilization can be played by mixing silver zeolite
Effect, the common material with humidity conditioning function while humidity is adjusted, can not kill the bacterium of growth.
It is preferred that, 25 parts of zeolite, 10 parts of allophane, 12 parts of sepiolite mixes 5 parts of silver zeolite, 15 parts of kaolinite, concave convex rod
10 parts of soil.
Second technical problem of the problem to be solved in the present invention is to provide a kind of preparation method for adjusting humidity floor tile.
A kind of preparation method for the floor tile for adjusting humidity, is prepared from according to the following steps：
A, kaolinite, attapulgite crushed with ball mill, cross 110~120 mesh sieves, add water obtained slurry, then by spray
Mist is dried and powder is made, standby；
B, by zeolite, allophane, sepiolite, mix silver zeolite, crush, cross 120~130 mesh sieves, add water obtained slurry, quiet
4~6h is put, the particle that water content is 6~8% is spray dried to, it is standby；
C, particle made from step a and step b mixed, be pressed into adobe, adobe is entered into kiln is drying to obtain a kind of regulation
The floor tile of humidity.
By zeolite, allophane, sepiolite, silver zeolite is mixed, after crushing, cross 120~130 mesh sieves, raw material can be made preferable
Performance moisture absorbing.
It is preferred that, adobe enters kiln drying drying method and is, adobe is warming up into 800~850 DEG C, guarantor with 5~9 DEG C/min speed
2~3h of temperature, then 1200~1220 DEG C are risen to 20~25 DEG C/min speed, it is incubated 4~6h.
The embodiment of the present invention is further described with reference to embodiment, not therefore by present invention limit
System is among described scope of embodiments.
Embodiment 1
A, by 15 parts of kaolinite, 10 parts of attapulgite, crushed with ball mill, cross 120 mesh sieves, add water obtained slurry, then passes through
Cross spray drying and powder is made, it is standby；
B, by 20 parts of zeolite, 10 parts of allophane, 11 parts of sepiolite, mix 4 parts of silver zeolite, crush, cross 120 mesh sieves, add water
Slurry is made, 6h is stood, the particle that water content is 6~8% is spray dried to, it is standby；
C, particle made from step a and step b mixed, is pressed into adobe, adobe is sent into kiln, adobe with 9 DEG C/
Min speed is warming up to 850 DEG C, is incubated 3h, then rises to 1220 DEG C with 20 DEG C/min speed, is incubated 4h, produces a kind of regulation
The floor tile of humidity.
Embodiment 2
A, by 15 parts of kaolinite, 10 parts of attapulgite, crushed with ball mill, cross 115 mesh sieves, add water obtained slurry, then passes through
Cross spray drying and powder is made, it is standby；
B, by 25 parts of zeolite, 10 parts of allophane, 12 parts of sepiolite, mix 5 parts of silver zeolite, crush, cross 125 mesh sieves, add water
Slurry is made, 6h is stood, the particle that water content is 6~8% is spray dried to, it is standby；
C, particle made from step a and step b mixed, is pressed into adobe, adobe is sent into kiln, adobe with 8 DEG C/
Min speed is warming up to 800 DEG C, is incubated 3h, then rises to 1220 DEG C with 20 DEG C/min speed, is incubated 4h, produces a kind of regulation
The floor tile of humidity.
Claims (4)
1. a kind of floor tile for adjusting humidity, it is characterised in that be made up of the component of following parts by weight：20~25 parts of zeolite, water aluminium
10~15 parts of diamond stone, 10~12 parts of sepiolite mixes 2~5 parts of silver zeolite, 15~18 parts of kaolinite, 10~15 parts of attapulgite.
2. a kind of floor tile for adjusting humidity according to claim 1, it is characterised in that 25 parts of zeolite, 10 parts of allophane,
12 parts of sepiolite, mixes 5 parts of silver zeolite, 15 parts of kaolinite, 10 parts of attapulgite.
3. the preparation method of the floor tile of a kind of regulation humidity described in claim 1 or 2, it is characterised in that make according to the following steps
It is standby to form：
A, kaolinite, attapulgite crushed with ball mill, cross 110~120 mesh sieves, add water obtained slurry, then it is dry by spraying
It is dry to be made powder, it is standby；
B, by zeolite, allophane, sepiolite, mix silver zeolite, crush, cross 120~130 mesh sieves, add water obtained slurry, stand 4
~6h, is spray dried to the particle that water content is 6~8%, standby；
C, particle made from step a and step b mixed, be pressed into adobe, adobe is entered into kiln is drying to obtain a kind of regulation humidity
Floor tile.
4. the preparation method of a kind of floor tile for adjusting humidity according to claim 3, it is characterised in that it is dry that adobe enters kiln drying
Method is that adobe is warming up into 800~850 DEG C with 5~9 DEG C/min speed, 2~3h is incubated, then with 20~25 DEG C/min's
Speed rises to 1200~1220 DEG C, is incubated 4~6h.