CN107226670A - A kind of plasterboard for adjusting humidity - Google Patents
A kind of plasterboard for adjusting humidity Download PDFInfo
- Publication number
- CN107226670A CN107226670A CN201710533561.1A CN201710533561A CN107226670A CN 107226670 A CN107226670 A CN 107226670A CN 201710533561 A CN201710533561 A CN 201710533561A CN 107226670 A CN107226670 A CN 107226670A
- Authority
- CN
- China
- Prior art keywords
- parts
- plasterboard
- powder
- humidity
- zeolite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of gypsum, and in particular to a kind of plasterboard of regulation humidity.A kind of plasterboard for adjusting humidity, is made up of the raw material of following parts by weight：30~35 parts of semi-hydrated gypsum, 10~12 parts of talcum powder, 10~15 parts of zeolite nano-zinc oxide composite material, 10~12 parts of montmorillonite, 0.2~0.3 part of cellulose ether, 1~3 part of latex powder.Plasterboard produced by the present invention, can adjust indoor humidity, and with the effect of sterilization.
Description
Technical field
The present invention relates to a kind of gypsum, and in particular to a kind of plasterboard of regulation humidity.
Background technology
The Sichuan Basin belongs to gentle subtropical monsoon climate, with the winter is warm, spring drought, summer heat, autumn rain the characteristics of.It is same with China
The In Middle And Lower Reaches of Changjiang River of latitude is compared, and 1 monthly mean temperature is typically all higher by more than 3 DEG C, and extreme minimum temperature is typically higher by 10
More than DEG C, the features such as causing basin moisture weight.
Due to climate reasons, indoor clothing and other items, food often get damp.For this reason, it may be necessary to which one kind can adjust humidity
Plasterboard solve this problem.
The content of the invention
The invention solves the problems that first technical problem be to provide it is a kind of adjust humidity plasterboard.
A kind of plasterboard for adjusting humidity, is made up of the raw material of following parts by weight：30~35 parts of semi-hydrated gypsum, talcum powder 10
~12 parts, 10~15 parts of zeolite-nano-zinc oxide composite material, 10~12 parts of montmorillonite, 0.2~0.3 part of cellulose ether, latex
1~3 part of powder.
It is preferred that, it is made up of the raw material of following parts by weight：30 parts of semi-hydrated gypsum, 12 parts of talcum powder, zeolite-nano zine oxide
15 parts of composite, 10 parts of montmorillonite, 0.3 part of cellulose ether, 1 part of latex powder.
The invention solves the problems that second technical problem be to provide it is a kind of adjust humidity plasterboard preparation method.
A kind of preparation method for the plasterboard for adjusting humidity, is prepared from as follows：
A, zeolite-nano-zinc oxide composite material and montmorillonite be subjected to ball milling, cross 100~120 mesh sieves, powder is made；
B, powder and semi-hydrated gypsum, talcum powder, cellulose ether, latex powder mixed, add water stirring, obtains slurry；
C, the slurry is sprayed on behind Thistle board surface cooled down, then be dried, the gypsum of adjusted humidity
Plate.
It is preferred that, in step c, the temperature of spraying slurry therewith is 50~55 DEG C.
It is preferred that, in step c, drying means is that 10~20min is dried at present 80~90 DEG C, then at 150~180 DEG C
5~8min of lower drying.
Beneficial effects of the present invention：Plasterboard produced by the present invention, can adjust indoor humidity, and with the work of sterilization
With.
Embodiment
The invention solves the problems that first technical problem be to provide it is a kind of adjust humidity plasterboard.
A kind of plasterboard for adjusting humidity, is made up of the raw material of following parts by weight：30~35 parts of semi-hydrated gypsum, talcum powder 10
~12 parts, 10~15 parts of zeolite-nano-zinc oxide composite material, 10~12 parts of montmorillonite, 0.2~0.3 part of cellulose ether, latex
1~3 part of powder.
Zinc oxide is difficult to disperse, using zeolite-zinc oxide composite, zinc oxide can be made to be more dispersible within plasterboard
On.And zeolite can also carry out moisture adsorption and releasing, indoor humidity is adjusted.The sterilization of zeolite-nano-zinc oxide composite material is more longlasting.
It is preferred that, it is made up of the raw material of following parts by weight：30 parts of semi-hydrated gypsum, 12 parts of talcum powder, zeolite-nano zine oxide
15 parts of composite, 10 parts of montmorillonite, 0.3 part of cellulose ether, 1 part of latex powder.
The invention solves the problems that second technical problem be to provide it is a kind of adjust humidity plasterboard preparation method.
A kind of preparation method for the plasterboard for adjusting humidity, is prepared from as follows：
A, zeolite-nano-zinc oxide composite material and montmorillonite be subjected to ball milling, cross 100~120 mesh sieves, powder is made；
B, powder and semi-hydrated gypsum, talcum powder, cellulose ether, latex powder mixed, add water stirring, obtains slurry；
C, the slurry is sprayed on behind Thistle board surface cooled down, then be dried, the gypsum of adjusted humidity
Plate.
It is preferred that, in step c, the temperature of spraying slurry therewith is 50~55 DEG C.
It is preferred that, in step c, drying means is that 10~20min is dried at present 80~90 DEG C, then at 150~180 DEG C
5~8min of lower drying.
The embodiment of the present invention is further described with reference to embodiment, not therefore by present invention limit
System is among described scope of embodiments.
Embodiment 1
A, 10 parts of zeolite-nano-zinc oxide composite materials and 10 parts of montmorillonites are subjected to ball millings, cross 100 mesh sieves, powder is made
Material；
B, powder and 30 parts of semi-hydrated gypsums, 10 parts of talcum powder, 0.3 part of cellulose ether, 1 part of latex powder mixed, add water and stir
Mix, obtain slurry；
C, the slurry is heated to 50 DEG C, then is sprayed on after Paper-faced gyp plate surface and cools down, be then dried again, first
20min, then dry 8min, the plasterboard of adjusted humidity at 150 DEG C are dried at 80 DEG C.
Embodiment 2
A, 15 parts of zeolite-nano-zinc oxide composite materials and 10 parts of montmorillonites are subjected to ball millings, cross 110 mesh sieves, powder is made
Material；
B, powder and 30 parts of semi-hydrated gypsums, 12 parts of talcum powder, 0.3 part of cellulose ether, 1 part of latex powder mixed, add water and stir
Mix, obtain slurry；
C, the slurry is heated to 52 DEG C, then is sprayed on after Paper-faced gyp plate surface and cools down, be then dried again, first
20min, then dry 5min, the plasterboard of adjusted humidity at 170 DEG C are dried at 80 DEG C.
Claims (5)
1. a kind of plasterboard for adjusting humidity, it is characterised in that be made up of the raw material of following parts by weight：Semi-hydrated gypsum 30~35
Part, 10~12 parts of talcum powder, 10~15 parts of zeolite-nano-zinc oxide composite material, 10~12 parts of montmorillonite, cellulose ether 0.2
~0.3 part, 1~3 part of latex powder.
2. a kind of plasterboard for adjusting humidity according to claim 1, it is characterised in that by the raw material group of following parts by weight
Into：30 parts of semi-hydrated gypsum, 12 parts of talcum powder, 15 parts of zeolite-nano-zinc oxide composite material, 10 parts of montmorillonite, cellulose ether 0.3
Part, 1 part of latex powder.
3. the preparation method of the plasterboard of a kind of regulation humidity described in any one of claim 1 or 2, it is characterised in that by such as
Lower step is prepared from：
A, zeolite-nano-zinc oxide composite material and montmorillonite be subjected to ball milling, cross 100~120 mesh sieves, powder is made；
B, powder and semi-hydrated gypsum, talcum powder, cellulose ether, latex powder mixed, add water stirring, obtains slurry；
C, the slurry is sprayed on behind Thistle board surface cooled down, then be dried, the plasterboard of adjusted humidity.
4. a kind of plasterboard for adjusting humidity according to claim 3, it is characterised in that in step c, spray slurry therewith
Temperature be 50~55 DEG C.
5. a kind of plasterboard for adjusting humidity according to claim 3, it is characterised in that in step c, drying means is,
10~20min, then dry 5~8min at 150~180 DEG C are first dried at 80~90 DEG C.