CN107287920A - A kind of waterproof anti-dye bar code printing trademark belt and its preparation technology - Google Patents
A kind of waterproof anti-dye bar code printing trademark belt and its preparation technology Download PDFInfo
- Publication number
- CN107287920A CN107287920A CN201710575839.1A CN201710575839A CN107287920A CN 107287920 A CN107287920 A CN 107287920A CN 201710575839 A CN201710575839 A CN 201710575839A CN 107287920 A CN107287920 A CN 107287920A
- Authority
- CN
- China
- Prior art keywords
- parts
- coating
- base fabric
- dye
- bar code
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of waterproof anti-dye bar code printing trademark belt and its preparation technology, the waterproof anti-dye bar code printing trademark belt includes base fabric and coating, base fabric is formed by warp thread and weft yarn plain weave, warp thread and weft yarn are used as main component using terylene, make base fabric inner hydrophobic, addition stainless steel fibre improves the toughness of base fabric and the zygosity with coating；Coating is made up of 20~30 parts of aqueous polyester resins, 8~15 parts of polyacrylate, 5~10 parts of fillers, 1.5~2.5 parts of modified polyvinylalcohols, 1~3 part of crosslinking agent, 0.5~1.5 part of brightening agent and 30~40 parts of water, polyacrylate and modified polyvinylalcohol create hydrophobic environment, improve and pad m-nitrobenzene sodium sulfonate solution in the use of titanium dioxide and preparation technology in the water proofing property of aqueous polyester resin stability and coating, filler and play dual resist printing effect.The characteristics of waterproof anti-dye bar code printing trademark belt of the present invention has good, wear-resisting dimensionally stable, printing adaptability, waterproof and anti-dye.
Description
Technical field
The present invention relates to trademark belt technical field, and in particular to a kind of waterproof anti-dye bar code printing trademark belt and its preparation
Technique.
Background technology
Printed label tape is the fritter fabric for being printed on the marks such as trade names, manufactory, name of the country, specification, generally with high branch
Cotton yarn, dacron thread, Polyamide Yarns or artificial silk make latitude and longitude, and plain weave or satin weave made-up belt are woven on inkle loom, is processed by dyeing and finishing,
Formed again by the label printing machine printing of band class.Requirement more and more higher with consumer to clothes, trade mark is used as the important of clothes
Mark, the object also increasingly paid close attention to as people.Some clothes fugitive color in washing, and trademark belt staining is caused trade mark
On printed data it is smudgy, bar code reading does not go out, by multiple clothes washing, the easy aging of trademark belt, water under the washing away of water
Inside into trademark belt yarn can be caused loosely to deform, fold occurs in surface, therefore clothes trade mark needs to meet pattern accurately,
It is smooth well-pressed, outside the good basic printing performance of printing adaptability, it should also have waterproof, the performance of anti-dye.
The Chinese invention patent application of Application No. 201610777726.5, discloses a kind of water proof fire retardant anti-dye trade mark
Band production technology.By adding waterproofing agent and resist agent in formula is padded so that the trademark belt produced possesses waterproof and anti-
The function of dyeing, but the firmness that is combined to waterproofing agent and resist agent in fabric of this mode and the uniformity of distribution will
Ask very high, do not ensure that anti-good waterproof and anti-dye performance, and coating does not possess waterproof and resist printing function, water and dyestuff
It can be trapped in into coating inside it, permanent accumulate can destroy the coating even internal structure of fabric, reduction of service life, because
This, is necessary to the processing that coating carries out waterproof anti-dye.
Fabric coating, is a kind of macromolecule compound for being spread evenly across fabric face, it is existed by adhesive effect
Fabric face formation film, can not only improve outward appearance, moreover it is possible to increase the function of fabric, fabric is had printable, waterproof, ventilation
The specific function such as moisture-inhibiting, fire-retardant, resist printing.Coating adhesive has two kinds of solvent-borne type and drainage pattern, solvent by medium classification when in use
Type has a water pressure resistance, good film-forming property the advantages of, but toxicity is big, and inflammable and explosive, solvent recovery is costly.And drainage pattern is nontoxic,
Safety, cost is relatively low, is more suitable for the coating adhesive of trademark belt, but its defect existed is good hydrophilic property.How one is developed
Plant using drainage pattern coating adhesive as main body, the coating suitable for trademark belt of good water proofing property is provided simultaneously with, as urgently to be resolved hurrily
The problem of.
The content of the invention
The invention solves the problems that above-mentioned technical problem is so as to provide a kind of waterproof anti-dye bar code printing trademark belt and its preparation
Technique.Described waterproof anti-dye bar code printing trademark belt has waterproof, anti-dye, dimensionally stable, printing adaptability good, wear-resisting
The characteristics of.Base fabric and coating all possess the function of waterproof and anti-dye, it is ensured that water and dyestuff cannot be introduced into inside trademark belt, coating
Play a major role.Main body of the coating using aqueous polyester resin as coating, adhesive property is good, safety non-toxic, while having good
Water-proof function.
To reach above-mentioned purpose, the concrete technical scheme that the present invention is used is as follows：
A kind of waterproof anti-dye bar code printing trademark belt, including base fabric and coating, the base fabric are formed by warp thread and weft yarn plain weave,
Warp thread and weft yarn use 50~75D complex yarn, and the complex yarn composition is：Terylene 65~80%, stainless steel fibre 20~
35%, 85~100g/m of base fabric grammes per square metre2；The coating is coated in scrim surfaces, coating by 20~30 parts of aqueous polyester resins, 8~
15 parts of polyacrylate, 5~10 parts of fillers, 1.5~2.5 parts of modified polyvinylalcohols, 1~3 part of crosslinking agent, 0.5~1.5 part brighten
Agent and 30~40 parts of water compositions.
It is preferred that, the coating by 24~28 parts of aqueous polyester resins, 8~13 parts of polyacrylate, 5~8 parts of fillers,
1.5~2 parts of modified polyvinylalcohols, 1.8~2.4 parts of crosslinking agents, 0.7~1.2 part of brightening agent and 35~40 parts of water compositions.
It is preferred that, the thickness of the coating is 0.3~0.5mm.
It is preferred that, the filler for etc. white carbon, talcum powder and the titanium dioxide of mass parts mix, the strong suction of white carbon
Ink and the good covering of titanium dioxide improve the printing adaptability of trademark belt, and talcum powder is used to increase the smooth degree of feel.
It is preferred that, the crosslinking agent is enclosed type water-based isocyanate, and enclosed type water-based isocyanate overcomes isocyanic acid
The big defect of the high reaction activity and toxicity of ester, reacts to form friendship with the hydroxyl on molecular resin chain, carboxyl, amino groups
Connection, significantly improves the adhesive force of polyester and polyacrylate, color stability, wearability.
A kind of preparation technology of waterproof anti-dye bar code printing trademark belt, comprises the following steps：
（1）Base fabric is manufactured：Base fabric, 85~100g/m of grammes per square metre are formed through weaving by skewer using warp thread and weft yarn2, warp thread and weft yarn
Using 50~75D complex yarn, complex yarn is obtained by 65~80% terylene and 20~35% stainless steel fibre blending；
（2）Desizing is washed：Clot, desizing washing, 80~90 DEG C of washing temperature；
（3）Thermal finalization is handled：180~185 DEG C of heat setting temperature, shape 40~60m/min of speed, and cloth pads resist printing before sizing
The agent aqueous solution, rolls 2~4kg/cm of power2；
（4）Coating：By weight by 20~30 parts of aqueous polyester resins, 8~15 parts of polyacrylate, 5~10 parts of fillers, 1.5
~2.5 parts of modified polyvinylalcohols, 1~3 part of crosslinking agent, 0.5~1.5 part of brightening agent and 30~40 parts of water are well mixed, roller coat in
Base fabric, wet coating amount during roller coat is 20~30g/ m2, coating layer thickness is 0.3~0.5mm；
（5）Drying：Base fabric feeding drying room after coating is subjected to drying and processing, drying temperature is controlled in 80~100 DEG C, time 15
~20min；
（6）Rewinding, cutting.
It is preferred that, step（3）The resist agent aqueous solution is that the m-nitrobenzene sodium sulfonate that mass fraction is 1.5~3% is molten
Liquid.
It is preferred that, the coating step is by weight by 24~28 parts of aqueous polyester resins, 8~13 parts of polyacrylate, 5
~8 parts of fillers, 1.5~2 parts of modified polyvinylalcohols, 1.8~2.4 parts of crosslinking agents, 0.7~1.2 part of brightening agent and 35~40 parts of water
Well mixed, wet coating amount of roller coat when base fabric, roller coat is 20~30g/ m2, coating layer thickness is 0.3~0.5mm.
It is preferred that, the coating compound method is as follows：First aqueous polyester resin, 5 fillers are added to the water, 65 are heated to
~80 DEG C stirring 25~30min, then sequentially add polyacrylate, modified polyvinylalcohol, brightening agent, crosslinking agent stirring 25~
30min。
The invention has the advantages that：
1st, warp thread and weft yarn be using terylene and the complex yarn of stainless steel fibre, terylene intensity is high, elastic good, high abrasion resistance,
Hydrophobicity is good, with its main component as yarn, plays a part of interior waterproof.But terylene is thermoplastic, and surface
Active group is few, therefore poor dimensional stability, is easily shunk after hot-working, easily occurs stress relaxation, it is difficult to glue at the interface obtained
Close effect.The present invention by terylene add stainless steel fibre solve the above problems, stainless steel fibre have be unlikely to deform,
The toughness of base fabric and the zygosity with coating can be improved after the advantages of high bending resistance, tensile strength, with terylene compound use, this
The electric conductivity that outer stainless steel fibre has can play a part of eliminating electrostatic.
2nd, using main body of the aqueous polyester resin as coating, waterborne polyester has the characteristics of full, hardness high glaze is good,
More importantly its cohesive force to dacron is strong, contains hydrophilic and hydrophobic grouping in waterborne polyester macromolecule in addition, can be with
The surface tension of water is reduced, contributes to wetting of the water to solid, is conducive to filler scattered in water.Made using polyacrylate
For assisted resin, polyacrylate can form good luster and water-fast film, and ageing-resistant performance is good, with good cohesive, glue
Knot pollution is small.Because the presence of a large amount of ester bonds in polyester causes the stability to hydrolysis resistance of waterborne polyester, storage stability poor, add
Plus the modified polyvinylalcohol with good water resistance, create hydrophobic environment jointly with polyacrylate, make hydrone be difficult to enter
Into ester bond, the water proofing property of aqueous polyester resin stability to hydrolysis resistance and material is improved.Coating preparation side of the present invention
Aqueous polyester resin, filler and water are first well mixed by method, dispersed filler, the abundant dissolving for ensureing aqueous polyester resin, then according to
It is secondary addition polyacrylate, modified polyvinylalcohol, brightening agent, crosslinking agent, be gradually completing aqueous polyester resin hydrophobically modified and
Crosslinking between molecular resin, obtained coating ingredients are evenly distributed, stabilized structure, and caking property is good, and waterproof action is strong.
3rd, filler occupies volume and played a role, and immobilization role is played to the side chain of resin, improves the intensity of coating and wear-resisting
Property.The present invention, as filler, improves the adaptability of printing using white carbon, talcum powder and titanium dioxide.Titanium dioxide is also as painting
The mechanical resist agent of layer prevents the entrance of dyestuff, while the process that the resist agent aqueous solution is padded in preparation technology is ensured on fiber not
Dyestuff can be adsorbed, both combine and obtain good anti-Color.
Embodiment
With reference to embodiment, the invention will be further described.
Embodiment 1
A kind of waterproof anti-dye bar code printing trademark belt, including base fabric and coating, the base fabric are formed by warp thread and weft yarn plain weave,
Warp thread and weft yarn use 50D complex yarn, and the complex yarn composition is：Terylene 80%, stainless steel fibre 20%, base fabric grammes per square metre
85 g/m2；The coating is coated in scrim surfaces, and the thickness of coating is 0.3mm, coating by 30 parts of aqueous polyester resins, 15 parts
Polyacrylate, 10 parts of fillers, 2.5 parts of modified polyvinylalcohols, 3 parts of enclosed type water-based isocyanates, 1.5 parts of brightening agents and 40 parts
Water is constituted, filler for etc. white carbon, talcum powder and the titanium dioxide of mass parts mix.
Waterproof anti-dye bar code printing trademark belt preparation technology is as follows：（1）Base fabric is manufactured：It is stainless by 80% terylene and 20%
Steel fibre blending obtains complex yarn, using 50D complex yarn as warp thread and weft yarn, and warp thread and weft yarn are by skewer through weaving
Form base fabric, the g/m of grammes per square metre 852；（2）Desizing is washed：Clot, desizing washing, 80 DEG C of washing temperature；（3）Thermal finalization is handled：Heat
180 DEG C of setting temperature, shape speed 40m/min, and cloth pads 1.5% m-nitrobenzene sodium sulfonate solution before sizing, rolls power 4kg/
cm；（4）Coating：First 30 parts of aqueous polyester resins, 10 parts of fillers are added in 40 parts of water, are heated to
80 DEG C of stirring 30min, then sequentially add 15 parts of polyacrylate, 2.5 parts of modified polyvinylalcohol, 1.5 parts of brightening agents,
3 parts of enclosed type water-based isocyanates stir 30min, and wet coating amount of roller coat when base fabric, roller coat is 25g/ m2；（5）Drying：Will
Base fabric feeding drying room after coating carries out drying and processing, and drying temperature is controlled in 90 DEG C, time 18min；（6）Rewinding, cutting.
Embodiment 2
A kind of waterproof anti-dye bar code printing trademark belt, including base fabric and coating, the base fabric are formed by warp thread and weft yarn plain weave,
Warp thread and weft yarn use 60D complex yarn, and the complex yarn composition is：Terylene 72%, stainless steel fibre 28%, base fabric grammes per square metre
90 g/m2；The coating is coated in scrim surfaces, and the thickness of coating is 0.4mm, coating by 25 parts of aqueous polyester resins, 10 parts
Polyacrylate, 8 parts of fillers, 1.8 parts of modified polyvinylalcohols, 2 parts of enclosed type water-based isocyanates, 1 part of brightening agent and 38 parts of water
Composition, filler for etc. white carbon, talcum powder and the titanium dioxide of mass parts mix.
Waterproof anti-dye bar code printing trademark belt preparation technology is as follows：（1）Base fabric is manufactured：It is stainless by 72% terylene and 28%
Steel fibre blending obtains complex yarn, using 60D complex yarn as warp thread and weft yarn, and warp thread and weft yarn are by skewer through weaving
Form base fabric, the g/m of grammes per square metre 902；（2）Desizing is washed：Clot, desizing washing, 85 DEG C of washing temperature；（3）Thermal finalization is handled：Heat
182 DEG C of setting temperature, shape speed 50m/min, and cloth pads 2% m-nitrobenzene sodium sulfonate solution before sizing, rolls power 3kg/
cm2；（4）Coating：First 25 parts of aqueous polyester resins, 8 parts of fillers are added in 38 parts of water, 70 DEG C of stirring 28min are heated to, so
10 parts of polyacrylate, 1.8 parts of modified polyvinylalcohol, 1 part of brightening agent, 2 parts of enclosed type water-based isocyanates are sequentially added afterwards
30min is stirred, wet coating amount of roller coat when base fabric, roller coat is 20g/ m2；（5）Drying：Base fabric feeding drying room after coating is entered
Row drying and processing, drying temperature is controlled in 80 DEG C, time 15min；（6）Rewinding, cutting.
Embodiment 3
A kind of waterproof anti-dye bar code printing trademark belt, including base fabric and coating, the base fabric are formed by warp thread and weft yarn plain weave,
Warp thread and weft yarn use 65D complex yarn, and the complex yarn composition is：Terylene 70%, stainless steel fibre 30%, base fabric grammes per square metre
92 g/m2；The coating is coated in scrim surfaces, and the thickness of coating is 0.3mm, coating by 24 parts of aqueous polyester resins, 12 parts
Polyacrylate, 6 parts of fillers, 1.6 parts of modified polyvinylalcohols, 1.8 parts of enclosed type water-based isocyanates, 0.8 part of brightening agent and 30
Part water composition, filler for etc. white carbon, talcum powder and the titanium dioxide of mass parts mix.
Waterproof anti-dye bar code printing trademark belt preparation technology is as follows：（1）Base fabric is manufactured：It is stainless by 70% terylene and 30%
Steel fibre blending obtains complex yarn, using 65D complex yarn as warp thread and weft yarn, and warp thread and weft yarn are by skewer through weaving
Form base fabric, the g/m of grammes per square metre 922；（2）Desizing is washed：Clot, desizing washing, 80 DEG C of washing temperature；（3）Thermal finalization is handled：Heat
185 DEG C of setting temperature, shape speed 45m/min, and cloth pads 1.8% m-nitrobenzene sodium sulfonate solution before sizing, rolls power
2.8kg/cm2；（4）Coating：First 24 parts of aqueous polyester resins, 6 parts of fillers are added in 30 parts of water, 68 DEG C of stirrings are heated to
30min, then sequentially adds 12 parts of polyacrylate, 1.6 parts of modified polyvinylalcohols, 0.8 part of brightening agent, 1.8 parts of enclosed type water
Property isocyanates stirring 25min, wet coating amount of roller coat when base fabric, roller coat be 28g/ m2；（5）Drying：By the base fabric after coating
Send into drying room and carry out drying and processing, drying temperature is controlled in 95 DEG C, time 16min；（6）Rewinding, cutting.
Embodiment 4
A kind of waterproof anti-dye bar code printing trademark belt, including base fabric and coating, the base fabric are formed by warp thread and weft yarn plain weave,
Warp thread and weft yarn use 70D complex yarn, and the complex yarn composition is：Terylene 68%, stainless steel fibre 32%, base fabric grammes per square metre
96 g/m2；The coating is coated in scrim surfaces, and the thickness of coating is 0.4mm, and coating is gathered by 28 parts of aqueous polyester resins, 8 parts
Acrylate, 6 parts of fillers, 2 parts of modified polyvinylalcohols, 2.4 parts of enclosed type water-based isocyanates, 1.2 parts of brightening agents and 36 parts of water
Composition, filler for etc. white carbon, talcum powder and the titanium dioxide of mass parts mix.
Waterproof anti-dye bar code printing trademark belt preparation technology is as follows：（1）Base fabric is manufactured：It is stainless by 68% terylene and 32%
Steel fibre blending obtains complex yarn, using 70D complex yarn as warp thread and weft yarn, and warp thread and weft yarn are by skewer through weaving
Form base fabric, grammes per square metre 96g/m2；（2）Desizing is washed：Clot, desizing washing, 88 DEG C of washing temperature；（3）Thermal finalization is handled：Heat is fixed
182 DEG C of type temperature, shape speed 52m/min, and cloth pads 2.4% m-nitrobenzene sodium sulfonate solution before sizing, rolls power 3.6kg/
cm2；（4）Coating：First 28 parts of aqueous polyester resins, 6 parts of fillers are added in 36 parts of water, 75 DEG C of stirring 28min are heated to, so
After sequentially add 8 parts of polyacrylate, 2 parts of modified polyvinylalcohols, 1.2 parts of brightening agents, 2.4 parts of enclosed type water-based isocyanates and stir
28min is mixed, wet coating amount of roller coat when base fabric, roller coat is 24g/ m2；（5）Drying：Base fabric feeding drying room after coating is carried out
Drying and processing, drying temperature is controlled in 85 DEG C, time 20min；（6）Rewinding, cutting.
Embodiment 5
A kind of waterproof anti-dye bar code printing trademark belt, including base fabric and coating, the base fabric are formed by warp thread and weft yarn plain weave,
Warp thread and weft yarn use 75D complex yarn, and the complex yarn composition is：Terylene 65%, stainless steel fibre 35%, base fabric grammes per square metre
98 g/m2；The coating is coated in scrim surfaces, and the thickness of coating is 0.5mm, and coating is gathered by 20 parts of aqueous polyester resins, 8 parts
Acrylate, 5 parts of fillers, 1.5 parts of modified polyvinylalcohols, 1 part of enclosed type water-based isocyanate, 0.5 part of brightening agent and 35 parts of water
Composition, filler for etc. white carbon, talcum powder and the titanium dioxide of mass parts mix.
Waterproof anti-dye bar code printing trademark belt preparation technology is as follows：（1）Base fabric is manufactured：It is stainless by 65% terylene and 35%
Steel fibre blending obtains complex yarn, using 75D complex yarn as warp thread and weft yarn, and warp thread and weft yarn are by skewer through weaving
Form base fabric, the g/m of grammes per square metre 982；（2）Desizing is washed：Clot, desizing washing, 90 DEG C of washing temperature；（3）Thermal finalization is handled：Heat
185 DEG C of setting temperature, shape speed 60m/min, and cloth pads 3% m-nitrobenzene sodium sulfonate solution before sizing, rolls power 2kg/
cm2；（4）Coating：First 20 parts of aqueous polyester resins, 5 parts of fillers are added in 35 parts of water, 65 DEG C of stirring 25min are heated to, so
After sequentially add 8 parts of polyacrylate, 1.5 parts of modified polyvinylalcohols, 0.5 part of brightening agent, 1 part of enclosed type water-based isocyanate and stir
28min is mixed, wet coating amount of roller coat when base fabric, roller coat is 30g/ m2；（5）Drying：Base fabric feeding drying room after coating is carried out
Drying and processing, drying temperature is controlled in 100 DEG C, time 20min；（6）Rewinding, cutting.
Comparative example 1：Other are same as Example 1 in addition to the compound method of the coating in preparation technology for trademark belt,
The compound method of the coating of comparative example 1 is by 30 parts of aqueous polyester resins, 10 parts of fillers, 15 parts of polyacrylate, 2.5 parts of modifications
Polyvinyl alcohol, 1.5 parts of brightening agents, 3 parts of enclosed type water-based isocyanates are added in 40 parts of water simultaneously, are heated to 80 DEG C of stirrings
60min。
Comparative example 2：Ordinary polyester trademark belt.
Water proofing property, anti-dye test are carried out to the trademark belt of embodiment 1~5 and comparative example 1~2, test result is such as
Shown in table 1.
Waterproofing tests method：With reference to FZ/T 01004-2008 test water permeability resistances, with reference to GB/T 4745-1997 tests
Surface moisture resistance.Surface moisture resistance is evaluated with spray rating：1 grade-surface is all soaked, the dewetting of 2 grades-surface one, 3 grades-
Surface has unconnected small area to soak, and when 4 grades-surface is not moistened but speckles with droplet, and 5 grades-surface, which is not soaked, is not also stained with
There is droplet.
Anti-dye method of testing：By trademark belt immersion temperature 60 C, the concentration 5g/L of embodiment 1~5 and comparative example
Aqueous dye solutions in, stand 30min after magnetic agitation 30min.Take out trademark belt cleaning, drying, counterstain degree.
Each embodiment the performance test results of table 1
It can be seen from upper table data, compared with ordinary polyester trademark belt, the water permeability resistance of embodiment 1~5, surface moisture resistance, anti-dye
Color is much better than ordinary polyester trademark belt, with good waterproof and anti-dye.Comparison with embodiment 2 can draw, this hair
Bright described coating compound method is particularly important, changes waterproof and anti-dye effect that component order of addition directly affects trademark belt
Really.
Embodiment described above is only explanation of the invention, is not limitation of the present invention, people in the art
Equivalent transformation and modification that member makes according to the present invention, belong to protection scope of the present invention.
Claims (9)
1. a kind of waterproof anti-dye bar code printing trademark belt, it is characterised in that：Including base fabric and coating, the base fabric by warp thread and
Weft yarn plain weave is formed, and warp thread and weft yarn are using 50~75D complex yarn, and the complex yarn, which is constituted, is：Terylene 65~80%,
Stainless steel fibre 20~35%, 85~100g/m of base fabric grammes per square metre2；The coating is coated in scrim surfaces, and coating is by 20~30 parts of water
Property polyester resin, 8~15 parts of polyacrylate, 5~10 parts of fillers, 1.5~2.5 parts of modified polyvinylalcohols, 1~3 part of crosslinking agent,
0.5~1.5 part of brightening agent and 30~40 parts of water compositions.
2. waterproof anti-dye bar code printing trademark belt according to claim 1, it is characterised in that：The coating is by 24~28
Part aqueous polyester resin, 8~13 parts of polyacrylate, 5~8 parts of fillers, 1.5~2 parts of modified polyvinylalcohols, 1.8~2.4 parts of friendships
Join agent, 0.7~1.2 part of brightening agent and 35~40 parts of water compositions.
3. waterproof anti-dye bar code printing trademark belt according to claim 1, it is characterised in that：The thickness of the coating is
0.3~0.5mm.
4. waterproof anti-dye bar code printing trademark belt according to claim 1, it is characterised in that：The filler for etc. quality
The white carbon, talcum powder and titanium dioxide of part are mixed.
5. waterproof anti-dye bar code printing trademark belt according to claim 1, it is characterised in that：The crosslinking agent is closing
Type water-based isocyanate.
6. a kind of preparation technology of waterproof anti-dye bar code printing trademark belt, it is characterised in that comprise the following steps：
（1）Base fabric is manufactured：Base fabric, 85~100g/m of grammes per square metre are formed through weaving by skewer using warp thread and weft yarn2, warp thread and weft yarn
Using 50~75D complex yarn, complex yarn is obtained by 65~80% terylene and 20~35% stainless steel fibre blending；
（2）Desizing is washed：Clot, desizing washing, 80~90 DEG C of washing temperature；
（3）Thermal finalization is handled：180~185 DEG C of heat setting temperature, shape 40~60m/min of speed, and cloth pads resist printing before sizing
The agent aqueous solution, rolls 2~4kg/cm of power2；
（4）Coating：By weight by 20~30 parts of aqueous polyester resins, 8~15 parts of polyacrylate, 5~10 parts of fillers, 1.5
~2.5 parts of modified polyvinylalcohols, 1~3 part of crosslinking agent, 0.5~1.5 part of brightening agent and 30~40 parts of water are well mixed, roller coat in
Base fabric, wet coating amount during roller coat is 20~30g/ m2, coating layer thickness is 0.3~0.5mm；
（5）Drying：Base fabric feeding drying room after coating is subjected to drying and processing, drying temperature is controlled in 80~100 DEG C, time 15
~20min；
（6）Rewinding, cutting.
7. the preparation technology of waterproof anti-dye printed label tape according to claim 6, it is characterised in that：Step（3）Institute
It is the m-nitrobenzene sodium sulfonate solution that mass fraction is 1.5~3% to state the resist agent aqueous solution.
8. the preparation technology of waterproof anti-dye printed label tape according to claim 6, it is characterised in that：The coating step
Suddenly 24~28 parts of aqueous polyester resins, 8~13 parts of polyacrylate, 5~8 parts of fillers, 1.5~2 parts of modifications are gathered by weight
Vinyl alcohol, 1.8~2.4 parts of crosslinking agents, 0.7~1.2 part of brightening agent and 35~40 parts of water are well mixed, and roller coat is in base fabric, roller coat
When wet coating amount be 20~30g/ m2, coating layer thickness is 0.3~0.5mm.
9. the preparation technology of waterproof anti-dye printed label tape according to claim 6, it is characterised in that：The coating is matched somebody with somebody
Method processed is as follows：First aqueous polyester resin, filler are added to the water, 65~80 DEG C of stirrings 25~30min, Ran Houyi are heated to
Secondary addition polyacrylate, modified polyvinylalcohol, brightening agent, crosslinking agent stir 25~30min.