CN107216038A - A kind of furnace transmutation glaze and be soaked with the glaze ceramic body method for cooking and application - Google Patents
A kind of furnace transmutation glaze and be soaked with the glaze ceramic body method for cooking and application Download PDFInfo
- Publication number
- CN107216038A CN107216038A CN201610157574.9A CN201610157574A CN107216038A CN 107216038 A CN107216038 A CN 107216038A CN 201610157574 A CN201610157574 A CN 201610157574A CN 107216038 A CN107216038 A CN 107216038A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- period
- ceramic body
- insulation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of furnace transmutation glaze and be soaked with the glaze ceramic body method for cooking and application, the glaze includes the raw material of following parts by weight:40 parts of albite, 50 parts of potassium feldspar, 60 parts of quartz, 20 parts of calcium carbonate, 10 parts of calcining zinc oxide, 10 parts of titanium oxide, 20 parts of Longyan kaolin, 3 parts of di-iron trioxide, 3 parts of import cobalt oxide, 6 parts of Britain's bovine bone powder.The sintering procedure is:After ceramic body leaching glaze 720 DEG C are burnt from 0 DEG C of heating, then 1125 DEG C are cooled to after being heated to 1140 DEG C after a while, it is anxious again to be warming up to 1220 DEG C, insulation a period of time is warming up to 1248 DEG C, oxidation is burnt till to 1260 DEG C, 910 DEG C are chilled to after being cooled to 1255 DEG C, insulation a period of time for a period of time again, normal cooling is incubated after a period of time again afterwards until opening kiln.The surface for the ceramic body fired by the glaze of the present invention is smooth fine and smooth, bright and lustrous gorgeous.
Description
Technical field
The present invention relates to a kind of ceramic glaze, and in particular to a kind of furnace transmutation glaze and be soaked with the glaze ceramic body burning
Method processed and application.
Background technology
When furnace transmutation glaze refers to that ceramic implement is fired in kiln, due in kiln also have multiple element, oxidized or reduction,
Unexpected glaze colours effect is presented after kiln discharge.Traditional furnace transmutation glaze firing temperature is high, the time is long, and heat consumption is big, causes production
Cost is high, and the pattern that existing furnace transmutation glaze is formed is generally crystallization flower, and its style sheet one, color and luster are dim, and appreciation effect is poor.
The content of the invention
There is provided a kind of furnace transmutation glaze and the ceramic body for being soaked with the glaze to overcome the deficiencies in the prior art by the present invention
Method for cooking and application, the surface for the ceramic body fired by the glaze of the present invention are smooth fine and smooth, bright and lustrous gorgeous.
The furnace transmutation glaze of the present invention, the technical scheme of use is to include the raw material of following parts by weight:
5-70 parts of albite 10-90 parts of quartz of 10-80 parts of potassium feldspar
6-50 parts of calcium carbonate 2-40 parts of titanium oxide of 3-40 parts of calcining zinc oxide
Kaolin 2-50 parts of Longyan 0.5-10 parts of import cobalt oxide of 0.5-10 parts of di-iron trioxide
Bovine bone powder 1-16 parts of Britain.
Further:
20-40 parts of albite 30-60 parts of quartz of 30-50 parts of potassium feldspar
12-20 parts of calcium carbonate 5-10 parts of titanium oxide of 6-10 parts of calcining zinc oxide
Kaolin 5-20 parts of Longyan 1-3 parts of import cobalt oxide of 1-3 parts of di-iron trioxide
Bovine bone powder 3-6 parts of Britain.
Further:
20 parts of albite, 30 parts of potassium feldspar, 30 parts of quartz
12 parts of calcium carbonate, 6 parts of calcining zinc oxide, 5 parts of titanium oxide
5 parts of Longyan kaolin, 1 part of di-iron trioxide, 1 part of import cobalt oxide
3 parts of Britain's bovine bone powder.
Further:
40 parts of albite, 50 parts of potassium feldspar, 60 parts of quartz
20 parts of calcium carbonate, 10 parts of calcining zinc oxide, 10 parts of titanium oxide
20 parts of Longyan kaolin, 3 parts of di-iron trioxide, 3 parts of import cobalt oxide
6 parts of Britain's bovine bone powder.
Further:
30 parts of albite, 40 parts of potassium feldspar, 45 parts of quartz
16 parts of calcium carbonate, 8 parts of calcining zinc oxide, 7 parts of titanium oxide
12 parts of Longyan kaolin, 2 parts of di-iron trioxide, 2 parts of import cobalt oxide
4.5 parts of Britain's bovine bone powder.
The method for cooking of the ceramic body of the furnace transmutation glaze of the present invention is soaked with, the technical scheme of use is to comprise the following steps:
1), ceramic body leaching glaze after burn 600-800 DEG C from 0 DEG C of heating,
2)And then cool to 985-1175 DEG C after being heated to 1000-1200 DEG C after a while,
3), it is anxious again be warming up to 1150-1250 DEG C, insulation a period of time is warming up to 1175-1280 DEG C, and 1200- is burnt till in oxidation
1320 DEG C,
4), be cooled to 1200-1315 DEG C for a period of time again, be chilled to 850-1000 DEG C after insulation a period of time,
5), after insulation a period of time afterwards again normal cooling until opening kiln.
Further,
1), ceramic body leaching glaze after burn 720 DEG C from 0 DEG C of heating,
2)And then cool to 1125 DEG C after being heated to 1140 DEG C after a while,
3), it is anxious again be warming up to 1220 DEG C, insulation a period of time is warming up to 1248 DEG C, and oxidation is burnt till to 1260 DEG C,
4), be cooled to 1255 DEG C for a period of time again, be chilled to 910 DEG C after insulation a period of time,
5), after insulation a period of time afterwards again normal cooling until opening kiln.
The beneficial effects of the invention are as follows:Firing temperature of the invention is low, the firing time is short, saves the energy, obtained pottery
Ceramic products are writing brush made of rabbit's hair blueness, and its surface is smooth fine and smooth, bright and lustrous gorgeous, the artistic appreciation with uniqueness, and glaze cost
Low, manufacture craft is simple, easy to use.
Embodiment:
Embodiment one
Furnace transmutation glaze in the present embodiment includes the raw material of following parts by weight:
30 parts of albite, 40 parts of potassium feldspar, 45 parts of quartz
16 parts of calcium carbonate, 8 parts of calcining zinc oxide, 7 parts of titanium oxide
12 parts of Longyan kaolin, 2 parts of di-iron trioxide, 2 parts of import cobalt oxide
4.5 parts of Britain's bovine bone powder,
The raw material of above-mentioned parts by weight is mixed and made into glaze,
Soaking the mode being fired after glaze to ceramic body with above-mentioned glaze is:
1), ceramic body leaching glaze after burn 720 DEG C from 0 DEG C of heating,
2)And then cool to 1125 DEG C after being heated to 1140 DEG C after a while,
3), it is anxious again be warming up to 1220 DEG C, insulation a period of time is warming up to 1248 DEG C, and oxidation is burnt till to 1260 DEG C,
4), be cooled to 1255 DEG C for a period of time again, be chilled to 910 DEG C after insulation a period of time,
5), after insulation a period of time afterwards again normal cooling until opening kiln.
Embodiment two
Furnace transmutation glaze in the present embodiment includes the raw material of following parts by weight:
5 parts of albite, 10 parts of potassium feldspar, 10 parts of quartz
6 parts of calcium carbonate, 3 parts of calcining zinc oxide, 2 parts of titanium oxide
2 parts of Longyan kaolin, 0.5 part of di-iron trioxide, 0.5 part of import cobalt oxide
1 part of Britain's bovine bone powder,
The raw material of above-mentioned parts by weight is mixed and made into glaze,
Soaking the mode being fired after glaze to ceramic body with above-mentioned glaze is:
1), ceramic body leaching glaze after burn 600 DEG C from 0 DEG C of heating,
2)And then cool to 985 DEG C after being heated to 1000 DEG C after a while,
3), it is anxious again be warming up to 1150 DEG C, insulation a period of time is warming up to 1175 DEG C, and oxidation is burnt till to 1220 DEG C,
4), be cooled to 1200 DEG C for a period of time again, be chilled to 850 DEG C after insulation a period of time,
5), after insulation a period of time afterwards again normal cooling until opening kiln.
Embodiment three
Furnace transmutation glaze in the present embodiment includes the raw material of following parts by weight:
70 parts of albite, 80 parts of potassium feldspar, 90 parts of quartz
50 parts of calcium carbonate, 40 parts of calcining zinc oxide, 40 parts of titanium oxide
50 parts of Longyan kaolin, 40 parts of di-iron trioxide, 40 parts of import cobalt oxide
16 parts of Britain's bovine bone powder,
The raw material of above-mentioned parts by weight is mixed and made into glaze,
Soaking the mode being fired after glaze to ceramic body with above-mentioned glaze is:
1), ceramic body leaching glaze after burn 800 DEG C from 0 DEG C of heating,
2)And then cool to 1175 DEG C after being heated to 1200 DEG C after a while,
3), it is anxious again be warming up to 1250 DEG C, insulation a period of time is warming up to 1280 DEG C, and oxidation is burnt till to 1320 DEG C,
4), be cooled to 1315 DEG C for a period of time again, be chilled to 1000 DEG C after insulation a period of time,
5), after insulation a period of time afterwards again normal cooling until opening kiln.
Example IV
Furnace transmutation glaze in the present embodiment includes the raw material of following parts by weight:
20 parts of albite, 30 parts of potassium feldspar, 30 parts of quartz
12 parts of calcium carbonate, 6 parts of calcining zinc oxide, 5 parts of titanium oxide
5 parts of Longyan kaolin, 1 part of di-iron trioxide, 1 part of import cobalt oxide
3 parts of Britain's bovine bone powder,
The raw material of above-mentioned parts by weight is mixed and made into glaze,
Soaking the mode being fired after glaze to ceramic body with above-mentioned glaze is:
1), ceramic body leaching glaze after burn 700 DEG C from 0 DEG C of heating,
2)And then cool to 1100 DEG C after being heated to 1110 DEG C after a while,
3), it is anxious again be warming up to 1200 DEG C, insulation a period of time is warming up to 1250 DEG C, and oxidation is burnt till to 1265 DEG C,
4), be cooled to 1260 DEG C for a period of time again, be chilled to 930 DEG C after insulation a period of time,
5), after insulation a period of time afterwards again normal cooling until opening kiln.
Embodiment five
Furnace transmutation glaze in the present embodiment includes the raw material of following parts by weight:
40 parts of albite, 50 parts of potassium feldspar, 60 parts of quartz
20 parts of calcium carbonate, 10 parts of calcining zinc oxide, 10 parts of titanium oxide
20 parts of Longyan kaolin, 3 parts of di-iron trioxide, 3 parts of import cobalt oxide
6 parts of Britain's bovine bone powder.
The raw material of above-mentioned parts by weight is mixed and made into glaze,
Soaking the mode being fired after glaze to ceramic body with above-mentioned glaze is:
1), ceramic body leaching glaze after burn 800 DEG C from 0 DEG C of heating,
2)And then cool to 1175 DEG C after being heated to 1200 DEG C after a while,
3), it is anxious again be warming up to 1250 DEG C, insulation a period of time is warming up to 1280 DEG C, and oxidation is burnt till to 1320 DEG C,
4), be cooled to 1315 DEG C for a period of time again, be chilled to 1000 DEG C after insulation a period of time,
5), after insulation a period of time afterwards again normal cooling until opening kiln.
Claims (7)
1. a kind of furnace transmutation glaze, it is characterised in that include the raw material of following parts by weight:
5-70 parts of albite 10-90 parts of quartz of 10-80 parts of potassium feldspar
6-50 parts of calcium carbonate 2-40 parts of titanium oxide of 3-40 parts of calcining zinc oxide
Kaolin 2-50 parts of Longyan 0.5-10 parts of import cobalt oxide of 0.5-10 parts of di-iron trioxide
Bovine bone powder 1-16 parts of Britain.
2. furnace transmutation glaze as claimed in claim 1, it is characterised in that:
20-40 parts of albite 30-60 parts of quartz of 30-50 parts of potassium feldspar
12-20 parts of calcium carbonate 5-10 parts of titanium oxide of 6-10 parts of calcining zinc oxide
Kaolin 5-20 parts of Longyan 1-3 parts of import cobalt oxide of 1-3 parts of di-iron trioxide
Bovine bone powder 3-6 parts of Britain.
3. furnace transmutation glaze as claimed in claim 2, it is characterised in that:
20 parts of albite, 30 parts of potassium feldspar, 30 parts of quartz
12 parts of calcium carbonate, 6 parts of calcining zinc oxide, 5 parts of titanium oxide
5 parts of Longyan kaolin, 1 part of di-iron trioxide, 1 part of import cobalt oxide
3 parts of Britain's bovine bone powder.
4. furnace transmutation glaze as claimed in claim 2, it is characterised in that:
40 parts of albite, 50 parts of potassium feldspar, 60 parts of quartz
20 parts of calcium carbonate, 10 parts of calcining zinc oxide, 10 parts of titanium oxide
20 parts of Longyan kaolin, 3 parts of di-iron trioxide, 3 parts of import cobalt oxide
6 parts of Britain's bovine bone powder.
5. furnace transmutation glaze as claimed in claim 2, it is characterised in that:
30 parts of albite, 40 parts of potassium feldspar, 45 parts of quartz
16 parts of calcium carbonate, 8 parts of calcining zinc oxide, 7 parts of titanium oxide
12 parts of Longyan kaolin, 2 parts of di-iron trioxide, 2 parts of import cobalt oxide
4.5 parts of Britain's bovine bone powder.
6. a kind of method for cooking of the ceramic body for the furnace transmutation glaze being soaked with as described in claim 1 or 5, it is characterised in that including
Following steps:
1), ceramic body leaching glaze after burn 600-800 DEG C from 0 DEG C of heating,
2)And then 985-1175 DEG C is cooled to after 4 hours are heated to 1000-1200 DEG C,
3), it is anxious again be warming up to 1150-1250 DEG C, insulation is warming up to 1175-1280 DEG C for 1 hour, and oxidation burns till 1200-1320 DEG C,
4), be cooled within 1.5 hours 1200-1315 DEG C again, insulation is chilled to 850-1000 DEG C after 0.5 hour,
5), be incubated 1 hour afterwards after again normal cooling until opening kiln.
7. the method for cooking of the ceramic body as claimed in claim 6 for being soaked with furnace transmutation glaze, it is characterised in that comprise the following steps:
1), ceramic body leaching glaze after burn 720 DEG C from 0 DEG C of heating,
2)And then cool to 1125 DEG C after being heated to 1140 DEG C after a while,
3), it is anxious again be warming up to 1220 DEG C, insulation a period of time is warming up to 1248 DEG C, and oxidation is burnt till to 1260 DEG C,
4), be cooled to 1255 DEG C for a period of time again, be chilled to 910 DEG C after insulation a period of time,
5), after insulation a period of time afterwards again normal cooling until opening kiln.