CN107200553A - One kind contains rare earth element porcelain and its preparation technology - Google Patents
One kind contains rare earth element porcelain and its preparation technology Download PDFInfo
- Publication number
- CN107200553A CN107200553A CN201710507485.7A CN201710507485A CN107200553A CN 107200553 A CN107200553 A CN 107200553A CN 201710507485 A CN201710507485 A CN 201710507485A CN 107200553 A CN107200553 A CN 107200553A
- Authority
- CN
- China
- Prior art keywords
- parts
- porcelain
- rare earth
- earth element
- lucium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
One kind of the present invention contains rare earth element porcelain, it is characterised in that the porcelain includes the raw material of following parts by weight:Lucium:0.5 2.5 parts;Clay:28 40 parts;Calcined kaolin:10 18 parts;Suzhou soil:8 15 parts;Sepiolite:13 parts;Medical stone:13 parts;Manganese dioxide:17 parts;Quartz sand:38 parts.One kind that the present invention is provided contains rare earth element porcelain, added with lucium so that the porcelain surface burnt out is more fine and smooth penetrating, improves the overall aesthetic property of porcelain, and technique is simple, it is easy to accomplish.
Description
Technical field
Contain rare earth element porcelain and its preparation technology the present invention relates to one kind.
Background technology
Porcelain is unique creation of Chinese people, and the long civilization of China is represent with its unique national cultural feature,
Nowadays, porcelain has goed deep into the life of people as the higher technique of artistic value and commodity.But traditional porcelain is
The need for it can not meet people, it is therefore desirable to which a kind of new porcelain replaces.
The content of the invention
To solve above-mentioned problem, contain rare earth element porcelain it is an object of the invention to provide one kind.It is described to contain
There is rare earth element porcelain, added with lucium so that the porcelain surface burnt out is more fine and smooth penetrating, improves porcelain whole
The aesthetic property of body, and technique is simple, it is easy to accomplish.
To reach above-mentioned purpose, the technical scheme is that:
One kind contains rare earth element porcelain, and the porcelain includes the raw material of following parts by weight:Lucium:0.5-2.5 parts;
Clay:28-40 parts;Calcined kaolin:10-18 parts;Suzhou soil:8-15 parts;Sepiolite:1-3 parts;Medical stone:1-3 parts;Dioxy
Change manganese:1-7 parts;Quartz sand:3-8 parts.
Further, the porcelain includes the raw material of following parts by weight:Lucium:1-2 parts;Clay:34-40
Part;Calcined kaolin:10-15 parts;Suzhou soil:11-15 parts;Sepiolite:1-2 parts;Medical stone:1-2 parts;Manganese dioxide:3-7
Part;Quartz sand:5-8 parts.
Further, the porcelain includes the raw material of following parts by weight:Lucium:1.5 part;Clay:38 parts;Forge
Burn kaolin:13 parts;Suzhou soil:12 parts;Sepiolite:1.8 part;Medical stone:1.2 part;Manganese dioxide:5 parts;Quartz sand:5.5
Part.
Further, the lucium be at least two of lanthanum rare earth or yttrium element or lanthanum rare earth or yttrium element with
On.
Further, the particle diameter of the calcined kaolin is 200 ~ 300 mesh.
A kind of preparation technology containing rare earth element porcelain, comprises the following steps:
(1)It is in proportion that calcined kaolin, Suzhou soil, sepiolite, medical stone, manganese dioxide, quartz is well mixed, wear into fineness
For the powder of 100-150 mesh, lucium and clay are added, training mud is prepared, by kiln-firing, system after training mud shaping and drying
Obtain plain embryo;
(2)Inside and outside glaze is uniformly wrapped using glaze method is swung in ceramic idiosome inner and outer surfaces, carries out glaze firing, firing must be containing rare earth member
Bique device.
Further, the step(1)The concrete operations of middle firing are:650 ~ 700 DEG C of 0.5 ~ 1.5h of calcining are first warming up to,
800 ~ 900 DEG C of 1 ~ 2h of calcining are continuously heating to, then are warming up to 1100 ~ 1180 DEG C of 5 ~ 8h of calcining.
The beneficial effects of the present invention are:
One kind that the present invention is provided contains rare earth element porcelain, added with lucium so that the porcelain surface burnt out is more
Refinement is greasy penetrating, improves the overall aesthetic property of porcelain, and technique is simple, it is easy to accomplish.
Embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, it is further detailed with reference to embodiments
Describe in detail bright.
Embodiment 1
One kind contains rare earth element porcelain, and the porcelain includes the raw material of following parts by weight:Lucium:0.5 part;It is viscous
Soil:28 parts;Calcined kaolin:10 parts;Suzhou soil:15 parts;Sepiolite:1 part;Medical stone:3 parts;Manganese dioxide:2 parts;Quartz
Sand:3 parts.
Embodiment 2
One kind contains rare earth element porcelain, and the porcelain includes the raw material of following parts by weight:Lucium:1 part;Clay:
30 parts;Calcined kaolin:12 parts;Suzhou soil:11 parts;Sepiolite:1 part;Medical stone:3 parts;Manganese dioxide:7 parts;Quartz sand:6
Part.
Embodiment 3
One kind contains rare earth element porcelain, and the porcelain includes the raw material of following parts by weight:Lucium:1.5 part;It is viscous
Soil:38 parts;Calcined kaolin:13 parts;Suzhou soil:12 parts;Sepiolite:1.8 part;Medical stone:1.2 part;Manganese dioxide:5 parts;Stone
Sand:5.5 part.
Embodiment 4
One kind contains rare earth element porcelain, and the porcelain includes the raw material of following parts by weight:Lucium:1 part;Clay:
35 parts;Calcined kaolin:18 parts;Suzhou soil:8 parts;Sepiolite:2 parts;Medical stone:2 parts;Manganese dioxide:1 part;Quartz sand:8
Part.
Embodiment 5
One kind contains rare earth element porcelain, and the porcelain includes the raw material of following parts by weight:Lucium:2.5 part;It is viscous
Soil:40 parts;Calcined kaolin:15 parts;Suzhou soil:12 parts;Sepiolite:2 parts;Medical stone:1 part;Manganese dioxide:3 parts;Quartz
Sand:7 parts.
The lucium is more than at least two of lanthanum rare earth or yttrium element or lanthanum rare earth or yttrium element.
A kind of preparation technology containing rare earth element porcelain, comprises the following steps:
(1)It is in proportion that calcined kaolin, Suzhou soil, sepiolite, medical stone, manganese dioxide, quartz is well mixed, wear into fineness
For the powder of 100-150 mesh, lucium and clay are added, training mud is prepared, kiln-firing after mud shaping and drying will be trained, first
650 ~ 700 DEG C of 0.5 ~ 1.5h of calcining are warming up to, 800 ~ 900 DEG C of 1 ~ 2h of calcining are continuously heating to, then be warming up to 1100 ~ 1180 DEG C and forge
5 ~ 8h is burnt, element embryo is made;
(2)Inside and outside glaze is uniformly wrapped using glaze method is swung in ceramic idiosome inner and outer surfaces, carries out glaze firing, firing must be containing rare earth member
Bique device.
One kind that the present invention is provided contains rare earth element porcelain, added with lucium so that the porcelain table burnt out
Face is more fine and smooth penetrating, improves the overall aesthetic property of porcelain, and technique is simple, it is easy to accomplish.
It should be noted that the above embodiments are merely illustrative of the technical solutions of the present invention and it is unrestricted.Although with reference to compared with
The present invention is described in detail good embodiment, it will be understood by those within the art that, can be to the technology of invention
Scheme is modified or equivalent substitution, and without departing from the scope of technical solution of the present invention, it all should cover the power in the present invention
In sharp claimed range.
Claims (7)
1. one kind contains rare earth element porcelain, it is characterised in that the porcelain includes the raw material of following parts by weight:Rare earth is mixed
Thing:0.5-2.5 parts;Clay:28-40 parts;Calcined kaolin:10-18 parts;Suzhou soil:8-15 parts;Sepiolite:1-3 parts;Wheat meal
Stone:1-3 parts;Manganese dioxide:1-7 parts;Quartz sand:3-8 parts.
2. one kind according to claim 1 contains rare earth element porcelain, it is characterised in that the porcelain includes following weight
The raw material of number:Lucium:1-2 parts;Clay:34-40 parts;Calcined kaolin:10-15 parts;Suzhou soil:11-15 parts;Sea
Afrodite:1-2 parts;Medical stone:1-2 parts;Manganese dioxide:3-7 parts;Quartz sand:5-8 parts.
3. one kind according to claim 1 contains rare earth element porcelain, it is characterised in that the porcelain includes following weight
The raw material of number:Lucium:1.5 part;Clay:38 parts;Calcined kaolin:13 parts;Suzhou soil:12 parts;Sepiolite:1.8
Part;Medical stone:1.2 part;Manganese dioxide:5 parts;Quartz sand:5.5 part.
4. one kind according to claim 1 contains rare earth element porcelain, it is characterised in that the lucium is that lanthanum is dilute
More than at least two of soil or yttrium element or lanthanum rare earth or yttrium element.
5. one kind according to claim 1 contains rare earth element porcelain, it is characterised in that the particle diameter of the calcined kaolin
For 200 ~ 300 mesh.
6. a kind of preparation technology containing rare earth element porcelain as claimed in claim 1, it is characterised in that including following step
Suddenly:
(1)It is in proportion that calcined kaolin, Suzhou soil, sepiolite, medical stone, manganese dioxide, quartz is well mixed, wear into fineness
For the powder of 100-150 mesh, lucium and clay are added, training mud is prepared, by kiln-firing, system after training mud shaping and drying
Obtain plain embryo;
(2)Inside and outside glaze is uniformly wrapped using glaze method is swung in ceramic idiosome inner and outer surfaces, carries out glaze firing, firing must be containing rare earth member
Bique device.
7. one kind according to claim 6 contains rare earth element porcelain, it is characterised in that the step(1)Middle firing
Concrete operations are:650 ~ 700 DEG C of 0.5 ~ 1.5h of calcining are first warming up to, 800 ~ 900 DEG C of 1 ~ 2h of calcining are continuously heating to, then be warming up to
1100 ~ 1180 DEG C of 5 ~ 8h of calcining.