CN107056173A - 一种保温建筑材料及其制备方法 - Google Patents
一种保温建筑材料及其制备方法 Download PDFInfo
- Publication number
- CN107056173A CN107056173A CN201710425248.6A CN201710425248A CN107056173A CN 107056173 A CN107056173 A CN 107056173A CN 201710425248 A CN201710425248 A CN 201710425248A CN 107056173 A CN107056173 A CN 107056173A
- Authority
- CN
- China
- Prior art keywords
- parts
- heat
- construction material
- insulating construction
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明提供一种保温建筑材料及其制备方法,涉及建筑材料领域,保温建筑材料包括以下重量份的原料:硅酸钙粉14‑20份、花岗岩粉10‑28份、聚氨酯15‑17份、硅酸铝粉17‑23份、氧化镁5‑9份、矿物棉7‑13份、聚酯纤维4‑8份、炉渣粉11‑23份、膨胀玻化微珠15‑19份、蛭石11‑31份、海绵橡胶15‑23份、废弃挤塑板15‑21份、膨胀珍珠岩20‑34份、石英玻璃纤维9‑17份、聚丙烯纤维13‑21份、水泥27‑35份、引气剂0.2‑0.4份、缓凝剂0.1‑0.7份、阻燃剂0.1‑0.3份、减水剂0.5‑0.7份、发泡剂0.2‑0.6份和水3‑7份;制备方法包括以下步骤:(1)称取原料、(2)焙烧、(3)粉碎、(4)搅拌、(5)加压成型、(6)烘干。本发明解决了现有保温建筑材料在应用于对抗压强度、保温隔热和环保节能要求高的建筑上还存在着不足的问题。
Description
技术领域
本发明属于建筑材料领域,具体涉及一种保温建筑材料及其制备方法。
背景技术
随着社会进步和人民生活水平的提高,人们对建筑材料的要求越来越高,尤其是建筑材料中的保温材料,但是,在现有的保温材料中,存在着抗压强度低、保温效果一般以及达不到节能环保要求的问题。
2016年7月13日公告的中国专利文献一种保温隔热的建筑材料及其制备方法(授权公告号CN104261776B),所述的保温隔热的建筑材料包括以下重量份的原料:硅酸钙粉为14-21份、花岗岩粉为8-17份、聚氨酯为15-19份、硅酸铝粉为17-25份、氧化镁为5-11份、矿物棉为7-13份、聚酯纤维为4-9份。所述保温隔热的建筑材料的制备方法包括以下步骤:(1)取上述的各成分在搅拌罐中进行搅拌,搅拌均匀后备用;(2)将步骤(1)制备得到的混合均匀后的复合材料注入到成型模具中,加压成型;(3)将步骤(2)加压成型后的复合建筑材料再进行烘干,烘干温度为75℃,烘干时间为3h,烘干后制备得到保温隔热的建筑材料。
该发明在面对高标准要求的建筑时,对其配方仍需要进一步的改进,使其具有抗压强度高、保温隔热性能好和环保节能的特点。
发明内容
为了解决现有保温建筑材料在应用于对抗压强度、保温隔热和环保节能要求高的建筑上还存在着不足的问题,本发明的目的是提供一种保温建筑材料及其制备方法,制得的保温建筑材料具有抗压强度高、保温隔热性能好和环保节能的优点。
本发明提供了如下的技术方案:
一种保温建筑材料,包括以下重量份的原料:硅酸钙粉14-20份、花岗岩粉10-28份、聚氨酯15-17份、硅酸铝粉17-23份、氧化镁5-9份、矿物棉7-13份、聚酯纤维4-8份、炉渣粉11-23份、膨胀玻化微珠15-19份、蛭石11-31份、海绵橡胶15-23份、废弃挤塑板15-21份、膨胀珍珠岩20-34份、石英玻璃纤维9-17份、聚丙烯纤维13-21份、水泥27-35份、引气剂0.2-0.4份、缓凝剂0.1-0.7份、阻燃剂0.1-0.3份、减水剂0.5-0.7份、发泡剂0.2-0.6份和水3-7份。
原料中添加了炉渣粉和废弃挤塑板,这些工业废料和建筑废料长期搁置在城市,不仅占用城市用地,而且污染当地的环境,现将这些工业废料和建筑废料循环再利用,达到了节能环保的目的;炉渣粉作为保温建筑材料的填料,能够填补原料混合过程中形成的孔隙,提高保温建筑材料的抗压强度;废弃挤塑板具有连续均匀表层及闭孔式蜂窝结构,完全不会出现空隙,有利于提高保温建筑材料的保温性能和抗压性能。
原料中添加了膨胀珍珠岩,膨胀珍珠岩为内部呈蜂窝状的白色颗粒材料,具有优良的保温隔热性能。
原料中添加了石英玻璃纤维,石英玻璃纤维具有耐高温、绝缘、耐腐蚀、隔热和化学稳定性好的特点。
原料中添加了聚丙烯纤维,聚丙烯纤维具有质轻、强度高、弹性好、耐磨、耐腐蚀、保温和电绝缘性好的特点。
优选地,包括以下重量份的原料:硅酸钙粉17份、花岗岩粉19份、聚氨酯16份、硅酸铝粉20份、氧化镁7份、矿物棉10份、聚酯纤维6份、炉渣粉17份、膨胀玻化微珠17份、蛭石21份、海绵橡胶19份、废弃挤塑板18份、膨胀珍珠岩27份、石英玻璃纤维13份、聚丙烯纤维17份、水泥31份、引气剂0.3份、缓凝剂0.4份、阻燃剂0.2份、减水剂0.6份、发泡剂0.4份和水5份。
优选地,所述引气剂为烷基苯磺酸盐类引气剂,提高保温建筑材料的原料流动性、可塑性以及降低保温建筑材料成品的导热系数。
优选地,所述缓凝剂为三聚磷酸钠,延缓保温建筑材料的原料硬化的时间,使得通过延长搅拌时间将原料搅拌的更加均匀,从而提高保温隔热性能和抗压强度。
优选地,所述阻燃剂为氢氧化铝阻燃剂,氢氧化铝阻燃剂通过提高聚合物的热容,使其在达到热分解温度前吸收更多的热量,从而提高其阻燃性能。
优选地,所述减水剂为聚羧酸系减水剂,具有掺量低、减水率高达45%、材料收缩小、产品稳定性好、绿色环保、成本低、使用时方便且安全的优点。
优选地,所述发泡剂为碳酸氢钠,加热放出二氧化碳,发泡效果好,提高保温建筑材料的保温隔热性能。
一种保温建筑材料的制备方法,包括以下步骤:
(1)按照保温建筑材料原料的重量份数称取原料;
(2)将蛭石放入窑炉中焙烧20-30min,焙烧温度控制在800-1000℃,即得焙烧后的蛭石;
(3)将废弃挤塑板加入到粉碎机中粉碎,粉碎时间为15-20min,即得粉碎料;
(4)将步骤(2)中的焙烧后的蛭石、步骤(3)中的粉碎料、硅酸钙粉、花岗岩粉、聚氨酯、硅酸铝粉、氧化镁、矿物棉、聚酯纤维、炉渣粉、膨胀玻化微珠、海绵橡胶、膨胀珍珠岩、石英玻璃纤维、聚丙烯纤维、水泥、引气剂、缓凝剂、阻燃剂、减水剂、发泡剂和水加入到搅拌机中搅拌,搅拌时间为35-40min,即得混合料;
(5)将步骤(4)中的混合料注入成型模具中,加压成型,即得成型料;
(6)将步骤(5)中的成型料进行烘干,烘干温度为75-85℃,烘干时间为4-5h,即得保温建筑材料。
本发明的有益效果是:
1、本发明解决了现有保温建筑材料在应用于对抗压强度、保温隔热和环保节能要求高的建筑上还存在着不足的问题。
2、本发明的原料中添加了炉渣粉和废弃挤塑板,这些工业废料和建筑废料长期搁置在城市,不仅占用城市用地,而且污染当地的环境,现将这些工业废料和建筑废料循环再利用,达到了节能环保的目的;炉渣粉作为保温建筑材料的填料,能够填补原料混合过程中形成的孔隙,提高保温建筑材料的抗压强度;废弃挤塑板具有连续均匀表层及闭孔式蜂窝结构,完全不会出现空隙,有利于提高保温建筑材料的保温性能和抗压性能。
3、本发明的原料中添加了膨胀珍珠岩,膨胀珍珠岩为内部呈蜂窝状的白色颗粒材料,具有优良的保温隔热性能。
4、本发明的原料中添加了石英玻璃纤维,石英玻璃纤维具有耐高温、绝缘、耐腐蚀、隔热和化学稳定性好的特点。
5、本发明的原料中添加了聚丙烯纤维,聚丙烯纤维具有质轻、强度高、弹性好、耐磨、耐腐蚀、保温和电绝缘性好的特点。
6、本发明中所述引气剂为烷基苯磺酸盐类引气剂,提高保温建筑材料的原料流动性、可塑性以及降低保温建筑材料成品的导热系数。
7、本发明中所述缓凝剂为三聚磷酸钠,延缓保温建筑材料的原料硬化的时间,使得通过延长搅拌时间将原料搅拌的更加均匀,从而提高保温隔热性能和抗压强度。
8、本发明中所述阻燃剂为氢氧化铝阻燃剂,氢氧化铝阻燃剂通过提高聚合物的热容,使其在达到热分解温度前吸收更多的热量,从而提高其阻燃性能。
9、本发明中所述减水剂为聚羧酸系减水剂,具有掺量低、减水率高达45%、材料收缩小、产品稳定性好、绿色环保、成本低、使用时方便且安全的优点。
10、本发明中所述发泡剂为碳酸氢钠,加热放出二氧化碳,发泡效果好,提高保温建筑材料的保温隔热性能。
具体实施方式
实施例1
一种保温建筑材料,包括以下重量份的原料:硅酸钙粉17份、花岗岩粉19份、聚氨酯16份、硅酸铝粉20份、氧化镁7份、矿物棉10份、聚酯纤维6份、炉渣粉17份、膨胀玻化微珠17份、蛭石21份、海绵橡胶19份、废弃挤塑板18份、膨胀珍珠岩27份、石英玻璃纤维13份、聚丙烯纤维17份、水泥31份、引气剂0.3份、缓凝剂0.4份、阻燃剂0.2份、减水剂0.6份、发泡剂0.4份和水5份。
原料中添加了炉渣粉和废弃挤塑板,这些工业废料和建筑废料长期搁置在城市,不仅占用城市用地,而且污染当地的环境,现将这些工业废料和建筑废料循环再利用,达到了节能环保的目的;炉渣粉作为保温建筑材料的填料,能够填补原料混合过程中形成的孔隙,提高保温建筑材料的抗压强度;废弃挤塑板具有连续均匀表层及闭孔式蜂窝结构,完全不会出现空隙,有利于提高保温建筑材料的保温性能和抗压性能。
原料中添加了膨胀珍珠岩,膨胀珍珠岩为内部呈蜂窝状的白色颗粒材料,具有优良的保温隔热性能。
原料中添加了石英玻璃纤维,石英玻璃纤维具有耐高温、绝缘、耐腐蚀、隔热和化学稳定性好的特点。
原料中添加了聚丙烯纤维,聚丙烯纤维具有质轻、强度高、弹性好、耐磨、耐腐蚀、保温和电绝缘性好的特点。
引气剂为烷基苯磺酸盐类引气剂,提高保温建筑材料的原料流动性、可塑性以及降低保温建筑材料成品的导热系数。
缓凝剂为三聚磷酸钠,延缓保温建筑材料的原料硬化的时间,使得通过延长搅拌时间将原料搅拌的更加均匀,从而提高保温隔热性能和抗压强度。
阻燃剂为氢氧化铝阻燃剂,氢氧化铝阻燃剂通过提高聚合物的热容,使其在达到热分解温度前吸收更多的热量,从而提高其阻燃性能。
减水剂为聚羧酸系减水剂,具有掺量低、减水率高达45%、材料收缩小、产品稳定性好、绿色环保、成本低、使用时方便且安全的优点。
发泡剂为碳酸氢钠,加热放出二氧化碳,发泡效果好,提高保温建筑材料的保温隔热性能。
一种保温建筑材料的制备方法,包括以下步骤:
(1)按照保温建筑材料原料的重量份数称取原料;
(2)将蛭石放入窑炉中焙烧20-30min,焙烧温度控制在800-1000℃,即得焙烧后的蛭石;
(3)将废弃挤塑板加入到粉碎机中粉碎,粉碎时间为15-20min,即得粉碎料;
(4)将步骤(2)中的焙烧后的蛭石、步骤(3)中的粉碎料、硅酸钙粉、花岗岩粉、聚氨酯、硅酸铝粉、氧化镁、矿物棉、聚酯纤维、炉渣粉、膨胀玻化微珠、海绵橡胶、膨胀珍珠岩、石英玻璃纤维、聚丙烯纤维、水泥、引气剂、缓凝剂、阻燃剂、减水剂、发泡剂和水加入到搅拌机中搅拌,搅拌时间为35-40min,即得混合料;
(5)将步骤(4)中的混合料注入成型模具中,加压成型,即得成型料;
(6)将步骤(5)中的成型料进行烘干,烘干温度为75-85℃,烘干时间为4-5h,即得保温建筑材料。
实施例2
一种保温建筑材料,包括以下重量份的原料:硅酸钙粉14份、花岗岩粉10份、聚氨酯15份、硅酸铝粉17份、氧化镁5份、矿物棉7份、聚酯纤维4份、炉渣粉11份、膨胀玻化微珠15份、蛭石11份、海绵橡胶15份、废弃挤塑板15份、膨胀珍珠岩20份、石英玻璃纤维9份、聚丙烯纤维13份、水泥27份、引气剂0.2份、缓凝剂0.1份、阻燃剂0.1份、减水剂0.5份、发泡剂0.2份和水3份。
原料中添加了炉渣粉和废弃挤塑板,这些工业废料和建筑废料长期搁置在城市,不仅占用城市用地,而且污染当地的环境,现将这些工业废料和建筑废料循环再利用,达到了节能环保的目的;炉渣粉作为保温建筑材料的填料,能够填补原料混合过程中形成的孔隙,提高保温建筑材料的抗压强度;废弃挤塑板具有连续均匀表层及闭孔式蜂窝结构,完全不会出现空隙,有利于提高保温建筑材料的保温性能和抗压性能。
原料中添加了膨胀珍珠岩,膨胀珍珠岩为内部呈蜂窝状的白色颗粒材料,具有优良的保温隔热性能。
原料中添加了石英玻璃纤维,石英玻璃纤维具有耐高温、绝缘、耐腐蚀、隔热和化学稳定性好的特点。
原料中添加了聚丙烯纤维,聚丙烯纤维具有质轻、强度高、弹性好、耐磨、耐腐蚀、保温和电绝缘性好的特点。
引气剂为烷基苯磺酸盐类引气剂,提高保温建筑材料的原料流动性、可塑性以及降低保温建筑材料成品的导热系数。
缓凝剂为三聚磷酸钠,延缓保温建筑材料的原料硬化的时间,使得通过延长搅拌时间将原料搅拌的更加均匀,从而提高保温隔热性能和抗压强度。
阻燃剂为氢氧化铝阻燃剂,氢氧化铝阻燃剂通过提高聚合物的热容,使其在达到热分解温度前吸收更多的热量,从而提高其阻燃性能。
减水剂为聚羧酸系减水剂,具有掺量低、减水率高达45%、材料收缩小、产品稳定性好、绿色环保、成本低、使用时方便且安全的优点。
发泡剂为碳酸氢钠,加热放出二氧化碳,发泡效果好,提高保温建筑材料的保温隔热性能。
一种保温建筑材料的制备方法,包括以下步骤:
(1)按照保温建筑材料原料的重量份数称取原料;
(2)将蛭石放入窑炉中焙烧20-30min,焙烧温度控制在800-1000℃,即得焙烧后的蛭石;
(3)将废弃挤塑板加入到粉碎机中粉碎,粉碎时间为15-20min,即得粉碎料;
(4)将步骤(2)中的焙烧后的蛭石、步骤(3)中的粉碎料、硅酸钙粉、花岗岩粉、聚氨酯、硅酸铝粉、氧化镁、矿物棉、聚酯纤维、炉渣粉、膨胀玻化微珠、海绵橡胶、膨胀珍珠岩、石英玻璃纤维、聚丙烯纤维、水泥、引气剂、缓凝剂、阻燃剂、减水剂、发泡剂和水加入到搅拌机中搅拌,搅拌时间为35-40min,即得混合料;
(5)将步骤(4)中的混合料注入成型模具中,加压成型,即得成型料;
(6)将步骤(5)中的成型料进行烘干,烘干温度为75-85℃,烘干时间为4-5h,即得保温建筑材料。
实施例3
一种保温建筑材料,包括以下重量份的原料:硅酸钙粉20份、花岗岩粉28份、聚氨酯17份、硅酸铝粉23份、氧化镁9份、矿物棉13份、聚酯纤维8份、炉渣粉23份、膨胀玻化微珠19份、蛭石31份、海绵橡胶23份、废弃挤塑板21份、膨胀珍珠岩34份、石英玻璃纤维17份、聚丙烯纤维21份、水泥35份、引气剂0.4份、缓凝剂0.7份、阻燃剂0.3份、减水剂0.7份、发泡剂0.6份和水7份。
原料中添加了炉渣粉和废弃挤塑板,这些工业废料和建筑废料长期搁置在城市,不仅占用城市用地,而且污染当地的环境,现将这些工业废料和建筑废料循环再利用,达到了节能环保的目的;炉渣粉作为保温建筑材料的填料,能够填补原料混合过程中形成的孔隙,提高保温建筑材料的抗压强度;废弃挤塑板具有连续均匀表层及闭孔式蜂窝结构,完全不会出现空隙,有利于提高保温建筑材料的保温性能和抗压性能。
原料中添加了膨胀珍珠岩,膨胀珍珠岩为内部呈蜂窝状的白色颗粒材料,具有优良的保温隔热性能。
原料中添加了石英玻璃纤维,石英玻璃纤维具有耐高温、绝缘、耐腐蚀、隔热和化学稳定性好的特点。
原料中添加了聚丙烯纤维,聚丙烯纤维具有质轻、强度高、弹性好、耐磨、耐腐蚀、保温和电绝缘性好的特点。
引气剂为烷基苯磺酸盐类引气剂,提高保温建筑材料的原料流动性、可塑性以及降低保温建筑材料成品的导热系数。
缓凝剂为三聚磷酸钠,延缓保温建筑材料的原料硬化的时间,使得通过延长搅拌时间将原料搅拌的更加均匀,从而提高保温隔热性能和抗压强度。
阻燃剂为氢氧化铝阻燃剂,氢氧化铝阻燃剂通过提高聚合物的热容,使其在达到热分解温度前吸收更多的热量,从而提高其阻燃性能。
减水剂为聚羧酸系减水剂,具有掺量低、减水率高达45%、材料收缩小、产品稳定性好、绿色环保、成本低、使用时方便且安全的优点。
发泡剂为碳酸氢钠,加热放出二氧化碳,发泡效果好,提高保温建筑材料的保温隔热性能。
一种保温建筑材料的制备方法,包括以下步骤:
(1)按照保温建筑材料原料的重量份数称取原料;
(2)将蛭石放入窑炉中焙烧20-30min,焙烧温度控制在800-1000℃,即得焙烧后的蛭石;
(3)将废弃挤塑板加入到粉碎机中粉碎,粉碎时间为15-20min,即得粉碎料;
(4)将步骤(2)中的焙烧后的蛭石、步骤(3)中的粉碎料、硅酸钙粉、花岗岩粉、聚氨酯、硅酸铝粉、氧化镁、矿物棉、聚酯纤维、炉渣粉、膨胀玻化微珠、海绵橡胶、膨胀珍珠岩、石英玻璃纤维、聚丙烯纤维、水泥、引气剂、缓凝剂、阻燃剂、减水剂、发泡剂和水加入到搅拌机中搅拌,搅拌时间为35-40min,即得混合料;
(5)将步骤(4)中的混合料注入成型模具中,加压成型,即得成型料;
(6)将步骤(5)中的成型料进行烘干,烘干温度为75-85℃,烘干时间为4-5h,即得保温建筑材料。
对比例1
一种保温隔热的建筑材料,包括以下重量份的原料:硅酸钙粉17.5份、花岗岩粉20份、聚氨酯17份、硅酸铝粉21份、氧化镁8 份、矿物棉10份、聚酯纤维6.5份和水4份。
一种保温隔热的建筑材料的制备方法,包括以下步骤:
(1)按照保温隔热的建筑材料原料的重量份数称取原料;
(2)将硅酸钙粉、花岗岩粉、聚氨酯、硅酸铝粉、氧化镁、矿物棉、聚酯纤维和水加入到搅拌机中搅拌,搅拌时间为30-40min,即得混合料;
(3)将步骤(2)中的混合料注入成型模具中,加压成型,即得成型料;
(4)将步骤(3)中的成型料进行烘干,烘干温度为75-85℃,烘干时间为4-5h,即得保温建筑材料。
将实施例1、实施例2和实施例3制得保温建筑材料和对比例1制得保温隔热的建筑材料进行性能测试,测试结果如表1所示:
指标 | 实施例1 | 实施例2 | 实施例3 | 对比例1 |
抗压强度(Mpa) | 47.2 | 41.6 | 39.5 | 30.7 |
导热系数(w/m﹒k) | 0.016 | 0.019 | 0.021 | 0.028 |
原料损耗减少率(%) | 29 | 23 | 18 | 0 |
从表1数据比较可以看出,本发明的优点是:
1、一种保温建筑材料及其制备方法,从测得的抗压强度值可以看出,实施例1-3的抗压强度值均高于对比例1,说明该保温建筑材料抗压强度高。
2、一种保温建筑材料及其制备方法,从测得的导热系数可以看出,实施例1-3的导热系数均低于对比例1,说明该保温建筑材料保温效果好。
3、一种保温建筑材料及其制备方法,从测得的原料损耗减少率可以看出,实施例1-3的原料损耗减少率均高于对比例1,说明该保温建筑材料的节能效果好。
4、一种保温建筑材料及其制备方法,从测得的各个指标的数据可以看出,实施例1均优于实施例2、实施例3和对比例1,说明该保温建筑材料的原料配方和制备方法的合理性。
以上所述仅为本发明的优选实施例而已,并不用于限制本发明,尽管参照前述实施例对本发明进行了详细的说明,对于本领域的技术人员来说,其依然可以对前述各实施例所记载的技术方案进行修改,或者对其中部分技术特征进行等同替换,凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (8)
1.一种保温建筑材料,其特征在于,包括以下重量份的原料:硅酸钙粉14-20份、花岗岩粉10-28份、聚氨酯15-17份、硅酸铝粉17-23份、氧化镁5-9份、矿物棉7-13份、聚酯纤维4-8份、炉渣粉11-23份、膨胀玻化微珠15-19份、蛭石11-31份、海绵橡胶15-23份、废弃挤塑板15-21份、膨胀珍珠岩20-34份、石英玻璃纤维9-17份、聚丙烯纤维13-21份、水泥27-35份、引气剂0.2-0.4份、缓凝剂0.1-0.7份、阻燃剂0.1-0.3份、减水剂0.5-0.7份、发泡剂0.2-0.6份和水3-7份。
2.根据权利要求1所述的保温建筑材料,其特征在于,包括以下重量份的原料:硅酸钙粉17份、花岗岩粉19份、聚氨酯16份、硅酸铝粉20份、氧化镁7份、矿物棉10份、聚酯纤维6份、炉渣粉17份、膨胀玻化微珠17份、蛭石21份、海绵橡胶19份、废弃挤塑板18份、膨胀珍珠岩27份、石英玻璃纤维13份、聚丙烯纤维17份、水泥31份、引气剂0.3份、缓凝剂0.4份、阻燃剂0.2份、减水剂0.6份、发泡剂0.4份和水5份。
3.根据权利要求1所述的保温建筑材料,其特征在于:所述引气剂为烷基苯磺酸盐类引气剂。
4.根据权利要求1所述的保温建筑材料,其特征在于:所述缓凝剂为三聚磷酸钠。
5.根据权利要求1所述的保温建筑材料,其特征在于:所述阻燃剂为氢氧化铝阻燃剂。
6.根据权利要求1所述的保温建筑材料,其特征在于:所述减水剂为聚羧酸系减水剂。
7.根据权利要求1所述的保温建筑材料,其特征在于:所述发泡剂为碳酸氢钠。
8.一种如权利要求1—7任意一项所述的保温建筑材料的制备方法,其特征在于,包括以下步骤:
(1)按照保温建筑材料原料的重量份数称取原料;
(2)将蛭石放入窑炉中焙烧20-30min,焙烧温度控制在800-1000℃,即得焙烧后的蛭石;
(3)将废弃挤塑板加入到粉碎机中粉碎,粉碎时间为15-20min,即得粉碎料;
(4)将步骤(2)中的焙烧后的蛭石、步骤(3)中的粉碎料、硅酸钙粉、花岗岩粉、聚氨酯、硅酸铝粉、氧化镁、矿物棉、聚酯纤维、炉渣粉、膨胀玻化微珠、海绵橡胶、膨胀珍珠岩、石英玻璃纤维、聚丙烯纤维、水泥、引气剂、缓凝剂、阻燃剂、减水剂、发泡剂和水加入到搅拌机中搅拌,搅拌时间为35-40min,即得混合料;
(5)将步骤(4)中的混合料注入成型模具中,加压成型,即得成型料;
(6)将步骤(5)中的成型料进行烘干,烘干温度为75-85℃,烘干时间为4-5h,即得保温建筑材料。