CN107022905A - A kind of terylene cotton elastic is knitted fabric dyeing - Google Patents
A kind of terylene cotton elastic is knitted fabric dyeing Download PDFInfo
- Publication number
- CN107022905A CN107022905A CN201710299602.5A CN201710299602A CN107022905A CN 107022905 A CN107022905 A CN 107022905A CN 201710299602 A CN201710299602 A CN 201710299602A CN 107022905 A CN107022905 A CN 107022905A
- Authority
- CN
- China
- Prior art keywords
- parts
- cloth
- fabric dyeing
- temperature
- carried out
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Fabric dyeing, including step one are knitted the invention discloses a kind of terylene cotton elastic：Polyester-cotton blend cloth is dipped in disperse dyes, a leaching one is carried out and pricks；Step 2：Polyester-cotton blend cloth after one leaching one is pricked is dried at a temperature of 80 ~ 90 DEG C；Step 3：Cloth after drying is carried out to baking 90 seconds at a temperature of 190 DEG C；Step 4：The cloth for bakeing completion is dipped secondary dip is carried out in reduction cleaning liquid；Step 5：Cloth after secondary dip is wrapped with plastic foil, decatize 2 minutes under 100 DEG C of vapor；Step 6：Carry out washing ventilative, soap boiling dries again afterwards.Fabric prepared by present invention process has the characteristic for being difficult balling-up.
Description
Technical field
The present invention relates to cloth dyeing, more particularly to a kind of terylene cotton elastic knitting fabric dyeing.
Background technology
Polyester-cotton blend refers to the general designation of the blend fabric of terylene and cotton, and yarn is mixed using 65% -67% terylene and 33% -35% cotton
The textile that line is made into, is commonly called as " dacron ".
Visually, polyester-cotton blend is more vivider than the color and luster of pure cotton；If calico, the positive and negative color density pair of pure cotton cloth
Than larger, and the positive and negative color of polyester-mixed cotton cloth is closer to.
In feel, pure cotton cloth is soft but unsmooth, and polyester-mixed cotton cloth hand, which is felt, feels that some are smooth.
To skin better, pure cotton, 100% cotton goods, feel touches up very soft comfortable to pure cotton.Polyester-cotton blend is to wash
Synthetic fibre and the mixture of cotton, feel are comfortable not as cotton.Wear and not as pure cotton absorbing sweat, with terylene short fiber peacekeeping cotton fiber blending
The various fabrics that yarn is made into, are commonly called as cotton dacron.
Polyester-cotton blend is larger due to the strength of polyester fiber, entangled with cotton fiber filoplume, it is very difficult to come off, and is thus formed
Pilling effect seen by us.
The content of the invention
In view of the deficienciess of the prior art, it is an object of the invention to provide a kind of terylene cotton elastic knitting for being difficult balling-up
Dyeing fabric technique.
To achieve the above object, the invention provides following technical scheme：
A kind of terylene cotton elastic is knitted fabric dyeing,
Including step one：
Polyester-cotton blend cloth is dipped in disperse dyes, a leaching one is carried out and pricks；
Step 2：
Polyester-cotton blend cloth after one leaching one is pricked is dried at a temperature of 80 ~ 90 DEG C；
Step 3：
Cloth after drying is carried out to baking 90 seconds at a temperature of 190 DEG C；
Step 4：
The cloth for bakeing completion is dipped secondary dip is carried out in reduction cleaning liquid；
Step 5：
Cloth after secondary dip is wrapped with plastic foil, decatize 2 minutes under 100 DEG C of vapor；
Step 6：
Carry out washing ventilative, soap boiling dries again afterwards；
The disperse dyes include following composition：
Dyestuff：6g/L
Dispersant：3 g/L
Anti- swimming agent：12 g/L
Softener：5 g/L；
The softener is constituted including following parts by weight：
3- (isobutene acyl-oxygen) propyl trimethoxy silicane：2 parts
3- (trimethyl silyl) ethyl propionate：5 parts
3,4- bis--O- acetyl group -6-O- (t-butyl-dimethylsilyl)-D- grape aldehyde：5 parts
Four (2- hydroxyl-oxethyls) silane;：10 parts.
As a further improvement on the present invention,
In the step one, it is 25 DEG C to dip temperature, and pick-up is 60 ~ 70%.
As a further improvement on the present invention,
The reduction cleaning liquid includes following composition：
Sodium hydroxide：20g/L
85% sodium hydrosulfite 20g/L
(N-Boc-2- pyrrole radicals) dimethyl-silicon alkanol：2g/L.
As a further improvement on the present invention,
Washing temperature is 40 DEG C in the step 6, and the time is 1 ~ 5 minute.
As a further improvement on the present invention,
Also include bleeding agent 3g/L in the disperse dyes.
As a further improvement on the present invention,
The bleeding agent is constituted including following weight parts：
3- [(methylol) methyl amine] propane sulfonic acid：2 parts
Disecoctylmaleate sodium sulfonate：10 parts
Hydroxy ethylene diphosphonic acid sylvite：2 parts.
In the present invention, by dyeing course, adding softener, entirety can be strengthened directly in dyeing course
Anti pilling ability, without follow-up arrangement step.
The key of we's invention is in the selection of softener that four (2- hydroxyl-oxethyls) silane in softener are in entirety
In play a part of compatilizer, other softener compositions are well dispersed in whole disperse dyes, while 3- (methacryloyls
Oxygen) propyl trimethoxy silicane and 3- (trimethyl silyl) ethyl propionate addition, increase considerably follow-up polyester-cotton blend material
Anti-pilling property, be eventually adding 3,4- bis--O- acetyl group -6-O- (t-butyl-dimethylsilyl)-D- grape aldehyde and play one
The effect of individual fixative so that last polyester-cotton blend is after long-time is cleaned, still with preferable anti pilling effect, by submissive
The synergy of each component, is further ensured that during routine use in agent, is maintained to good anti pilling ability.
Homemade bleeding agent is particularly added, enables to shortening processing time, and obtains preferable anti pilling effect
Really.
Embodiment
Embodiment one：
A kind of terylene cotton elastic is knitted fabric dyeing,
Including step one：
Polyester-cotton blend cloth is dipped in disperse dyes, a leaching one is carried out and pricks；
Step 2：
Polyester-cotton blend cloth after one leaching one is pricked is dried at a temperature of 80 ~ 90 DEG C；
Step 3：
Cloth after drying is carried out to baking 90 seconds at a temperature of 190 DEG C；
Step 4：
The cloth for bakeing completion is dipped secondary dip is carried out in reduction cleaning liquid；
Step 5：
Cloth after secondary dip is wrapped with plastic foil, decatize 2 minutes under 100 DEG C of vapor；
Step 6：
Carry out washing ventilative, soap boiling dries again afterwards；
The disperse dyes include following composition：
Dyestuff：6g/L
Dispersant：3 g/L
Anti- swimming agent：12 g/L
Softener：5 g/L；
The softener is constituted including following parts by weight：
3- (isobutene acyl-oxygen) propyl trimethoxy silicane：2 parts
3- (trimethyl silyl) ethyl propionate：5 parts
3,4- bis--O- acetyl group -6-O- (t-butyl-dimethylsilyl)-D- grape aldehyde：5 parts
Four (2- hydroxyl-oxethyls) silane;：10 parts.
In the step one, it is 25 DEG C to dip temperature, and pick-up is 60 ~ 70%.
The reduction cleaning liquid includes following composition：
Sodium hydroxide：20g/L
85% sodium hydrosulfite 20g/L
(N-Boc-2- pyrrole radicals) dimethyl-silicon alkanol：2g/L.
Washing temperature is 40 DEG C in the step 6, and the time is 1 ~ 5 minute.
Also include bleeding agent 3g/L in the disperse dyes.
The bleeding agent is constituted including following weight parts：
3- [(methylol) methyl amine] propane sulfonic acid：2 parts
Disecoctylmaleate sodium sulfonate：10 parts
Hydroxy ethylene diphosphonic acid sylvite：2 parts.
Embodiment two：
A kind of terylene cotton elastic is knitted fabric dyeing,
Including step one：
Polyester-cotton blend cloth is dipped in disperse dyes, a leaching one is carried out and pricks；
Step 2：
Polyester-cotton blend cloth after one leaching one is pricked is dried at a temperature of 80 ~ 90 DEG C；
Step 3：
Cloth after drying is carried out to baking 90 seconds at a temperature of 190 DEG C；
Step 4：
The cloth for bakeing completion is dipped secondary dip is carried out in reduction cleaning liquid；
Step 5：
Cloth after secondary dip is wrapped with plastic foil, decatize 2 minutes under 100 DEG C of vapor；
Step 6：
Carry out washing ventilative, soap boiling dries again afterwards；
The disperse dyes include following composition：
Dyestuff：6g/L
Dispersant：3 g/L
Anti- swimming agent：12 g/L
Softener：5 g/L；
The softener is constituted including following parts by weight：
3- (isobutene acyl-oxygen) propyl trimethoxy silicane：2 parts
3- (trimethyl silyl) ethyl propionate：5 parts
3,4- bis--O- acetyl group -6-O- (t-butyl-dimethylsilyl)-D- grape aldehyde：5 parts
Four (2- hydroxyl-oxethyls) silane;：10 parts.
In the step one, it is 25 DEG C to dip temperature, and pick-up is 60 ~ 70%.
The reduction cleaning liquid includes following composition：
Sodium hydroxide：20g/L
85% sodium hydrosulfite 20g/L
(N-Boc-2- pyrrole radicals) dimethyl-silicon alkanol：2g/L.
Washing temperature is 40 DEG C in the step 6, and the time is 1 ~ 5 minute.
Embodiment three：
A kind of terylene cotton elastic is knitted fabric dyeing,
Including step one：
Polyester-cotton blend cloth is dipped in disperse dyes, a leaching one is carried out and pricks；
Step 2：
Polyester-cotton blend cloth after one leaching one is pricked is dried at a temperature of 80 ~ 90 DEG C；
Step 3：
Cloth after drying is carried out to baking 90 seconds at a temperature of 190 DEG C；
Step 4：
The cloth for bakeing completion is dipped secondary dip is carried out in reduction cleaning liquid；
Step 5：
Cloth after secondary dip is wrapped with plastic foil, decatize 2 minutes under 100 DEG C of vapor；
Step 6：
Carry out washing ventilative, soap boiling dries again afterwards；
The disperse dyes include following composition：
Dyestuff：6g/L
Dispersant：3 g/L
Anti- swimming agent：12 g/L
Softener：5 g/L；
The softener is constituted including following parts by weight：
3- (isobutene acyl-oxygen) propyl trimethoxy silicane：2 parts
3- (trimethyl silyl) ethyl propionate：5 parts
3,4- bis--O- acetyl group -6-O- (t-butyl-dimethylsilyl)-D- grape aldehyde：5 parts
Four (2- hydroxyl-oxethyls) silane;：10 parts.
In the step one, it is 25 DEG C to dip temperature, and pick-up is 60 ~ 70%.
The reduction cleaning liquid includes following composition：
Sodium hydroxide：20g/L
85% sodium hydrosulfite 20g/L
Washing temperature is 40 DEG C in the step 6, and the time is 1 ~ 5 minute.
Also include bleeding agent 3g/L in the disperse dyes.
The bleeding agent is constituted including following weight parts：
3- [(methylol) methyl amine] propane sulfonic acid：2 parts
Disecoctylmaleate sodium sulfonate：10 parts
Hydroxy ethylene diphosphonic acid sylvite：2 parts.
Comparative example one：
A kind of terylene cotton elastic is knitted fabric dyeing,
Including step one：
Polyester-cotton blend cloth is dipped in disperse dyes, a leaching one is carried out and pricks；
Step 2：
Polyester-cotton blend cloth after one leaching one is pricked is dried at a temperature of 80 ~ 90 DEG C；
Step 3：
Cloth after drying is carried out to baking 90 seconds at a temperature of 190 DEG C；
Step 4：
The cloth for bakeing completion is dipped secondary dip is carried out in reduction cleaning liquid；
Step 5：
Cloth after secondary dip is wrapped with plastic foil, decatize 2 minutes under 100 DEG C of vapor；
Step 6：
Carry out washing ventilative, soap boiling dries again afterwards；
The disperse dyes include following composition：
Dyestuff：6g/L
Dispersant：3 g/L
Anti- swimming agent：12 g/L
In the step one, it is 25 DEG C to dip temperature, and pick-up is 60 ~ 70%.
The reduction cleaning liquid includes following composition：
Sodium hydroxide：20g/L
85% sodium hydrosulfite 20g/L
Washing temperature is 40 DEG C in the step 6, and the time is 1 ~ 5 minute.
Examination criteria：
Anti-pilling detection is detected according to GB/T4802.3-1997 standard；
Antistatic test is detected according to the standards of GB/T 12703.3.
In the present invention, by dyeing course, adding softener, entirety can be strengthened directly in dyeing course
Anti pilling ability, without follow-up arrangement step.
The key of we's invention is in the selection of softener that four (2- hydroxyl-oxethyls) silane in softener are in entirety
In play a part of compatilizer, other softener compositions are well dispersed in whole disperse dyes, while 3- (methacryloyls
Oxygen) propyl trimethoxy silicane and 3- (trimethyl silyl) ethyl propionate addition, increase considerably follow-up polyester-cotton blend material
Anti-pilling property, be eventually adding 3,4- bis--O- acetyl group -6-O- (t-butyl-dimethylsilyl)-D- grape aldehyde and play one
The effect of individual fixative so that last polyester-cotton blend is after long-time is cleaned, still with preferable anti pilling effect, by submissive
The synergy of each component, is further ensured that during routine use in agent, is maintained to good anti pilling ability.
Homemade bleeding agent is particularly added, enables to shortening processing time, and obtains preferable anti pilling effect
Really.
Pass through above-mentioned experimental data, it can be deduced that, for adding (N-Boc-2- pyrrole radicals) dimethylsilane in reducing agent
Alcohol serves preferable effect.
Described above is only the preferred embodiment of the present invention, and protection scope of the present invention is not limited merely to above-mentioned implementation
Example, all technical schemes belonged under thinking of the present invention belong to protection scope of the present invention.It should be pointed out that for the art
Those of ordinary skill for, some improvements and modifications without departing from the principles of the present invention, these improvements and modifications
It should be regarded as protection scope of the present invention.
Claims (6)
1. a kind of terylene cotton elastic is knitted fabric dyeing, it is characterised in that：
Including step one：
Polyester-cotton blend cloth is dipped in disperse dyes, a leaching one is carried out and pricks；
Step 2：
Polyester-cotton blend cloth after one leaching one is pricked is dried at a temperature of 80 ~ 90 DEG C；
Step 3：
Cloth after drying is carried out to baking 90 seconds at a temperature of 190 DEG C；
Step 4：
The cloth for bakeing completion is dipped secondary dip is carried out in reduction cleaning liquid；
Step 5：
Cloth after secondary dip is wrapped with plastic foil, decatize 2 minutes under 100 DEG C of vapor；
Step 6：
Carry out washing ventilative, soap boiling dries again afterwards；
The disperse dyes include following composition：
Dyestuff：6g/L
Dispersant：3 g/L
Anti- swimming agent：12 g/L
Softener：5 g/L；
The softener is constituted including following parts by weight：
3- (isobutene acyl-oxygen) propyl trimethoxy silicane：2 parts
3- (trimethyl silyl) ethyl propionate：5 parts
3,4- bis--O- acetyl group -6-O- (t-butyl-dimethylsilyl)-D- grape aldehyde：5 parts
Four (2- hydroxyl-oxethyls) silane;：10 parts.
2. a kind of terylene cotton elastic knitting fabric dyeing according to claim 1, it is characterised in that：The step one
In, it is 25 DEG C to dip temperature, and pick-up is 60 ~ 70%.
3. a kind of terylene cotton elastic knitting fabric dyeing according to claim 2, it is characterised in that：
The reduction cleaning liquid includes following composition：
Sodium hydroxide：20g/L
85% sodium hydrosulfite 20g/L
(N-Boc-2- pyrrole radicals) dimethyl-silicon alkanol：2g/L.
4. a kind of terylene cotton elastic knitting fabric dyeing according to claim 3, it is characterised in that：
Washing temperature is 40 DEG C in the step 6, and the time is 1 ~ 5 minute.
5. a kind of terylene cotton elastic knitting fabric dyeing according to claim 4, it is characterised in that：
Also include bleeding agent 3g/L in the disperse dyes.
6. a kind of terylene cotton elastic knitting fabric dyeing according to claim 5, it is characterised in that：
The bleeding agent is constituted including following weight parts：
3- [(methylol) methyl amine] propane sulfonic acid：2 parts
Disecoctylmaleate sodium sulfonate：10 parts
Hydroxy ethylene diphosphonic acid sylvite：2 parts.