A kind of automobile heat insulation insulation nanometer putty paste and preparation method thereof
Technical field
The present invention relates to paint field.Specifically related to a kind of automobile heat insulation insulation nanometer putty paste and preparation method thereof.
Background technology
The summer high temperature time sustainable growth all over the world in view of the increasingly thin global climate of earth's ozone layer warms year by year.From
It is also fabulous guiding, the promulgation of National Renewable law of resources and Ministry of Construction's building energy conservation regulations, building section in terms of national policy
The implementation of energy regulations.Government advocates building energy conservation from each aspect Implementation of Recycling Economy, and the key of the weight of architectural energy consumption weight is just
It is glass, reaches the standard of the energy-conservation 60% of national Tenth-Five Year Plan, it is to stand in the breach to solve automobile power consumption.With the modern times
The development of science and technology, energy-conservation and environmental protection receive the concern of more and more national.
It is well known that orthodox car spraying coating process is nothing but:One layer of putty paste is first scraped on car body, is sprayed again after polishing smooth
Paint.Nobody expects car body heat-insulating problem always.
Novelty of the present invention is:Summer, which can effectively reduce vehicle interior temperature 20-25 degree, winter, can prevent in-car heat losses
5 --- 10 automobile putty paste.Automobile hardly uses air-conditioning!This industry has been overturned completely, will produce the economy of hundreds billion of members
Value.
Construction Principle is very simple:First without traditional putty paste on the new car body for assembling, being welded, but use this hair instead
Bright novel heat-insulation putty paste, sprays surface lacquer again after polishing smooth --- so both played that summer is heat-insulated, the effect of winter insulation!
For used car, polish off after traditional vehicle paint and putty paste, table is sprayed again after scraping novel heat-insulation putty paste of the invention
Finish paint --- equally play that summer is heat-insulated, the effect of winter insulation!
At present, traditional putty paste per kilogram cost is 20 yuan or so, and one new car of blade coating is at 1.5 kilograms, just 30 yuan;And this
Just 3 times higher than traditional putty paste or so of the novel heat insulation and preservation putty paste per kilogram cost of invention, consumption and traditional putty paste one
Sample, just 90 yuan or so of one new car of blade coating.And the heat-insulation and heat-preservation benefit that it is produced is the hundred times of traditional putty paste --- no matter
All it is a big attractable point for automaker or vehicle repairing factory, especially for user, the air-conditioning expense of thousands of members will be saved.Close
Key is, hot summer into the car after again by " baking ", cold winter into the car after industry it is no longer so not ice-cold.
The content of the invention
It is an object of the invention to for China's national situation, it is proposed that a kind of automobile heat insulation insulation nanometer putty paste and its preparation
Method, can effectively reduce the cost of vehicle fuel consumption and air-conditioning cost.
To achieve these goals, the technical solution adopted in the present invention is that a kind of automobile heat insulation is incubated nanometer putty paste
And preparation method thereof, its raw material is calculated as by weight:55~65 parts of unsaturated-resin, solid content are 30 ± 2% nano heat insulatings
25~35 parts of mixed slurry, 5~7 parts of cobalt naphthenate (4% content), N, 2~3 parts of the dimethylanilines of N mono- (20% content), benzene
4~6 parts of formol polymerization retarder, 0., 8~1.2 parts of 731A dispersants.
Further, a kind of automobile heat insulation insulation nanometer putty paste and preparation method thereof, its raw material is calculated as by weight:Film forming
60 parts of resin, solid content are 30 parts of 30 ± 2% nano heat insulating mixed slurry, 3 parts of cobalt naphthenate (4% content), N, the diformazans of N mono-
2 parts of base aniline (20% content), 4 parts of benzaldehyde polymerization inhibitor, 1 part of 731A dispersants are preferably, described film-forming resin is water
Property fluorocarbon resin.
Further, described unsaturated-resin is the nano heat insulating that unsaturated polyester resin is 30 ± 2% with solid content
Cobalt naphthenate (4% content), N, the dimethylanilines of N mono- (20% content), benzaldehyde polymerization inhibitor, 731A points are added after material mixing
Powder stir grinding after gained.
The method for preparing heat insulation nano putty paste as described above, comprises the following steps:
A. by 10 ± 1% aerosil finished products and 10 ± 2% expanded perlite finished product, 10 ± 3% vermiculite
Finished product, 10 ± 3% sepiolite powder finished products, 10 ± 3% hydroxypropyl methyl cellulose finished products, 10 ± 3% diatomite finished products, it is put into and grinds
In grinding machine, 2.7~3.3 times of ethanol is put into grinder, adds 1% 731A dispersants, 12h is ground in grinder,
Solid content is obtained for 30 ± 2% heat-insulated mixed slurries;
B. ground mixed slurry is extracted into residual ethanol again, heat-insulated solid material must be mixed.
C. mix in mass ratio:Mix heat-insulated solid material: unsaturated polyester resin=3: 7 are added to unsaturated polyester resin
In, stirred on 1100~1300r/min high speed dispersor, obtain solid content for 30 ± 2% by synthetic insulating material;
D. again in synthetic insulating material add cobalt naphthenate (4% content), N, the dimethylanilines of N mono- (20% content),
Benzaldehyde polymerization inhibitor is placed in dispersion machine, on high speed dispersor with 800~1200r/min rotating speeds disperse 0.5h, obtain every
Hot putty paste product.
In construction, curing agent is common putty paste curing agent..
Further, the step a be by aerosil, expanded perlite, 10 ± 3% vermiculite, sepiolite powder,
After hydroxypropyl methyl cellulose, diatomite final product quality are than 1: 1: 1: 1: 1: 1 mixing, 3 times of ethanol and 1% 731A are scattered
Agent, is placed in sand mill, and 36h is ground under 3000r/min rotating speeds.Further, the step c is again by ground ATO slurry
Expect after being mixed with ground rare earth-polycrystalline silicon material, in mass ratio mixed slurry: ethanol=1: 2 add ethanol, in 1200r/
Stirred on min high speed dispersor, ATO slurries will be synthesized for 30% by obtaining solid content.
Further, the step b must mix heat-insulated solid material again to extract ground slurry after residual ethanol.
Further, dispersant is 731A in the step b.
Surface is first sprayed after polishing smooth again with novel heat-insulation putty paste of the invention on the new car body for assembling, being welded
Paint --- summer, which can effectively reduce vehicle interior temperature 20-25 degree, winter, can prevent in-car heat losses 5 --- 10 automobile putty
Cream.Automobile hardly uses air-conditioning!
The present invention possesses advantages below:
1. traditional talcum powder, dicalcium powder etc. instead of using nano heat insulating mixing material, and each material proportioning is adapted to
With fine barrier thermal effect;
2. instead of expensive wetting agent with cheap ethanol, cost is set further to reduce;
3. use 731A several materials is effectively reached nanoscale in process of lapping for dispersant;
4. product safety is nontoxic, summer is that (28~40) have good heat-insulated rate in temperature, heat-insulated rate up to 90~95%,
Winter is that (- 25~10) have good insulation rate in temperature, reaches energy-saving heat preserving effect, saves up to 25~30%;
5. product has good construction quality, coordinate conventional curing agents 20 minutes dry tack frees (normal temperature) of construction, you can
Polishing;
6. preparation method advantages of simple, can be effectively obtained nano level heat-insulated mixed slurry, product quality is ensured, and
Easily operated, device input is relatively low.
Embodiment
The present invention is described in further detail below by specific embodiment.
Embodiment 1:A kind of automobile heat insulation insulation nanometer putty paste and preparation method thereof, its raw material is calculated as by weight:No
60 parts of saturated resin, solid content are 30 parts of 30 ± 2% nano heat insulating mixed slurry, 8 parts of cobalt naphthenate (4% content), N, N mono-
1 part of dimethylaniline (20% content), 1 part of benzaldehyde polymerization inhibitor.
A kind of automobile heat insulation insulation nanometer putty paste as described above and preparation method thereof is prepared, is comprised the following steps:
A. by 9% aerosil finished product and 11% expanded perlite finished product, 8% vermiculite finished product, 12% sea
Afrodite powder finished product, 10% hydroxypropyl methyl cellulose finished product, 10% diatomite finished product, it is put into grinder, 2.7~3.3 times
Ethanol, is put into grinder, adds 1% 731A dispersants, 12h is ground in grinder, and it is 30 ± 2% to obtain solid content
Heat-insulated mixed slurry;
B. ground mixed slurry is extracted into residual ethanol again, heat-insulated solid material must be mixed.
C. mix in mass ratio:Mix heat-insulated solid material: unsaturated polyester resin=3: 7 are added to unsaturated polyester resin
In, stirred on 1100~1300r/min high speed dispersor, obtain solid content for 30 ± 2% by synthetic insulating material;
D. again in synthetic insulating material add cobalt naphthenate (4% content), N, the dimethylanilines of N mono- (20% content),
Benzaldehyde polymerization inhibitor is placed in dispersion machine, on high speed dispersor with 800~1200r/min rotating speeds disperse 0.5h, obtain every
Hot putty paste product.
Embodiment 2:A kind of automobile heat insulation insulation nanometer putty paste and preparation method thereof, its raw material is calculated as by weight:No
65 parts of saturated resin, solid content are 35 parts of 30 ± 2% nano heat insulating mixed slurry, 7 parts of cobalt naphthenate (4% content), N, N mono-
3 parts of dimethylaniline (20% content), 1 part of benzaldehyde polymerization inhibitor.
A kind of automobile heat insulation insulation nanometer putty paste as described above and preparation method thereof is prepared, is comprised the following steps:
A. by 10% aerosil finished product and 9% expanded perlite finished product, 10% vermiculite finished product, 10% sea
Afrodite powder finished product, 8% hydroxypropyl methyl cellulose finished product, 12% diatomite finished product, it is put into grinder, 2.7~3.3 times of second
Alcohol, is put into grinder, adds 1.2% 731A dispersants, 12h is ground in grinder, and it is 30 ± 2% to obtain solid content
Heat-insulated mixed slurry;
B. ground mixed slurry is extracted into residual ethanol again, heat-insulated solid material must be mixed.
C. mix in mass ratio:Mix heat-insulated solid material: unsaturated polyester resin=3: 7 are added to unsaturated polyester resin
In, stirred on 1100~1300r/min high speed dispersor, obtain solid content for 30 ± 2% by synthetic insulating material;
D. again in synthetic insulating material add cobalt naphthenate (4% content), N, the dimethylanilines of N mono- (20% content),
Benzaldehyde polymerization inhibitor is placed in dispersion machine, on high speed dispersor with 800~1200r/min rotating speeds disperse 0.5h, obtain every
Hot putty paste product.
Embodiment 3:A kind of automobile heat insulation insulation nanometer putty paste and preparation method thereof, its raw material is calculated as by weight:No
63 parts of saturated resin, solid content are 37 parts of 30 ± 2% nano heat insulating mixed slurry, 8 parts of cobalt naphthenate (4% content), N, N mono-
1 part of dimethylaniline (20% content), 1 part of benzaldehyde polymerization inhibitor.
A kind of automobile heat insulation insulation nanometer putty paste as described above and preparation method thereof is prepared, is comprised the following steps:
A. by 8% aerosil finished product and 12% expanded perlite finished product, 9% vermiculite finished product, 11% sea
Afrodite powder finished product, 9% hydroxypropyl methyl cellulose finished product, 11% diatomite finished product, it is put into grinder, 2.7~3.3 times of second
Alcohol, is put into grinder, adds 1.3% 731A dispersants, 12h is ground in grinder, and it is 30 ± 2% to obtain solid content
Heat-insulated mixed slurry;
B. ground mixed slurry is extracted into residual ethanol again, heat-insulated solid material must be mixed.
C. mix in mass ratio:Mix heat-insulated solid material: unsaturated polyester resin=3: 7 are added to unsaturated polyester resin
In, stirred on 1100~1300r/min high speed dispersor, obtain solid content for 30 ± 2% by synthetic insulating material;
D. again in synthetic insulating material add cobalt naphthenate (4% content), N, the dimethylanilines of N mono- (20% content),
Benzaldehyde polymerization inhibitor is placed in dispersion machine, on high speed dispersor with 800~1200r/min rotating speeds disperse 0.5h, obtain every
Hot putty paste product.
Embodiment 4:A kind of automobile heat insulation insulation nanometer putty paste and preparation method thereof, its raw material is calculated as by weight:No
68 parts of saturated resin, solid content are 32 parts of 30 ± 2% nano heat insulating mixed slurry, 7 parts of cobalt naphthenate (4% content), N, N mono-
2 parts of dimethylaniline (20% content), 1 part of benzaldehyde polymerization inhibitor.
A kind of automobile heat insulation insulation nanometer putty paste as described above and preparation method thereof is prepared, is comprised the following steps:
A. by 8% aerosil finished product and 12% expanded perlite finished product, 8% vermiculite finished product, 12% sea
Afrodite powder finished product, 9% hydroxypropyl methyl cellulose finished product, 11% diatomite finished product, it is put into grinder, 2.7~3.3 times of second
Alcohol, is put into grinder, adds 1.1% 731A dispersants, 12h is ground in grinder, and it is 30 ± 2% to obtain solid content
Heat-insulated mixed slurry;
B. ground mixed slurry is extracted into residual ethanol again, heat-insulated solid material must be mixed.
C. mix in mass ratio:Mix heat-insulated solid material: unsaturated polyester resin=3: 7 are added to unsaturated polyester resin
In, stirred on 1100~1300r/min high speed dispersor, obtain solid content for 30 ± 2% by synthetic insulating material;
D. again in synthetic insulating material add cobalt naphthenate (4% content), N, the dimethylanilines of N mono- (20% content),
Benzaldehyde polymerization inhibitor is placed in dispersion machine, on high speed dispersor with 800~1200r/min rotating speeds disperse 0.5h, obtain every
Hot putty paste product.
Embodiment 5:A kind of automobile heat insulation insulation nanometer putty paste and preparation method thereof, its raw material is calculated as by weight:No
70 parts of saturated resin, solid content are 30 parts of 30 ± 2% nano heat insulating mixed slurry, 8 parts of cobalt naphthenate (4% content), N, N mono-
1 part of dimethylaniline (20% content), 1 part of benzaldehyde polymerization inhibitor.
A kind of automobile heat insulation insulation nanometer putty paste as described above and preparation method thereof is prepared, is comprised the following steps:
A. by 11% aerosil finished product and 9% expanded perlite finished product, 11% vermiculite finished product, 9% sea
Afrodite powder finished product, 8% hydroxypropyl methyl cellulose finished product, 12% diatomite finished product, it is put into grinder, 2.7~3.3 times of second
Alcohol, is put into grinder, adds 1.2% 731A dispersants, 12h is ground in grinder, and it is 30 ± 2% to obtain solid content
Heat-insulated mixed slurry;
B. ground mixed slurry is extracted into residual ethanol again, heat-insulated solid material must be mixed.
C. mix in mass ratio:Mix heat-insulated solid material: unsaturated polyester resin=3: 7 are added to unsaturated polyester resin
In, stirred on 1100~1300r/min high speed dispersor, obtain solid content for 30 ± 2% by synthetic insulating material;
D. again in synthetic insulating material add cobalt naphthenate (4% content), N, the dimethylanilines of N mono- (20% content),
Benzaldehyde polymerization inhibitor is placed in dispersion machine, on high speed dispersor with 800~1200r/min rotating speeds disperse 0.5h, obtain every
Hot putty paste product.
Embodiment 6:Substantially similar to embodiment 1, its difference is, silane coupler is added in unsaturated-resin.
Embodiment 7:Substantially similar to embodiment 2, its difference is, unsaturated-resin uses unsaturated polyester (UP) tree
Fat.
The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the invention, for the skill of this area
For art personnel, there can be various modifications and variations in the spirit and principles in the present invention, these equivalent modifications or replacement etc.,
It is all contained within protection scope of the present invention.