CN106695193B - 导电碳毡与铅质极耳的连接方法 - Google Patents
导电碳毡与铅质极耳的连接方法 Download PDFInfo
- Publication number
- CN106695193B CN106695193B CN201611233229.5A CN201611233229A CN106695193B CN 106695193 B CN106695193 B CN 106695193B CN 201611233229 A CN201611233229 A CN 201611233229A CN 106695193 B CN106695193 B CN 106695193B
- Authority
- CN
- China
- Prior art keywords
- carbon felt
- conductive carbon
- lead matter
- lug
- lead
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种导电碳毡与铅质极耳的连接方法,所述连接方法按以下步骤进行:首先分别按尺寸剪裁导电碳毡,剪裁片状的铅质极耳,接着在导电碳毡上边框一边或两边平叠片状的铅质极耳,然后实施点焊。本发明通过实施点焊工艺实现铅质极耳与导电碳毡的连接,该连接工艺设计合理、实施容易,最重要的是点焊形成的电阻热使铅质极耳局部熔化,此处的液态铅合金渗透到所在位置的导电碳毡缝隙中,待冷却后即形成相互嵌合结构。交错嵌合形成紧密连接的接头,该接头的连接强度相对于现有技术同规格产品提高了近一倍,而且导电率也显著提高。
Description
技术领域
本发明涉及一种异质构件的连接方法,具体地讲,本发明涉及一种导电碳毡与铅质极耳的连接方法。
背景技术
众所周知,铅酸蓄电池中的核心构件板栅是铅制品,两电极之间的电解液为稀硫酸。本行业制造过程中的污染源主要是铅和酸,其中对环境污染最大的是铅污染。近几年来,本行业一直努力寻找铅和酸的替代品,力争产品中少用铅和酸。最新研制的非铅质板栅就是遵照此原则研制的产品,它用两种不同种类的材质制造而成,即板栅主体用导电碳毡制作,用于外连接的极耳仍然用铅材料制作。目前,本行业制造非铅质板栅采用铅铸造模式实现两件相连,即在导电毡上直接浇铸铅极耳,由于相结合的两种材质不同类,再加上比重悬殊大,界面又不相容,使得铅质极耳与导电碳毡仅是铅皮贴靠式连接。此种连接结构尽管能够达到传输电能的目的,但机械强度低、界面欧姆电阻大,降低了导电效率。另外因制成的板栅结合部机械强度低,配套安装后存在承载能力不足、抗冲击能力差等现实问题,若不切实解决导电碳毡与铅质极耳的连接方法,制成的蓄电池产品必然存在安全、质量隐患。
发明内容
本发明主要针对现有技术的不足,提出一种方法简便、实施容易、连接可靠、导电效率高,用铅量极少的导电碳毡与铅质极耳的连接方法。
本发明通过下述技术方案实现技术目标。
导电碳毡与铅质极耳的连接方法,其改进之处在于:所述连接方法按以下步骤进行:A、备料——分别按尺寸剪裁导电碳毡,剪裁片状的铅质极耳;
B、叠合——在导电碳毡上边框一边或两边平叠片状的铅质极耳;
C、点焊——沿着铅质极耳长度方向每隔10~20mm间距实施点焊,点焊极头为φ5.0~φ8.0mm的平面,点焊工艺参数在许可范围内选取,其中电源电压220V或380V、加压时间0.08s~0.12s、预热时间0.3s~0.5s、预热电流12KA~13KA、焊接时间0.6s~0.7s、焊接电流14KA~15KA、维持时间0.16s~0.3s、施压3.5KG~4.0KG。
作为进一步改进方案,所述铅质极耳片厚0.5~1.5mm,导电碳毡厚1.0~2.5mm。
本发明与现有技术相比,具有以下积极效果:
1、在叠合的基础上实施点焊,工艺方法简单,实施容易;
2、通过点焊使铅质极耳局部熔化,此处的液态铅合金流进导电碳毡的缝隙中,待冷却后即形成相互嵌合结构,嵌合结构相对于贴靠连接结合面大、强度高、导电效率高;
3、极板上仅外连接的极耳保留铅质,此种复合结构简单、降铅量多,故减污成效大。
附图说明
图1是本实施例示意图。
图2是图1的侧视图,图中一层导电碳毡上叠合一层铅质极耳。
图3是图1的侧视图,图中一层导电碳毡上左右两面分别叠合一层铅质极耳。
具体实施方式
下面结合实施例,对本发明作进一步说明。
本发明所述的导电碳毡与铅质极耳的方法,是一种物理连接方法,它按以下步骤进行:
A、备料——分别按尺寸剪裁导电碳毡,剪裁片状的铅质极耳,本实施例导电碳毡尺寸为200×150×2.0mm,铅质极耳尺寸为170×30×1.0mm;
B、叠合——在导电碳毡上边框一边平叠片状的铅质极耳,本实施例如图1和图2所示,在导电碳毡上边框一边平叠一块片状的铅质极耳;
C、点焊——沿着铅质极耳长度方向每隔10mm间距实施点焊,点焊极头为φ5.0mm的平面,点焊工艺参数如下:电源电压380V、加压时间0.08s、预热时间0.5s、预热电流12KA、焊接时间0.7s、焊接电流14KA、维持时间0.16s、施压3.5KG。
本发明通过实施点焊工艺实现 铅质极耳与导电碳毡的连接,该连接工艺设计合理、实施容易,最重要的是点焊形成的电阻热使铅质极耳局部熔化,此处的液态铅合金渗透到所在位置的导电碳毡缝隙中,待冷却后即形成相互嵌合结构。交错嵌合形成紧密连接的接头,该接头的连接强度相对于现有技术提高近一倍,而且导电率也显著提高。本发明除上述实施例所述的,也可以按图3所示结构进行连接,尽管该连接结构采用双层铅质极耳夹持导电碳毡,但所用工艺相同,仅部分工艺参数按上限指标选取而已,其连接效果相同。
Claims (2)
1.一种导电碳毡与铅质极耳的连接方法,其特征在于:所述连接方法按以下步骤进行:A、备料——分别按尺寸剪裁导电碳毡,剪裁片状的铅质极耳;
B、叠合——在导电碳毡上边框一边或两边平叠片状的铅质极耳;
C、点焊——沿着铅质极耳长度方向每隔10~20mm间距实施点焊,点焊极头为φ5.0~φ8.0mm的平面,点焊工艺参数在许可范围内选取,其中电源电压220V或380V、加压时间0.08s~0.12s、预热时间0.3s~0.5s、预热电流12KA~13KA、焊接时间0.6s~0.7s、焊接电流14KA~15KA、维持时间0.16s~0.3s、施压3.5KG~4.0KG。
2.根据权利要求1所述的导电碳毡与铅质极耳的连接方法,其特征在于:所述铅质极耳片厚0.5~1.5mm,导电碳毡厚1.0~2.5mm。