CN106680902B - 无光损光学镜头及其制备工艺 - Google Patents
无光损光学镜头及其制备工艺 Download PDFInfo
- Publication number
- CN106680902B CN106680902B CN201611102147.7A CN201611102147A CN106680902B CN 106680902 B CN106680902 B CN 106680902B CN 201611102147 A CN201611102147 A CN 201611102147A CN 106680902 B CN106680902 B CN 106680902B
- Authority
- CN
- China
- Prior art keywords
- parts
- graphene
- optical lens
- minutes
- light loss
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及光学镜头技术领域，具体涉及无光损光学镜头，该镜头由如下重量份数的原料制成：石英砂52‑58份、明矾4‑8份、纯碱10‑13份、纳米二氧化硅4‑6份、改性石墨烯8‑12份、氢氧化锂4‑6份、硼化铪7.5‑8份、氯化钾8‑10份、五氧化二钒5‑8份、碳化铁5‑8份、硅化钡4‑6份、硅化钨1‑2份、二氧化钴4‑5.5份、玻化纤维2.5‑3份。本发明镜头对光线的衍射好，光损极低，非常适合于强光下的摄像使用，而且镜头像漂移低。
Description
技术领域
本发明涉及光学镜头技术领域，具体涉及一种无光损光学镜头及其制备工艺。
背景技术
光学镜头是机器视觉***中必不可少的部件，直接影响成像质量的优劣，影响算法的实现和效果。光学镜头从焦距上可分为短焦镜头、中焦镜头，长焦镜头；从视场大小分有广角、标准，远摄镜头；结构上分有固定光圈定焦镜头，手动光圈定焦镜头，自动光圈定焦镜头，手动变焦镜头、自动变焦镜头，自动光圈电动变焦镜头，电动三可变(光圈、焦距、聚焦均可变)镜头等。目前的光学镜头由于其材料的限制，所以其光损大。
发明内容
本发明所要解决的技术问题在于提供一种无光损光学镜头及其制备工艺，镜头对光线的衍射好，光损极低，非常适合于强光下的摄像使用，而且镜头像漂移低。
本发明所要解决的技术问题采用以下技术方案来实现：
无光损光学镜头，该镜头由如下重量份数的原料制成：
石英砂52-58份、明矾4-8份、纯碱10-13份、纳米二氧化硅4-6份、改性石墨烯8-12份、氢氧化锂4-6份、硼化铪7.5-8份、氯化钾8-10份、五氧化二钒5-8份、碳化铁5-8份、硅化钡4-6份、硅化钨1-2份、二氧化钴4-5.5份、玻化纤维2.5-3份。
所述改性石墨烯制备方法是，将石墨烯用240-300℃高温氮气加压30分钟，压力为1.2-1.8MPa，接着用32.5nm的紫外线对石墨烯照射，然后用40-60MHz超声波超声处理10分钟，接着将石墨烯在300-350℃温度下煅烧30分钟，待石墨烯自然冷却至常温即得改性石墨烯。
无光损光学镜头的制备方法，包括以下步骤：
(1)将除了改性石墨烯、玻化纤维外的各原料混合投入熔炼炉内熔融，加热至1200℃时投入改性石墨烯，然后将温度降至800-850℃后向熔炼炉内投入玻化纤维，然后继续熔炼加热至1300-1400℃，熔炼30分钟后向熔料内吹入常温氮气，30分钟后再升温至1300-1400℃；
(2)将步骤(1)的熔炼物料成型成镜头状，然后冷却处理，按每分钟冷却30℃的速度冷却至常温即得该光学镜头。
步骤(1)中继续熔炼加热至1350℃。
本发明的有益效果是：本发明镜头对光线的衍射好，光损极低，非常适合于强光下的摄像使用，而且镜头像漂移低。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施例，进一步阐述本发明。
实施例1
无光损光学镜头，该镜头由如下重量份数的原料制成：
石英砂58份、明矾8份、纯碱13份、纳米二氧化硅6份、改性石墨烯12份、氢氧化锂6份、硼化铪8份、氯化钾10份、五氧化二钒8份、碳化铁8份、硅化钡6份、硅化钨2份、二氧化钴5.5份、玻化纤维3份。
所述改性石墨烯制备方法是，将石墨烯用240-300℃高温氮气加压30分钟，压力为1.2-1.8MPa，接着用32.5nm的紫外线对石墨烯照射，然后用40-60MHz超声波超声处理10分钟，接着将石墨烯在300-350℃温度下煅烧30分钟，待石墨烯自然冷却至常温即得改性石墨烯。
无光损光学镜头的制备方法，包括以下步骤：
(1)将除了改性石墨烯、玻化纤维外的各原料混合投入熔炼炉内熔融，加热至1200℃时投入改性石墨烯，然后将温度降至800-850℃后向熔炼炉内投入玻化纤维，然后继续熔炼加热至1400℃，熔炼30分钟后向熔料内吹入常温氮气，30分钟后再升温至1400℃；
(2)将步骤(1)的熔炼物料成型成镜头状，然后冷却处理，按每分钟冷却30℃的速度冷却至常温即得该光学镜头。
实施例2
无光损光学镜头，该镜头由如下重量份数的原料制成：
石英砂55份、明矾6份、纯碱11份、纳米二氧化硅5份、改性石墨烯10份、氢氧化锂5份、硼化铪7.8份、氯化钾9份、五氧化二钒7份、碳化铁7份、硅化钡5份、硅化钨1.5份、二氧化钴5份、玻化纤维2.8份。
所述改性石墨烯制备方法是，将石墨烯用240-300℃高温氮气加压30分钟，压力为1.2-1.8MPa，接着用32.5nm的紫外线对石墨烯照射，然后用40-60MHz超声波超声处理10分钟，接着将石墨烯在300-350℃温度下煅烧30分钟，待石墨烯自然冷却至常温即得改性石墨烯。
无光损光学镜头的制备方法，包括以下步骤：
(1)将除了改性石墨烯、玻化纤维外的各原料混合投入熔炼炉内熔融，加热至1200℃时投入改性石墨烯，然后将温度降至800-850℃后向熔炼炉内投入玻化纤维，然后继续熔炼加热至1350℃，熔炼30分钟后向熔料内吹入常温氮气，30分钟后再升温至1350℃；
(2)将步骤(1)的熔炼物料成型成镜头状，然后冷却处理，按每分钟冷却30℃的速度冷却至常温即得该光学镜头。
实施例3
无光损光学镜头，该镜头由如下重量份数的原料制成：
石英砂52份、明矾4份、纯碱10份、纳米二氧化硅4份、改性石墨烯8份、氢氧化锂4份、硼化铪7.5份、氯化钾8份、五氧化二钒5份、碳化铁5份、硅化钡4份、硅化钨1份、二氧化钴4份、玻化纤维2.5份。
所述改性石墨烯制备方法是，将石墨烯用240-300℃高温氮气加压30分钟，压力为1.2-1.8MPa，接着用32.5nm的紫外线对石墨烯照射，然后用40-60MHz超声波超声处理10分钟，接着将石墨烯在300-350℃温度下煅烧30分钟，待石墨烯自然冷却至常温即得改性石墨烯。
无光损光学镜头的制备方法，包括以下步骤：
(1)将除了改性石墨烯、玻化纤维外的各原料混合投入熔炼炉内熔融，加热至1200℃时投入改性石墨烯，然后将温度降至800-850℃后向熔炼炉内投入玻化纤维，然后继续熔炼加热至1300℃，熔炼30分钟后向熔料内吹入常温氮气，30分钟后再升温至1300℃；
(2)将步骤(1)的熔炼物料成型成镜头状，然后冷却处理，按每分钟冷却30℃的速度冷却至常温即得该光学镜头。
试验
本发明实施例1、2、3制得的镜头与普通镜头性能对比如下表：
由上表可见，本发明镜头使用效果非常好。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (2)
1.无光损光学镜头，其特征在于，该镜头由如下重量份数的原料制成：
石英砂52-58份、明矾4-8份、纯碱10-13份、纳米二氧化硅4-6份、改性石墨烯8-12份、氢氧化锂4-6份、硼化铪7.5-8份、氯化钾8-10份、五氧化二钒5-8份、碳化铁5-8份、硅化钡4-6份、硅化钨1-2份、二氧化钴4-5.5份、玻化纤维2.5-3份；
所述改性石墨烯制备方法是，将石墨烯用240-300℃高温氮气加压30分钟，压力为1.2-1.8MPa，接着用32.5nm的紫外线对石墨烯照射，然后用40-60MHz超声波超声处理10分钟，接着将石墨烯在300-350℃温度下煅烧30分钟，待石墨烯自然冷却至常温即得改性石墨烯；
上述无光损光学镜头的制备方法如下：
(1)将除了改性石墨烯、玻化纤维外的各原料混合投入熔炼炉内熔融，加热至1200℃时投入改性石墨烯，然后将温度降至800-850℃后向熔炼炉内投入玻化纤维，然后继续熔炼加热至1300-1400℃，熔炼30分钟后向熔料内吹入常温氮气，30分钟后再升温至1300-1400℃；
(2)将步骤(1)的熔炼物料成型成镜头状，然后冷却处理，按每分钟冷却30℃的速度冷却至常温即得该光学镜头。
2.如权利要求1所述的无光损光学镜头的制备方法，其特征在于，步骤(1)中继续熔炼加热至1350℃。