CN106566598A - Universal nonferrous metal and stainless steel cold rolling oil composite additive and preparation method thereof - Google Patents
Universal nonferrous metal and stainless steel cold rolling oil composite additive and preparation method thereof Download PDFInfo
- Publication number
- CN106566598A CN106566598A CN201610986121.7A CN201610986121A CN106566598A CN 106566598 A CN106566598 A CN 106566598A CN 201610986121 A CN201610986121 A CN 201610986121A CN 106566598 A CN106566598 A CN 106566598A
- Authority
- CN
- China
- Prior art keywords
- rolling oil
- steel cold
- additive
- universal
- butyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a universal nonferrous metal and stainless steel cold rolling oil composite additive and a preparation method thereof and belongs to the field of lubricating agents. According to the universal nonferrous metal and stainless steel cold rolling oil composite additive, lauryl alcohol, butyl stearate, pentaerythritol oleate and lauric acid are selected as oily agents; 2,6-di-tert-butyl-4-methylphenol is selected as an antioxidant; benzotriazole and thiadiazole derivatives are used as metal deactivators; dialkyl phosphorodithioate serves as an antiwear agent; and hydrogenated base oil serves as a solvent. The alcohol-ester type oily agents are mainly used for compounding with a little amount of acid oily agents as supplementation; a little amount of dialkyl phosphorodithioate is used as the antiwear agent to reinforce an oil film so as to improve the surface quality of a rolled stock; the service life of rolling oil is prolonged through a little amount of the antioxidant and the metal deactivators, the cyclic use frequency is increased, and rolled pieces are protected against corrosion. The universal nonferrous metal and stainless steel cold rolling oil composite additive is convenient to use, low in cost and little in dosage, and has the characteristics of high oil film strength, good antiwear and antifriction effect, high oxidation resistance and excellent annealing performance.
Description
Technical field
The present invention relates to lubricant and the cold rolling field of metal plate and belt foil, the lubrication belonged in process of metal working is specifically related to
And a kind of universal cold-rolled lubricating oil compound additive and preparation method thereof.
Background technology
It is to ensure the operation of rolling during non-ferrous metal stocking (such as aluminium sheet, band, paper tinsel, Copper Foil) and stainless-steel cold-rolling
Be smoothed out, and obtain the regular stocking of excellent surface quality, plate shape, it is necessary to adopt Lubrication Technology.
ROLLING OIL is made up of base oil and additive, and the base oil of Modern New predominantly passes through hydrorefined mineral
Oil, its composition is mainly the different alkane of carbon chain lengths and cycloalkanes hydrocarbon mixture;Additive can improve the specificity of oil product
Matter, improves the greasy property of mineral oil.Generally require to add a certain amount of oiliness improver, antiwear additive, antioxidant etc. in ROLLING OIL with
Reaching improves the effect of lubrication.The additive of unitary type can not play comprehensive effect, often using multiple in actual production
Additive is closed, film strength is improved, is reduced wear extent, improves ROLLING OIL service life and other effects to reach.
In technical field of lubricant, additive types are various, and various formula species mix in industrialized production, to using
Person causes inconvenience.Therefore a kind of universal compound additive of research is needed, for the processing of different metal, from suitable
Compound additive consumption, improves the convenience that uses and can reach excellent resultant effect.
The content of the invention
It is an object of the invention to provide a kind of universal non-ferrous metal and stainless-steel cold-rolling oil compound additive, the present invention makes
With conveniently, low cost, consumption is few, can reach to use by the consumption of change compound additive for different metal stocking and wants
Ask.According to experimental results, the present invention has film strength high, and antiwear and antifriction effect is good, and non-oxidizability is strong, and Annealing Property is excellent
Good the characteristics of.
The technical scheme is that:From lauryl alcohol, butyl stearate, PETO and
Used as oiliness improver, used as antioxidant, BTA and thiadiazoles derivative are used as gold for 2,6 ditertiary butyl p cresol for lauric acid
Category passivator, used as antiwear additive, hydrogenated base oil is used as solvent naphtha for dialkyl dithiophosphate.
The concrete composition of compound additive by mass percentage, in oiliness improver, lauryl alcohol:28~42%;
Butyl stearate and PETO mixed ester:28~42%:
Lauric acid:2~5%;
Antioxidant, is 2,6 ditertiary butyl p cresol:0.5~1%;
In metal deactivator, BTA:0.3~0.9%;
Thiadiazoles derivative:0.3~0.9%;
Antiwear additive, is dialkyl dithiophosphate:0.5~2%;
Solvent naphtha, is hydrogenated base oil:Surplus.
In concrete composition, oiliness improver lauryl alcohol is answered with the mixed ester of butyl stearate and PETO composition
It is 2 with mass ratio range:3~3:2, the two gross mass is overall 70% of compound additive;Butyl stearate in mixed ester
It is with the compounding mass ratio range of PETO:2:3~3:2, metal deactivator BTA and thiadiazoles spread out
Biological compounding mass ratio range is 1:3~3:1.
Above-mentioned universal non-ferrous metal and stainless-steel cold-rolling oil compound additive preparation process be:
First the butyl stearate and PETO of above-mentioned formula ratio are added to into reaction vessel according to correspondence ratio
In, then sequentially add lauryl alcohol, lauric acid, 2,6 ditertiary butyl p cresol, BTA, thiadiazoles derivative, dioxane
Base phosphorodithioate, is eventually adding hydrogenated base oil.Reaction vessel is placed on thermostatic electromagnetic agitator and is heated while stirring
To 60~70 DEG C, mixing speed is 100~180r/min, and constant temperature mixing time is 10~20 minutes until the mixing of each additive is equal
It is even, be subsequently cooled to room temperature, that is, obtain a kind of universal non-ferrous metal and stainless-steel cold-rolling oil compound additive.
It is an advantage of the current invention that the comprehensive consideration film strength of ROLLING OIL, antiwear and friction reduction property, non-oxidizability and moving back
Fiery detergency.By being combined to oiliness improver, optimization oiliness improver is optimal effect, monoesters in the absorption array of metal surface
The butyl stearate of type has excellent annealing cleanness and extreme pressure property is slightly worse, and the PETO of polyhydric alcohol ester type
Preferably lubrication and extreme pressure property can be shown, the feature of the two is complementary to one another;By add a small amount of annealing cleanness compared with
Good antiwear additive improves the antiwear and antifriction effect of ROLLING OIL, while its content controls to have no significant effect annealing cleanness
In the range of;The service life of oil product is improved by adding antioxidant, cost is reduced;Suppress gold by adding metal deactivator
The catalytic action of category ion pair ROLLING OIL oxidation, and corrosion of metal is prevented, improve the surface quality of rolled piece.
The present invention carries out assessment of performance using following experimental technique in the lab:
◆ lubricant extreme pressure property algoscopy (four ball method) (GB/T 12583)
◆ lubrication oil antiwear damages performance measurement method (four ball method) (SH/T 0189)
◆ the measure (rotary bomb oxidation test) (SH/T 0193) of lubricating oil oxidation stability
◆ EXXON standard anneal box methods
◆ oil product copper corrosion laboratory method (GB/T 5096)
Specific embodiment
Embodiment 1
The formula of embodiment 1 (based on gross mass 100g) is shown in Table 1:
Table 1
Sequence number | Ingredient names | Quality (g) |
1 | Lauryl alcohol | 28.0 |
2 | Butyl stearate | 16.8 |
3 | PETO | 25.2 |
4 | Lauric acid | 2.0 |
5 | 2,6 ditertiary butyl p cresol | 0.5 |
6 | BTA | 0.3 |
7 | Thiadiazoles derivative | 0.9 |
8 | Dialkyl dithiophosphate | 0.5 |
9 | Hydrogenated base oil | 25.8 |
By each component quality formula of upper table, universal non-ferrous metal and stainless-steel cold-rolling oil compound additive are prepared.Will
Lauryl alcohol (28.0g), butyl stearate (16.8g), PETO (25.2g), lauric acid (2.0g), the tertiary fourths of 2,6- bis-
Base paracresol (0.5g), BTA (0.3g), thiadiazoles derivative (0.9g), dialkyl dithiophosphate (0.5g) and
Hydrogenated base oil (25.8g), specifies order to add after container in by specification, be placed on thermostatic electromagnetic agitator top heating side and stir
Mix to 60~70 DEG C, constant temperature mixing time is 10~20 minutes, mixing speed is 100~180r/min, until each additive is mixed
Close uniform, obtain uniform oil body, be subsequently cooled to room temperature.
Embodiment 2
The formula of embodiment 2 (based on gross mass 100g) is shown in Table 2:
Table 2
Sequence number | Ingredient names | Quality (g) |
1 | Lauryl alcohol | 35.0 |
2 | Butyl stearate | 17.5 |
3 | PETO | 17.5 |
4 | Lauric acid | 3.0 |
5 | 2,6 ditertiary butyl p cresol | 0.7 |
6 | BTA | 0.5 |
7 | Thiadiazoles derivative | 0.5 |
8 | Dialkyl dithiophosphate | 1.0 |
9 | Hydrogenated base oil | 24.3 |
By each component quality formula of upper table, universal non-ferrous metal and stainless-steel cold-rolling oil compound additive are prepared.Will
Lauryl alcohol (35.0g), butyl stearate (17.5g), PETO (17.5g), lauric acid (3.0g), the tertiary fourths of 2,6- bis-
Base paracresol (0.7g), BTA (0.5g), thiadiazoles derivative (0.5g), dialkyl dithiophosphate (1.0g) and
Hydrogenated base oil (24.3g), specifies order to add after container in by specification, be placed on thermostatic electromagnetic agitator top heating side and stir
Mix to 60~70 DEG C, constant temperature mixing time is 10~20 minutes, mixing speed is 100~180r/min, until each additive is mixed
Close uniform, obtain uniform oil body, be subsequently cooled to room temperature.
Embodiment 3
The formula of embodiment 3 (based on gross mass 100g) is shown in Table 3:
Table 3
Sequence number | Ingredient names | Quality (g) |
1 | Lauryl alcohol | 42.0 |
2 | Butyl stearate | 16.8 |
3 | PETO | 11.2 |
4 | Lauric acid | 5.0 |
5 | 2,6 ditertiary butyl p cresol | 1.0 |
6 | BTA | 0.9 |
7 | Thiadiazoles derivative | 0.3 |
8 | Dialkyl dithiophosphate | 2.0 |
9 | Hydrogenated base oil | 20.8 |
By each component quality formula of upper table, universal non-ferrous metal and stainless-steel cold-rolling oil compound additive are prepared.Will
Lauryl alcohol (42.0g), butyl stearate (16.8g), PETO (11.2g), lauric acid (5.0g), the tertiary fourths of 2,6- bis-
Base paracresol (1.0g), BTA (0.9g), thiadiazoles derivative (0.3g), dialkyl dithiophosphate (2.0g) and
Hydrogenated base oil (20.8g), specifies order to add after container in by specification, be placed on thermostatic electromagnetic agitator top heating side and stir
Mix to 60~70 DEG C, constant temperature mixing time is 10~20 minutes, mixing speed is 100~180r/min, until each additive is mixed
Close uniform, obtain uniform oil body, be subsequently cooled to room temperature.
Product performance index
The compound additive formula of above three embodiment is taken, aluminium sheet basis is added to the addition of mass fraction 3%
(it is used for aluminium rolling) in oily A100, its performance indications such as table 4:
Table 4
The compound additive formula of above three embodiment is taken, is added in No. 5 white oils with the addition of mass fraction 5%
(for copper material and rolled stainless steel), its performance indications such as table 5:
Table 5
The embodiment of the above only preferably applies example for the present invention, not limits the practical range of the present invention with this, therefore
All component ratios according to the present invention, the equivalence changes that method and principle are made all should be covered by protection scope of the present invention.
Claims (4)
1. a kind of universal non-ferrous metal and stainless-steel cold-rolling oil compound additive, it is characterised in that from lauryl alcohol, stearic acid
, used as oiliness improver, 2,6 ditertiary butyl p cresol is used as antioxidant, BTA for butyl ester, PETO and lauric acid
With thiadiazoles derivative as metal deactivator, used as antiwear additive, hydrogenated base oil is used as solvent for dialkyl dithiophosphate
Oil.
2. universal non-ferrous metal as claimed in claim 1 and stainless-steel cold-rolling oil compound additive, it is characterised in that compound
Additive it is specifically as follows by mass percentage into being grouped into:
Oiliness improver:Lauryl alcohol:28~42%;
Butyl stearate and PETO mixed ester:28~42%;
Lauric acid:2~5%;
Antioxidant:2,6 ditertiary butyl p cresol:0.5~1%;
Metal deactivator:BTA:0.3~0.9%;
Thiadiazoles derivative:0.3~0.9%;
Antiwear additive:Dialkyl dithiophosphate:0.5~2%;
Solvent naphtha:Hydrogenated base oil:Surplus.
3. universal non-ferrous metal as claimed in claim 1 or 2 and stainless-steel cold-rolling oil compound additive, it is characterised in that
In concrete composition, the compounding mass ratio of the mixed ester that oiliness improver lauryl alcohol is constituted with butyl stearate and PETO
Example scope is 2:3~3:2, lauryl alcohol is overall 70% of compound additive with the gross mass of mixed ester;Stearic acid in mixed ester
The compounding mass ratio range of butyl ester and PETO is:2:3~3:2, metal deactivator BTA and thiophene two
The compounding mass ratio range of Zole derivatives is 1:3~3:1.
4. the as claimed in claim 2 or claim 3 preparation method of universal non-ferrous metal and stainless-steel cold-rolling oil compound additive, its
It is characterised by that concrete preparation process is:
First the butyl stearate and PETO of above-mentioned formula ratio are added in reaction vessel according to correspondence ratio, so
After sequentially add lauryl alcohol, lauric acid, 2,6 ditertiary butyl p cresol, BTA, thiadiazoles derivative, dialkyl disulfides
Substituted phosphate, is eventually adding hydrogenated base oil;Reaction vessel is placed on thermostatic electromagnetic agitator heat while stirring to 60~
70 DEG C, mixing speed is 100~180r/min, constant temperature mixing time be 10~20 minutes until each additive mix homogeneously, so
After be cooled to room temperature, that is, obtain a kind of universal non-ferrous metal and stainless-steel cold-rolling oil compound additive.