CN106541623B - 弹性透气折绉式复合无纺布及成型方法 - Google Patents
弹性透气折绉式复合无纺布及成型方法 Download PDFInfo
- Publication number
- CN106541623B CN106541623B CN201610834066.XA CN201610834066A CN106541623B CN 106541623 B CN106541623 B CN 106541623B CN 201610834066 A CN201610834066 A CN 201610834066A CN 106541623 B CN106541623 B CN 106541623B
- Authority
- CN
- China
- Prior art keywords
- air
- woven fabrics
- permeable elastic
- nonwoven cloth
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种弹性透气折绉式复合无纺布及成型方法,包括无纺布,弹性膜的膜面有很多透气孔,带有很多透气孔的弹性膜在拉伸状态下与面层无纺布和底层无纺布热压复合后回弹构成弹性透气折绉式复合无纺布且弹性膜位于面层无纺布和底层无纺布之间。优点:一是无需热熔胶,即可实现面层无纺布、底层无纺布与弹性膜的复合,确保了弹性膜及无纺布本身的透气性不受热熔胶的影响;二是开孔弹性膜的设计,不仅使弹性膜拉伸率大大地增大,而且具有高弹力、大拉伸率的特点;三是弹性膜中孔口凸台的设计,实现了底层无纺布与弹性膜凸台孔口部的复合,开创造中空多点支撑通透复合无纺布的先例。
Description
技术领域
本发明涉及一种既无需热熔胶,也无需拉伸无纺布,便能将面层无纺布和底层无纺布复合在拉伸状态下弹性膜两面的弹性透气折绉式复合无纺布及成型方法,主要用于医用绷带和纸尿裤弹性腰围,属医用弹性绷带及纸尿裤腰围制造领域。
背景技术
CN202213263U、名称“一种复合无纺布”,由至少一层弹性无纺布和至少一层弹性膜复合而成。所述弹性膜为聚氨酯薄膜。所述弹性无纺布和弹性膜藉由粘合剂复合而成。所述粘合剂为热熔胶。弹性无纺布和弹性聚氨酯透气膜在进行复合操作时均处于拉伸状态,在复合完成后自动回缩。其不足之处:一是该复合无纺布复合成型时需要弹性无纺布和弹性聚氨酯透气膜在处于拉伸状态完成复合,复合成型后的无纺布的弹性膜的弹性受弹性受弹性无纺布的制约,得到的是以弹性无纺布弹性为限的复合无纺布,其弹性非常有限;二是弹性无纺布与弹性聚氨酯透气膜的复合依赖于热熔胶,而热熔胶的基本树脂是乙烯和醋酸乙烯在高温高压下共聚而成的EVA树脂,而EVA树脂的粘性本身很低,需加入增粘剂,如改性松香(138或145),C5石油树脂,C9石油树脂,萜烯树脂等,这些成份的加入使得热熔胶的粘性增强,但其作为弹性无纺布与弹性聚氨酯透气膜的复合介质时,却大大堵塞了弹性无纺布的透气性,使复合成型后的复合无纺布的透气性大大降低,甚至很差。
发明内容
设计目的:避免背景技术中的不足之处,设计一种既无需热熔胶,也无需拉伸无纺布,便能将面层无纺布和底层无纺布复合在拉伸状态下弹性膜两面的弹性透气折绉式复合无纺布及成型方法。
设计方案:为了实现上述设计目的。本发明在结构设计上:1、弹性膜的膜面有很多透气孔的设计,是本发明的技术特征之一。这样设计的目的在于:由于本发明所述弹性透气膜是在拉伸的状态下与无纺布面无胶(无热熔胶)复合,即弹性膜的膜面是在拉伸状态下与无纺布直接热压复合,不会发生热熔胶堵塞弹性膜面透气孔的现象。其次,弹性透气膜的好处在于:一是它不仅能够使本不透气的弹性膜变成透气膜,而且能使布满透气孔的弹性膜的拉伸率增大---弹性好,有效地提高了弹性透气膜的伸缩率;二是采用本发明的弹性透气膜,它能够它取代目前纸尿裤弹性腰围采用橡筋制作所带来的制造设备复杂、制作工艺复杂、成本高,效率低,以及采用胶粘剂定位橡筋所导致的腰围弹力下降、透气性差、手感生硬、舒适性差的缺陷;二是采用本发明的弹性透气膜所制作的绷带,不仅弹性好,透气性好,而且绷扎时的平整度好,制作成本低。2、带有很多透气孔的弹性膜在拉伸状态下与面层无纺布和底层无纺布热压复合的设计,是本发明的技术特征之二。这样设计的目的在于:由于用于医用绷带和卫生用品的无纺布既要求具有良好透气性和平整度,又要求具有良好的弹性,同时价格低,而能够满足上述要求的面层无纺布和底层无纺布的弹性非常小,基本上可以忽略不计,但是医用绷带和卫生用品中纸尿裤腰围所需的复合无纺布则既要求满足平整度,又要求满足强力弹性伸缩的要求,为此本发明将弹性透气膜在拉伸的状态下与面层无纺布和底层无纺布热压复合后回弹形成弹性透气折绉式复合无纺布,既满足了医用绷带透气、平整、弹性绑扎的要求,又满足了纸尿裤腰围所需平整、透气、强力弹性伸缩的要求。3、弹性膜中透气孔成形的负压吸口沿呈凸台口结构的设计,是本发明的技术特征之三。这样设计的目的在于:弹性膜面在由负压辊面的负压口抽气打孔的过程中,其弹性膜面中的负压抽吸孔(负压出气一端)的孔沿呈被抽也凸台口,该凸台台就犹如布在弹性膜面的多个孔形支撑,由于该孔形支撑的孔口部高于膜面,因此当其与底层无纺布热压复合时,使得底层无纺布面与弹性膜面的凸台口部之间形成热压复合,不仅大大地减少了无纺布面与弹性膜的复合面积,而且使底层无纺布面与弹性透气膜之间形成多路且路路相通的中空多点支撑,不仅透气性极佳,而且弹性伸缩性好,开创造中空多点支撑通透复合无纺布的先例。
技术方案1:一种弹性透气折绉式复合无纺布,包括无纺布,弹性膜的膜面有很多透气孔,带有很多透气孔的弹性膜在拉伸状态下与面层无纺布和底层无纺布热压复合后回弹构成弹性透气折绉式复合无纺布且弹性膜位于面层无纺布和底层无纺布之间。
技术方案2:一种弹性透气折绉式复合无纺布的成型方法,弹性高分子树脂颗粒在熔融的状态下通过膜成型工艺制成弹性膜或弹性透气膜,或弹性膜通过膜打孔辊组打孔构成弹性打孔透气膜,弹性打孔透气膜或弹性透气膜在拉伸的状态下将面层无纺布和底层无纺布复合在弹性打孔透气膜或弹性透气膜的两面后,弹性打孔透气膜或弹性透气膜回弹迫使面层无纺布和底层无纺布随弹性打孔透气膜或弹性透气膜形成弹性透气折绉式复合无纺布。
本发明与背景技术相比,一是无需热熔胶,即可实现面层无纺布、底层无纺布与弹性透气膜的复合,确保了弹性透气膜及无纺布本身的透气性不受热熔胶的影响;二是弹性膜膜面布有很多开孔的设计,不仅使弹性膜拉伸率大大地增大,而且具有高弹力、大拉伸缩率的特点;三是弹性透气膜中孔口凸台口的设计,实现了底层无纺布与弹性透气膜凸台孔口部的热压复合,不仅极大地减少了无纺布与弹性透气膜的复合面积,而且使复无纺布具有上下、左右、前后透气的功能且透气性极佳,而且伸缩弹性好,开创造中空多点支撑通透复合无纺布的先例。
附图说明
图1是弹性透气折绉式复合无纺布第一种实施例的结构示意图。
图2是弹性透气折绉式复合无纺布第二种实施例的结构示意图。
具体实施方式
实施例1:参照附图1。一种弹性透气折绉式复合无纺布,包括无纺布,弹性膜2的膜面有很多透气孔4,带有很多透气孔4的弹性膜2在拉伸状态下与面层无纺布1和底层无纺布3热压复合后回弹构成弹性透气折绉式复合无纺布且弹性膜2位于面层无纺布1和底层无纺布3之间。
所述弹性膜为弹性打孔透气膜,或弹性透气膜。所述弹性打孔透气膜2中透气孔由布满负压孔辊面上的负压抽吸流道抽吸而成,且透气孔口沿呈凸台口5;或弹性打孔透气膜2中透气孔由凹凸打孔辊组构成,该凹凸辊组包括条状刀口凹凸打孔刀辊组,或锥状刀口凹凸打孔刀辊组(即弹性打孔透气膜2中透气孔由布满锥形针头的打孔膜成型膜辊组打孔成型)。
所述弹性透气膜是由有机成份与无机成份构成的弹性膜在拉伸状态下形成的透气孔,该透气孔在人体温度的作用下,能够透气,但具有阻止水份子通的的功能。所述弹性透气膜的拉伸率在50%-500%之间且包括端值。
实施例2:参照附图2。在实施例1的基础上,所述面层无纺布1和底层无纺布3在弹性透气膜2被拉伸的状态下通过凸凹辊组被热压复合在弹性透气膜2的两面且构成凹凸面折皱式弹性透气复合无纺布且复合粘接面为凹凸面,即面层无纺布1和底层无纺布3与弹性膜2的粘接复合部为凹凸压合面,非凹凸压合面不粘接。
实施例3:在实施例1的基础上,所述底层无纺布3与打孔透气膜2中的凸台口5部复合而成,且底层无纺布面与弹性打孔膜之间形成多路且路路相通的中空多点支撑空间6,即底层无纺布3与打孔透气膜2中负压抽吸而成的孔口凸台口沿部复合,非复合部形成透气相通的空间。
实施例4:一种弹性透气折绉式复合无纺布的成型方法,弹性高分子树脂颗粒在熔融的状态下通过膜成型工艺制成弹性膜2或弹性透气膜,或弹性膜通过膜打孔辊组打孔构成弹性打孔透气膜,弹性打孔透气膜或弹性透气膜在拉伸的状态下将面层无纺布1和底层无纺布3复合在弹性打孔透气膜或弹性透气膜的两面后,弹性打孔透气膜或弹性透气膜回弹迫使面层无纺布1和底层无纺布3随弹性打孔透气膜或弹性透气膜形成弹性透气折绉式复合无纺布。所述弹性膜为弹性打孔透气膜,或弹性透气膜。
实施例5:在实施例4的基础上,所述弹性打孔透气膜或弹性透气膜在拉伸的状态下通过凹凸复合辊组将面层无纺布1和底层无纺布3复合在弹性打孔透气膜或弹性透气膜的两面,即面层无纺布1和底层无纺布3与弹性透气膜2的粘接复合部为凹凸压合面,非凹凸压合面不粘接。
所述膜成型工艺是指流延膜成型及打孔工艺。所述流延膜成型及打孔工艺由流延模头和膜成型打孔装置构成。所述膜成型打孔装置负压抽吸孔辊组构成,或由凹凸辊组构成,该凹凸辊组包括条状刀口凹凸刀辊组,或锥状刀口凹凸刀辊组。
需要理解到的是:上述实施例虽然对本发明的设计思路作了比较详细的文字描述,但是这些文字描述,只是对本发明设计思路的简单文字描述,而不是对本发明设计思路的限制,任何不超出本发明设计思路的组合、增加或修改,均落入本发明的保护范围内。
Claims (7)
1.一种弹性透气折绉式复合无纺布,包括无纺布,其特征是:弹性透气膜面在由负压辊面的负压口抽气打孔的过程中,其弹性透气膜面中的负压抽吸孔负压出气一端的孔沿呈被抽成凸台口,该凸台就犹如布在弹性透气膜面的多个孔形支撑,由于该孔形支撑的孔口部高于膜面,当凸台口与底层无纺布热压复合时,使得底层无纺布面与弹性透气膜面的凸台口部之间形成热压复合,而且带有很多透气孔(4)的弹性透气膜(2)在拉伸状态下与面层无纺布(1)和底层无纺布(3)热压复合后回弹构成弹性透气折绉式复合无纺布且弹性膜(2)位于面层无纺布(1)和底层无纺布(3)之间。
2.根据权利要求1所述的弹性透气折绉式复合无纺布,其特征是:所述面层无纺布(1)和底层无纺布(3)在弹性透气膜(2)被拉伸的状态下通过凸凹辊组被热压复合在弹性透气膜(2)的两面且构成凹凸面折皱式弹性透气复合无纺布且复合粘接面为凹凸面。
3.根据权利要求1或2所述的弹性透气折绉式复合无纺布,其特征是:所述弹性透气膜中透气孔由布满负压孔辊面上的负压抽吸流道抽吸而成,且抽气孔口沿呈凸台口(5);或弹性透气膜中透气孔由布满锥形针头的打孔膜成型膜辊打孔成型。
4.根据权利要求1或2所述的弹性透气折绉式复合无纺布,其特征是:所述底层无纺布(3)与弹性透气膜中的凸台口(5)部复合而成,且底层无纺布面与弹性透气膜之间形成多路且路路相通的中空多点支撑空间(6)。
5.根据权利要求1所述的弹性透气折绉式复合无纺布,其特征是:所述弹性透气膜的拉伸率在50%-500%之间且包括端值。
6.一种如权利要求1所述的弹性透气折绉式复合无纺布的成型方法,其特征是:弹性高分子树脂颗粒在熔融的状态下通过膜成型工艺制成弹性透气膜(2),弹性透气膜(2)在拉伸的状态下将面层无纺布(1)和底层无纺布(3)复合在弹性透气膜(2)的两面后,弹性透气膜(2)回弹迫使面层无纺布(1)和底层无纺布(3)随弹性透气膜(2)形成弹性透气折绉式复合无纺布。
7.根据权利要求6所述的弹性透气折绉式复合无纺布的成型方法,其特征是:所述弹性透气膜在拉伸的状态下通过凹凸复合辊组将面层无纺布(1)和底层无纺布(3)复合在弹性透气膜的两面。