CN106526729A - 一种开放型彩色反射片及其制备方法 - Google Patents
一种开放型彩色反射片及其制备方法 Download PDFInfo
- Publication number
- CN106526729A CN106526729A CN201610391296.3A CN201610391296A CN106526729A CN 106526729 A CN106526729 A CN 106526729A CN 201610391296 A CN201610391296 A CN 201610391296A CN 106526729 A CN106526729 A CN 106526729A
- Authority
- CN
- China
- Prior art keywords
- layer
- binder course
- pigment
- reflective piece
- colour reflective
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种开放型彩色反射片及其制备方法,包括支持层;结合层,被沉积在所述支持层的一侧,含有粘合树脂、颜料和无泛黄聚氨酯;反射层,被粘附至所述结合层,包含多个珠型反射体;和硅系防水涂层,被沉积在所述反射层的一侧,且选择性地进一步包括印刷层,被形成在反射层的一侧或另一侧。根据本发明的开放型彩色反射片不仅可表现多种色彩,还可防止因外部原因的损伤,从而可防止亮度低下同时提高可视性。
Description
技术领域
本发明涉及一种反射片,特别是,一种可维持亮度和可视性,同时可表现多种色彩的开放型彩色反射片及其制备方法。
技术背景
目前,使入射的光按入射的方向原样进行反射来提高可视性的反射片被广泛使用。反射片(Reflective Sheet)可使片上标示的一定纹样和文字等被容易地识别。一般,反射片通过粘附剂或提封等方法被附着在道路的标示牌、衣服、鞋子、广告上等。例如,反射片被附着在类似环境美化员、消防队员、建设现场劳动者等在道路或危险的场所工作的人员衣服上,从而可确定着用人员的位置,具有保护着用者使其安全的效果。不仅如此,在用于道路边的标示牌时,夜间驾驶时,可使汽车前灯射出的光原样反射至驾驶者侧,从而可提高对于道路标示牌的识别力。
反射片一般分为角锥型(Cube corner type)和珠型(Bead type)。角锥型是使用常规三角锥形的多个棱柱多面体来作为反射体,且珠型是使用玻璃珠(glass bead)来作为反射体。图1是现有技术中提出的角锥型反射体的概略性横截面图。
参照图1,对现有技术的角锥型反射片1进行说明,基片薄膜10和再归反射部30之间具有在部分粘附树脂层20被形成的状态下热被压缩粘附的隔离空间22。再归反射部30包括:由热硬化性合成树脂形成的保护薄膜32;和由热塑性合成树脂形成的角锥层34;以及将角锥层34以加热的摸具按压图案化从而被加工成三角锥形的角锥件36。角锥件36以突出的结构被形成,因此可提高反射亮度,增加可视性。但是,为了提高该角锥型反射片的可视性所形成的角锥件36具有突出的结构,因此和粘附树脂层20的接触表面较小,粘附力低下,由此,基片薄膜10容易剥离。不仅如此,反射片的侧面由于雨水或异物的侵入反射亮度及可视性会下降,且具有反射片的内构成低下的问题。
此外,珠型反射片作为反射体一般具备类似玻璃(glass)的多个透明微细球。在这种情况下,将玻璃珠作为反射体的开放型(Open Type)反射片,为了提高反射亮度使入射的光再归反射,将作为反射体的玻璃珠和用于增加玻璃珠反射力的灰色铝浆层暴露在反射片的表面。
据此,现有技术开发的开放型的珠型反射片也仍旧没有解决由于异物的侵入使反射亮度减少以及内构成低下的问题,不仅如此,利用铝浆层的玻璃珠反射片的特征上为只能体现深灰色系列的色彩来做为底色,较难表现及体现多种颜色。即使可以体现多个颜色,但底部仍须包含具有深灰色的铝浆,因此在体现正确的颜色时具有局限性(例如,当要表现黄色时,灰色和黄色混合成为深褐黄色)。
如上所述,现有技术开发的开放型的珠型反射片一般被用于类似附着在危险环境下工作人员的衣服上等,其用途具有局限性,且在用于需要体现及表现鲜艳及多种色彩的广告牌或是作为服饰材料时受到很多限制。
先行技术
专利文献
(专利文献1)韩国专利公开10-2011-0084667(2011年7月26日公开)
发明内容
技术课题
由此,本发明是为了解决现有技术的问题而提出的,本发明的目的在于提供一种开放型彩色反射片及其制备方法,防止由于异物侵入和外部环境的原因所引起的亮度低下,同时在较差的条件下也可维持亮度。
本发明的另一个目的在于提供一种开放型彩色反射片及其制备方法,自由地体现及表现多种色彩和颜色。
最后,本发明提供一种开放型彩色反射片及其制备方法,防止因外部环境原因所造成的内构成低下。
技术方案
根据具上述目的的本发明的一个侧面,提供一种开放型彩色反射片,包括:支持层;结合层,被沉积在所述支持层的一侧,含有粘合树脂、颜料和无泛黄聚氨酯;反射层,被粘附至所述结合层,包含多个珠型反射体;和硅系防水涂层,被沉积在所述反射层的一侧。
在一个示例性实施例中,本发明可进一步包括:印刷层,被形成在构成所述开放型彩色反射片的所述结合层和所述反射层之间或所述反射层和所述防水涂层之间中的至少一处。
此外,所述印刷层可包括具有粘附成分的单组分紫外线油墨。
在一个示例性实施例中,所述防水涂层可包括高分子二氧化硅(SiO2)、氟素处理的纳米二氧化硅、硅系单组分防水涂剂、以及由上述的组合构成的群中被选出的硅系防水涂剂。
此外,所述结合层中包含的所述颜料包括:有色颜料和荧光颜料,其中所述有色颜料,从由白色颜料、黄色颜料、赤色颜料、青色颜料、绿色颜料、紫色颜料和黑色颜料构成的群中选出至少一个。
此外,构成所述反射层的所述多个珠型反射体,以整个直径的1/3至2/3被露于所述结合层一侧的形态,嵌入至所述结合层。
其中,支持开放型彩色反射片的所述支持层,由从薄膜类构成的群中选出的材料形成,所述薄膜类由纤维类、纸类、皮革类、合成树脂或量子点屏障被制备。
在需要时,可进一步包括:异型薄膜层,通过所述支持层的另一侧所粘附的粘结层脱附式地被形成。
根据本发明的另一个侧面,提供一种开放型彩色反射片制备方法,包括以下步骤:在准备的支持层的一侧,至少沉积含有粘合树脂、颜料和无泛黄聚氨酯的结合层;在所述结合层的一侧,粘附含有多个珠型反射体的反射层;以及在所述反射层的一侧,沉积硅系防水涂层。
在一个示例性实施例中,可进一步包括以下步骤:在所述结合层和所述反射层之间或所述反射层和所述防水涂层之间中的至少一处形成印刷层。
例如,在所述结合层的一侧,粘附所述反射层的步骤中,可将构成所述所述多个珠型反射体,以整个直径的1/3至2/3被露于所述结合层一侧的形态,嵌入至所述结合层。
技术效果
根据本发明的开放型彩色反射片,可在支持层的上面形成掺和有多种颜料和粘合树脂的结合层,并在由多个玻璃珠形成的反射层的上面沉积硅系反射层,选择性地,可在反射层的至少一侧形成印刷层。
根据本发明,可在支持开放型彩色反射片的支持层的上面形成掺和有多种颜料和粘合树脂的结合层,来体现多种颜色,在需要时,可通过配置在反射层至少一侧的印刷层来形成多种图案。
特别是,本发明中,在反射层的一侧形成防水涂层,因此可防止因类似湿气或雨水和/或异物的外部环境原因所造成的反射亮度低下,从而可维持良好的反射亮度及可视性。同时可防止由于异物的侵入所造成的反射片的内构成低下的问题。
附图说明
图1是示出根据现有技术的角锥(Cube Corner)型彩色反射片的概略性横截面图。
图2是示出根据本发明的示例性第1实施例的珠型(开放型)彩色反射片的概略性横截面图。
图3是示出根据本发明的另一个示例性第2实施例的开放型彩色反射片的概略性横截面图。
图4是示出根据本发明的又另一个示例性第3实施例的开放型彩色反射片的概略性横截面图。
图5是示出根据本发明的示例性实施例的制备开放型彩色反射片的工程的流程图,包括形成印刷层的步骤。
图6是概略性地示出根据本发明的示例性实施例,在结合层的一侧形成有印刷层的状态下粘附反射层过程的分解立体图。
图7a和图7b是分别概略性地示出根据本发明的示例性实施例,在结合层(图7a)和印刷层(图7b)的上面粘附多个玻璃珠后,将玻璃珠上面粘结的剥离用薄膜除去的状态的横截面图。
图8是概略性地示出根据本发明的另一个示例性实施例,在反射层上面形成印刷层的过程的分解立体图。
具体实施方式
本发明者多年来对于表现及体现多种色彩的方法进行了研究,完成了本发明,解决了有关因类似异物侵入的外部环境原因所造成的反射片的亮度和/或可视性减少以及内构成低下的问题。以下在需要的情况下参照附图对本发明进行详细说明。
[彩色反射片]
图2是示出根据本发明的示例性实施例的开放型彩色反射片的概略性横截面图。在本发明中,开放型(open type)是指作为用于使光反射的手段,沉积在珠上的层以与珠相对应的曲线结构被形成,珠为向外部(光入射的方向)突出的形态。此外,在本说明书中,基于附加的横截面图,上部被称为一侧,且下部被称为另一侧,但是其只是为了方便说明,本发明并不仅局限于此。
参照图2,根据本实施例的开放型彩色反射片100,一种开放型彩色反射片,包括:支持层110,用于支持彩色反射层;结合层120,被沉积在所述支持层110的一侧;反射层130,具有多个反射手段,在所述支持层110的相反侧,被粘附至所述结合层120的一侧;和硅系防水涂层150,在所述结合层120的相反侧,被沉积在所述反射层130的一侧。
选择性地,根据本实施例的开放型彩色反射片100,可进一步包括:异型薄膜层170,在结合层120的相反侧,通过所述支持层110的另一侧所粘附的粘结层160,被脱附式地附着于所述支持层110的另一侧。
在一个示例性实施例中,所述结合层120和所述反射层130可形成一种反射薄膜。
支持层100用来支持:被沉积在其一侧可体现多种色彩并针对开放型反射片100来体现多种底色的结合层120;和反射光的反射层130;以及防止可视性低下的防水涂层150。例如,支持层110克使用透明、半透明或不透明的材质。在示例性实施例中,支持层110可由从薄膜类构成的群中选出的至少一种材料形成,所述薄膜类由纤维类、纸类、皮革类、合成树脂或量子点屏障(quantum dot barrier)被制备。
更具体地,可形成支持层110的纤维类的非限制性示例可以是从棉(cotton)、聚酯、毛、人造纤维、莱塞尔纤维(lyocell)、醋酸纤维、尼龙、丙烯酸、氨纶、聚丙烯、维纶、以及上述的组合(混纺纤维)所构成的群中被选出的织物(woven)或是非织物(non-woven)。
此外,可构成支持层110的混纺纤维类的非限制性示例可以是T/C(聚酯-棉)、T/R(聚酯-人造纤维)、A/T(丙烯酸-聚酯)、C/N(棉-尼龙)、C/R(棉-人造纤维)等。可形成支持层110的皮革类的非限制性示例可包括合成皮革、天然皮革等。
此外,可形成支持层110的薄膜类的非限制性示例包括合成树脂薄膜,其含有从聚酯系、聚烯烃系、聚氨酯系、聚氯乙烯系、聚酰亚胺系、聚碳酸酯系、丙烯酸系等构成的群中被选出的至少一个以上树脂。更具体地,作为构成所述支持层110的薄膜类,可使用从聚氯乙烯(PVC)、聚对苯二甲酸乙二酯(PET)、聚对苯二甲酸丁二酯(PBT)、聚萘二甲酸乙二醇酯(PEN)、聚萘二酸丁醇酯(PBN)、聚氨酯(PU)、丙烯酸树脂、聚甲基丙烯酸甲酯(PMMA)、聚乙烯(PE)、聚丙烯(PP)、聚碳酸酯(PC)、聚酰亚胺(PI)、聚酯、密胺树脂、环氧树脂、以及上述的共聚物构成的群中被选出的至少一种合成树脂薄膜,但并不局限于此。
所述支持层110的一侧所沉积的所述结合层120将作为反射手段的具有多个珠型反射体132的反射层130结合至所述支持层120的一侧。同时,所述结合层120被构成为可针对本实施例的开放型彩色反射片100体现多种底色。为了该目的,所述结合层120可至少包括粘合树脂、无泛黄聚氨酯、及颜料,进一步包括纳米珍珠粉。
结合层120中包含的所述粘合树脂,可作为将珠型反射体132的一部分嵌入结合层120具有固定、支持的结合力的任意粘合树脂。在一个示例性实施例中,结合层120中包含的粘合树脂为可使纳米珍珠粉等粒子强力融合的粘合树脂。例如,粘合树脂可以是从天然树脂和/或合成树脂中被选出,具体地,可以是从丙烯酸系、尿烷系、硅系、环氧系、聚氯乙烯系、及聚酯系中被选出的合成树脂。在一个示例性实施例中,为了使珠型反射体132稳定地被固定可使用丙烯酸系的粘合树脂。
现有技术中,作为体现反射片的底色的方法,为了增加反射力,铝、镍、晶石、锌等金属粒子以浆的形态被用于粘附剂中。但是,该方法,由于金属粒子的特性只能体现灰色系列的底色,在体现多种色彩时具有局限性。即使可体现多个颜色,由于背景中必须包含具有深灰色的铝浆,因此最终表现的颜色,例如不是黄色,而是灰色与黄色混合的深褐黄色,从而在表现正确的颜色时具有局限性。
由此,现有技术的彩色反射片仅局限于类似附着在危险场所中工作的工作人员的衣服上用于安全等,且在用于需要多种底色的服饰材料或是广告牌时具有局限性。对此,本说明中,在结合层120中掺和可体现多种颜色的颜料。根据本发明,结合层120中掺和的有色颜料和/或荧光颜料的大小并不特别受限制,例如,可具有2.0μm以下的平均粒度(averagesize),优选是0.01~2.0μm的平均粒度。
为了与粘合树脂掺和来体现多种颜色,结合层120中掺和的颜料可使用白色颜料、黄色颜料、赤色颜料、青色颜料、绿色颜料、紫色颜料和黑色颜料和/或荧光颜料。由此,通过适当地掺和颜料可体现多种底色,还可体现四周连续纹理摸样的色彩。例如,作为白色颜料,可使用二氧化钛(TiO2)系、氧化锌(zinc oxides)系、硫化锌(ZnS)系、以及硫化锌和氧化钡(BaO4)混合的尘粒(lithopon)、碱性碳酸铅白(lead white)、氧化锑(Sb2O3)系等,且并不局限于此。
黄色颜料的非限制性示例包括:铬璜(Chrome yellow,Lead chromate)、铬酸锌、主成分为CdS的镉黄(Cadmium yellow)、主成分为PbCN2的氰氨化铅(Lead cyanamide)、由TiO2/NiO/Sb2O3构成的钛镍黄(Titanium yellow,Titanium nickel yellow)、主成分为SrCrO4的铬酸锶(Stronium chromate)。
赤色颜料的非限制性示例包括:主成分为氧化铁(Fe2O3)的铁红(Iron oxidered)、主成分为氧化铅(PbO4)的红丹(Red lead)、主成分为氧化铜(CuO2)的红色氧化铜(Cuprous oxide,red copper oxide)、主成分为硫化汞(HgS)的朱红色(Vermillion)、CdS与HgS混合结晶所构成的镉红(Cadmium Red,Selenium Red)。
青色颜料非限制性示例包括:主成分为Fe2(CN)6的绀青(Milori blue,Prussianblue,Iron blue)、群青(Ultramarine blue)、主成分为铝酸钴的钴蓝(Cobalt blue)。
绿色颜料非限制性示例可使用:铬绿(Chrome green)、主成分为Cr2O3的氧化铬绿(Chromate oxide green)、主成分为Cr2O(OH)4的鲜绿(Viridian)、ZrCrO4和绀青的混合物锌绿(Zinc green)、钴绿(Cr2O3-Al2O3-CoO)、类似青蓝(cyanine blue)的无机颜料或类似酞菁染料的有机颜料。
紫色颜料非限制性示例包括:主成分为NH4MnP2O7的矿紫(Manganess violet,mineral violet)、及主成分为Co3(PO4)2的深钴紫。
黑色颜料非限制性示例包括:碳黑、黑墨、主成分为四氧化三铁(Fe3O4)的镉黄(cadnium yellow)。
此外,作为荧光颜料,可以是在无机界的荧光物质硫化锌(ZnS)或硫化锌镉(ZnCdS)、硫化锶钙(CaSrS)等重金属盐或硫化钙(CaS)等碱土金属的硫化物中加入微量的金属(Cu,Ag,Bi,Pb)作为活性剂进行结晶来制备。例如,虽然可使用CaS/Bi(青色)、CaSrS/Bi(丹青色)、ZnS/Cu(绿色)、ZnCdS/Cu(黄色)、ZnS/Mn(黄色)、ZnCdS/Cu(橙色)、ZnS/Ag(紫色)、ZnCdS/Cu(红橙色)、和ZnS/Bi(赤色)等荧光颜料,但本发明并不局限于此。
根据本实施例,结合层120中掺和的所述白色、黄色、赤色、青色、绿色、紫色、和黑色等的有色颜料可根据需要被单独使用或适当的掺和,从而可体现所需的底色。该有色颜料优选是具有无泛黄特性。由于使用具有无泛黄特性的颜料,从而可防止由于褪色而造成的底色可视性低下。
同时,所述结合层120可防止粘附在其一侧的反射层130的珠型反射体132脱离,并可维持稳定的色彩,并含有可提高开放型彩色反射片100可视性的无泛黄聚氨酯。在一个示例性实施例中,无泛黄聚氨酯具有特别的高弹性特征,并具有良好的耐冲击性、耐磨性以及耐化学性。特别是硬化后对于湿气和盐分具有较好的抵抗性,因此可解决由于雨水或湿气或异物的侵入而引起的开放型彩色反射片100的亮度低下或内构成减少的问题。
在一个示例性实施例中,结合层120中嵌入的无泛黄聚氨酯可通过多羟基化合物和具异氰酸酯的化合物被合成。例如,为了合成无泛黄聚氨酯所使用多羟基化合物的其他示例可包括聚酯系多羟基化合物、碳化氢系多羟基化合物、聚碳酸酯系多羟基化合物、和内酯系聚酯多羟基化合物。例如,聚酯系多羟基化合物可使用通过类似肥酸、焦油酸、壬二酸的脂肪族酸以及类似酞酸、对苯二甲酸、环烷酸的芳香酸等中被选出的二羧酸与乙二醇、二甘醇、1,6-乙烯乙二醇等的乙二醇类;丙三醇、三羟甲基丙烷、季戊四醇等的多元醇类二元醇的合成被获得的聚酯系多羟基化合物。
异氰酸酯化合物可使用芳香族、脂肪族、或是饱和或非饱和异氰酸酯化合物。具体地,作为异氰酸酯化合物,可使4,4'-二苯基甲烷二异氰酸酯(MDI)、苯二亚甲基二异氰酸酯、异戊二烯二异氰酸酯、二异氰酸酯(CHDI)等构成的群中被选出的一种以上,但本发明并不局限于此。
在合成无泛黄聚氨酯时,适当地调节异氰酸酯化合物的异氰酸酯基(-NCO)与多羟基化合物的氢氧基(-OH)的摩尔率(NCO/OH),从而可调节硬链段和软链段的比例。在一个示例性实施例中,合成的无泛黄聚氨酯中硬链段的比例可为5~40wt%,NCO/OH比例范围约为1.3~3.5。当硬链段的比例未满5wt%时,不能起到结合层120中嵌入的珠反射体132的脱离防止效果,当硬链段的比例超过40wt%时,由于过度的粘弹性,珠反射体132的接触面积减少,紧贴特性降低。
聚氨酯可通过使用金属和/或胺类等催化剂经多羟基化合物和异氰酸酯化合物的反应被合成。需要时,可选择性地使用扩链剂(chain extender),例如二乙醇胺、1,4-丁烯、1,6-己二胺等低分子量胺类,或是类似乙二醇、丁二醇、1,6-己二醇、1,4-环己烷等氢氧基化合物的聚合性低分子化合物。通常以多羟基化合物100%为基准可添加1.5~20%的扩链剂。无泛黄聚氨酯可以是水性或油性类型,固形粉的含量约为20~50wt%,但本发明的无泛黄聚氨酯的固形粉的含量并不局限于该范围。
此外,结合层120除了上述的粘合树脂、颜料、和无泛黄聚氨酯以外,还可进一步掺加、掺和具有纳米分子大小的纳米珍珠粉(Nano-pearl)。当纳米珍珠粉被掺和时,可使入射至本实施例的开放型彩色反射片100的光反射率进一步提高。纳米珍珠粉的材料可以是类似鸟嘌呤/次黄嘌呤(Guanine/Hypoxanthine)混合结晶的天然珍珠精华(Natural pearlessence)、和金属氧化物被膜云母系、碳酸铅白(Basic lead carbonate)系、以及氯氧化铋(Bismuth Oxychloride)系中被选择的合成珍珠粉。
金属氧化物被膜云母系可使用白云母的小片块上涂有氧化钛的云母钛(Titaniumdioxide-Coated mica)、涂有氧化铁的云母铁、涂有氧化铋的云母、云母钛表面涂有上述的有色颜料。优选是,在一个实施例中,可使用具无泛黄特性的作为纳米珍珠粉,因此可防止褪色,体现鲜明的色彩,从而改善可视性。
构成本发明的结合层120的所述成分的含量并不受限制,例如,可按以下的相对性比例被掺和:粘合树脂80~120%、颜料5~20%、无泛黄聚氨酯40~80%、纳米珍珠粉1~10%。
所述支持层110的一侧所粘附的结合层120的一侧,即,支持层110的相对面,粘附、沉积有反射层130。所述反射层130中排列有多个珠型反射体132。珠型反射体132可以是使入射至本实施例的开放型彩色反射片100的光再归反射的具有适当的折射率的任意珠。
珠型反射体132作为透明的珠,可以是选自例如玻璃珠(glass bead)、非玻璃质的陶瓷珠(ceramic bead)、或是丙烯酸系等的透明合成树脂系珠等。优选是,珠型反射体132使用具高折射率的玻璃珠。珠型反射体132的横截面形态可以是球形或椭圆形,且优选是球形来实现均一的反射效率。珠型反射体132的大小并不特别被限制,可本实施例的开放型彩色反射片100被适用的基片的用途或目的而有所不同。作为示例,珠型反射体132的直径(D)可为1.0μm~2.0mm,优选是10μm~1.0mm,更优选是20μm~50μm,特别,更优选是28~40μm,但本发明的珠型反射体132的大小并不受限制。
在这种情况下,根据本发明的珠型反射体132在结合层120的一侧,即光入射面方向,以突出的结构被嵌入结合层120。在一个示例性实施例中,珠型反射体132其一部分被嵌入结合层120,且剩余部分则在结合层120的一侧被突出,即,突出于光入射的表面。一个示例性实施例中,珠型反射体132整个直径的1/3至2/3可被突出。具体地,突出于结合层120表面的珠型反射体132的高度(H),即,突出高度约为珠型反射体132的整个直径(D)的1/3至2/3左右。
当珠型反射体132的突出高度具有上述范围时,可具有较好的反射亮度同时可坚固地被结合至结合层120。珠型反射体132的突出高度(H)未满直径(D)的1/3时,由于珠型反射体132被过度地嵌入至结合层120,因此,珠型反射体132的折射率较低,较难确保良好的反射亮度。
此外,珠型反射体132的突出高度(H)超过直径(D)的2/3时,结合层120的珠型反射体132的结合力变弱,因此珠型反射体132不能坚固地被嵌入结合层120中,可能会脱离。即,优选是,珠型反射体132其直径的一半被嵌入结合层120,且剩余的一半突出于结合层120的表面。
此外,根据本实施例,防水涂层150被沉积在与开放型彩色反射片130的结合层120相对的一侧中,来形成反射片100的表面。现有技术的反射片仅注重确保良好的亮度,但无法防止类似湿气或雨水的水分成分或其他异物的侵入。类似湿气、雨水、异物的外部环境因子可能会侵入反射片的内部,减少反射手段的折射率,从而发生反射效率低下亮度减少的问题,不仅如此,无法解决由于异物的侵入造成反射片的内构成低下的问题。对此,在本说明书中,开放型彩色100的表面形成防水涂层150,不仅可防止湿气或雨水等水分成分,还可防止异物的侵入。
在一个示例性实施例中,防水涂层150可由硅系的防水涂剂被制成。硅系防水涂剂可使具有较低的临界表面张力的-CH3背向,且价格低廉,特别是具有可防止氯化物离子侵入的优点。构成防水涂层150的硅系防水涂剂的非限制性示例包括高分子二氧化硅(SiO2)、氟素处理的纳米二氧化硅、硅系单组分防水涂剂、以及由上述的组合。特别是,氟素处理的纳米二氧化硅,由于氟素成分,可使-CF3和-CF2-背向,从而具有可使防水特性增大的优点。更具体地,形成防水涂层150的防水剂可以是,使用具有类似的高分子二氧化硅衍生物、具有偶氮基的硅高分子开始剂,从而将丙烯酸单体中和自由基所获得的异氰酸盐硬化型硅-丙烯酸共聚物,或是丙烯酸-硅树脂和有机硅防水剂等,但本发明并不局限于此。
此外,选择性地,根据本实施例的开放型彩色反射片100可进一步包括:异型薄膜层170,在一侧按顺序沉积、形成有结合层120、反射层130、及防水涂层150的支持层110的另一侧,通过粘结层160被脱附式地形成。
粘合层160,使本实施例的开放型彩色反射片100可附着在类似消防员、警察、清洁工等执行危险工作的人所穿的衣服上、道路标识牌等基片上。特别是,在用于时装界的衣服、包、饰品、及广告用材料中十分有效。
例如,粘结层160可通过高热压方式或高频方式等被热熔附于基片上。粘结层160可使用在支持层110和异型薄膜层170之间具有附着力的任意的粘结剂。例如,粘结层160中使用的粘结剂可使用,在支持层110的另一侧被附着后可被去除的拆卸型(removabletype)粘结剂;和在支持层110的另一侧可完全被附着的永久型(permanent type)粘结剂;以及热熔型(hot melt type)等粘结剂。
例如,基片为服饰类时,考虑到服饰类等纤维制品的特征和洗涤后的维持原样等,可使用收缩性及弹性较好的热熔型粘结剂。此外,粘结剂160热熔于基片被附着时,特别优选是具有低熔点系列粘结剂。作为示例,特别是可使用聚乙烯(PE)、聚丙烯(PP)等的聚烯烃系的粘结剂,或是醋酸乙烯酯共聚物(EVA)系的低熔点粘结剂。
该粘结剂的非限制性示例可从天然树脂和/或合成树脂中被选出。例如,包括类似低密度聚乙烯(LDPE)的聚氯乙烯系粘结剂、经多羟基化合物和异氰酸酯化合物的反应被形成的聚氨酯系粘结剂、醋酸乙烯酯共聚物(EVA)系粘结剂、和聚氯乙烯(PVC)系粘结剂中被选出的一个以上的粘结剂,但是并不局限于此。根据情况,粘结层160可直接被涂至结合层120。
将根据本实施例的开放型彩色反射片100附着在基片时,为了粘结层160和基片之间的附着,可将异型薄膜层170从粘结层160中剥离、去除。为了该目的,可通过在所述异型薄膜层170的一侧形成涂有硅组成物等的异型层等方法进行异型处理。例如,异型薄膜层170可由纸材、合成树脂材、及纤维材等被构成。
例如,构成异型薄膜层170的合成树脂可从由聚酯系、聚烯烃系、聚氨酯系、聚酰亚胺系、丙烯酸系、及上述组合所构成的合成树脂中被选出。更具体地,构成异型薄膜层170的合成树脂材料,可使用从由聚对苯二甲酸乙二醇酯(PET)、聚对苯二甲酸丁二醇酯(PBT)、聚萘二甲酸乙二醇酯(PEN)、聚萘二酸丁醇酯(PBN)、聚乙烯(PE)、聚丙烯(PP)、聚氨酯(PU)、聚氯乙烯(PVC)、聚酰亚胺(PI)、聚碳酸酯(PC)、聚酰胺(PA)、醋酸乙烯酯共聚物(EVA)、及上述的共聚物构成的群中被选出的至少一个合成树脂,但本发明并不局限于此。此外,构成异型薄膜层170的纤维的非限制性示例可以是由棉纤维、聚酯纤维、尼龙纤维、人造纤维、及上述的混纺纤维等构成的织物或非织物。
根据上述第1实施例的开放型彩色反射片100可解决由于外部环境因子所造成的反射亮度低下及内构成低下的问题,并具有可体现多种底色而非灰色的优点。
在替代性的实施例中,为了体现多种底色所形成的所述结合层120的一侧可进一步具备具多种颜色或图案的印刷层240。图3是概略性地示出根据本发明的另一个实施例的开放型彩色反射片200的横截面图,反射层230的下面,即,反射层230与结合层220之间配置有印刷层240。
如图3所示出的,根据本实施例的开放型彩色反射片200包括:支持层210;结合层220,被沉积、结合在支持层的一侧;和印刷层240,被形成在结合层220的一侧;和反射层230,通过所述印刷层240被粘附在结合层220的一侧,具有多个珠型反射体232;和硅系防水涂层250,被沉积在所述反射层230的一侧。选择性地,可包括异型薄膜层270,通过所述支持层210的另一侧涂抹的粘结层260,被脱附式地形成。
根据本发明的第2实施例,开放型彩色反射片200的结构中,支持层210;结合层220;反射层230;硅系防水涂层250;粘结层260;以及异型薄膜层270的结构与图2中所示的本发明的第1实施例的开放型彩色反射片100的结构相对应并实质相同,在此省略详细说明。
根据本发明的第2实施例,以掺和有粘合树脂、多个颜料无泛黄聚乙烯和纳米珍珠粉的形态被沉积在支持层210上部的结合层220一侧,和具备有多个珠型反射体232的反射层230的另一侧之间,可形成印刷层240,其被印刷有类似文字和/或四周连续纹理的图案。
在一个示例性实施例中,所述印刷层240,可使用适当的墨水来形成四周连续纹理的图案。用于形成印刷层240中配备的四周连续纹理图案的墨水,优选是使用含有粘附成分的单组分UV硬化性墨水。当使用UV硬化性墨水时,可短时间内硬化墨水,从而不仅可颜色鲜明地印刷想要体现的文字或多种纹样等图案,还可容易地印刷出4原色全彩色的颜色,具有可自由表现颜色的优点。
例如,墨水可包含具粘附性的基础树脂、和墨引物、和溶剂。构成印刷层240的粘附性基础树脂的非限制性示例为从硅系树脂、聚氨酯(PU)系树脂、密胺树脂、聚氯乙烯(PVC)系树脂、聚乙烯醇(PVA)系树脂、丙烯酸系树脂等中被选出的至少一种粘合树脂。在一个示例性实施中,粘附性基础树脂可使用单组分UV(紫外线)硬化性粘合树脂,但是在这种情况下,构成印刷层240中所形成的图案的墨水可以是含有粘附成分的基础树脂的单组分UV墨水。
此外,墨引物可被体现为使墨水能更好地被附着于印刷层。在选择性的示例性实施中,所述墨引物可包括体现多种颜色的适当的色素体、和使色素体中包含的色素迅速扩散的润湿剂(wetting agent)、以及用于提高经墨引物印刷的图案界面特征的表面活性剂(surfactant)。在需要时,所述墨引物可进一步包括无机填充剂(inorganic filler)。在一个示例性实施例中,为了在印刷层240形成图案,以构成所使用的墨水的粘附性粘合树脂100%为基准可掺和0.1~50%的墨引物。
构成墨引物的所述色素体的颜色并不特别被限制。在一个示例性实施例中,色素体至少包括4原色C(青色)、M(红色)、Y(黄色)、和K(黑色)的色素。除此以外,色素体可进一步包含其他染料或类似颜料的其他色素体。
构成墨引物的润湿剂的非限制性示例可以是1,3-丁二醇、1,4-丁二醇、1-5-戊二醇、2-丁烯-1、4-二醇、和2-甲基-2-戊二醇等二醇类,和/或丙三醇、乙二醇、二乙二醇、三乙二醇、丙二醇、二丙二醇、己二醇等甘醇类中被选出的至少一种润湿剂。在示例性实施例中,以粘附性基础树脂100%为基准可含有0.05~30%的润湿剂。
此外,构成墨引物的表面活性剂的非限制性示例可以是从脂肪醇聚氧乙烯醚、聚氧乙烯烷基苯基醚、聚甘油脂肪酸酯、和山梨醇脂肪酸酯中被选出的至少一种表面活性剂,但本发明并不局限于此。
在示例性实施例中,以粘附性基础树脂100%为基准可含有0.05~20%的表面活性剂。构成墨引物的润湿剂和表面活性剂的含量以上述的范围被组成,不妨碍构成反射层230的珠型反射体232的反射亮度,同时以最佳状态将通过墨水印刷的图案附于印刷层240。
选择性地,墨引物可进一步包括无机填充剂。构成墨引物的无机填充剂可包括从硅、粘土、硅藻土、沸石、碳酸钙、矾土、氧化锌、氧化钛等所构成的群中被选出的至少一种,但本发明并不局限于此。在一个示例性实施中,以粘附性基础树脂100%为基准可含有0.1~10%的无机填充剂用于构成墨引物,例如,2.0μm以下的平均粒度,优选是0.01~2.0μm的平均粒度。
构成墨引物的溶剂的非限制性示例可包含从水、乙醇、丁醇、和戊醇、丁酮(MEK)、及甲苯等中被选出的至少一种溶剂。在一个示例性实施例中,以粘附性基础树脂100%为基准可含有30~150%比例的溶剂。
选择性地,墨水可进一步包括羧基纤维素的粘性调节剂。根据需要,也可进一步包括通常使用的其他添加剂成分。
与第1实施例相比较,反射层230中所具备的多个珠型反射体232以整个直径(D)的1/3至2/3露出(突出高度(H))于印刷层240的一侧的形态被嵌入至印刷层240。印刷层240的一侧嵌入有构成反射层230的多个珠型反射体232,同时印刷层240具有与珠型反射体232被嵌入的底面突出结构相对应的表面结构。据此,印刷层240中表现的多个四周连续纹理图案的可视性不会被降低。
此外,虽然在图3中,示出反射层230的底面形成有印刷层240的实施例,与此不同,印刷层也可形成在反射层的表面(即,光入射的方向)。
图4是示出根据本发明的又另一个示例性实施例的开放型彩色反射片300的概略性横截面图。参照图4,在本实施例中开放型彩色反射片300包括:支持层310;结合层320,被沉积在所述支持层210的一侧;反射层330,含有被粘附至所述结合层320一侧的多个珠型反射体332;和印刷层340,被形成在反射层330的上面;和硅系防水涂层350,被涂在印刷层340的上面;以及选择性的异型薄膜层370,通过支持层310的另一侧所配置的粘结层360,被脱附式地形成。
与图3中所示出的第2实施例相比较,本实施例的开放型彩色反射片300,反射层330的表面形成有印刷层340,印刷有文字或多种四周连续纹理图案。根据本实施例,对于具有多个珠型反射体332的反射层330,印刷层340以光入射的方向形成在珠型反射体332的突出面。由于珠型反射体332所对应的表面曲线结构,就算反射层330的表面形成有印刷层340,反射亮度也不会被降低。同时,印刷层340中形成的四周连续纹理图案等图案或图形可具有良好的可视性,因此,在远距离也可容易地识别印刷层340上所形成的图案或图形。
此外,如图3、4中分别示出的,反射层230、330的上面或下面形成印刷层240、340,从而形成多种颜色的文字或四周连续纹理等图案时,根据掺和有多种有机颜料和/或荧光颜料的结合层220、320的多种颜色和交叉方向,具有两层的阶梯式色彩被着用的立体质感这一优点。同时,在需要的情况下,结合层220、320和反射层230、330之间,以及反射层230、330和防水涂层250、350之间都形成有印刷层,从而具有三层的阶梯式色彩被着用的立体质感这一优点。
特别是,本发明的开放型彩色反射片100、200、300中,反射层130、230、330的表面沉积有防水涂层150、250、350,以及印刷层340以与珠型反射体132、232、332相对应的曲线结构被形成。据此,反射片100、200、300中,光入射的表面具有与珠型反射体132、232、332相似的突出结构,因此可具有优秀的反射亮度。特别是,印刷层340的高度可确保可视性,具有可容易地识别印刷层340中所形成的图形的优点。
[彩色反射片制备方法]
以下参照图5,对本发明的开放型彩色反射片的制备工程进行说明。
如图5所示,根据本发明的开放型彩色反射片制备工程科包括以下步骤:准备适当材料的支持层(步骤S510);在支持层的一侧(上面)沉积结合层(步骤S520);选择性地,在结合层的一侧形成第1印刷层(步骤S530);在结合层或印刷层的表面粘附反射层(步骤S540);选择性地,在反射层的一侧形成第2印刷层(步骤S550);在反射层或第2印刷层的表面沉积防水涂层(步骤S560);选择性地,在支持层的另一侧(底面)涂上粘结层(步骤S570),以及粘结层的另一侧附着异型薄膜层(步骤S580)。
首先,准备适当材料的的支持层110、210、310(步骤S510),支持层110、210、310可使用透明、半透明、或不透明材质,来作为可支持本发明的开放型彩色反射片100、200、300的材料。在一个示例性实施例中,支持层110、210、310的材料可使用由纤维类、纸类、皮革类及合成树脂,或是以量子点屏障(quantum dot barrier)制备的薄膜类构成的群中被选出的至少一种材料。支持层110、210、310的厚度可根据选择的材料进行适当的选择。
支持层110、210、310的一侧(上面,即,光入射的片表面)可沉积结合层120、220、320(步骤S520),所述结合层被掺和有适当的粘合树脂、有色和/或荧光颜料,优选是,无泛黄颜料、无泛黄聚氨酯、和纳米珍珠粉等。根据本发明的结合层120、220、320包含白色、黄色、赤色、青色、绿色、紫色、黑色等多种无泛黄颜料和/或荧光颜料,可体现多种底色,而不是现有技术中使用的金属性浆。此外,由于使用无泛黄材料,因此可防止褪色,增加可视性。
此外,支持层120、220、320中掺和的无泛黄聚氨酯和粘合树脂,可防止反射层130、230、330中多个珠型反射体132、232、332脱离的现象,由于使用纳米珍珠粉材料,可增强光的反射效率。在一个非限制性实施例中,为了体现多种颜色,掺和有颜料及粘合树脂等的结合层120、220、320的厚度可约为10~100μm,优选是20~80μm,更优选是30~70μm,被涂抹、沉积在支持层110、210、310的一侧。
此外,选择性地,在结合层220的一侧形成印刷层240,在反射片上附于文字和/或四周连续纹理等多种图案(步骤S530)。如上所述,由于结合层220中掺和的颜料成分,反射片中可体现多种底色,由于形成印刷层240,因此可体现两层的动感及立体质感。印刷层240中可使用硬化性墨水来形成图案,例如,单组分UV硬化性墨水。
如上所述,墨水可包括粘结性基础树脂、色素体、润湿剂、和表面活性剂、以及含有选择性的无机颜料的墨引物、和溶剂。用于在印刷层240形成图案的一个示例性方法可以是,将基础树脂和含有4原色色素体的墨引物混合,从而获得配料后,将该配料和适当的硬化剂(例如UV硬化剂)以约100:5~10的重量比混合,获得混合物,并在甲苯与丁酮(MEK)以4:6~6:4的重量比被混合的稀释溶剂中将该混合物稀释,所获得的墨水被用于印刷。在这种情况下,墨水可通过以下的比列被混合:配料与硬化剂的混合物为60~70%,且稀释溶剂为30~40%。
印刷层240可通过多种色彩和纹理等以多种图案或图形的形态被体现、表现。印刷层240中可体现的图案或图形并不特别被局限,例如,可通过文字、图形、图画、照片或上述的组合被体现。作为一个示例,图6中示出印刷层240,以四周连续纹理形态的花纹图案被体现。在一个示例性实施例中,印刷层240的厚度可以是珠型反射体232突出高度(H)的1/2以下。选择性地,结合层220的一侧所形成的印刷层240,其以约0.1~100μm的厚度被涂抹、印刷,优选是0.5~10μm,更优选是0.5~3μm。当印刷层240的厚度在上述范围以下时,较难识别图形,且超过上述范围时则较难形成曲线结构。
将印刷层240形成在结合层220一侧的方法并不特别被局限,可使用多种涂抹或印刷方法。在一个示例性实施例中,印刷层240可通过UV胶印、UV凹版印刷、UV灼印、数码实写输出(溶解、水性、UV等)、印刷的图形的升华或转录等方法被形成,但本发明的印刷层240的形成方法并不局限于此。
在示例性实施例中,结合层230的一侧形成有印刷层240时,其上所沉积的反射层230可稳定地被沉积在多种颜料被掺和的结合层230和图案图形被体现的印刷层240的上面。同时,在反射层240的另一侧(底面)可按顺序地形成体现出不同颜色的结合层220和印刷层240,因此可提供视觉上的不同质感。
然后,在掺和有粘合树脂、颜料、无泛黄聚氨酯、和纳米珍珠粉材料及为了体现多种底色所形成的结合层120、220、320,或印刷层240、340的一侧结合形成具有多个珠型反射体130、230、330(步骤S540)。在这种情况下,如上所述,多个珠型132、232、332以整个直径(D)的1/3至2/3突出于结合层120、220、320或印刷层240表面的形式被嵌入,在增大反射亮度的同时,可防止珠型反射体132、232、332的脱离。
在一个示例性实施例中,构成反射层130、230、330的珠型反射体132、232、332的直径(D)约为1.0μm~2.0mm,优选是10μm~1.0mm,更优选是20μm~50μm,特别更优选是28~40μm,但本发明并不局限于此。反射层130、230、330可通过与现有技术中形成含珠型反射体的反射层相同的方法被形成。
例如,如图6所示出的,支持层210的一侧所附着的结合层220的另一侧形成有印刷层240的情况下,可涂抹类似PET薄膜的适当的剥离剥离或载体薄膜236上可被脱附的具有粘合性的树脂,从而形成分离层,然后在分离层上将珠型反射体232以适当的深度嵌入。然后,在印刷层240的一侧粘附具珠型反射体232的反射层230之后,经熟成过程使载体薄膜236和分离层与珠型反射体232分离,从而在印刷层240的一侧形成反射层230(参照图7b的横截面图)。
在将反射层130、230直接结合在结合层120、220的一侧时,也可使用以下方法,在载体薄膜上涂抹树脂,形成分离层,并在分离层以适当的深度嵌入珠型反射体132、232后,在结合层120、220的一侧粘附具珠型反射体132、232的反射层130、230之后,经熟成过程使载体薄膜136、236和分离层与珠型反射体132、232分离(参照图7a,7b的横截面图)。
选择性地,在一个示例性实施例中,结合层120、220和反射层130、230直接接触的情况下,其可形成反射薄膜。在这种情况下,在载体薄膜136、236上涂抹粘附性树脂,并在分离层上嵌入珠型反射体132、232。然后,珠型反射体132、232上涂抹掺和有多种颜料、粘合剂树脂、无泛黄聚氨酯等的结合及,从而形成结合层120、220,并可利用载体薄膜136、236和分离层与珠型反射体132、232分离的方法(参照图6a的横截面图)。
然后,选择性地,在形成有反射层130、230、330的表面可形成第二印刷层340(步骤S550以及参照图8)。第二印刷层340的形成方法可与第一印刷层240的方法实质相同,在此省略详细说明。结合层120、220、320中所体现的多种底色,选择性的下部印刷层240中所体现的图案图形等的作用及反作用的结果,可对上部印刷层340中的图案图形体现出颜色的立体感及质感。
上部印刷层340的厚度可以是珠型反射体332的突出高度(H)的1/2以下。选择性地,结合层320,结合层320的一侧所形成的印刷层340,其以约0.1~100μm的厚度被涂抹、印刷,优选是0.5~10μm,更优选是0.5~3μm。用于将印刷层340形成在结合层320一侧的方法并不特别被局限,可是使用多种涂抹或印刷的方法。
此外,在反射层130、230或选择性的上部印刷层340的表面沉积防水涂层150、250、350(步骤S560)。由于形成防水涂层150、250、350,因此可解决类似雨水、湿气等水分成分或异物的侵入的外部环境原因而造成的反射亮度低下,内构成减少及可视性减少的问题。根据示例性实施例,构成防水涂层150、250、350的防水涂剂可以是硅系。例如,高分子二氧化硅(SiO2)、氟素处理的纳米二氧化硅、硅系单组分防水涂剂、以及由上述的组合。在一个示例性实施例中,防水涂层150、250、350以0.1~100μm的厚度被涂抹、印刷,优选是0.5~10μm,更优选是0.5~3μm。
此外,选择性地,可利用具适当粘附力的粘附剂在支持层110、210、310的另一侧(底面)涂抹粘结层160、260、360(步骤S570)。可使用的粘结剂的示例包括:可去除类型、永久性类型、或热熔类型。粘结层160、260、360的厚度并不特别被局限,可约为1~100μm,优选是5~80μm、更优选是10~50μm。
此外,在粘结层160、260、360的另一侧(底面)附着可脱附的异型薄膜层170、270、370(步骤S580)。在将开放型彩色反射片100、200、300附着在基片上时,为了粘结层160、260、360和基片之间的附着,需要将粘结层160、260、360剥离、去除,因此,可在异型薄膜层170、270、370的一侧形成涂有硅组合物的异型层。异型薄膜层170、270、370的材料可由纸类、合成树脂、及纤维材料构成,根据材料可适当地调节其厚度。
在示例性实施例中,根据本发明的开放型彩色反射片100、200、330可通过附着的形式被用于基片上。基片并不特别被限制,可以是危险场所中工作的工作人员的服饰、鞋子、包、印刷物、道路、标示牌、各种广告等。例如,可以是基片平板上的物体、或是印刷物、广告用屏幕、服饰、包等。
根据本发明的开放型彩色反射片100、200、300可通过缝制或粘附等方法被附于基片上,或是将以一定形态被加工的反射片100、200、300的最边缘缝制在基片的表面来进行附着。例如,本发明的反射片100、200、300可通过高频率或高热过程被热熔,从而被粘附。热熔粘附可通过支持层110、210、310的底面所涂抹的粘结层160、260、360被体现。
上述中,基于本发明的示例性实施例及示例对本发明进行了说明,但本发明并不局限于在此所述的实施例及示例。本发明所属技术领域中的普通技术人员可通过上述实施例及示例容易地进行多种变形和修改。但该变形和修改由后附的权利要求范围以及权利要求范围等同内容定义。
符号说明
100,200,300:彩色反射片 110,210,310:支持层
120,220,320:结合层 130,230,330:反射层
132,232,332:珠型反射体 150,250,350:防水涂层
160,260,360:粘结层 170,270,370:异型薄膜层
240,340:印刷层
Claims (14)
1.一种开放型彩色反射片,包括:
支持层;
结合层,被沉积在所述支持层的一侧,含有粘合树脂、颜料和无泛黄聚氨酯;
反射层,被粘附至所述结合层,含有多个珠型反射体;和
硅系防水涂层,被沉积在所述反射层的一侧。
2.根据权利要求1所述的开放型彩色反射片,进一步包括:印刷层,被形成在所述结合层和所述反射层之间,或所述反射层和所述防水涂层之间中的至少一处。
3.根据权利要求2所述的开放型彩色反射片,其中,所述印刷层包括具有粘附成分的单组分紫外线油墨。
4.根据权利要求1所述的开放型彩色反射片,其中,所述防水涂层包括高分子二氧化硅、氟素处理的纳米二氧化硅、硅系单组分防水涂剂、以及由上述的组合构成的群中被选出的硅系防水涂剂。
5.根据权利要求1所述的开放型彩色反射片,所述结合层中包含的所述颜料包括:有色颜料和荧光颜料,其中所述有色颜料,从由白色颜料、黄色颜料、赤色颜料、青色颜料、绿色颜料、紫色颜料和黑色颜料构成的群中选出至少一个。
6.根据权利要求1所述的开放型彩色反射片,其中,所述多个珠型反射体,以整个直径的1/3至2/3被露于所述结合层一侧的形态,嵌入至所述结合层。
7.根据权利要求1所述的开放型彩色反射片,其中,所述支持层,由纤维类、纸类、皮革类、合成树脂、或是以量子点屏障制备的薄膜类构成的群中被选出的材料形成。
8.根据权利要求1-7中任何一项所述的开放型彩色反射片,进一步包括:异型薄膜层,通过所述支持层的另一侧所粘附的粘结层脱附式地被形成。
9.一种开放型彩色反射片制备方法,包括以下步骤:
在准备的支持层的一侧,沉积至少含有粘合树脂、颜料和无泛黄聚氨酯的结合层;
在所述结合层的一侧,粘附含有多个珠型反射体的反射层;以及
在所述反射层的一侧,沉积硅系防水涂层。
10.根据权利要求9所述的开放型彩色反射片制备方法,进一步包括以下步骤:在所述结合层和所述反射层之间或所述反射层和所述防水涂层之间中的至少一处形成印刷层。
11.根据权利要求10所述的开放型彩色反射片制备方法,其中,所述印刷层,通过使用具有粘附成分的单组分紫外线油墨被形成。
12.根据权利要求9所述的开放型彩色反射片制备方法,其中,所述防水涂层包括高分子二氧化硅、氟素处理的纳米二氧化硅、硅系单组分防水涂剂、以及由上述的组合构成的群中被选出的硅系防水涂剂。
13.根据权利要求9所述的开放型彩色反射片制备方法,其中,在所述结合层的一侧粘附所述反射层的步骤中,将构成所述反射层的所述多个珠型反射体,以整个直径的1/3至2/3被露于所述结合层一侧的形态,嵌入至所述结合层。
14.根据权利要求9所述的开放型彩色反射片制备方法,其中,所述支持层,由纤维类、纸类、皮革类、合成树脂、或是以量子点屏障制备的薄膜类构成的群中被选出的材料形成。